LAMPIRAN I PEMERIKSAAN BAHAN. Universitas Sumatera Utara

LAMPIRAN I PEMERIKSAAN BAHAN

ANALISA AYAKAN PASIR UNTUK MATERIAL BETON (ASTM C 136-84a) Nama Nim Material Tanggal : Rumanto : 8 44 153 : Pasir : 12 Maret 214 9.5 (3/8 - in) 4.75 (No.4) 2.36 (No.8) 1.18 (No.16).6 (No.3).3 (No.5).15 (No.1) Pan Total Berat Fraksi Tertahan Berat Berat Berat Kumulatif Sampel 1 Sampel 2 Total Tertahan Lolos (gram) (gram) (gram) (%) (%). 1 23 21 44 2.2 2.2 97.8 43 56 99 4.95 7.15 92.85 128 132 26 13. 2.15 79.85 335 342 677 33.85 54 46 265 26 525 26.25 8.25 19.75 187 175 362 18.1 98.35 1.65 19 14 33 1.65 1 1 1 2 1 Diameter Ayakan. (No.) % Fineness Modulus (FM) = Klasifikasi pasir yang baik : Halus : 2.2 < FM < 2.6 Sedang : 2.6 < FM < 2.9 Kasar : 2.9 < FM < 3.2 262.1 1 = 2.62 Mengetahui, Asisten Lab. Beton USU Muhaad Fauzi

BERAT ISI AGREGAT HALUS UNTUK MATERIAL BETON ASTM C 29/C 29M - 9 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Pasir : 12 Maret 214 1. Calibration Of Measure Suhu Ruangan Suhu Air Berat Bejana Berat Air Berat Isi Air Faktor Koreksi, C=(B/A) Diameter Agregat Maksimum o C 29 o C 26 kg.47 kg 1.85 kg/m 3 996.77 539.96 5 2. Hasil Pemeriksaan Sampel 1 Sampel 2 Total Rata-rata Net Weight (G) Berat Isi (G*K), kg/m 3 Cara Merojok 3.1 2.97 5.97 2.99 2.52 1361.79 Berat Cara Longgar 2.79 2.74 5.53 2.77 2.3 1241.11 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

BERAT JENIS DAN ABSORBSI AGREGAT HALUS UNTUK MATERIAL BETON ASTM C 128-88 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Pasir : 12 Maret 214 Berat agregat dalam keadaan SSD di udara, g (S) Sampel 1 Sampel 2 Rata-rata 5 5 5 Berat piknometer + agregat + air yang dikalibrasi, g ( C ) 975 974 974.5 Berat kering oven agregat di udara, g (A) Berat piknometer yang terisi air, g (B) Berat Jenis Kering = Berat Jenis SSD = Berat Jenis Semu = Absorbsi, % = A (B+S-C) S (B+S-C) A (B+A-C) (S-A)x1 A 494 493 493.5 676 676 676 2.46 2.49 2.53 1.21 2.44 2.48 2.53 1.42 2.45 2.48 2.53 1.32 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

PEMERIKSAAN KADAR LUMPUR AGREGAT HALUS UNTUK MATERIAL BETON ASTM C 117-9 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Pasir : 12 Maret 214 Berat agregat mula-mula, g Berat kering agregat setelah dicuci, g Sample 1 Sample 2 Average 5 5 5 49 491 49 Berat lumpur yang telah dicuci dengan ayakan No.2, g 1 9 9.5 Kadar lumpur pada agregat yang telah dicuci dengan ayakan No.2, % 2 1.8 1.9 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

KESIMPULAN PEMERIKSAAN AGREGAT HALUS Nama Nim Material Tanggal : Rumanto : 8 44 153 : Pasir : 12 Maret 214 Pemeriksaan Analisa Ayakan Berat Jenis Berat Isi Kadar Lumpur Absorbsi Hasil FM = 2.62 SSD = 2.48 UW = 1241.11 kg/m 3 1.9% 1.32% Spesifikasi 2.2-3.2 Kering<SSD<Semu >1125 kg/m 3 < 5% < 5% Kontrol OK OK OK OK OK Mengetahui, Asisten Lab.Beton Muhaad Fauzi

