KARAKTERISASI DAN PEMANFAATAN STYROFOAM SEBAGAI PENGGANTI SEBAGIAN PASIR UNTUK BAHAN BANGUNAN SKRIPSI NUR AYU RAMADHANI

Transkripsi

1 KARAKTERISASI DAN PEMANFAATAN STYROFOAM SEBAGAI PENGGANTI SEBAGIAN PASIR UNTUK BAHAN BANGUNAN SKRIPSI Diajukan untuk melengkapi dan memenuhi syarat mencapai gelar Sarjana Sains NUR AYU RAMADHANI DEPARTEMEN FISIKA FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA MEDAN 2009

2 PERSETUJUAN JUDUL : KARAKTERISASI DAN PEMANFAATAN STYROFOAM SEBAGAI PENGGANTI SEBAGIAN PASIR UNTUK BAHAN BANGUNAN Kategori : SKRIPSI Nama ; NUR AYU RAMADHANI Nomor Induk Mahasiswa : Program studi : SARJANA (SI) FISIKA Departemen : FISIKA Fakultas : MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) UNIVERSITAS SUMATERA UTARA Diluluskan di Medan, Mei 2009 Diketahui/disetujui oleh Ketua departemen Fisika FMIPA USU Pembimbing (Dr. Marhaposan Situmorang) (Prof. Dr. Timbangen Sembiring,Msc) NIP : NIP :

3 PERNYATAAN KARAKTERISASI DAN PEMANFAATAN STYROFOAM SEBAGAI PENGGANTI PASIR UNTUK BAHAN BANGUNAN SKRIPSI Saya mengakui bahwa skripsi ini adalah hasil kerja sendiri, kecuali beberapa kutipan dan ringkasan ringkasan yang masing masing disebutkan sumbernya Medan, Mei 2009 Nur Ayu Ramadhani

4 PENGHARGAAN Segala puji dan syukur penulis panjatkan kepada Allah S.W.T yang maha pemurah dan maha penyayang, dengan limpahan karunia-nya sehingga skripsi ini dapat diselesaikan. Ucapan terima kasih saya sampaikan kepada Prof.Dr.Timbangen Sembiring, selaku pembimbing, dan Bachtiar ST selaku pembimbing lapangan pada penyelesaian skripsi ini yang telah memberikan panduan dan penuh kepercayaan kepada saya untuk menyempurnakan skripsi ini. Ucapan terimaksih juga saya ajukan kepada ketua departemen Fisika FMIPA USU Dr. Marhaposan Situmorang dan sekretaris departemen Fisika FMIPA USU Dra. Yustinon. Ms. Dekan dan Pembantu Dekan FMIPA USU. Ucapan terimakasih juga saya sampaikan kepada karyawan PTKI yang banyak memberikan masukan untuk penyempurnaan skripsi ini. Teman teman saya, Khai, Ucil, Aise, Risma, Bryan dan seluruh mahasiswa fisika khususnya stambuk 2003 terima kasih atas semangat dan motivasinya. Akhirnya tidak terlupakan dan yang teristimewa kepada Ayahanda eddy Syahputra (Alm). Ibunda Ratna Dewi Harahap. Abangda Dedy, Kakak saya Rini Meilina, Adik saya M.Maulana Serta semua sanak keluarga. Terimakasih atas dukungan, bantuan dan semangat yang kalian berikan kepada saya selama ini. Semoga Allah SWT akan membalasnya. Penulis

5 ABSTRAK Telah dilakukan pembuatan beton ringan dengan penambahan limbah styrofoam. Pembentukan sampel dilakukan dengan menggunakan cetakan dan mengalami masa aging selama 7,14,21 dan 28 hari. Karakterisasi meliputi analisa kuat tekan, porositas dan penyerapan air. Kuat tekan beton tanpa styrofoam berkisar : (6,72 MPa 10,71 MPa), dengan 5% styrofoam : (2,76MPa 7,60MPa), dengan 10% styrofoam : (0,73 MPa-1,56 MPa), dengan 15% styrofoam berkisar (0,4 MPa 1,06 MPa). Kuat tekan mortar tanpa styrofoam berkisar (12,08 MPa 18,94 MPa), dengan 5% styrofoam (1,4 MPa 4,56 MPa), dengan 10% styrofoam kuat tekan mortar berkisar (1,02 MPa 2,76 MPa), dan dengan 15% styrofoam kuat tekan mortar berkisar (0,39 MPa 1,56 MPa). Penyerapan air untuk beton styrofoam dan mortar styrofoam berkisar (15,56% - 43,96%) dan (33,24% - 39,53%), sedangkan penyerapan air beton normal dan mortar normal adalah 5,98% dan 9,31%. Porositas untuk beton styrofoam dan mortar styrofoam berkisar (23,58% - 26,60%) dan (25,29% - 29,93%), sedangkan porositas beton normal dan mortar normal adalah 15,51% dan 22,86%.

