MECHANICAL PROPERTIES OF CONCRETE MIXED WITH WASTE GLASS
|
|
- Lanny Lesmono
- 7 tahun lalu
- Tontonan:
Transkripsi
1 MECHANICAL PROPERTIES OF CONCRETE MIXED WITH WASTE GLASS THESIS Arranged By: HAMED.A.EMHEMED ABUSHAREB S POST GRADUATE PROGRAM MASTER PROGRAM IN CIVIL ENGINEERING UNIVERSITAS MUHAMMADIYAH SURAKARTA 2015 i
2 MECHANICAL PROPERTIES OF CONCRETE MIXED WITH WASTE GLASS Arranged by: HAMED.A.EMHEMED ABUSHAREB S This thesis approved 11 March 2015 by. ii
3 iii
4 iv
5 Abstract The study of waste glass (WG) concrete mix was done to study mechanical properties of concrete mix with target characteristics strength 30MPa at 28 days age. The laboratory experimental study was conducted at Muhammadiyah University between October and December 2014,to find out the high strength and amount for Waste Glass as fine aggregates replacement in a concrete mix. Also alkali silica reaction (ASR) was determined by expansion test. For mechanical properties compressive strength, flexural strength and modulus of elasticity (MOE) were determined. All measurement was done in accordance to ASTM standard methods. Three sample content types of 10%, 15% and 20% concrete mix containing waste glass and control 0% concrete mix were prepared, casted and cured for 28 days before determination of mechanical properties, and mortar bar were caste and cured for 14 days for ASR determination. Results showed that highest measured characteristics strength was 30.72MPa, for flexural strength was 6.8MPa and for modulus of elasticity was 37.42MPa, and the high expansion test was 28% compared to control concrete mix. For the amount waste glass replacement was determined in relation to high characteristics strength yield which was found at 10% WG replacement. The conclusion reached to this study were; Maximum characteristic strength for glass concrete mix was reached with 10% fine aggregate replaced was 30.72Mpa at 28 days age. While for ASR,fine aggregate replacement by waste glass showed expansion at all amount replaced. v
6 Abstract Studi tentang limbah kaca (WG) beton dilakukan untuk mempelajari sifat mekanik beton dengan karakteristik sasaran kekuatan 30MPa pada 28 hari usia. Laboratorium Penelitian eksperimental dilakukan di Universitas Muhammadiyah antara Oktober dan Desember 2014, untuk mengetahui kekuatan tinggi dan jumlah Limbah Kaca sebagai pengganti agregat halus dalam campuran beton. Juga silika reaksi alkali (ASR) ditentukan dengan uji ekspansi. Untuk sifat mekanik kuat tekan, kuat lentur dan modulus elastisitas (MOE) ditentukan. Semua pengukuran dilakukan sesuai dengan metode standar ASTM. Tiga jenis konten sampel dari 10%, 15% dan 20% campuran beton yang mengandung limbah kaca dan kontrol 0% campuran beton siap, dicor dan sembuh selama 28 hari sebelum penentuan sifat mekanik, dan bar mortir yang kasta dan sembuh selama 14 hari untuk Penentuan ASR. Hasil penelitian menunjukkan bahwa kekuatan karakteristik diukur tertinggi adalah 30.72MPa, lentur adalah 6.8MPa dan modulus elastisitas adalah 37.42MPa, dan uji ekspansi tinggi adalah 28% dibandingkan dengan kontrol campuran beton. Untuk penggantian kaca jumlah limbah ditentukan dalam kaitannya dengan hasil kekuatan karakteristik tinggi yang ditemukan pada 10% pengganti WG. Kesimpulan yang dicapai penelitian ini adalah; Kekuatan karakteristik maksimum untuk kaca beton dicapai dengan 10% agregat halus diganti adalah 30.72Mpa pada 28 hari usia. Sedangkan untuk ASR, penggantian agregat halus oleh kaca limbah menunjukkan ekspansi di semua jumlah yang diganti. vi
7 بسم الله الرحمن الرحیم ACKNOWLEDGEMENT First and foremost, want thank Allah I would like to express my sincere thanks and appreciation to my mother, and academic supervisors Assoc.Dr. Mohamad Solikin and Dr.Ir. Sri Sunarjono who continuously guided me throughout every step of my study and generously shared their time and knowledge with me. My special thanks must be extended to technical staff members post graduate program master program in civil engineering MUHAMMADIYAH UNIVERSITY SURAKARTA Million words of thanks for fellow friends who showed their Concern and support all the way. Abdullah.their views and tips are useful indeed. Unfortunately, it is not possible to list all of them in this limited space. vii
8 TABLE OF CONTENT CHAPTER I BACKGROUND Introduction Problems statement Hypothesis Objectives Scope of Study Justification, Significance or Benefit Methodology of the study. 8 CHAPTER II LITERETURE REVIEW AND BASIC THEORY Literature Review Previous Studies on Waste Glass Uses in a Concrete Mixture Basic Theory Concrete Cement Water Aggregates Admixtures Pozzolans Glass Waste glass Alkali Silica Reaction ASR Mechanism..21 CHAPTER III RESEARCH METHODOLOGY Research Explanation Introduction Location and Time.23 viii
9 3.1.3 Data collection techniques Testing For Material Cement Aggregates Glass Water Mix Design Of Concrete Concrete mix Design target strength 30 MPa for 28 days age Method selection Determination of the Mean Target Strength (Ft) Procedure for Mix Design Slump Test Making and Curing of cube Testing for Specimens Plan and Methods Compressive strength test Flexural strength testing Modulus of elasticity Alkali-Silica Reaction (ASR) Test Matrix Of Specimens Data Analysis Methods.. 42 CHAPTER IV RESULT ANDDISCUSSION Introduction Material Properties Tests Cement Natural Coarse Aggregate Test Fine Aggregate Test..48 ix
