Pengamatan Model Pengendalian Korosi pada Media Korosi Air Laut Salinitas 35 o / Oo menggunakan Anoda Terumpan Zap Type S-3
|
|
- Benny Pranoto
- 7 tahun lalu
- Tontonan:
Transkripsi
1 Pengamatan Model Pengendalian Korosi pada Media Korosi Air Laut Salinitas 35 o / Oo menggunakan Anoda Terumpan Zap Type S-3 Dwisetiono Marine Engineering Department, Faculty of Marine Engineering and Science, Hang Tuah University, Jl. Arif Rahman Hakim 150, Surabaya. dwisetiono@hangtuah.ac.id Abstract: Corrosion is one of some necessary field that must be concerned by maritime and ship industries in Indonesia. The phenomenon of corrosion should be more attended, because it makes much money lost unpredictly. Corrosion couldn t be avoid because the process happens naturally, but corrosion must be controlled to minimize the negative effects, specially in economics, technics and safety fields. One of some popular methods to control the corrosion process is cathodic protection method, with sacrificial anode. This research observed the effectivity of Znanode (type S-3) that is used to protect a kind of material as cathode. The cathode material is A- grade of mild steels, a material that is commonly used for many sea water constructions, especially for ship building materials. The observation was taken in Fluid Laboratory, Marine Engineering Department, The faculty of Marine Engineering and Sciense, Hang Tuah University, Surabaya. The weight of sacrificial anode and the cathode is 1:4. They are connected and immersed in a model vessel with 35 O / OO salinity sea water as corrosion media. This research presents that the average weight lost of the sacrificial anode is 1.637%, and the average weight lost of the cathode is 0.170% in 16 weeks observation. The calculation predicted that the sacrificial anode will be lost 5.5% of the weight in a year. Keywords: corrosion, cathodic protection, sacrificial anode PENDAHULUAN Korosi merupakan salah satu permasalahan penting yang harus dihadapi oleh berbagai macam sektor industri di Indonesia, terutama industri perkapalan. Tidak sedikit biaya yang harus dikeluarkan sebagai akibat langsung dari masalah tersebut. Menyadari keadaan ini, pengendalian masalah korosi dan penanggulangannya perlu dilakukan dengan lebih efektif. Hingga sekarang Indonesia belum punya data yang kongkret tentang korosi ini. (Widyanto, 2005). Kerugian yang dapat ditimbulkan oleh korosi tidak hanyabiaya langsung seperti penggantian peralatan industri, perawatan jembatan konstruksi dan sebagainya, tetapi juga biaya tidak langsung seperti terganggunya proses produksi dalam industri serta kelancaran transportasi, yang umumnya lebih besar dibandingkan biaya langsung. Faktor yang berpengaruh terhadap korosi dapat dibedakan menjadi dua, yaitu yang berasal dari bahan itu sendiri dan dari lingkungan (Chamberlain, 1991). (a) Faktor dari bahan meliputi kemurnian bahan, struktur bahan, bentuk kristal, unsur-unsur kelumit yang ada dalam bahan, teknik pencampuran bahan dan sebagainya. (b) Faktor dari lingkungan meliputi tingkat pencemaran udara, suhu, kelembaban, keberadaan zat-zat kimia yang bersifat korosif dan sebagainya. (c) Faktor kelistrikan yang berpengaruh pada unsur-unsur logam dalam proses kimia yang akan menghasilkan korosi. 26
2 Dalam upaya pengendalian korosi, sangat penting untuk diketahui secara pasti terlebih dahulu jenis korosi yang terjadi dan penyebabnya, barulah dapat dilakukan perencanaan untuk pengendaliannya. Dalan kenyataan, sering dipilih suatu material sebagai sacrificial anode untuk melindungi baja yang bekerja di lingkungan air laut yang tidak statis (ada aliran). Pertimbangan yang dilakukan hanya berdasarkan bahwa material tersebut telah terbukti dapat melindungi baja pada suatu media lain, atau media yang sama tetapi bersifat statis, tanpa adanya gerakan dari media korosinya. Dengan diketahuinya jenis dan penyebab korosi yang tepat, dapat dilakukan perencanaan yang tepat pula dalam pengendalian korosi yang terjadi, sehingga kerugian yang ditimbilkan dapat diminimasi, baik kerugian biaya maupun waktu untuk perbaikan/penggantian material (Chandler, 1985) Dalam penelitian ini direncanakan untuk menguji kemampuan suatu logam yang digunakan sebagai anoda untuk melindungi logam lain dari kerusakan akibat proses korosi. Sebagai sacrificial anode digunakan logam Zn-alloys (ZAP Type S-3) dan sebagai katoda atau logam yang dilindungi digunakan logam baja lunak grade A yang sering dipakai sebagai konstruksi kapal dan bangunan laut (sesuai spesifikasi ABS Rule Requirements for Material and Welding, 2002). METODE PENELITIAN Dalam penelitian ini digunakan spesimen anoda berupa Zn-anode (ZAP Type S-3) dan spesimen katoda adalah baja lunak grade A yang biasa dipakai sebagai material badan kapal. Penelitian dilakukan dengan membuat model aliran dinamis (turbulen) dalam skala laboratorium. Sebagai media korosi adalah air laut yang diambil dari perairan Surabaya, tepatnya di area perairan PT. Dok dan Perkapalan, Surabaya dengan tingkat salinitas yang diuji di Laboratorium sebesar 35 O / OO. Material yang telah dibuat dengan dimensi dan berat yang diinginkan, dibersihkan dengan metode sandblasting, dengan level SA-2. Setelah bersih, material diletakkan dalam media korosi. Dari waktu ke waktu, secara periodik, dilakukan pengambilan data berat spesimen untuk mengetahui pengurangan berat yang terjadi akibat korosi. anoda dibuat dengan dimensi 20 mm x 20 mmx 40 mm, sedangkan spesimen katoda dibuat dengan dimensi 80 mm x 60 mm x 10 mm. Anoda dan katoda dirangkai seperta pada skema percobaan: Gambar 1. Skema Percobaan Pengamatan Model Pengendalian Korosi pada. 27