ANALISA AYAKAN AGREGAT KASAR UNTUK MATERIAL BETON ASTM C 136-84a & ASTM D 448-86 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Batu pecah : 12 Maret 214 Diameter Ayakan. (No.) 38.1 19.1 9.52 4.76 2.38 1.19.6.3.15 Pan Total Berat Sampel 1 (gram) Berat Fraksi Tertahan Berat Sampel 2 (gram) Berat Total (gram) Tertahan (%) Kumulatif Lolos %). 1. 16 1112 2118 52.95 52.95 47.5 757 657 1414 35.35 88.3 11.7 23 227 457 11.43 99.73.28. 99.73.28. 99.73.28. 99.73.28. 99.73.28. 99.73.28 7 4 11.28 1.. 2 2 4 1 % Fineness Modulus = 7.4 Mengetahui, Asisten lab.beton Muhaad Fauzi

BERAT ISI AGREGAT KASAR UNTUK MATERIAL BETON ASTM C 29/C 29 M - 9 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Batu pecah : 12 Maret 214 1. Calibration Of Measure Suhu Ruangan Suhu Air Berat Bejana Berat Air (A) Berat Isi Air (B) Faktor Koreksi, C=(B/A) Diameter Maksimum Agregat o C 28 o C 26 kg 5 kg 8.1 kg/m 3 996.77 123.58 25 2. Hasil Pemeriksaan Berat Cara Merojok Cara Longgar Sampel 1 19.1 18.4 Sampel 2 19.2 18.2 Total 38.3 36.6 Rata-rata 19.15 18.3 Net Weight (G) 14.15 13.3 Berat Isi (G*K), kg/m 3 1741.28 1636.68 Mengetahui, Asisten Lab.Beton Muhaad Fauzi

BERAT JENIS DAN ABSORBSI AGREGAT KASAR UNTUK MATERIAL BETON ASTM C 127-88 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Batu pecah : 12 Maret 214 Sample 1 Sample 2 Average Berat agregat dalam keadaan SSD di udara, g (B) 125 125 125 Berat agregat dalam air, g (C ) Berat kering oven agregat di udara, g (A) Berat Jenis Kering = Berat Jenis SSD Berat Jenis Semu = Absorbsi, % = = A (B-C) B (B-C) A (A-C) (B-A)x1 A 753 751 752 1232 123 1231 2.48 2.46 2.47 2.52 2.51 2.51 2.57 2.57 1.46 1.63 2.57 1.54 Mengetahui. Asisten Lab.Beton Muhaad Fauzi

PEMERIKSAAN KADAR LUMPUR AGREGAT KASAR UNTUK MATERIAL BETON ASTM C 117-9 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Batu pecah : 12 Maret 214 Berat agregat mula-mula, g Berat kering agregat setelah dicuci, g Berat lumpur yang telah dicuci dengan ayakan No.2, g Kadar lumpur pada agregat yang telah dicuci dengan ayakan No.2, % Sampel 1 Sampel 2 Rata-rata 1 1 1 993 992 992.5 7 8 7.5.7.8.75 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

KESIMPULAN PEMERIKSAAN AGREGAT KASAR Nama Nim Material Tanggal : Rumanto : 8 44 153 : Pasir : 12 Maret 214 Pemeriksaan Hasil Spesifikasi Analisa Ayakan FM = 7.41 5.5-7.5 Berat Jenis SSD = 2.51 Kering<SSD<Semu Berat Isi UW = 1636.68 kg/m 3 >125 kg/m 3 Kadar Lumpur.75% < 1% Absorbsi 1.54% < 5% Kontrol OK OK OK OK OK Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

KESIMPULAN PEMERIKSAAN AGREGAT KASAR (BAMBU) Nama Nim Material Tanggal : Rumanto : 8 44 153 : Potongan Bambu Betung : 12 Maret 214 Pemeriksaan Hasil Spesifikasi Analisa Ayakan FM = 7.26 5.5-7.5 Berat Jenis SSD = 1.14 Kering<SSD<Semu Berat Isi UW = 379.21 kg/m 3 - Absorbsi 45.8% - Kontrol OK OK - - Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

ANALISA AYAKAN AGREGAT KASAR (BAMBU) UNTUK MATERIAL BETON ASTM C 136-84a & ASTM D 448-86 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Potongan bambu betung : Berat Fraksi Tertahan Kumulatif Diameter Ayakan. (No.) Berat Sampel 1 (gram) Berat Sampel 2 (gram) Berat Total (gram) % Tertahan (%) Lolos %) 38.1 19.1 9.52 4.76 2.38 1.19.6.3.15 Pan Total.. 1. 475 553.5 128.5 25.71 25.71 74.29 1525 1446.5 2971.5 74.29 1... 1... 1... 1... 1... 1... 1... 1.. 2 2 4 1 Fineness Modulus = 7.3 Mengetahui, Asisten lab.beton Muhaad Fauzi