10 4.2.4 Waste Glass Aggregate Test Mixing, Slump test, Molding and Curing Mix Proportion Mixing and Molding Curing Slump Test Testing for specimens Compressive Strength Flexural Strength Modulus of Elasticity Alkali Silica Reaction (ASR) ASTM C 227and C Comparison between the Measured Mechanical Properties...69 CHAPTER V Conclusion Suggestion. 73 REFERENCE 74 x
11 LIST OF TABLE Table.2.1 shows approximate compositions and the corresponding uses of various common forms of glass..19 Table 3.1 Table 3.2 Table 3.3 Table 3.4 Table 3.5 Table 3.6 General Properties and Composition of OPC Type The Grading requirement for Fine aggregate as designated by ASTM C Grading Requirement for Coarse Aggregates as designated by ASTM C Glass chemical composition. 29 Given Concrete Data Description Recommended values of slump for various types of construction as given by A CI (reapproved 2002). 32 Table 3.7 Approximate requirements for mixing water and air content workability and nominal maximum sizes of aggregates according to ACI Table. 3.8 Relation between water/cementation material ratio average compressive strength of concrete, according to ACI (reapproved 2002 ) Table 3.9 Dry bulk volume of coarse aggregate per unit volume of concrete as given by ACI (reapproved 2002) Table 3.10 Concrete mix design outputs at 30 MPa Table 3.11 Concrete mix design materials description Table.3.12 Table.3.13 for Variables Parameters Matrix for Specimens Description.. 42 Table Batch Material Proportioning...43 Table. 4.1 Test, Standard and Samples Specimens.. 44 xi
12 Table 4.2 Table 4.3 Table 4.4 Table 4.5 Table 4.6 Table. 4.7 Table 4.8 Table 4.9 Table 4.10 Table 4.11 Table 4.12 Table: 4.13 Table 4.14 Coarse Aggregate Test Result.. 45 Gradation of Coarse Aggregate Fine aggregate test result Gradation of Fine Aggregate 49 Fine aggregate test result. 50 Fine Aggregates (Glass) Gradation. 51 Mixtures Proportion. 53 Slump Test Result description Characteristic Strength (MPa) Flexural Strength (MPa) at 28 days Modulus of Elasticity (MOE) at 28 days as ASTM C Mortar Mixtures proportions used for ASTM C 1260 (ASR test)..65 ASTM C 1260 Expansion Test Results Table: Comparison of Measured Mechanical Properties.70 xii
13 TABLE OF FIGURE Figure: 3.1. Flow chart for procedures for making waste glass concrete mix and experimental testing 25 Figure: 3.2. Flow chart showing the procedure for preparation of waste glass fine aggregate 26 Figure 4.1 Figure: 4.2 Figure: 4.3 Figure: 4.4 Figure 4.5 Coarse aggregates gradation Fine aggregates gradation Glass Sieve gradation as in accordance to ASTM C Slump test for Fresh prepared WG concrete mix Characteristic Strength of WG concrete at 28 Days 58 Figure. 4.6 Flexural Strength of WG concrete mix 61 Figure: 4.7 Figure 4.8 MOE WG concrete for 28 days age. Research Result ( Graphical illustration of ASR expansion test Results xiii
14 APPENDIX LEST. APPENDIX A : NCA and NFA and GA tests. APPENDIX B : Slump test APPENDIX C: Compressive strengths test. APPENDIX D: Flexural strengths test. APPENDIX E: Modulus of elasticity test. APPENDIX F: Alkali-Silica Reaction (ASR) test. APPENDIX G: Pictures of the Tests from the Laboratory xiv
EFFECT OF RECYCLED COARSE AGGREGATE ON CONCRETE PROPERTIES
EFFECT OF RECYCLED COARSE AGGREGATE ON CONCRETE PROPERTIES Thesis Arranged By: FATHEI RAMADAN SALEH LAMEIN S100130012 POST GRADUATE PROGRAM MASTER PROGRAM IN CIVIL ENGINEERING MUHAMMADIYAH UNIVERSITY SURAKARTA
Lebih terperinciTHE USE OF POLYMER MODIFIED BITUMEN FOR THIN SURFACING AT HOT AND ARID REGION
THE USE OF POLYMER MODIFIED BITUMEN FOR THIN SURFACING AT HOT AND ARID REGION T HESIS Submitted to the Post Graduate of Civil Engineering Program in Partial Fulfillment of the Requirements for the Degree
Lebih terperinciMECHANICAL PROPERTIES OF CONCRETE USING COARSE AND FINE RECYCLED CONCRETE AGGREGATES Buen Sian 1, Johannes Adhijoso Tjondro 1 and Sisi Nova Rizkiani 2 1 Department of Civil Engineering, Parahyangan Catholic
Lebih terperinciPERBANDINGAN KUAT TEKAN BETON MENGGUNAKAN AGREGAT JENUH KERING MUKA DENGAN AGREGAT KERING UDARA
Perbandingan Tekan.. Kering Udara PERBANDINGAN KUAT TEKAN BETON MENGGUNAKAN AGREGAT JENUH KERING MUKA DENGAN AGREGAT KERING UDARA Dosen Jurusan Teknik Sipil, Fakultas Teknik, Universitas Janabadra, Yogyakarta
Lebih terperinciABSTRACT. Key word: listening, running dictation
ABSTRACT Aftina, Esti. 2012. The Listening Ability of Tenth Grade Students of SMA N 2 Kudus Taught by Using Running Dictation In The Academic Year 2012/2013. Skripsi: English Education Department Teacher
Lebih terperinciEXPERIMENT OF EARLY AGE CONCRETE WITH FLY-ASH USING HIGH-STRENGTH DESIGN
EXPERIMENT OF EARLY AGE CONCRETE WITH FLY-ASH USING HIGH-STRENGTH DESIGN Final Project Submitted to comply with one the requirement Behavior Muhammadiyah University of Surakarta Submitted by : BINTAR TRY
Lebih terperinciSTUDI EKSPERIMENTAL PENGARUH CAMPURAN LIMBAH KULIT KERANG TERHADAP MUTU KUAT TEKAN BETON f c = 25 MPa DAN KETAHANANNYA TERHADAP REMBESAN AIR LAUT
STUDI EKSPERIMENTAL PENGARUH CAMPURAN LIMBAH KULIT KERANG TERHADAP MUTU KUAT TEKAN BETON f c = 25 MPa DAN KETAHANANNYA TERHADAP REMBESAN AIR LAUT Metta Sridevi Simokar NRP: 0821004 Pembimbing: Winarni
Lebih terperinciPENGARUH PERBANDINGAN AGREGAT HALUS DENGAN AGREGAT KASAR TERHADAP WORKABILITY DAN KUAT TEKAN BETON
PENGARUH PERBANDINGAN AGREGAT HALUS DENGAN AGREGAT KASAR TERHADAP WORKABILITY DAN KUAT TEKAN BETON Arusmalem Ginting Staf Pengajar Jurusan Teknik Sipil, Fakultas Teknik, Universitas Janabadra, Yogyakarta