3 Penelitian dilakukan di Laboratorium Fluida, Jurusan Teknik Sistem Perkapalan, Fakultas Teknik dan Ilmu Kelautan, Universitas Hang Tuah, Surabaya. Laju korosi yang terjadi diamati dengan menghitung percent weight loss dari masing-masing spesimen. korosi (gram) = berat awal spesimen berat spesimen setelah dibersihkan Rata rata berat (gr) korosi (3 spesimen) % Korosi X100% Rata rata berat (gr) awal (3 spesimen) Dalam hal ini, % korosi yang didapat digunakan dalam menentukan percent weight loss dari spesimen (Kristiyono,dkk., 2007). Dari data periodik yang didapat, dilakukan peramalan atau trend dari korosi yang terjadi untuk suatu periode yang lebih lama. Peramalan dilakukan karena pengamatan hanya dilakukan dalam suatu rentang waktu yang terbatas, sedangkan proses korosi masih tetap berlangsung di luar rentang waktu tersebut. Selain itu dilakukan pengamatan metallographic terhadap spesimen untuk mengetahui jenis korosi yang terjadi. HASIL DAN PEMBAHASAN Dari percobaan didapatkan laju korosi sacrificial anode yang ditunjukkan dengan persentase weight loss tampak dalam tabel berikut: Tabel 1. Data Laju Korosi Sacrificial Anode Pada Salinitas 35 O / OO Waktu 1 (gr) 2 (gr) 3 (gr) Rata-rata (gr) Standar Deviasi Korosi Rata-rata (gr) Percent Weight loss (%) Week 0 111, , , ,229 3, ,000 Week 2 111, , , ,971 3,184 0,259 0,225 Week 4 111, , , ,674 3,239 0,555 0,482 Week 6 110, , , ,374 3,304 0,856 0,743 Week 8 110, , , ,113 3,566 1,116 0,968 Week , , , ,879 3,577 1,350 1,172 Week , , , ,699 3,552 1,530 1,328 Week , , , ,480 3,571 1,750 1,518 Week , , , ,343 3,615 1,886 1,637 Tabel 2. Data Laju Korosi Cathode Pada Salinitas 35 O / OO Waktu 1 (gr) 2 (gr) 3 (gr) Rata-rata (gr) Standar Deviasi Korosi Rata-rata (gr) Percent Weight loss (%) Week 0 380, , , ,002 10, ,000 Week , , , ,352 10,493 0,651 0, Neptunus, Vol. 15, No. 2, Januari 2009: 26-33
4 Percent Weight Loss (%) y = Ln(x) Corrosion Rate Trendline Laju Korosi Week 0 Week 2 Week 4 Week 6 Week 8 Week 10 Week 12 Week 14 Week 16 Waktu Gambar 2. Grafik persentase weight loss Sacrificial Anode selama 16 minggu Percent Weight Loss (%) y = Ln(x) Trendline Laju Korosi Week 0 Week 16 Waktu Gambar 3. Grafik Laju Korosi Katoda selama 16 minggu Pada gambar 2 dan gambar 3 terlihat bahwa laju korosi (percent weight loss) yang terjadi pada sacrificial anode adalah rata-rata sebesar 1,637% sedangkan pada baja lunak grade A (katoda) adalah rata-rata sebesar 0,170% pada salinitas 35 O / OO dalam kurun waktu 16 minggu. Dengan demikian efisiensi perlindungan yang diberikan oleh anoda adalah sebesar 99,830%. Selanjutnya dari data yang didapat, dilakukan peramalan dengan jalan melakukan ekstrapolasi selama kurun waktu satu tahun. Hasil peramalan tampak pada gambar 3. Dengan perbandingan masa antara sacrificial anode dengan katoda yaitu 1:4 pada salinitas 35 O / OO, didapatkan hasil peramalan untuk waktu satu tahun sacrificial anode akan terkorosi sebanyak 5,5% dari berat awalnya. Pengamatan Model Pengendalian Korosi pada. 29
5 Gambar 4. Grafik Peramalan Laju Korosi Sacrificial Anode selama 1 tahun PENGAMATAN METALOGRAFI Hasil pengamatan metalografi tampak dalam gambar-gambar berikut: Gambar 5. Foto makro spesimen katoda setelah percobaan Gambar 6. Foto makro spesimen katoda setelah percobaan dengan pembesaran 30 Neptunus, Vol. 15, No. 2, Januari 2009: 26-33
6 Gambar 4. Foto makro spesimen anoda setelah percobaan Gambar 5. Foto makro spesimen anoda setelah percobaan dengan pembesaran Gambar 6. Foto mikro spesimen katoda sebelum pengujian dengan pembesaran 500x Pengamatan Model Pengendalian Korosi pada. 31
7 Gambar 7. Foto mikro spesimen katoda sesudah pengujian dengan pembesaran 500x Gambar 8. Foto mikro spesimen katoda sebelum pengujian dengan pembesaran 500x Gambar 9. Foto mikro spesimen katoda sesudah pengujian dengan pembesaran 500x 32 Neptunus, Vol. 15, No. 2, Januari 2009: 26-33
8 Korosi Yang Terjadi Dari hasil pengamatan metalografi, baik secara makrografi maupun mikrografi, terlihat bahwa beberapa jenis korosi yang terjadi pada kedua kelompok spesimen (sacrificial anode dan katoda) adalah sebagai berikut: Korosi galvanis. Korosi galvanis ini terjadi karena ada dua material yang berbeda potensial, dan saling berdekatan, dipercepat dengan adanya media elektrolit. Korosi abrasi. Korosi abrasi ini terjadi karena permukaan logam mengalami gesekan, dalam hal ini gesekan dengan aliran media korosi secara kontinyu. Korosi pitting. Korosi pitting ini terlihat dengan adanya lubang-lubang kecil di permukaan logam, yang terjadi akibat adanya konsentrasi ion Cl yang tinggi. Hal ini terjadi karena adanya usaha penyesuaian dari permukaan katoda yang menerima elektron dari anoda yang berbeda potensialnya. KESIMPULAN Dari hasil pengamatan pada model yang dibuat dapat diramalkan kemampuan proteksi dari sacrificial anode dengan perbandingan massa sacrificial anode:katoda = 1:4 di mana laju korosi sacrificial anode akan mengikuti persamaan Y = 0,2092X - 0,149 dengan Y menyatakan kehilangan massa anoda akibat korosi dan X menyatakan waktu pengamatan. Laju korosi akan bertambah dengan semakin besarnya perbandingan massa antara sacrificial anode dengan katoda yang dilindungi. DAFTAR PUSTAKA ABS Welding and Fabrication, Weld Test, Rule Requirements for Material and Welding. USA: American Bureau of Shipping. American Society for Testing and Materials section Metal Test Method and Analitical Procedure. ASTM Standards Vol New York: ASTM International. Chamberlain J Korosi untuk Mahasiswa dan Rekayasawan. Jakarta: Gramedia Pustaka Utama. Chandler dan Kenneth A Marine and Offshore Corrosion. London: Butterworth. Kristiyono., Nugroho dan Dwisetiono Pengaruh Sandblasting Terhadap Laju Korosi Pelat Baja Lunak Grade A Pada Media Korosi Air Laut Statis. LIGHT Journal for Engineering Vol. 4.1, April Surabaya: Universitas Muhammadiyah. Widyanto, B Korosi Sebabkan Kerugian Rp. 20T. Sriwijaya Post. Pengamatan Model Pengendalian Korosi pada. 33
PENGAMATAN MODEL KOROSI PADA PIPA SEA WATER SYSTEM KAPAL DENGAN VARIASI LAJU ALIRAN FLUIDA AIR LAUT
PENGAMATAN MODEL KOROSI PADA PIPA SEA WATER SYSTEM KAPAL DENGAN VARIASI LAJU ALIRAN FLUIDA AIR LAUT Dwisetiono Dosen Jurusan Teknik Sistem Perkapalan, Fakultas Teknik dan Ilmu Kelautan, Universitas Hang
Lebih terperinciJURNAL TEKNIK POMITS Vol. 1, No. 1, (2012) 1-6 1
JURNAL TEKNIK POMITS Vol. 1, No. 1, (2012) 1-6 1 PENGARUH VARIASI BENTUK DAN UKURAN GORESAN PADA LAPIS LINDUNG POLIETILENA TERHADAP SISTEM PROTEKSI KATODIK ANODA TUMBAL PADUAN ALUMINIUM PADA BAJA AISI
Lebih terperinciEFEKTIVITAS PENGGUNAAN ANODA KORBAN PADUAN ALUMINIUM PADA PELAT BAJA KAPAL AISI E 2512 TERHADAP LAJU KOROSI DI DALAM MEDIA AIR LAUT
EFEKTIVITAS PENGGUNAAN ANODA KORBAN PADUAN ALUMINIUM PADA PELAT BAJA KAPAL AISI E 2512 TERHADAP LAJU KOROSI DI DALAM MEDIA AIR LAUT EFFECTIVENEES OF USING SACRIFICIAL ANODE OF ALUMINUM ALLOY FOR SHIP STEEL
Lebih terperinciPENGARUH LAJU KOROSI PELAT BAJA LUNAK PADA LINGKUNGAN AIR LAUT TERHADAP PERUBAHAN BERAT.
