PEMANFAATAN ABU PEMBAKARAN AMPAS TEBU DAN TANAH LIAT PADA PEMBUATAN BATU BATA SKRIPSI Diajukan untuk melengkapi tugas dan memenuhi syarat mencapai gelar Sarjana Sains NURAISYAH SIREGAR 040801039 DEPARTEMEN FISIKA FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA MEDAN 2010
PERSETUJUAN Judul : PEMANFAATAN ABU PEMBAKARAN AMPAS TEBU DAN TANAH LIAT PADA PEMB UATAN BATU BATA Kategori : SKRIPSI Nama : NURAISYAH SIREGAR Nomor Induk Mahasiswa : 040801039 Program Studi : FISIKA (S1) Departemen : FISIKA Fakultas : MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) UNIVERSITAS SUMATERA UTARA Diluluskan di Medan, Oktober 2009 Diketahui Departemen Fisika FMIPA USU Ketua, Pembimbing, Dr.Marhaposan Situmorang Drs.Kerista Sebayang,M.S NIP : 195510301980031003 NIP : 195806231986011001
PERNYATAAN PEMANFAATAN ABU PEMBAKARAN AMPAS TEBU DAN TANAH LIAT PADA PEMBUATAN BATU BATA SKRIPSI Saya mengakui bahwa skripsi ini adalah hasil kerja saya sendiri,kecuali beberapa kutipan dan ringkasan yang masing-masing disebutkan sumbernya. Medan, November 2009 NURAISYAH SIREGAR 040801039
PENGHARGAAN Puji dan syukur Penulis panjatkan kepada Allah SWT.yang telah melimpahkan rahmat dan karunia-nya kepada Penulis sehingga dapat menyelesaikan kripsi ini sebagai salah satu syarat untuk menyelesaikan pendidikan di Program Studi Fisika S1,Fakultas Matematika dan Ilmu Pengetahuan Alam. Ucapan terimakasih Penulis sampaikan kepada bapak Drs.Kerista Sebayang,MS, yang telah membimbing dan memberikan kepercayaan kepada Penulis sehingga skripsi ini dapat diselesaikan dalam waktu yang telah ditetepkan.ucapan terimakasih juga ditujukan kepada ketua dan sekretaris departemen fisika Dr.Marhaposan Situmorang dan Dra.Yustinon,M.Si, dekan dan pembantu dekan Fakultas Matematika dan Ilmu Pengetahuan Alam (FMIPA),semua dosen dan pegawai departemen matematika FMIPA USU,serta tak lupa pula Penulis ucapkan terimakasih kepada ayah,ibu tercinta yang selalu memberikan yang terbaik,dorongan dan dukungan sehingga tugas akhir ini dapat diselesaikan.semoga Allah SWT.akan membalasnya. Penulis menyadari bahwa dalam penyusunan tugas akhir ini belum sempurna. Oleh karena itu segala kritik dan saran yang yang bersifat membangun untuk kesempurnaan tugas akhir ini,dari siapapun datangnya,penulis akan menerima dan menyambut dengan segala kerendahan hati.semoga Allah.Swt membalasnya dengan yang lebih baik.
ABSTRAK Telah dilakukan pembuatan batu bata lempung dengan campuran berupa abu pembakaran ampas tebu yang dicetak dengan cara pemadatan, pengeringan dan dibakar pada temperatur 300-400 o C.Setelah umur pengeringan 7,14 dan 28 hari,dilakukan pengujian karakteristik sifat sifat mekanik dan fisis benda uji seperti; Kuat tekan,porositas,daya serap air dan susut kering. Batu bata dibuat dengan variasi campuran 0%,5%,10%,20%,30% abu ampas tebu terhadap tanah lempung dan dibandingkan hasilnya terhadap batu bata yang diproduksi oleh pabrik tradisional.berdasarkan Standar Industri (SI No.21/51/1973), batu bata yang diproduksi pabrik setempat yang memiliki kuat tekan maksimal senilai 89kg/cm 2 termasuk kelas batu bata standar mutu II,yaitu kuat tekan 80-100 kg/cm 2.Sedangkan kuat tekan batu bata dengan campuran abu ampas tebu yang memiliki kuat tekan maksimal pada variasi campuran 5% terhadap lempung diperoleh senilai 59,60 kg/cm 2,masih mendekati standar mutu III yaitu 60-80 kg/cm 2.Nilai porositas rata-rata adalah 14,857% - 23,479 %. Penyerapan air rata-rata adalah 16,789 %- 55,238%.Penyusutan kering adalah 3,17% - 9.17%.