Lebih terperinciPENGARUH PENGGUNAAN SERBUK KACA SEBAGAI BAHAN SUBSTITUSI AGREGAT HALUS TERHADAP SIFAT MEKANIK BETON
Volume 1, No. 1, Oktober 214, 1 11 PENGARUH PENGGUNAAN SERBUK KACA SEBAGAI BAHAN SUBSTITUSI AGREGAT HALUS TERHADAP SIFAT MEKANIK BETON Johanes Januar Sudjati, Tri Yuliyanti, Rikardus Program Studi Teknik
Lebih terperinciBAB I MATERIAL BETON (MIX DESIGN)
BAB MATERAL BETON (MX DESGN) 1.1. APA TU MX DESGN Beton merupakan bahan bangunan yang sangat serbaguna, karena dapat dirancang untuk kekuatan mulai Mpa sampai Mpa dan kemampuan kerja (workability) slump
Lebih terperinciPENGARUH PEMADATAN DENGAN GYRATORY TESTING MACHINE (GTM) TERHADAP KINERJA LABORATORIUM DARI CAMPURAN ASBUTON BERGRADASI SUPERPAVE TESIS
PENGARUH PEMADATAN DENGAN GYRATORY TESTING MACHINE (GTM) TERHADAP KINERJA LABORATORIUM DARI CAMPURAN ASBUTON BERGRADASI SUPERPAVE TESIS Karya tulis sebagai salah satu syarat untuk memperoleh gelar Magister
Lebih terperinciTINJAUAN KUAT TEKAN DAN MODULUS ELASTISITAS BETON DENGAN MENGGUNAKAN KAPUR PADAM DAN TANAH PADAS
TINJAUAN KUAT TEKAN DAN MODULUS ELASTISITAS BETON DENGAN MENGGUNAKAN KAPUR PADAM DAN TANAH PADAS (Compressive strength and modulus elasticity concrete with lime stone and trass) SKRIPSI Diajukan Sebagai
Lebih terperinciSTUDI EKSPERIMENTAL PENGARUH BERBAGAI KADAR VISCOCRETE PADA BERBAGAI UMUR KUAT TEKAN BETON MUTU TINGGI f c = 45 MPa
STUDI EKSPERIMENTAL PENGARUH BERBAGAI KADAR VISCOCRETE PADA BERBAGAI UMUR KUAT TEKAN BETON MUTU TINGGI f c = 45 MPa Willyanto Wantoro NRP : 0221107 Pembimbing : Ny. Winarni Hadipratomo, Ir. FAKULTAS TEKNIK
Lebih terperinciPENGARUH KANDUNGAN LUMPUR PADA AGREGAT HALUS TERHADAP KUAT TEKAN DAN KUAT TARIK BELAH BETON NORMAL
PENGARUH KANDUNGAN LUMPUR PADA AGREGAT HALUS TERHADAP KUAT TEKAN DAN KUAT TARIK BELAH BETON NORMAL PUBLIKASI ILMIAH Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan Teknik
Lebih terperinciPEMBUATAN BETON RINGAN DENGAN CRUMB RUBBER LIGHTWEIGHT CONCRETE MAKING WITH RUBBER CRUMB
Jurnal Teknik dan Ilmu Komputer PEMBUATAN BETON RINGAN DENGAN CRUMB RUBBER LIGHTWEIGHT CONCRETE MAKING WITH RUBBER CRUMB Dirga Wijaya 1, Darma Widjaja 2 Fakultas Teknik dan Ilmu Komputer Jurusan Teknik
Lebih terperinciKARAKTERISTIK CAMPURAN BETON ASPAL DENGAN LIMBAH PLTU SEBAGAI PENGGANTI AGREGAT SEBAGIAN TESIS ROBBY TRIAWAN NIM :
KARAKTERISTIK CAMPURAN BETON ASPAL DENGAN LIMBAH PLTU SEBAGAI PENGGANTI AGREGAT SEBAGIAN TESIS Karya tulis sebagai salah satu syarat Untuk memperoleh gelar Magister dari Institut Teknologi Bandung Oleh
Lebih terperinciPENGARUH UKURAN MAKSIMUM DAN NILAI KEKERASAN AGREGAT KASAR TERHADAP KUAT TEKAN BETON NORMAL
PENGARUH UKURAN MAKSIMUM DAN NILAI KEKERASAN AGREGAT KASAR TERHADAP KUAT TEKAN BETON NORMAL Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan Teknik Sipil Fakultas Teknik
Lebih terperinciPerhitungan Mix Design Beton (ACI 211.4R-93)
DAFTAR PUSTAKA 1. www.kapanlagi.com/h/0000182852.html 2. http://eprints.ums.ac.id/579/1/1._subroto.pdf 3. Lea, F.M., The Chemistry of Cement and Concrete, Edward Arnold Publishers, 1956 4. www.fhwa.dot.gov
Lebih terperinciDaftar Pustaka D.P-1 DAFTAR PUSTAKA
Daftar Pustaka D.P-1 DAFTAR PUSTAKA 1. ACI 211.4R-93. Specifications of the Concrete Mix for High Strength Concrete Used During the Experimens. 2. Product Data Polyolefin Fibers by 3M Scotchcast TM Polyolefin
Lebih terperinciPENGARUH METODE TWO-STAGE MIXING APPROACH (TSMA) TERHADAP KUAT TEKAN BETON POROUS DENGAN VARIASI KOMPOSISI AGREGAT KASAR DAUR ULANG (RCA)
PENGARUH METODE TWO-STAGE MIXING APPROACH (TSMA) TERHADAP KUAT TEKAN BETON POROUS DENGAN VARIASI KOMPOSISI AGREGAT KASAR DAUR ULANG (RCA) NASKAH PUBLIKASI TEKNIK SIPIL Ditujukan untuk memenuhi persyaratan
Lebih terperinciPENGARUH TEMPERATUR AIR TERHADAP KUAT TEKAN BETON PADA BETON SCC (SELF COMPACTING CONCRETE) TUGAS AKHIR. Diajukan Untuk Melengkapi Syarat Penyelesaian
PENGARUH TEMPERATUR AIR TERHADAP KUAT TEKAN BETON PADA BETON SCC (SELF COMPACTING CONCRETE) TUGAS AKHIR Diajukan Untuk Melengkapi Syarat Penyelesaian Pendidikan Sarjana Teknik Sipil Disusun Oleh : NOVAN
Lebih terperinciPENGARUH PASIR BATU BREKSI SEBAGAI PENGGANTI AGREGAT HALUS DITINJAU DARI KUAT TEKAN DAN MODULUS ELASTISITAS BETON
ISSN 2354-863 PENGARUH PASIR BATU BREKSI SEBAGAI PENGGANTI AGREGAT HALUS DITINJAU DARI KUAT TEKAN DAN MODULUS ELASTISITAS BETON Yurri Nosepa Cahyo 1), Kusno Adi Sambowo 2), Supardi 3) 1) Mahasiswa Fakultas
Lebih terperinciSTUDI EKSPERIMENTAL PENGARUH PENGGUNAAN PS BALL SEBAGAI PENGGANTI PASIR TERHADAP KUAT LENTUR BETON
STUDI EKSPERIMENTAL PENGARUH PENGGUNAAN PS BALL SEBAGAI PENGGANTI PASIR TERHADAP KUAT LENTUR BETON Prasthi Aldri Pratiwi NRP:1021009 Pembimbing: Ronald Simatupang, S.T., M.T. ABSTRAK Saat ini pemanasan
Lebih terperinciPEMANFAATAN LIMBAH BATU KAPUR SEBAGAI PENGGANTI AGREGAT KASAR PADA BETON LAPORAN PROYEK AKHIR
PEMANFAATAN LIMBAH BATU KAPUR SEBAGAI PENGGANTI AGREGAT KASAR PADA BETON LAPORAN PROYEK AKHIR Oleh Muhammad Iqbal Habibi NIM 091903103002 PROGRAM DIPLOMA III TEKNIK JURUSAN TEKNIK SIPIL FAKULTAS TEKNIK
Lebih terperinciPEMANFAATAN CLAY EX. BENGALON SEBAGAI AGREGAT BUATAN DAN PASIR EX. PALU DALAM CAMPURAN BETON DENGAN METODE STANDAR NASIONAL INDONESIA
PEMANFAATAN CLAY EX. BENGALON SEBAGAI AGREGAT BUATAN DAN PASIR EX. PALU DALAM CAMPURAN BETON DENGAN METODE STANDAR NASIONAL INDONESIA 03-2847-2002 USE OF CLAY EX. BENGALON AS AGGREGATE MADE AND SAND EX.