PENGARUH LAJU KOROSI PELAT BAJA LUNAK PADA LINGKUNGAN AIR LAUT TERHADAP PERUBAHAN BERAT. Hartono Program Diploma III Teknik Perkapala, Fakultas Teknik, Universitas Diponegoro ABSTRACT One of the usage
Lebih terperinciANALISA PERBANDINGAN LAJU KOROSI MATERIAL STAINLESS STEEL SS 316 DENGAN CARBON STEEL A 516 TERHADAP PENGARUH AMONIAK
ANALISA PERBANDINGAN LAJU KOROSI MATERIAL STAINLESS STEEL SS 316 DENGAN CARBON STEEL A 516 TERHADAP PENGARUH AMONIAK * Ir. Soewefy, M.Eng, ** Indra Prasetyawan * Staff Pengajar Jurusan Teknik Perkapalan
Lebih terperinciSTUDI KINERJA BEBERAPA RUST REMOVER
STUDI KINERJA BEBERAPA RUST REMOVER Ferry Budhi Susetyo Jurusan Teknik Mesin, Fakultas Teknik, Universitas Negeri Jakarta e-mail : fbudhi@unj.ac.id Abstrak Rust remover akan menghilangkan seluruh karat
Lebih terperinciBAB I PENDAHULUAN. terjadinya perubahan metalurgi yaitu pada struktur mikro, sehingga. ketahanan terhadap laju korosi dari hasil pengelasan tersebut.
BAB I PENDAHULUAN 1.1 Latar Belakang Pengelasan merupakan proses penyambungan setempat dari logam dengan menggunakan energi panas. Akibat panas maka logam di sekitar lasan akan mengalami siklus termal
Lebih terperinciANALISIS PENGARUH SALINITAS DAN TEMPERATUR AIR LAUT PADA WET UNDERWATER WELDING TERHADAP LAJU KOROSI
JURNAL TEKNIK POMITS Vol. 2, 1, (2013 ISSN: 2337-3539 (2301-9271 Print G-95 ANALISIS PENGARUH SALINITAS DAN TEMPERATUR AIR LAUT PADA WET UNDERWATER WELDING TERHADAP LAJU KOROSI Adrian Dwilaksono, Heri
Lebih terperinciMoch. Novian Dermantoro NRP Dosen Pembimbing Ir. Muchtar Karokaro, M.Sc. NIP
Pengaruh Variasi Bentuk dan Ukuran Scratch Polyethylene Wrap Terhadap Proteksi Katodik Anoda Tumbal Al-Alloy pada Baja AISI 1045 di Lingkungan Air Laut Moch. Novian Dermantoro NRP. 2708100080 Dosen Pembimbing
Lebih terperinciPerlindungan Lambung Kapal Laut Terhadap Korosi Dengan Sacrificial Anode. Oleh : Fahmi Endariyadi
Perlindungan Lambung Kapal Laut Terhadap Korosi Dengan Sacrificial Anode Oleh : Fahmi Endariyadi 20408326 1.1 Latar Belakang Salah satu sumber kerusakan terbesar pada pelat kapal laut adalah karena korosi
Lebih terperinciTERSELESAIKAN H+7 P2
TELAH TERSELESAIKAN PADA P2 Penyusunan Pendahuluan Penyusunan Dasar Teori Metodologi : - Studi Literatur - Pengumpulan Data Lapangan dan Non lapangan - Mapping Sector dan Input Data - Pembuatan Spread
Lebih terperinciAnalisis Perbandingan Laju Korosi Pelat ASTM A36 antara Pengelasan di Udara Terbuka dan Pengelasan Basah Bawah Air dengan Variasi Tebal Pelat
JURNAL TEKNIK POMITS Vol. 2, 1, (2013) ISSN: 2337-3539 (2301-9271 Print) G-73 Analisis Perbandingan Pelat ASTM A36 antara di Udara Terbuka dan Basah Bawah Air dengan Variasi Tebal Pelat Yanek Fathur Rahman,
Lebih terperinciSemarang, 6 juli 2010 Penulis
v KATA PENGANTAR Puji syukur penulis panjatkan kehadirat Allah SWT, karena atas limpahan rahmat dan karunianya penulis dapat menyelesaikan Tesis ini. Dalam penyusunan Tesis dengan judul Efektivitas Penggunaan
Lebih terperinciBAB I PENDAHULUAN Latar Belakang Permasalahan. PT Perusahaan Gas Negara (Persero) Tbk adalah perusahaan yang bergerak
BAB I PENDAHULUAN 1. 1 Latar Belakang Permasalahan PT Perusahaan Gas Negara (Persero) Tbk adalah perusahaan yang bergerak dalam bidang transportasi dan distribusi gas bumi, penggunaan jaringan pipa merupakan
Lebih terperinciAnalisis Pengaruh Cooling Rate pada Material ASTM A36 Akibat Kebakaran Kapal Terhadap Nilai Kekuatan, Kekerasan dan Struktur Mikronya
JURNAL TEKNIK ITS Vol. 6, No. 1, (2017) ISSN: 2337-3539 (2301-9271 Print) G-42 Analisis Pengaruh Cooling Rate pada Material ASTM A36 Akibat Kebakaran Kapal Terhadap Nilai Kekuatan, Kekerasan dan Struktur
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1 Data Hasil Uji Korosi Dari pengujian yang telah dilakukan maka diperoleh hasil berupa data hasil perhitungan weight loss, laju korosi dan efisiensi inhibitor dalam Tabel
Lebih terperinciSTRATEGI PENGENDALIAN UNTUK MEMINIMALISASI DAMPAK KOROSI. Irwan Staf Pengajar Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe ABSTRAK
STRATEGI PENGENDALIAN UNTUK MEMINIMALISASI DAMPAK KOROSI Irwan Staf Pengajar ABSTRAK Korosi merupakan proses pengrusakan bahan akibat interaksi dengan lingkungannya yang terjadi secara alamiah dan tidak
Lebih terperinciPENGARUH TEGANGAN DALAM (INTERNAL STRESS) TERHADAP LAJU KOROSI PADA BAUT
PENGARUH TEGANGAN DALAM (INTERNAL STRESS) TERHADAP LAJU KOROSI PADA BAUT Toto Rusianto Jurusan Teknik Mesin, FTI, IST AKPRIND Yogyakarta Email: totorusianto@yahoo.com ABSTRACT Stress Corrosion Craking
Lebih terperinciLAJU KOROSI PELAT BAJA LUNAK GRADE A YANG TELAH MENGALAMI DEFORMASI PLASTIS PADA MEDIA AIR LAUT
LAJU KOROSI PELAT BAJA LUNAK GRADE A YANG TELAH MENGALAMI DEFORMASI PLASTIS PADA MEDIA AIR LAUT Tri Agung Kristiyono 1, Nur Yanu Nugroho 2 1,2 Jurusan Teknik Perkapalan, Fakultas Teknik dan Ilmu Kelautan
Lebih terperinciPerhitungan Laju Korosi di dalam Larutan Air Laut dan Air Garam 3% pada Paku dan Besi ASTM A36
Perhitungan Laju Korosi di dalam Larutan Air Laut dan Air Garam 3% pada Paku dan Besi ASTM A36 Gurum AP. Ayu SA, Dita Rahmayanti, dan Nindy EM. Jurusan Fisika FMIPA Universitas Lampung. Jl Prof. Dr. Sumantri
Lebih terperinciOptimasi Proses Sand Blasting Terhadap Laju Korosi Hasil Pengecatan Baja Aisi 430
Optimasi Proses Sand Blasting Terhadap Laju Korosi Hasil Pengecatan Baja Aisi 430 Putu Hadi Setyarini, Erwin Sulistyo Jurusan Teknik Mesin Fakultas Teknik Universitas Brawijaya Jl. Mayjend Haryono no.