6 ABSTARCT A Research on making lightweight concrete by adding industrial waste Styrofoam. Forming sample used template and angingtime was carriedout for 7,14,21 and 28 days. Charactirized by the strength pressure, porosity and water absorbtion analytis. The strength pressure lightweight concrete without Styrofoam was : (6,72 MPa 10,71 MPa), with 5% Styrofoam was : (0,276 MPa 0,760 MPa), with 10% Styrofoam was : (0,073 MPa 0,156 MPa) and with 15% Styrofoam was : (0,04 MPa 0,106 MPa). The strength pressure mortar without Styrofoam was : (12,08 MPa 18,94 MPa), with 5% Styrofoam was : (0,14 MPa 0,456 MPa), with 10% Styrofoam was : (0,102MPa 0,276MPa) and with 15% Styrofoam was : (0,039MPa -0,156MPa). The water absorbtion of lightweight concrete and mortar with Styrofoam was : (15,56% - 43,96%) and (33,24% - 39,53%), then the water absorbtion of normal concrete and normal mortar was 5,98% and 9,31%. The porosity of lightweight concrete with Styrofoam and mortar Styrofoam was (23,58% - 26,60%) and (25,29% - 29,93%), then the porosity of normal concrete and normal mortar was 15,51% and 22,86%.

7 DAFTAR ISI Halaman Persetujuan...i Pengharagaan...ii Abstrak iii Daftar isi..iv Daftar tabel...v Daftar gambar..vi BAB I. PENDAHULUAN 1.1 Latar Belakang Batasan Masalah Tujuan penelitian Manfaat Penelitian Tempat Penelitian Sistematika Penulisan.4 BAB II. TINJAUAN PUSTAKA 2.1 Beton Mortar Semen Semen Portland Agregat Agregat Halus Agregat Kasar Air Styrofoam Pengujian Sampel Pengujian Kuat Tekan Pengujian Penyerapan Air Pengujian Porositas..17 BAB III METODOLOGI PENELITIAN 3.1 Alat dan Bahan Peralatan Bahan Bahan Metodologi Penelitian Diagram Alir Pembuatan Beton Normal Diagram Alir Pembuatan Beton Styrofoam Diagram Alir Pembuatan Mortar Normal Diagram Alir Pembuatan Mortar Styrofoam

8 3.3 Prosedur Pembuatan Benda Uji Beton Prosedur Pengujian Kuat tekan Beton Prosedur Pengujian Penyerapan Air Prosedur Pengujian Porositas Prosedur Pembuatan Benda Uji Mortar Prosedur Pengujian Kuat Tekan Mortar Prosedur Pengujian Penyerapan Air Mortar Prosedur Pengujian Porositas Mortar...29 BAB IV HASIL DAN PEMBAHASAN 4.1 Analisa Data Pengujian Kuat Tekan Pengujian Kuat Tekan Beton Pengujian Kuat Tekan Mortar Pengujian Penyerapan Air Pengujian Penyerapan Air Beton Pengujian Penyerapan Air Mortar Pengujian Porositas Pengujian Porositas Beton Pengujian Porositas Mortar..48 BAB V KESIMPULAN DAN SARAN 5.1 Kesimpulan Saran..54 DAFTAR PUSTAKA..55 LAMPIRAN

9 DAFTAR TABEL Halaman Tabel 2.4 Batas dan izin air untuk campuran beton...15 Tabel 4.1 Data Hasil Pengujian Kuat Tekan Beton Dengan Waktu Pengeringan 7 hari 30 Tabel 4.2 Data Hasil Pengujian Kuat Tekan Beton Dengan Waktu Pengeringan 14 hari..31 Tabel 4.3 Data Hasil Pengujian Kuat Tekan Beton Dengan Waktu Pengeringan 21 hari..33 Tabel 4.4 Data Hasil Pengujian Kuat Tekan Beton Dengan Waktu Pengeringan 28 hari..34 Tabel 4.5 Data Hasil Pengujian Kuat Tekan Mortar Dengan Waktu Pengeringan 7 hari 38 Tabel 4.6 Data Hasil PengujianKuat Tekan Mortar Dengan Waktu Pengeringan 14 hari..39 Tabel 4.7 Data Hasil Pengujian Kuat Tekan Mortar Dengan Waktu Pengeringan 21 hari..40 Tabel 4.8 Data Hasil Pengujian Kuat Tekan Mortar Dengan Waktu Pengeringan 28 hari..42 Tabel 4.9 Data Hasil Pengujian Penyerapan Air Beton...45 Tabel 4.10 Data Hasil Pengujian Penyerapan Air Mortar...46 Tabel 4.11 Data Hasil Pengujian Porositas Beton Tabel 4.12 Data Hasil Pengujian Porositas Mortar..48

10 DAFTAR GAMBAR Halaman Gambar 4.1 Grafik kuat tekan beton terhadap komposisi campuran Styrofoam Gambar 4.2 Grafik kuat tekan mortar terhadap komposisi campuran Styrofoam 44 Gambar 4.3 Grafik pengujian porositas dan penyerapan air beton terhadap Komposisi campuran Styrofoam...50 Gambar 4.4 Grafik pengujian porositas dan penyerapan air mortar terhadap Komposisi campuran Styrofoam