Lebih terperinciPEMANFAATAN BATU KAPUR DIDAERAH SAMPANG MADURA SEBAGAI BAHAN PENGGANTI AGREGAT KASAR PADA CAMPURAN BETON
JHP17 Jurnal Hasil Penelitian LPPM Untag Surabaya September 2016, Vol. 01, No. 02, hal 217-226 PEMANFAATAN BATU KAPUR DIDAERAH SAMPANG MADURA SEBAGAI BAHAN PENGGANTI AGREGAT KASAR PADA CAMPURAN BETON Nurul
Lebih terperinciPENGARUH VARIASI PERAWATAN BETON TERHADAP SIFAT MEKANIK HIGH VOLUME FLY ASH CONCRETE UNTUK MEMPRODUKSI BETON KUAT TEKAN NORMAL
PENGARUH VARIASI PERAWATAN BETON TERHADAP SIFAT MEKANIK HIGH VOLUME FLY ASH CONCRETE UNTUK MEMPRODUKSI BETON KUAT TEKAN NORMAL Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada
Lebih terperinciKUAT TEKAN BETON CAMPURAN 1:2:3 DENGAN AGREGAT LOKAL SEKITAR MADIUN
KUAT TEKAN BETON CAMPURAN 1:2:3 DENGAN AGREGAT LOKAL SEKITAR MADIUN Rosyid Kholilur Rohman Dosen Fakultas Teknik Universitas Merdeka Madiun Abstract The composition of concrete with a mixture 1: 2: 3 (volume
Lebih terperinciSPEECH FUNCTIONS IN MALE AND FEMALE LANGUAGE IN COSMETIC ADVERTISEMENT A THESIS JOHAN CHRISTIAN TOBING REG. NO
SPEECH FUNCTIONS IN MALE AND FEMALE LANGUAGE IN COSMETIC ADVERTISEMENT A THESIS BY JOHAN CHRISTIAN TOBING REG. NO. 080705020 DEPARTMENT OF ENGLISH FACULTY OF CULTURAL STUDIES UNIVERSITY OF SUMATERA UTARA
Lebih terperinciPENGARUH BESAR BUTIR MAKSIMUM AGREGAT TERHADAP MUTU BETON NORMAL EFFECT OF MAXIMUM GRAIN LARGE OF AGGREGATES TO NORMAL CONCRETE QUALITY
PENGARUH BESAR BUTIR MAKSIMUM AGREGAT TERHADAP MUTU BETON NORMAL EFFECT OF MAXIMUM GRAIN LARGE OF AGGREGATES TO NORMAL CONCRETE QUALITY Laporan ini disusun untuk memenuhi salah satu syarat menyelesaikan
Lebih terperinciTHE USE OF DISCOURSE MARKER IN WRITTEN TEXT OF PRESIDENT SUSILO BAMBANG YUDHOYONO S SPEECHES A THESIS BY: ROSALINA MUNTHE
THE USE OF DISCOURSE MARKER IN WRITTEN TEXT OF PRESIDENT SUSILO BAMBANG YUDHOYONO S SPEECHES A THESIS BY: ROSALINA MUNTHE 040705025 UNIVERSITY OF SUMATERA UTARA FACULTY OF LETTERS ENGLISH DEPARTMENT MEDAN
Lebih terperinciPERILAKU MEKANIK BETON BERONGGA MENGGUNAKAN AIR LAUT
PERILAKU MEKANIK BETON BERONGGA MENGGUNAKAN AIR LAUT Magfirah Burhan 1, M.W. Tjaronge 2, Rita Irmawaty 2 ABSTRAK : World Health Organization (WHO) memperkirakan bahwa ketersediaan air bersih akan berkurang
Lebih terperinciPENGGUNAAN TERAK NIKEL SEBAGAI AGREGAT DALAM CAMPURAN BETON
TESIS PENGGUNAAN TERAK NIKEL SEBAGAI AGREGAT DALAM CAMPURAN BETON WAYAN MUSTIKA PROGRAM PASCASARJANA UNIVERSITAS UDAYANA DENPASAR 2015 TESIS PENGGUNAAN TERAK NIKEL SEBAGAI AGREGAT DALAM CAMPURAN BETON
Lebih terperinciPENGARUH TREATMENT PADA BOTTOM ASH TERHADAP KUAT TEKAN BETON HIGH VOLUME FLY ASH
PENGARUH TREATMENT PADA BOTTOM ASH TERHADAP KUAT TEKAN BETON HIGH VOLUME FLY ASH Kevin Desailly, Singgih Suryajaya 2, Antoni 3, Djwantoro Hardjito 4 ABSTRAK : Pembangunan dalam bidang konstruksi di Indonesia
Lebih terperinciPENGARUH PENAMBAHAN FLY ASH DAN VOLUME FOAM TERHADAP KUAT TEKAN, DAYA SERAP AIR, DAN BERAT JENIS BETON RINGAN FOAM DENGAN PERBANDINGAN 1 PC : 1 PS
PENGARUH PENAMBAHAN FLY ASH DAN VOLUME FOAM TERHADAP KUAT TEKAN, DAYA SERAP AIR, DAN BERAT JENIS BETON RINGAN FOAM DENGAN PERBANDINGAN 1 PC : 1 PS SKRIPSI Oleh : MAHARANI K1512039 FAKULTAS KEGURUAN DAN
Lebih terperinciBy: Elfira Fibriani Student Number: Approved by:
A thesis on Students Language Anxiety in English Lesson and Students Expectation to Cope with the Language Anxiety: A Study at the First Year Students of SMA 6 Semarang By: Elfira Fibriani Student Number:
Lebih terperinciSTUDI EKSPERIMEN KUAT TEKAN BETON BERDASARKAN URUTAN PENCAMPURAN MATERIAL PENYUSUN BETON DENGAN ADUKAN MANUAL. Abstract:
STUDI EKSPERIMEN KUAT TEKAN BETON BERDASARKAN URUTAN PENCAMPURAN MATERIAL PENYUSUN BETON DENGAN ADUKAN MANUAL Endra Pramana Asmita 1) Crisna Djaya Mungok 2) Cek Putra Handalan 2) Email: job_sipil@yahoo.co.id
Lebih terperinciTESIS. Oleh : Nama : Rina Martsiana Nim : Pembimbing
PENGUKURAN MODULUS RESILIEN CAMPURAN BETON ASPAL YANG MENGANDUNG ROADCEL-50 DENGAN BEBAN STATIS DAN BEBAN BERULANG TESIS Oleh : Nama : Rina Martsiana Nim : 250 99 100 Pembimbing PROGRAM STUDI TEKNIK SIPIL
Lebih terperinciPENGGUNAAN MIX DESIGN SPEEDCRETE DAN BAHAN TAMBAH VISCOCRETE - 10 PADA TINJAUAN KUAT TEKAN DAN TARIK BETON NORMAL.