Lebih terperinciProteksi Katodik dengan Menggunakan Anoda Korban pada Struktur Baja Karbon dalam Larutan Natrium Klorida
Proteksi Katodik dengan Menggunakan Anoda Korban pada Struktur Baja Karbon dalam Larutan Natrium Klorida Rahmat Ilham, Komalasari, Rozanna Sri Irianty Jurusan S1 Teknik Kimia, Fakultas Teknik, Universitas
Lebih terperinciPengaruh Polutan Terhadap Karakteristik dan Laju Korosi Baja AISI 1045 dan Stainless Steel 304 di Lingkungan Muara Sungai
Pengaruh Polutan Terhadap Karakteristik dan Laju Korosi Baja AISI 1045 dan Stainless Steel 304 di Lingkungan Muara Sungai Muhammad Nanang Muhsinin 2708100060 Dosen Pembimbing Budi Agung Kurniawan, ST,
Lebih terperinciStudi Perbandingan Kinerja Anoda Korban Paduan Aluminium dengan Paduan Seng dalam Lingkungan Air Laut
Studi Perbandingan Kinerja Anoda Korban Paduan Aluminium dengan Paduan Seng dalam Lingkungan Air Laut Juliana Anggono, Soejono Tjitro Dosen Fakultas Teknik, Jurusan Teknik Mesin Universitas Kristen Petra
Lebih terperinciAnalisa Pengaruh Jenis Elektroda terhadap Laju Korosi pada Pengelasan Pipa API 5L Grade X65 dengan Media Korosi FeCl 3
JURNAL TEKNIK ITS Vol. 1, No. 1 (Sept. 2012) ISSN: 2301-9271 G-124 Analisa Pengaruh Jenis Elektroda terhadap Laju Korosi pada Pengelasan Pipa API 5L Grade X65 dengan Media Korosi FeCl 3 Gita Anggaretno,
Lebih terperinciTUGAS SARJANA. KOROSI GALVANIS PADA STEEL AISI Cu DENGAN VARIASI PEMBIASAN SCRAP STEEL SEBAGAI ANODA KEDUA PADA MEDIUM NaCl
TUGAS SARJANA KOROSI GALVANIS PADA STEEL AISI 1018 - Cu DENGAN VARIASI PEMBIASAN SCRAP STEEL SEBAGAI ANODA KEDUA PADA MEDIUM NaCl Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Kesarjanaan Strata
Lebih terperinciBAB I PENDAHULUAN. juga menjadi bisnis yang cukup bersaing dalam perusahaan perbajaan.
BAB I PENDAHULUAN 1.1. Latar Belakang. Pipa merupakan salah satu kebutuhan yang di gunakan untuk mendistribusikan aliran fluida dari suatu tempat ketempat yang lain. Berbagi jenis pipa saat ini sudah beredar
Lebih terperinciPengukuran Laju Korosi Aluminum 1100 dan Baja 1020 dengan Metoda Pengurangan Berat Menggunakan Salt Spray Chamber
TUGAS AKHIR Pengukuran Laju Korosi Aluminum 1100 dan Baja 1020 dengan Metoda Pengurangan Berat Menggunakan Salt Spray Chamber Disusun Oleh: FEBRIANTO ANGGAR WIBOWO NIM : D 200 040 066 JURUSAN TEKNIK MESIN
Lebih terperinciTUGAS AKHIR S T U DI LAJU KOROSI WELD JOINT M A T ERIAL PHYTRA AGASTAMA
TUGAS AKHIR S T U DI LAJU KOROSI WELD JOINT M A T ERIAL BAJA A 36 PADA U N DERWATER WELDING PHYTRA AGASTAMA 4305 100 027 DOSEN PEMBIMBING : Yeyes Mulyadi, ST. M.Sc. Ir. Heri Supomo, M.Sc. HOME LATAR BELAKANG
Lebih terperinciBAB I PENDAHULUAN. 1.1 Latar Belakang. Penggunaan logam dalam perkembangan teknologi dan industri
BAB I PENDAHULUAN 1.1 Latar Belakang Penggunaan logam dalam perkembangan teknologi dan industri sebagai salah satu material penunjang sangat besar peranannya, akan tetapi dalam kehidupan sehari-hari banyak
Lebih terperinciPENGARUH VARIASI KONSENTRASI LARUTAN NaCl DENGAN KONSENTRASI 3,5%, 4% DAN 5% TERHADAP LAJU KOROSI BAJA KARBON SEDANG
TUGAS AKHIR PENGARUH VARIASI KONSENTRASI LARUTAN NaCl DENGAN KONSENTRASI 3,5%, 4% DAN 5% TERHADAP LAJU KOROSI BAJA KARBON SEDANG Disusun : RULENDRO PRASETYO NIM : D 200 040 074 JURUSAN TEKNIK MESIN FAKULTAS
Lebih terperinciPENGARUH VARIASI KONSENTRASI LARUTAN NaCl DENGAN KONSENTRASI 3,5%, 4% DAN 5% TERHADAP LAJU KOROSI ALUMINUM 5052
TUGAS AKHIR PENGARUH VARIASI KONSENTRASI LARUTAN NaCl DENGAN KONSENTRASI 3,5%, 4% DAN 5% TERHADAP LAJU KOROSI ALUMINUM 5052 Disusun : HARI SUPRIYADI NIM : D 200 040 039 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK
Lebih terperinciDosen Pembimbing : Sutarsis,ST,M.Sc.Eng. Oleh : Sumantri Nur Rachman
Pengaruh Konsentrasi O 2 Terhadap Kebutuhan Arus Proteksi dan Umur Anoda pada sistem Impressed Current Cathodic Protection (ICCP) dengan menggunakan anoda SS 304 mesh pada Beton Bertulang Oleh : Sumantri
Lebih terperinciLAJU DAN BENTUK KOROSI PADA BAJA KARBON MENENGAH YANG MENDAPAT PERLAKUAN PADA SUHU AUSTENIT DIUJI DI DALAM LARUTAN NaCl 3 N
Jurnal Desiminasi Teknologi, Volume 1, Nomor 1, Januari 2013, Hal 44-49 LAJU DAN BENTUK KOROSI PADA BAJA KARBON MENENGAH YANG MENDAPAT PERLAKUAN PADA SUHU AUSTENIT DIUJI DI DALAM LARUTAN NaCl 3 N R. KOHAR
Lebih terperinciPENGARUH TEMPERATUR PADA COATING WRAPPING TAPE TERHADAP COATING BREAKDOWN
PENGARUH TEMPERATUR PADA COATING WRAPPING TAPE TERHADAP COATING BREAKDOWN DAN CURRENT DENSITY PADA PIPA BAJA DALAM APLIKASI IMPRESSED CURRENT CATHODIC PROTECTION (ICCP) R.E.Dinar Rahmawati 1,a, Muhammad
Lebih terperinciPEMANFAATAN DAUN JAMBU BIJI (Psidiifolium) SEBAGAI BIOINHIBITOR KOROSI PADA LOGAM BAJA KARBON
PEMANFAATAN DAUN JAMBU BIJI (Psidiifolium) SEBAGAI BIOINHIBITOR KOROSI PADA LOGAM BAJA KARBON DiajukanSebagaiPersyaratanUntukMenyelesaikan Pendidikan Diploma III JurusanTeknik Kimia PoliteknikNegeriSriwijaya
Lebih terperinciANALISA LAJU KOROSI PENGARUH POST WELD HEAT TREATMENT TERHADAP UMUR PIPA PADA PIPA API 5L GRADE B
ANALISA LAJU KOROSI PENGARUH POST WELD HEAT TREATMENT TERHADAP UMUR PIPA PADA PIPA API 5L GRADE B Oleh : Ikhsan Kholis *) ABSTRAK Jaringan perpipaan banyak digunakan dalam kegiatan eksplorasi minyak dan
Lebih terperinciDESAIN PROSES LAS PENGURANG PELUANG TERJADINYA KOROSI. Abstrak
Seminar Nasional Teknologi Terapan (SNTT) 2015-JTM Polinema 36 DESAIN PROSES LAS PENGURANG PELUANG TERJADINYA KOROSI 1 Muhammad Akhlis Rizza, 2 Agus Dani 1,2 Teknik Mesin Politeknik Negeri Malang, Jl.