UTILIZATION OF ASH AND BERNING OF SUGAR CANE PULP IN THE MANUFACTURE OF CLAY BRICKS ABSTRACT Has been making bricks made of clay with a mixture of combustion ash residue of sugar cane printed by compaction, drying, and baked at a temperature of 300-drying 400 0 C.After age 7.14 and 28 days, testing the characteristics of mechanical properties and physical properties test objects such as; Strong press, porosity, water absorption and decrease dry. The bricks are made with varying mixtures 0%, 5%, 10%, 20%, 30% ash residue on clay cane and compared the results of the bricks produced by the factory traditional. Based on Industry Standards (SI No.21/51/1973 ), produced brick factory which has a strong local press including the maximum value 89kg/cm 2 bricks class II quality standard, ie 80-100 kg/cm 2.Sedangkan strong strong tap tap brick with a mixture of sugar cane husks ash has strong press maximum the variation of 5% mixture of clay valued at 59.60 kg/cm 2 obtained, still close to the quality standard of 60-80 kg/cm 2.Nilai III average porosity is 14.857% - 23.479%. Water absorption is on average 16.789% - 55.238%. Depreciation of dry is 3.17% - 9:17%
DAFTAR ISI Persetujuan Pernyataan Penghargaan Abstrak Abstract Daftar Isi Daftar Tabel Daftar Gambar Halaman ii iii iv v vi vii ix x Bab 1 Pendahuluan 1.1 Latar Belakang 1 1.2 Batasan Masalah 3 1.3 Tujuan Penelitian 3 1.4 Manfaat Penelitian 4 1.5 Tempat Penelitian 4 1.6 Sistematika Penulisan 5 Bab 2 Tinjauan Pustaka 2.1 Ampas Tebu 6 2.1.1 Pengertian Ampas Tebu 6 2.2 Abu Pembakaran Ampas Tebu 8 2.2.1 Definisi 8 2.2.2 Abu Pembakaran Ampas Tebu Sebagai Fly Ash 9 2.2.3 Abu Pembakaran Ampas Tebu Sebagai Bottom Ash 10 2.3 Batu Bata Merah 10 2.3.1 Bahan Pembentuk Batu Bata 12 2.3.1.1 Tanah Liat (Lempung) 12 2.3.1.2 Jenis-Jeis Lempung Pembuat Batu Bata 13 2.3.1.3 Sifat Lempung Pada Pembakaran Temperatur tinggi 15 2.3.1.4 Bahan Campuran 16 2.3.1.5.Abu Ampas Tebu sebagai Limbah 17 2.3.2 Batu Bata Abu Pembakaran Ampas Tebu 18 2.3.3 Bata Ringan 18
Bab 3 Metodologi Penelitian 3.1 Alat dan Bahan 20 3.1.1 Peralatan 20 3.1.2 Bahan 20 3.2 Diagram Alir Penelitian 21 3.2.1 Diagram Alir 21 3.3 Prosedur Pembuatan Sampel Batu Bata 22 3.3.1 Persiapan Bahan 22 3.3.2 Pembuatan Bahan 22 3.3.3 Pencetakan 23 3.3.4 Pengeringan 24 3.3.5 Pembakaran 24 3.4 Prosedur Pengujian Sampel 25 3.4.1 Pengujian Kuat Tekan 25 3.4.2 Pengujian Penyerapan Air 26 3.4.3 Pegujian Porositas 26 3.4.4 Pengujian Penyusutan 27 Bab 4 Hasil dan Pembahasan 4.1 Hasil Penelitian 28 4.1.1 Pengujian Kuat Tekan 28 4.1.2 Pengujian Porositas 29 4.1.3 Pengujian Penyerapan Air 30 4.1.4 Pengujian Penyusutan kering 31 4.2 Pembahasan 33 4.2.1 Pengujian Kuat Tekan 33 4.2.2 Pengujian Porositas 35 4.2.3 Pengujian Penyerapan Air 36 4.2.4 Pengujian Penyusutan 37 Bab 5 Kesimpulan dan Saran 5.1 Kesimpulan 39 5.2 Saran 40 Daftar Pustaka 41 Lampiran
DAFTAR TABEL Tabel 2.1 Komposisi Kimia Abu Ampas Tebu 9 Tabel 2.2 Komposisi Kimia Pasir 9 Tabel 2.3 Jenis Campuran Batu Bata dan Manfaatnya 17 Tabel 3.1 Komposisi Adukan Bahan Batu Bata 23 Tabel 4.1 Data Hasil Pengujian Kuat Tekan 28 Tabel 4.2 Data Hasil Pengujian Porositas 29 Tabel 4.3 Data Hasil Pengujian Penyerapan Air 30 Tabel 4.4 Data Hasil Pengujian Penyusutan Kering 31 Halaman
DAFTAR GAMBAR Gambar 2.1 Proses Penggiligan Tebu 6 Gambar 4.1 Grafik Kuat Tekan terhadap Persentase Komposisi Abu Tebu 33 Gambar 4.2 Grafik Porositas terhadap Persentase Komposisi Abu Tebu 35 Gambar 4.3 Grafik Penyerapan Air terhadap Persentase Komposisi Abu Ampas Tebu 36 Gambar 4.4 Grafik Penyusutan Kering terhadap Persentase Komposisi Abu Tebu 37 Halaman