PENGGUNAAN MIX DESIGN SPEEDCRETE DAN BAHAN TAMBAH VISCOCRETE - PADA TINJAUAN KUAT TEKAN DAN TARIK BETON NORMAL Naskah Publikasi untuk memenuhi persyaratan mencapai derajat S-1 Teknik Sipil Reni Setiyawan
Lebih terperinciUSE OF CLAY EX. BENGALON AS AGGREGATE MADE AND SAND EX. MUARA BADAK IN MIXED CONCRETE METHOD STANDART NATIONAL INDONESIAN
PEMANFAATAN CLAY EX. BENGALON SEBAGAI AGREGAT BUATAN DAN PASIR EX. MUARA BADAK DALAM CAMPURAN BETON DENGAN METODE STANDAR NASIONAL INDONESIA 03-2847-2002 USE OF CLAY EX. BENGALON AS AGGREGATE MADE AND
Lebih terperinciSKRIPSI UJI EKSPERIMENTAL BETON NORMAL DIBANDINGKAN BETON SELF COMPACTING DENGAN AGREGAT DAUR ULANG DAN LIMBAH GENTENG TANAH LIAT
SKRIPSI UJI EKSPERIMENTAL BETON NORMAL DIBANDINGKAN BETON SELF COMPACTING DENGAN AGREGAT DAUR ULANG DAN LIMBAH GENTENG TANAH LIAT Dewin Juniadhari NPM: 2010410101 PEMBIMBING: BUEN SIAN, Ir, MT. UNIVERSITAS
Lebih terperinciJURNAL REKAYASA SIPIL DAN LINGKUNGAN Jurnal Teoritis dan Terapan Bidang Rekayasa Ketekniksipilan dan Lingkungan
JURNAL REKAYASA SIPIL DAN LINGKUNGAN Jurnal Teoritis dan Terapan Bidang Rekayasa Ketekniksipilan dan Lingkungan ISSN 0000-0000, Jurnal homepage: http://jurnal.unej.ac.id/index.php/jrsl Pengaruh Campuran
Lebih terperinciSTUDI EKSPERIMENTAL KUAT TEKAN BETON DENGAN PLASTIK DAUR ULANG OLAHAN JENIS HDPE PENGGANTI SEBAGIAN AGREGAT HALUS
SKRIPSI STUDI EKSPERIMENTAL KUAT TEKAN BETON DENGAN PLASTIK DAUR ULANG OLAHAN JENIS HDPE PENGGANTI SEBAGIAN AGREGAT HALUS CLAUDIO AGUSTA NPM : 2012410166 PEMBIMBING: Dr. Cecilia Lauw Giok Swan UNIVERSITAS
Lebih terperinciPENENTUAN MUTU AGREGAT HALUS DARI BERBAGAI QUARRY PADA PRODUKSI BETON
Penentuan Agregat Halus dari Berbagai Quarry pada Produksi Beton PENENTUAN MUTU AGREGAT HALUS DARI BERBAGAI QUARRY PADA PRODUKSI BETON Suprasman 1, Ermiyati 2, Azhari 3, Edria Dianjani 4 ABSTRAK Penelitian
Lebih terperinciAcknowledgements. First of all, I would like to say Alhamdulillahhirabbil alamin. My utmost
ǀ vii Acknowledgements First of all, I would like to say Alhamdulillahhirabbil alamin. My utmost gratitude goes to Allah SWT, for His endless blessing and amazing life given to me. I owe my sincere appreciation
Lebih terperinciSTUDI PENGARUH UKURAN BUTIR TERHADAP PARAMETER KOMPAKSI MATERIAL CRUSHED LIMESTONE ABSTRAK
STUDI PENGARUH UKURAN BUTIR TERHADAP PARAMETER KOMPAKSI MATERIAL CRUSHED LIMESTONE Jordan Dean Fahlevi NRP : 1021037 Pembimbing : Andrias Suhendra Nugraha., S.T., M.T. ABSTRAK Limestone adalah batu kapur
Lebih terperinciTEACHERS CHALLENGES OF TEACHING ENGLISH AS A FOREIGN LANGUAGE IN SENIOR HIGH SCHOOLS A THESIS
TEACHERS CHALLENGES OF TEACHING ENGLISH AS A FOREIGN LANGUAGE IN SENIOR HIGH SCHOOLS A THESIS by Yuannita Student Number: 12.80.0036 FACULTY OF LANGUAGE AND ARTS SOEGIJAPRANATA CATHOLIC UNIVERSITY SEMARANG
Lebih terperinciPERILAKU MEKANIK LEKATAN BETON DAN TULANGAN PADA BETON MUTU TINGGI AKIBAT BEBAN STATIK TESIS
PERILAKU MEKANIK LEKATAN BETON DAN TULANGAN PADA BETON MUTU TINGGI AKIBAT BEBAN STATIK TESIS SEBAGAI SALAH SATU SYARAT UNTUK MENYELESAIKAN PROGRAM MAGISTER TEKNIK SIPIL PADA PROGAM PASCA SARJANA INSTITUT
Lebih terperinciSTUDI EKSPERIMENTAL PROPORSI BETON KEKUATAN RENCANA 40 MPa SESUAI ACI 211.4R-08 DENGAN SEMEN SCG TIPE PCC DAN DIKOREKSI ACI 211.
SKRIPSI STUDI EKSPERIMENTAL PROPORSI BETON KEKUATAN RENCANA 40 MPa SESUAI ACI 211.4R-08 DENGAN SEMEN SCG TIPE PCC DAN DIKOREKSI ACI 211.7R-15 DAVID SETIAWAN NPM: 2012410105 PEMBIMBING: Dr. Cecilia Lauw
Lebih terperinciKINERJA BETON SERAT MENGGUNAKAN UJI TOUGHNESS PANEL PADA KANDUNGAN SERAT YANG BERBEDA
KINERJA BETON SERAT MENGGUNAKAN UJI TOUGHNESS PANEL PADA KANDUNGAN SERAT YANG BERBEDA (performance of fiber reinforced concrete containing various fiber dosages on panel toughness test) SKRIPSI Disusun
Lebih terperinciSTUDI PERBANDINGAN KUAT TEKAN BETON DENGAN AGREGAT KASAR MENGGUNAKAN METODE SNI DAN METODE MAXIMUM DENSITY
Volume 13, No. 1, Oktober 14: 12 17 STUDI PERBANDINGAN KUAT TEKAN BETON DENGAN AGREGAT KASAR MENGGUNAKAN METODE SNI DAN METODE MAXIMUM DENSITY Muhammad Shalahuddin Jurusan Teknik Sipil, Fakultas Teknik,
Lebih terperinciPengaruh Substitusi Sebagian Agregat Halus Dengan Serbuk Kaca Dan Silica Fume Terhadap Sifat Mekanik Beton
Volume 13, No., April 15: 94-13 Pengaruh Substitusi Sebagian Agregat Halus Dengan Serbuk Kaca Dan Silica Fume Terhadap Sifat Mekanik Beton Johanes Januar Sudjati, Aphrodita Emawati Atmaja, Gabriella Agnes
Lebih terperinciSTUDI EKSPERIMEN PENGARUH WAKTU PENUANGAN ADUKAN BETON READY MIX KE DALAM FORMWORK TERHADAP MUTU BETON NORMAL
STUDI EKSPERIMEN PENGARUH WAKTU PENUANGAN ADUKAN BETON READY MIX KE DALAM FORMWORK TERHADAP MUTU BETON NORMAL Hardiyanto Eka Putra 1)., Dharma Sardjana 2)., Eddy Samsurizal 2) ABSTRACT In the manufacture
Lebih terperinciSTUDI BETON BERKEKUATAN TINGGI (HIGH PERFORMANCE CONCRETE) DENGAN MIX DESIGN MENGGUNAKAN METODE ACI (AMERICAN CONCRETE INSTITUTE)