Lebih terperinciTugas Akhir. Studi Corrosion Fatigue Pada Sambungan Las SMAW Baja API 5L Grade X65 Dengan Variasi Waktu Pencelupan Dalam Larutan HCl
Tugas Akhir Studi Corrosion Fatigue Pada Sambungan Las SMAW Baja API 5L Grade X65 Dengan Variasi Waktu Pencelupan Dalam Larutan HCl Oleh : Wishnu Wardhana 4305 100 024 Dosen Pembimbing: Murdjito, M.Sc.
Lebih terperinciELEKTROKIMIA DAN KOROSI (Continued) Ramadoni Syahputra
ELEKTROKIMIA DAN KOROSI (Continued) Ramadoni Syahputra 3.3 KOROSI Korosi dapat didefinisikan sebagai perusakan secara bertahap atau kehancuran atau memburuknya suatu logam yang disebabkan oleh reaksi kimia
Lebih terperinciANALISIS LAJU KOROSI PADA BAJA KARBON DENGAN MENGGUNAKAN AIR LAUT DAN H 2 SO 4
ANALISIS LAJU KOROSI PADA BAJA KARBON DENGAN MENGGUNAKAN AIR LAUT DAN H 2 SO 4 Kevin J. Pattireuw, Fentje A. Rauf, Romels Lumintang. Teknik Mesin, Universitas Sam Ratulangi Manado 2013 ABSTRACT In this
Lebih terperinciPerhitungan Teknis LITERATUR MULAI STUDI SELESAI. DATA LAPANGAN : -Data Onshore Pipeline -Data Lingkungan -Mapping Sector HASIL DESAIN
MULAI STUDI LITERATUR DATA LAPANGAN : -Data Onshore Pipeline -Data Lingkungan -Mapping Sector DATA NON LAPANGAN : -Data Dimensi Anode -Data Harga Anode DESAIN MATERIAL ANODE DESAIN TIPE ANODE Perhitungan
Lebih terperinciANALISA DESAIN SISTEM SS IMPRESSED CURRENT CATHODIC PROTECTION (ICCP) PADA OFFSHORE PIPELINE MILIK JOB PERTAMINA PETROCHINA EAST JAVA
ANALISA DESAIN SISTEM SS IMPRESSED CURRENT CATHODIC PROTECTION (ICCP) PADA OFFSHORE PIPELINE MILIK JOB PERTAMINA PETROCHINA EAST JAVA OLEH : Rizky Ayu Trisnaningtyas 4306100092 DOSEN PEMBIMBING : 1. Ir.
Lebih terperinciKorosi telah lama dikenal sebagai salah satu proses degradasi yang sering terjadi pada logam, khusunya di dunia body automobiles.
JURUSAN TEKNIK MATERIAL DAN METALURGI FAKULTAS TEKNOLOGI INDUSTRI INSTITUT TEKNOLOGI SEPULUH NOPEMBER SURABAYA Korosi telah lama dikenal sebagai salah satu proses degradasi yang sering terjadi pada logam,
Lebih terperinciANALISIS KEGAGALAN AKIBAT KOROSI DAN KERETAKAN PADA PIPA ALIRAN GAS ALAM DI NEB#12 PETROCHINA INTERNATIONAL JABUNG LTD
ANALISIS KEGAGALAN AKIBAT KOROSI DAN KERETAKAN PADA PIPA ALIRAN GAS ALAM DI NEB#12 PETROCHINA INTERNATIONAL JABUNG LTD Nama Mahasiswa : B A S U K I NRP : 2702 100 017 Jurusan : Teknik Material FTI-ITS
Lebih terperinciAnalisa Kekuatan Material Carbon Steel ST41 Pengaruh Preheat dan PWHT Dengan Uji Tarik Dan Micro Etsa
JURNAL TEKNIK POMITS Vol. 2, No. 1, (2013) ISSN: 2337-3539 (2301-9271 Print) 1 Analisa Kekuatan Material Carbon Steel ST41 Pengaruh Preheat dan PWHT Dengan Uji Tarik Dan Micro Etsa Bagus Cahyo Juniarso,
Lebih terperinciPENINGKATAN KETAHANAN KOROSI BAJA JIS S45C HASIL ELECTROPLATING NIKEL PADA APLIKASI MATERIAL CRYOGENIC
PENINGKATAN KETAHANAN KOROSI BAJA JIS S45C HASIL ELECTROPLATING NIKEL PADA APLIKASI MATERIAL CRYOGENIC Mirza Pramudia 1 1 Fakultas Teknik, Universitas Trunojoyo, Madura Jl. Raya Telang, Po. Box 2 Kamal,
Lebih terperinciDAFTAR ISI LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL...
DAFTAR ISI Halaman LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL... DAFTAR LAMPIRAN... i ii iii iv v vi ix xi xii BAB 1
Lebih terperinciPRESENTASI FIELD PROJECT
PRESENTASI FIELD PROJECT TEKNIK PERANCANGAN DAN KONSTRUKSI KAPAL JURUSAN TEKNIK BANGUNAN KAPAL POLITEKNIK PERKAPALAN NEGERI SURABAYA INSTITUT TEKNOLOGI SEPULUH NOPEMBER 2011 Presented by: Khairul Akbar
Lebih terperinciPENGARUH VARIASI TEMPERATUR PADA PROSES PERLAKUAN PANAS BAJA AISI 304 TERHADAP LAJU KOROSI
Teknika : Engineering and Sains Journal Volume, Nomor, Juni 207, 67-72 ISSN 2579-5422 online ISSN 2580-446 print PENGARUH VARIASI TEMPERATUR PADA PROSES PERLAKUAN PANAS BAJA AISI 304 TERHADAP LAJU KOROSI
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1. Analisa Laju Korosi Stainless Steel AISI 304 Pengujian terhadap impeller dengan material baja tahan karat AISI 304 dengan media limbah pertambangan batu bara di BATAN Puspitek
Lebih terperinciSTUDI EKONOMIS PENGARUH POST WELD HEAT TREATMENT TERHADAP UMUR PIPA
STUDI EKONOMIS PENGARUH POST WELD HEAT TREATMENT TERHADAP UMUR PIPA OLEH : NICKY ERSANDI NRP. 4105 100 041 DOSEN PEMBIMBING : DONY SETYAWAN, ST., M.Eng 1. PENDAHULUAN A. Latar belakang Material kapal harus
Lebih terperinciSTUDI PENGARUH VARIASI KUAT ARUS PENGELASAN PELAT AISI 444 MENGGUNAKAN ELEKTRODA AWS E316L
EKSERGI Jurnal Teknik Energi Vol 13 No. 1 Januari 2017; 10-14 STUDI PENGARUH VARIASI KUAT ARUS PENGELASAN PELAT AISI 444 MENGGUNAKAN ELEKTRODA AWS E316L Ojo Kurdi Departement Teknik Mesin, Fakultas Teknik,
Lebih terperinciEfektivitas Penggunaan Anoda Korban Paduan Seng Pada Pelat Baja Kapal AISI E 2512 Terhadap Laju Korosi Di Dalam Media Air Laut
Efektivitas Penggunaan Anoda Korban Paduan Seng Pada Pelat Baja Kapal AISI E 2512 Terhadap Laju Korosi Di Dalam Media Air Laut Lia Pongsapan 1), 1) Amin Suhadi 2) Program Studi Teknik Mesin Fakultas Teknologi
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1. Analisis Laju Korosi Baja Karbon Pengujian analisis dilakukan untuk mengetahui prilaku korosi dan laju korosi baja karbon dalam suatu larutan. Pengujian ini dilakukan dengan
Lebih terperinciJumlah Anoda (N) Tahanan Kabel (R2) Tahanan Total (Rt) = Ic / Io = 21,62 / 7 = 3,1. R2 = R1 + α (T2 T1) = 0, ,00393 (30-24) = 0,02426 ohm/m
Jumlah Anoda (N) N = Ic / Io = 21,62 / 7 = 3,1 Tahanan Kabel (R2) R2 = R1 + α (T2 T1) = 0,00068 + 0,00393 (30-24) = 0,02426 ohm/m Tahanan Total (Rt) Rt = Tahanan Anoda Rectifier + Tahanan Anoda = 1,02
Lebih terperinciSTUDI LAJU KOROSI WELD JOINT MATERIAL A36 PADA UNDERWATER WELDING
STUDI LAJU KOROSI WELD JOINT MATERIAL A36 PADA UNDERWATER WELDING Phytra Agastama 1, Yeyes Mulyadi 2, Heri Supomo 3 1) Mahasiswa Jurusan Teknik Kelautan 2) Staf Pengajar Jurusan Teknik Kelautan 3) Staf
Lebih terperinciCARBON STEEL CORROSION IN THE ATMOSPHERE, COOLING WATER SYSTEMS, AND HOT WATER Gatot Subiyanto and Agustinus Ngatin
CARBON STEEL CORROSION IN THE ATMOSPHERE, COOLING WATER SYSTEMS, AND HOT WATER Gatot Subiyanto and Agustinus Ngatin Chemical Engineering Department Bandung State Polytechnic E.mail : Gattot_Subiyanto@yahoo.com
Lebih terperinciJURNAL SAINS DAN SENI POMITS Vol. 1, No. 1, (2012) 1-5 1
JURNAL SAINS DAN SENI POMITS Vol. 1, No. 1, (2012) 1-5 1 Pengaruh Perlakuan Panas Pada Anoda Korban Aluminium Galvalum Iii Terhadap Laju Korosi Pelat Baja Karbon Astm A380 Grade C Kharisma Permatasari,
Lebih terperinciPENGARUH TEGANGAN DAN KONSENTRASI NaCl TERHADAP KOROSI RETAK TEGANG PADA BAJA DARI SPONS BIJIH LATERIT SKRIPSI
PENGARUH TEGANGAN DAN KONSENTRASI NaCl TERHADAP KOROSI RETAK TEGANG PADA BAJA DARI SPONS BIJIH LATERIT SKRIPSI Oleh BUDI SETIAWAN 04 03 04 015 8 DEPARTEMEN METALURGI DAN MATERIAL FAKULTAS TEKNIK UNIVERSITAS
Lebih terperinciPENGARUH RASIO DIAMETER TERHADAP KEDALAMAN PADA LAJU KOROSI BAJA KARBON SEDANG
TUGAS AKHIR PENGARUH RASIO DIAMETER TERHADAP KEDALAMAN PADA LAJU KOROSI BAJA KARBON SEDANG Disusun Oleh: ADI PRABOWO D 200 040 049 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH SURAKARTA
Lebih terperinciJURNAL TEKNIK ITS Vol. 4, No. 1, (2015) ISSN: ( Print) F-56
JURNAL TEKNIK ITS Vol., No., () ISSN: -9 (-9 Print) F- Pengaruh Variasi Goresan Lapis Lindung dan Variasi ph Tanah terhadap Arus Proteksi Sistem Impressed Current Cathodic Protection (ICCP) pada Pipa API
Lebih terperinciKata kunci : BEM, Korosi, Beton berulang, Proteksi katodik, Anoda korban, Simulasi
Simulasi Desain Sistem Proteksi Katodik Anoda Korban pada Balok Beton Bertulang Dermaga Menggunakan Metode Elemen Batas M. Ridha a, S. Fonna b, M. R. Hidayatullah c, S. Huzni, S. Thalib Jurusan Teknik
Lebih terperinciPENGARUH VARIASI SUHU PREHEAT TERHADAP SIFAT MEKANIK MATERIAL SA 516 GRADE 70 YANG DISAMBUNG DENGAN METODE PENGELASAN SMAW
Abstrak PENGARUH VARIASI SUHU PREHEAT TERHADAP SIFAT MEKANIK MATERIAL SA 516 GRADE 70 YANG DISAMBUNG DENGAN METODE PENGELASAN SMAW Gathot DW1*, Nur H 2* Budi LS 3*,Abdillah GB 4* Prodi D-3 Teknik Mesin
Lebih terperinciSTUDI PENGGUNAAN EKSTRAK BAHAN ALAMI SEBAGAI INHIBITOR KOROSI PADA CAT UTUK PELAT KAPAL A36
JURNAL TEKNIK POMITS Vol. 2, No. 1, (2013) ISSN: 2337-3539 (2301-9271 Print) 1 STUDI PENGGUNAAN EKSTRAK BAHAN ALAMI SEBAGAI INHIBITOR KOROSI PADA CAT UTUK PELAT KAPAL A36 Roni Septiari, Heri Supomo Jurusan
Lebih terperinciPengaruh variasi pembagian jumlah anoda dengan pola horisontal terhadap laju korosi baja SS400 pada media air laut
Dinamika Teknik Mesin 8 (2018) 14-20 Pengaruh variasi pembagian jumlah anoda dengan pola horisontal terhadap laju korosi baja SS400 pada media air laut A. Faisol *, Sumarji, G. Djatisukamto 1,2 Teknik
Lebih terperinciLaju Korosi Sea Chest Grate Galvanis Terhadap Variasi Waktu Dan Salinitas Air Laut
Laju Korosi Sea Chest Grate Galvanis Terhadap Variasi Waktu Dan Salinitas Air Laut LAJU KOROSI SEA CHEST GRATE GALVANIS TERHADAP VARIASI WAKTU DAN SALINITAS AIR LAUT Bary Juang Sulaiman Putra Hidayat S1
Lebih terperinciMODEL LAJU KOROSI BAJA KARBON ST-37 DALAM LINGKUNGAN HIDROGEN SULFIDA
MODEL LAJU KOROSI BAJA KARBON ST-37 DALAM LINGKUNGAN HIDROGEN SULFIDA Oleh : Agus Solehudin 1), Ratnaningsih E. Sardjono 2), Isdiriayani Nurdin 3) dan Djoko H.Prajitno 4) (1) Jurusan Pendidikan Teknik
Lebih terperinciBAB I PENDAHULUAN. Pengelasan adalah suatu proses penggabungan antara dua. logam atau lebih yang menggunakan energi panas.