STUDI BETON BERKEKUATAN TINGGI (HIGH PERFORMANCE CONCRETE) DENGAN MIX DESIGN MENGGUNAKAN METODE ACI (AMERICAN CONCRETE INSTITUTE) Abstrak Riyu 1) Chrisna Djaja Mungok 2) dan Aryanto 2) Dalam pembuatan
Lebih terperinciPENGARUH VARIASI BENTUK PAVING BLOCK TERHADAP KUAT TEKAN
PENGARUH VARIASI BENTUK PAVING BLOCK TERHADAP KUAT TEKAN Arie Putra Mahasiswa Jurusan Teknik Sipil Fakultas Teknik Universitas Riau Tel. 076166596, Pekanbaru 28293 Riau, E-mail: Arie_200789@yahoo.co.id
Lebih terperinciMuhammad Wihardi Tjaronge 1 ABSTRACT PENDAHULUAN
Studi Dasar Mengenai Beton yang Menggunakan Agregat Buatan Yang Ringan Sebagai Agregat Kasar STUDI DASAR MENGENAI BETON YANG MENGGUNAKAN AGREGAT BUATAN YANG RINGAN SEBAGAI AGREGAT KASAR Muhammad Wihardi
Lebih terperinciPengaruh Penggunaan Bambu Sebagai Pengganti Agregat Split terhadap Kuat Tekan Beton Ringan
JURNAL ILMIAH SEMESTA TEKNIKA Vol. 15, No. 2, 143-148, November 2012 143 Pengaruh Penggunaan Bambu Sebagai Pengganti Agregat Split terhadap Kuat Tekan Beton Ringan (Effect of Using Bamboo as Split Aggregate
Lebih terperinciAN ANALYSIS OF LEXICAL AND STRUCTURAL AMBIGUITIES IN NEWS TITLES OF SUARA MERDEKA NEWSPAPER A THESIS
AN ANALYSIS OF LEXICAL AND STRUCTURAL AMBIGUITIES IN NEWS TITLES OF SUARA MERDEKA NEWSPAPER A THESIS RenandaAyuKinanti Student Number: 10.80.0022 FACULTY OF LANGUAGE AND ARTS SOEGIJAPRANATA CATHOLIC UNIVERSITY
Lebih terperinciJURNAL TUGAS AKHIR. PENGARUH AIR LAUT DAN NaCl TERHADAP KUAT TARIK BELAH MORTAR ABDUL FAJAR ALAMSYAH D
JURNAL TUGAS AKHIR PENGARUH AIR LAUT DAN NaCl TERHADAP KUAT TARIK BELAH MORTAR ABDUL FAJAR ALAMSYAH D 111 10 298 JURUSAN TEKNIK SIPIL FAKULTAS TEKNIK UNIVERSITAS HASANUDDIN 2015 PENGARUH AIR LAUT DAN NaCl
Lebih terperinciSTUDI EKSPERIMEN KUAT TEKAN BETON MENGGUNAKAN SEMEN PPC DENGAN TAMBAHAN SIKAMENT LN
STUDI EKSPERIMEN KUAT TEKAN BETON MENGGUNAKAN SEMEN PPC DENGAN TAMBAHAN SIKAMENT LN Sutrianus Arief 1, Chrisna Djaya Mungok 2, Eddy Samsurizal 2 1 Program Studi Teknik Sipil, Universitas Tanjungpura, Pontianak
Lebih terperinciSTUDI EKSPERIMENTAL PENGARUI BEBAN AKSIAL DAN MULTI AKSIAL TEKAN PADA BETON MUTU TINGGI TESIS MAGISTER. Oleh : SUHARWANTO
STUDI EKSPERIMENTAL PENGARUI BEBAN AKSIAL DAN MULTI AKSIAL TEKAN PADA BETON MUTU TINGGI TESIS MAGISTER Oleh : SUHARWANTO 25094033 BIDANG KHUSUS REKAYASA STRUKTUR PROGRAM STUDI REKAYASA SIPIL PROGRAM PASCA
Lebih terperinciSTUDI EKSPERIMENTAL PENGGUNAAN PECAHAN KERAMIK SEBAGAI PENGGANTI AGREGAT KASAR DALAM PERANCANGAN CAMPURAN BETON
STUDI EKSPERIMENTAL PENGGUNAAN PECAHAN KERAMIK SEBAGAI PENGGANTI AGREGAT KASAR DALAM PERANCANGAN CAMPURAN BETON Abstrak Joni Kristian 1) Joko Goetomo 2) dan Eddy Samsurizal 2) Karya ilmiah mempresentasikan
Lebih terperinciLaksmi Irianti dan Eddy Purwanto 2. Abstrak
PENGGUNAAN ACCELERATOR PADA BETON ABU KETEL SEBAGAI UPAYA MEMPERCEPAT LAJU PENGERASAN 1 (The use of accelerator in Kettle-ash concrete as the effort of hardening accelerate) Laksmi Irianti dan Eddy Purwanto
Lebih terperinciABSTRAK. PERBAIKAN KARAKTERISTIK CAMPURAN SEMEN DENGAN SEKAM PADI DAN LEMPUNG (xvii + 90 halaman: 23 gambar; 22 tabel; 10 lampiran)
ABSTRAK Hendo Winata (02120060013) PERBAIKAN KARAKTERISTIK CAMPURAN SEMEN DENGAN SEKAM PADI DAN LEMPUNG (xvii + 90 halaman: 23 gambar; 22 tabel; 10 lampiran) Hasil penelitian studi eksperimental peningkatan
Lebih terperinciPEMANFAATAN CLAY EX. BENGALON SEBAGAI AGREGAT BUATAN DAN PASIR EX. PALU DALAM CAMPURAN BETON DENGAN METODE (AMERICAN CONCRETE INSTITUTE) ACI 211
PEMANFAATAN CLAY EX. BENGALON SEBAGAI AGREGAT BUATAN DAN PASIR EX. PALU DALAM CAMPURAN BETON DENGAN METODE (AMERICAN CONCRETE INSTITUTE) ACI 211 USE OF CLAY EX. BENGALON AS AGGREGATE MADE AND SAND EX.
Lebih terperinciPENGARUH PENGGUNAAN AGREGAT DAUR ULANG TERHADAP KUAT TEKAN DAN MODULUS ELASTISITAS BETON BERKINERJA TINGGI GRADE 80
ISSN 2354-863 PENGARUH PENGGUNAAN AGREGAT DAUR ULANG TERHADAP KUAT TEKAN DAN MODULUS ELASTISITAS BETON BERKINERJA TINGGI GRADE 8 Deni Anwar Hamid 1), Solihin As ad 2), Endah Safitri 3) 1) Mahasiswa Jurusan
Lebih terperinciTESIS. Oleh : SUJATMIKO NUGROHO
KARAKTERISTIK TEKNIK AGREGAT BUATAN DARI ABU TERBANG DAN PENGGUNAANNYA DALAM CAMPURAN BETON ASPAL TESIS Oleh : SUJATMIKO NUGROHO 25099116 Pembimbing : Ir. BAMBANG ISMANTO SISWOSOEBROTHO, MSc, PhD. PROGRAM
Lebih terperinciSTUDI EKSPERIMENTAL PROPORSI BETON PORTLAND POZOLAN GRESIK SESUAI ACI 211.4R-08 YANG DIKOREKSI SESUAI ACI 211.7R-15
SKRIPSI STUDI EKSPERIMENTAL PROPORSI BETON c 60 MPa DENGAN SEMEN PORTLAND POZOLAN GRESIK SESUAI ACI 211.4R-08 YANG DIKOREKSI SESUAI ACI 211.7R-15 ARDY PATAR NPM: 2012410199 PEMBIMBING: Dr. Cecilia Lauw
Lebih terperinciPengaruh Penambahan Serat Polypropylene Terhadap Sifat Mekanis Beton Normal
Pengaruh Penambahan Serat Polypropylene Terhadap Sifat Mekanis Beton Normal Yuri Khairizal 1, Alex Kurniawandy 2, Alfian Kamaldi 2 1 Mahasiswa Jurusan Teknik Sipil Fakultas Teknik Universitas Riau 2 Dosen
Lebih terperinciProporsi Pessimum dan Ekspansi. Mohd. Isneini 1)
Proporsi Pessimum dan Ekspansi Mohd. Isneini 1) Abstract Expansion in mortar or concrete could happen due to chemical reaction inside it. Some various proportion of reactives aggregate with non reactive
Lebih terperinciPENGGUNAAN TERAK NIKEL SEBAGAI AGREGAT PADA BETON MUTU TINGGI
PENGGUNAAN TERAK NIKEL SEBAGAI AGREGAT PADA BETON MUTU TINGGI T 624. 183 4 KHO ABSTRAK Beton merupakan material konstruksi bangunan yang sering digunakan karena mudah dibentuk dan biaya pemeliharaan yang
Lebih terperinciINDIVIDUAL RESEARCH A STUDY OF PUBLIC SPEAKING USED BY THE FIFTH SEMESTER STUDENTS OF MURIA KUDUS UNIVERSITY IN THE ACADEMIC YEAR 2014/2015
INDIVIDUAL RESEARCH RESEARCH REPORT A STUDY OF PUBLIC SPEAKING USED BY THE FIFTH SEMESTER STUDENTS OF MURIA KUDUS UNIVERSITY IN THE ACADEMIC YEAR 2014/2015 By: Atik Rokhayani, S.Pd.,M.Pd. Funded by Anggaran
Lebih terperinciTinjauan Kembali Mengenai Pengaruh Modulus Kehalusan Pasir terhadap Kuat Tekan Beton
Reka Racana Jurusan Teknik Sipil Vol. 2 No. 3 Jurnal Online Institut Teknologi Nasional September 2016 Tinjauan Kembali Mengenai Pengaruh Modulus Kehalusan Pasir terhadap Kuat Tekan Beton BRAYN GILANG
Lebih terperinciThe Perception Of The Eight Semester Students Of English Department. On Thesis Writing : A Study On English Departments In Semarang
The Perception Of The Eight Semester Students Of English Department On Thesis Writing : A Study On English Departments In Semarang A Thesis Presented as a Partial Fulfilment of the Requirements to Obtain
Lebih terperinciPENGARUH KADAR AIR AGREGAT TERHADAP KUAT TEKAN BETON ABSTRACT
Pengaruh Kadar Air.. Kuat Tekan Beton Arusmalem Ginting PENGARUH KADAR AIR AGREGAT TERHADAP KUAT TEKAN BETON Arusmalem Ginting 1, Wawan Gunawan 2, Ismirrozi 3 1 Dosen Jurusan Teknik Sipil, Fakultas Teknik,
Lebih terperinciJURNAL SKRIPSI KARAKTERISTIK BATU KORAL UKURAN 20 MM DAN BATU KORAL GRADASI MENERUS PADA CAMPURAN BETON
JURNAL SKRIPSI KARAKTERISTIK BATU KORAL UKURAN 20 MM DAN BATU KORAL GRADASI MENERUS PADA CAMPURAN BETON Disusun dan dipersiapkan oleh : HERRY NATANAEL ABENG 11.11.1001.7311.045 Telah disetujui oleh Dosen
Lebih terperinciA STUDY OF LISTENING CLASS RELATED PROBLEM A THESIS
A STUDY OF LISTENING CLASS RELATED PROBLEM A THESIS By : Fiona Andrianto Student Number: 07.80.0058 ENGLISH LETTERS STUDY PROGRAMME FACULTY OF LANGUAGE AND ARTS SOEGIJAPRANATA CATHOLIC UNIVERSITY SEMARANG
Lebih terperinciPENGARUH BATU KAPUR SEBAGAI FILLER PADA CAMPURAN LASTON LAPIS AUS (AC-WC) ABSTRAK
PENGARUH BATU KAPUR SEBAGAI FILLER PADA CAMPURAN LASTON LAPIS AUS (AC-WC) Dennis Aldimus NRP: 1221063 Pembimbing: Tan Lie Ing, S.T., M.T. ABSTRAK Penelitian tentang agregat pengganti maupun filler untuk
Lebih terperinciTABLE OF CONTENTS.. APPROVAL PAGE... DECLARATION... ACKNOWLEDGMENT ABSTRACT.. LIST OF TABLES... LIST OF FIGURE. LIST OF APPENDICES xii
TABLE OF CONTENTS APPROVAL PAGE... DECLARATION... PREFACE. ACKNOWLEDGMENT ABSTRACT.. TABLE OF CONTENTS.. LIST OF TABLES... LIST OF FIGURE. i ii iii iv v vi x xi LIST OF APPENDICES xii CHAPTER I: INTRODUCTION.
Lebih terperinciINFLUENCE OF USING NON-STANDARD SPECIMEN ON COMPRESSIVE STRENGTH OF NORMAL AND HIGH STRENGTH CONCRETE EXPERIMENTAL AND SIMULATION.
INFLUENCE OF USING NON-STANDARD SPECIMEN ON COMPRESSIVE STRENGTH OF NORMAL AND HIGH STRENGTH CONCRETE EXPERIMENTAL AND SIMULATION Thesis Submitted to the Post Graduate of Civil Engineering Program in Partial
Lebih terperinciPEMANFAATAN LIMBAH LUMPUR INDUSTRI PENGOLAHAN BAJA SEBAGAI PENGGANTI PARSIAL PASIR UNTUK BAHAN BANGUNAN
NO. Urut : 070/S2-TL/TPL/1997 PEMANFAATAN LIMBAH LUMPUR INDUSTRI PENGOLAHAN BAJA SEBAGAI PENGGANTI PARSIAL PASIR UNTUK BAHAN BANGUNAN TESIS Sebagai Salah Satu Persyaratan untuk Menyelesaikan Program Magister
Lebih terperinciI. REFERENSI II. TUJUAN III. DASAR TEORI
I. REFERENSI LABORATORIUM UJI BAHAN Materi : Uji Kuat Tekan Beton Halaman : 1 1. ASTM C.39: Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens. 2. ASTM C.31: Standard Practice
Lebih terperinciSTUDI EKSPERIMEN KUAT TEKAN BETON BERDASARKAN URUTAN DAN WAKTU PERPUTARAN PENCAMPURAN MATERIAL PENYUSUN BETON DENGAN ADUKAN MENGGUNAKAN MESIN MOLEN
STUDI EKSPERIMEN KUAT TEKAN BETON BERDASARKAN URUTAN DAN WAKTU PERPUTARAN PENCAMPURAN MATERIAL PENYUSUN BETON DENGAN ADUKAN MENGGUNAKAN MESIN MOLEN Rosita Hermiyati 1, Chrisna Djaya Mungok 2, Asep Supriadi
Lebih terperinciSTUDI EKSPERIMENTAL PROPORSI BETON KEKUATAN TINGGI RENCANA 80 MPa DENGAN SEMEN OPC SESUAI ACI 211.4R-08
SKRIPSI STUDI EKSPERIMENTAL PROPORSI BETON KEKUATAN TINGGI RENCANA 80 MPa DENGAN SEMEN OPC SESUAI ACI 211.4R-08 IGNASIUS DANNY SOEBIANTO NPM: 2012410015 PEMBIMBING: Dr. Cecilia Lauw Giok Swan UNIVERSITAS
Lebih terperinciPENGARUH PENGGUNAAN AGREGAT DAUR ULANG BETON KEDALAM CAMPURAN BETON K 175 (PENELITIAN)