BAB I PENDAHULUAN 1.1. Latar Belakang Pengelasan adalah suatu proses penggabungan antara dua logam atau lebih yang menggunakan energi panas. Teknologi pengelasan tidak hanya digunakan untuk memproduksi
Lebih terperinciPENGENDALIAN KOROSI PADA PLAT LAMBUNG KAPAL DENGAN MENGGUNAKAN ANODA KORBAN
PENGENDALIAN KOROSI PADA PLAT LAMBUNG KAPAL DENGAN MENGGUNAKAN ANODA KORBAN Ir. Edi Septe.,MT 1) Iman Satria, ST.,MT 2) Khairul Huda 3) Program Studi Teknik Mesin-Fakultas Teknologi Industri Universitas
Lebih terperinciBAB III METODOLOGI PENELITIAN
komposisi tidak homogen akan memiliki perbedaan kelarutan dalam pembersihan, sehingga beberapa daerah ada yang lebih terlarut dibandingkan dengan daerah yang lainnya. Ketika oksida dihilangkan dari permukaan,
Lebih terperinciGambar 3.1 Diagram Alir Penelitian
22 BAB 3 METODOLOGI PENELITIAN 3.1 Alur Proses Penelitian Mulai Preparasi dan larutan Pengujian Polarisasi Potensiodinamik untuk mendapatkan kinetika korosi ( no. 1-7) Pengujian Exposure (Immersion) untuk
Lebih terperinciPengujian Impak (Hentakan) Pengujian Metalografi Pengujian Korosi Parameter pada Lambung Kapal...
DAFTAR ISI HALAMAN JUDUL... i LEMBAR PENGESAHAN DOSEN PEMBIMBING... ii LEMBAR PENGESAHAN DOSEN PENGUJI... iii HALAMAN PERSEMBAHAN... iv HALAMAN MOTTO... v KATA PENGANTAR... vi ABSTRAK... viii ABSTRACT...
Lebih terperinciANALISA PROTEKSI KATODIK DENGAN MENGGUNAKAN ANODA TUMBAL PADA PIPA GAS BAWAH TANAH PT. PUPUK KALIMANTAN TIMUR DARI STASIUN KOMPRESSOR GAS KE KALTIM-2
JURNAL TEKNIK POMITS Vol. 2, No. 1, (2014) ISSN: 2337-3539 (2301-9271 Print) 1 ANALISA PROTEKSI KATODIK DENGAN MENGGUNAKAN ANODA TUMBAL PADA PIPA GAS BAWAH TANAH PT. PUPUK KALIMANTAN TIMUR DARI STASIUN
Lebih terperinciBAB IV ANALISA DAN PEMBAHASAN
BAB IV ANALISA DAN PEMBAHASAN 4.1. Hasil Anodizing Hasil anodizing aluminium 1XXX dengan variasi intensitas arus 0,016A/mm 2, 0,022A/mm 2, 0,028A/mm² dan waktu pencelupan 10 menit, terdapat kegagalan atau
Lebih terperinciBAB I PENDAHULUAN 1.1. Latar belakang
BAB I PENDAHULUAN 1.1. Latar belakang Aluminium merupakan jenis logam yang banyak digunakan dalam industri maupun rumah tangga. Aluminium banyak dimanfaatkan dikarenakan memiliki kelebihan diantaranya
Lebih terperinciSTUDI IMPRESSED CURRENT CATHODIC PROTECTION
TUGAS SARJANA STUDI IMPRESSED CURRENT CATHODIC PROTECTION PADA BAJA AISI 1018 DENGAN MENGGUNAKAN ANODA SCRAP STEEL DAN PENGGUNAAN TEMBAGA SEBAGAI ANODA KEDUA PADA MEDIUM NaCl Diajukan Sebagai Salah Satu
Lebih terperinciAnalisa Tegangan pada Pipa yang Memiliki Korosi Sumuran Berbentuk Limas dengan Variasi Kedalaman Korosi
1 Analisa Tegangan pada Pipa yang Memiliki Sumuran Berbentuk Limas dengan Variasi Kedalaman Muhammad S. Sholikhin, Imam Rochani, dan Yoyok S. Hadiwidodo Jurusan Teknik Kelautan, Fakultas Teknologi Kelautan,
Lebih terperinciANTI KOROSI BETON DI LINGKUNGAN LAUT
ANTI KOROSI BETON DI LINGKUNGAN LAUT Pendahuluan : Banyak bangunan di lingkungan Unit Bisnis Pembangkitan Suralaya terkena korosi terutama konstruksi beton di bawah duck beton dermaga Oil Jetty ( SPOJ
Lebih terperinciBAB IV HASIL PENELITIAN DAN PEMBAHASAN. A. Deskripsi Data
BAB IV HASIL PENELITIAN DAN PEMBAHASAN A. Deskripsi Data Penelitian ini merupakan eksperimen untuk mengetahui pengaruh temperatur media pendingin pasca pengelasan terhadap laju korosi dan struktur mikro.