PENGARUH PENGGUNAAN AGREGAT DAUR ULANG BETON KEDALAM CAMPURAN BETON K 175 (PENELITIAN) Rahmat Taufik, Jurusan Teknik Sipil STTH Medan, Jl H.M Jhoni No. 70 Medan, Indonesia taufikrahmat68@gmail.com Abstrak
Lebih terperinciPROSEDUR PENGUJIAN TANAH UNTUK BEBERAPA DAERAH DI JAWA BARAT
PROSEDUR PENGUJIAN TANAH UNTUK BEBERAPA DAERAH DI JAWA BARAT RINGRASAN PROCEDURES FOR TESTING OF WEST JAVA SOILS, Bemby Sunaryo, 1992, Program Magister Sistem dan Teknik Jalan Raya, Program Pasca Sarjana,
Lebih terperinciPENGARUH PEMAKAIAN ABU SEKAM PADI SEBAGAI CEMENTITIOUS TERHADAP PERKEMBANGAN KUAT TEKAN BETON. Abstract
PENGARUH PEMAKAIAN ABU SEKAM PADI SEBAGAI CEMENTITIOUS TERHADAP PERKEMBANGAN KUAT TEKAN BETON Mochamad Solikin 1, Susilo 2 1 Fakultas Teknik, Universitas Muhammadiyah Surakarta email: msolikin@ums.ac.id
Lebih terperinci8KUAT TEKAN BETON BERDASARKAN SNI-DT PADA BERBAGAI VARIASI KADAR AIR AGREGAT
JURNAL TEKNIK VOL. 3 NO. 1 / APRIL 2013 8KUAT TEKAN BETON BERDASARKAN SNI-DT-91-0008-2007 PADA BERBAGAI VARIASI KADAR AIR AGREGAT 1 Arusmalem Ginting 2 Aji Nurhendra Satriyajati 1 Dosen Jurusan Teknik
Lebih terperinciTUGAS AKHIR. Disusun oleh : FRANS EKA P. L2A NUGROHO BUDI U. L2A
i TUGAS AKHIR PENGARUH SILICA FUME PADA KUAT TEKAN DAN KUAT TARIK BETON NORMAL DAN BETON SLAG (Influence Of Silica Fume Againts Compressive Strength and Tensile Strength At Normal Concrete and Slag Concrete)
Lebih terperinciPenggunaan Campuran Abu Sampah Organik dan Limbah Karbit sebagai Bahan Pengganti Semen pada Mortar
86 JURNAL ILMIAH SEMESTA TEKNIKA Vol. 12, No.1, 86-91, Mei 2009 Penggunaan Campuran Abu Sampah Organik dan Limbah Karbit sebagai Bahan Pengganti Semen pada Mortar (Use of Organic-Waste Ash and Carbide
Lebih terperinciPENGARUH PENAMBAHAN SERAT GALVALUM PADA BETON RINGAN DENGAN TEKNOLOGI FOAM TERHADAP KUAT LENTUR, TOUGHNESS, DAN STIFFNESS
PENGARUH PENAMBAHAN SERAT GALVALUM PADA BETON RINGAN DENGAN TEKNOLOGI FOAM TERHADAP KUAT LENTUR, TOUGHNESS, DAN STIFFNESS The Effect of Adding Galvalum Fiber on Lightweight Concrete Foam Technology towards
Lebih terperinciEVALUASI GRADASI MATERIAL CRUSHED LIMESTONE WELL GRADED SAAT PRA KOMPAKSI DAN PASCA KOMPAKSI ABSTRAK
EVALUASI GRADASI MATERIAL CRUSHED LIMESTONE WELL GRADED SAAT PRA KOMPAKSI DAN PASCA KOMPAKSI ADITIA FAIZAL NRP: 0921021 Pembimbing: Ir. Herianto Wibowo, M.Sc ABSTRAK Limestone atau batu gamping merupakan
Lebih terperinciSTUDI EKSPERIMEN KUAT TEKAN BETON MENGGUNAKAN SEMEN PPC DENGAN TAMBAHAN GLENIUM
STUDI EKSPERIMEN KUAT TEKAN BETON MENGGUNAKAN SEMEN PPC DENGAN TAMBAHAN GLENIUM F. Windy Yolanda 1, Chrisna Djaya Mungok 2, Eddy Samsurizal 2 Abstract This paper presents the results of the use of material
Lebih terperinciAN ANALYSIS OF REALISM FOUND IN DANIEL DEFOE S NOVEL ROBINSON CRUSOE
AN ANALYSIS OF REALISM FOUND IN DANIEL DEFOE S NOVEL ROBINSON CRUSOE A THESIS BY: SATRIA NOVA AGESTA Reg. No. 030705001 FACULTY OF LETTERS ENGLISH DEPARTMENT NORTH SUMATERA UNIVERSITY MEDAN 2008 ACKNOWLEDGENTS
Lebih terperinciA DESCRIPTIVE STUDY ON THE USE OF SONG AS A TECHNIQUE OF TEACHING VOCABULARY AT ELEMENTARY SCHOOL A THESIS
A DESCRIPTIVE STUDY ON THE USE OF SONG AS A TECHNIQUE OF TEACHING VOCABULARY AT ELEMENTARY SCHOOL A THESIS by Brigittha Desi Arianie Student Number : 01.80.0014 ENGLISH LETTERS STUDY PROGRAMME FACULTY
Lebih terperinciEXPERIMENT OF EARLY AGE STRENGTH CONCRETE USING RICE HUSK ASH
EXPERIMENT OF EARLY AGE STRENGTH CONCRETE USING RICE HUSK ASH Arranged as one of the requirements of completing stratum I program in Civil Engineering Department of Engineering Faculty Submitted by: WAFIQOTUL
Lebih terperinciSTUDI EKSPERIMEN KUAT TEKAN BETON NON AGREGAT KASAR SEMEN PCC DENGAN SIKAMENT LN
STUDI EKSPERIMEN KUAT TEKAN BETON NON AGREGAT KASAR SEMEN PCC DENGAN SIKAMENT LN Derina Ika Kumalasari Siregar 1, Chrisna Djaya Mungok 2, Eddy Samsurizal 2 1 Program Studi Teknik Sipil, Universitas Tanjungpura,
Lebih terperinciSTUDI EKSPERIMENTAL PERKEMBANGAN KUAT TEKAN BETON SEMEN TIPE I MERK SCG f c 50 MPa YANG DIPROPORSIKAN SESUAI ACI 211.4R-08
SKRIPSI STUDI EKSPERIMENTAL PERKEMBANGAN KUAT TEKAN BETON SEMEN TIPE I MERK SCG f c 50 MPa YANG DIPROPORSIKAN SESUAI ACI 211.4R-08 Yosua Daniel Salim NPM : 2011 410 004 PEMBIMBING : Dr. Cecilia Lauw Giok
Lebih terperinciPENGARUH SULFAT TERHADAP KUAT TEKAN BETON DENGAN VARIASI BUBUK KACA SUBSTITUSI SEBAGIAN SEMEN DENGAN w/c 0,60 DAN 0,65
PENGARUH SULFAT TERHADAP KUAT TEKAN BETON DENGAN VARIASI BUBUK KACA SUBSTITUSI SEBAGIAN SEMEN DENGAN w/c 0,60 DAN 0,65 Fikkriansyah 1*, Gunawan Tanzil 2 1,2 Jurusan Teknik Sipil Fakultas Teknik Universitas
Lebih terperinciKELAYAKAN PASIR KALI MAS SEBAGAI AGREGAT HALUS PADA CAMPURAN BETON DAN MORTAR
KELAYAKAN PASIR KALI MAS SEBAGAI AGREGAT HALUS PADA CAMPURAN BETON DAN MORTAR Aristofel R. Resi 1 (aristofelronaldzresi@gmail.com) Elia Hunggurami 2 (eliahunggurami@yahoo.com) Sudiyo Utomo (diyotomo@gmail.com)
Lebih terperinci