Lebih terperinciBAB I PENDAHULUAN. adalah karena sifat-sifat dari logam jenis ini yang bervariasi, yaitu bahwa
BAB I PENDAHULUAN A. LATAR BELAKANG Dewasa ini penggunaan baja semakin meningkat sebagai bahan industri. Hal ini sebagian ditentukan oleh nilai ekonominya, tetapi yang paling penting adalah karena sifat-sifat
Lebih terperinciPERANCANGAN ALAT UJI KOROSI SALT SPRAY CHAMBER DAN APLIKASI PENGUKURAN LAJU KOROSI PLAT BODY AUTOMOBILES PRODUKSI EROPA DAN PRODUKSI JEPANG PADA
PERANCANGAN ALAT UJI KOROSI SALT SPRAY CHAMBER DAN APLIKASI PENGUKURAN LAJU KOROSI PLAT BODY AUTOMOBILES PRODUKSI EROPA DAN PRODUKSI JEPANG PADA MEDIA NaCl DENGAN VARIASI KONSENTRASI RANDI AGUNG PRATAMA
Lebih terperinciBAB I PENDAHULUAN. 1.1 Latar Belakang. Proses akhir logam (metal finishing) merupakan bidang yang sangat luas,
BAB I PENDAHULUAN 1.1 Latar Belakang Proses akhir logam (metal finishing) merupakan bidang yang sangat luas, yang dimana tujuan utamanya adalah untuk mencegah logam dengan korosifnya, namun juga mendapatkan
Lebih terperinciProteksi Katodik Metoda Anoda Tumbal Untuk Mengendalikan Laju Korosi
Proteksi Katodik Metoda Anoda Tumbal Untuk Mengendalikan Laju Korosi Fitri Afriani S, Komalasari, Zultiniar Laboratorium Konversi Elektrokimia Program Studi Sarjana Teknik Kimia, Fakultas Teknik Universitas
Lebih terperinciI. PENDAHULUAN. keling. Ruang lingkup penggunaan teknik pengelasan dalam konstruksi. transportasi, rel, pipa saluran dan lain sebagainya.
I. PENDAHULUAN A. Latar Belakang Pengembangan teknologi di bidang konstruksi yang semakin maju tidak dapat dipisahkan dari pengelasan, karena mempunyai peranan penting dalam rekayasa dan reparasi logam.
Lebih terperinciANALISIS STRESS CORROSION CRACKING LOGAM TEMBAGA DENGAN METODE U-BEND PADA MEDIA KOROSI NH4OH 1M
ANALISIS STRESS CORROSION CRACKING LOGAM TEMBAGA DENGAN METODE U-BEND PADA MEDIA KOROSI NH4OH 1M *Ardia Wanandi Suwarno 1, Athanasius Priharyoto Bayuseno 2 1 Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik,
Lebih terperinciPENDAHULUAN PERUMUSAN MASALAH. Bagaimana pengaruh interaksi antar korosi terhadap tegangan pada pipa?
PENDAHULUAN Korosi yang menyerang sebuah pipa akan berbeda kedalaman dan ukurannya Jarak antara korosi satu dengan yang lain juga akan mempengaruhi kondisi pipa. Dibutuhkan analisa lebih lanjut mengenai
Lebih terperinciPENGARUH FEED RATE TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN BENDING PADA PENGELASAN FRICTION STIR WELDING ALUMINIUM 5052
PENGARUH FEED RATE TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN BENDING PADA PENGELASAN FRICTION STIR WELDING ALUMINIUM 505 Lukito Adi Wicaksono Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah
Lebih terperinciKEKERASAN DAN TEGANGAN TARIK LASAN BAJA ST-37 PADA POSISI VERTIKAL DAN HORIZONTAL ABSTRAK
KEKERASAN DAN TEGANGAN TARIK LASAN BAJA ST-37 PADA POSISI VERTIKAL DAN HORIZONTAL Author Guidance : Afrian Sugiharto : I Dewa Gede Ary Subagia ST.,MT.,PhD : Ir. I Nyoman Budiarsa, M.T.,PhD ABSTRAK Las
Lebih terperinciPENGGUNAN LAS TAHANAN LISTRIK PADA PROSES PERAKITAN SHADOW MASK PADA INDUSTRI TABUNG TELEVISI
PENGGUNAN LAS TAHANAN LSTRK PADA PROSES PERAKTAN SHADOW MASK PADA NDUSTR TABUNG TELEVS Melvin Emil Simanjuntak *) *) Staf Pengajar Jurusan Teknik Mesin Politeknik Negeri Medan Abstrak Proses welding adalah
Lebih terperinciSKRIPSI. PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM :
SKRIPSI PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM : 1104305004 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS UDAYANA
Lebih terperinciBAB 1 PENDAHULUAN. Universitas Sumatera Utara
BAB 1 PENDAHULUAN 1.1 Latar belakang Air merupakan unsur yang vital dalam kehidupan manusia. Seseorang tidak dapat bertahan hidup tanpa air, karena itulah air merupakan salah satu penopang hidup bagi manusia.
Lebih terperinciTUGAS KOROSI FAKTOR FAKTOR YANG MEMPENGARUHI LAJU KOROSI
TUGAS KOROSI FAKTOR FAKTOR YANG MEMPENGARUHI LAJU KOROSI Makalah ini disusun untuk memenuhi tugas mata kuliah Korosi Dosen pengampu: Drs. Drs. Ranto.H.S., MT. Disusun oleh : Deny Prabowo K2513016 PROGRAM
Lebih terperinciANALISA LAJU KOROSI DUPLEX SS AWS 2205 DENGAN METODE WEIGHT LOSS
ANALISA LAJU KOROSI DUPLEX SS AS 2205 DENGAN METODE EIGHT LOSS Minto Basuki 1, Abdul Aris acana Putra 1, Dzikri Hidayat 1 1 Jurusan Teknik Perkapalan Fakultas Teknologi Mineral dan Kelautan Institut Teknologi
Lebih terperinciBAB I PENDAHULUAN. semakin dibutuhkan. Semakin luas penggunaan las mempengaruhi. mudah penggunaannya juga dapat menekan biaya sehingga lebih
BAB I PENDAHULUAN 1.1 Latar Belakang Perkembangan teknologi dalam bidang konstruksi semakin maju, baik di dalam perakitan maupun perawatan. Seiring kemajuan teknologi dalam bidang konstruksi, membuat kebutuhan
Lebih terperinciANALISA KEKUATAN BAHAN STEEL 304 TERHADAP KEKUATAN IMPAK BENDA JATUH BEBAS ABSTRAK
ANALISA KEKUATAN BAHAN STEEL 304 TERHADAP KEKUATAN IMPAK BENDA JATUH BEBAS M Bima Syah Alam 1, Din Aswan Amran Ritonga, ST, MT 2 1,2 Jurusan Teknik Mesin Sekolah Tinggi Teknik Harapan Medan 2016 E-mail
Lebih terperinciBAB I PENDAHULUAN. Banyak cara yang dapat dilakukan dalam teknik penyambungan logam misalnya
BAB I PENDAHULUAN A. Latar Belakang Teknik penyambungan logam telah diketahui sejak dahulu kala. Sumber energi yang digunakan pada zaman dahulu diduga dihasilkan dari pembakaran kayu atau sampah. Karena
Lebih terperinciPengaruh Jarak Anoda-Katoda dan Durasi Pelapisan Terhadap Laju Korosi pada Hasil Electroplating Hard Chrome
JTERA - Jurnal Teknologi Rekayasa, Vol. 1, No. 1, Desember 2016, Hal. 1-6 ISSN 2548-737X Pengaruh Jarak Anoda-Katoda dan Durasi Pelapisan Terhadap Laju Korosi pada Hasil Electroplating Hard Chrome Abid
Lebih terperinciBAB I PENDAHULUAN 1.1 Latar belakang
BAB I PENDAHULUAN 1.1 Latar belakang Dalam proses pembuatan komponen-komponen atau peralatan-peralatan permesinan dan industri, dibutuhkan material dengan sifat yang tinggi maupun ketahanan korosi yang
Lebih terperinciPertemuan <<22>> <<PENCEGAHAN KOROSI>>
Matakuliah Tahun : Versi : / : Pertemuan 1 Learning Outcomes Pada akhir pertemuan ini, diharapkan mahasiswa akan mampu
Lebih terperinci