BERAT ISI AGREGAT KASAR (BAMBU) UNTUK MATERIAL BETON ASTM C 29/C 29 M - 9 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Potongan bambu betung : 12 Maret 214 1. Calibration Of Measure Suhu Ruangan Suhu Air Berat Bejana Berat Air (A) Berat Isi Air (B) Faktor Koreksi, C=(B/A) Diameter Maksimum Agregat o C 28 o C 26 kg 5 kg 9.2 kg/m 3 996.77 18.3446 2 2. Hasil Pemeriksaan Berat Cara Longgar Sampel 1 8.5 Net Weight (G) 3.5 Berat Isi (G*K), kg/m 3 379.21 Mengetahui, Asisten Lab.Beton Muhaad Fauzi

BERAT JENIS DAN ABSORBSI AGREGAT KASAR (BAMBU) UNTUK MATERIAL BETON ASTM C 127-88 Nama Nim Material Tanggal : Rumanto : 8 44 153 : Potongan bambu betung : 12 Maret 214 A (B-C) B Berat Jenis SSD = 1.14 (B-C) Sample 1 Sample 2 Average Berat agregat dalam keadaan SSD di udara, g (B) 1 1 1 Berat agregat dalam air, g (C) Berat kering oven agregat di udara, g (A) Berat Jenis Kering = 125 115 12 536 548 542 A Berat Jenis Semu = 1.3 1.27 1.28 (A-C) (B-A)x1 Absorbsi, % = 87.5 B.61.62.62 1.13 1.14 88.5 88 Mengetahui. Asisten Lab.Beton Muhaad Fauzi

LAMPIRAN II CONCRETE MIX DESIGN

MIX DESIGN BETON (f'c = 17 MPa) Nama : Rumanto Semen : Semen Padang Type 1 Ag. Halus : Pasir Ag. Kasar : Batu Pecah Air : PDAM Slump : 6-18 cm Mutu Rencana : f'c 17 Mpa Deviasi : 55 Rencana pelaksanaan di lokasi : 259.82 kg/cm 2 1. Perencanaan Faktor Air Semen Faktor Air Semen Standar :.5 Jenis Umur Beton Pada Saat Diuji (hari) Agregat Kasar 3 7 28 91 Kerikil 17 23 33 4 Batu Pecah 19 27 37 45 Berdasarkan grafik faktor air semen :.57 Koefisien koreksi laboratorium Faktor air semen maksimum,95 :.54 :.6 Direncanakan faktor air semen :.54 2. Perencanaan air bebas untuk campuran beton (1lt/m 3 ) Agregat Slump Ø max Jenis -1 cm 1-3 cm 3-6 cm 6-18 cm 1 2 3 Tidak pecah Tidak pecah Tidak pecah 15 135 115 18 16 14 25 18 16 225 195 175 Pecah Pecah Pecah 18 17 155 25 19 175 23 21 19 25 225 25 Direncanakan memakai air sebanyak Pemakaian semen sebanyak Persyaratan semen minimum : 185 lt/m 3 beton : 341,6 kg/m 3 beton : 33 kg/m 3 beton

3. Klasifikasi agregat halus Diameter Persentase lolos ayakan ayakan Agregat Zona I Zona II Zona III Zona IV 9.5 1 1 1 1 1 4.75 9-1 9-1 9-1 95-1 97.8 2.2 2.36 6-95 75-1 85-1 95-1 92.85 7.2 1.18 3-7 55-9 75-1 9-1 79.85 2.2.6 15-34 35-59 6-79 8-1 46 54.3 5--2 8--3 12--4 15-5 19.75 8.3.15-1 -1-1 -15 1.65 98.4 1 Zona I 1 Zona II 8 8 % Lolos 6 4 % Lolos 6 4 2 2.15.3.6 1.18 2.36 Diameter Ayakan 4.75 9.5.15.3.6 1.18 2.36 Diameter Ayakan 4.75 9.5 1 Zona III 1 Zona IV 8 8 % Lolos 6 4 % Lolos 6 4 2 2.15.3.6 1.18 2.36 Diameter Ayakan 4.75 9.5.15.3.6 1.18 2.36 Diameter Ayakan 4.75 9.5 Klasifikasi daerah perbutiran Faktor I II III IV Ø agregat zona pasir max 71 1 86 57 (%) %min 4. 32. 26.5 22. 4 %max 48. 4. 32. 26.5 diperlukan pasir antara : 32% - 4% dari total agregat

4. Klasifikasi agregat campuran Komposisi agregat campuran yang digunakan Diameter ayakan % pasir tertahan % Ag. Kasar tertahan Komposisi rencana Komposisi Kumulatif lolos Kumulatif tertahan Pasir Ag.kasar Fraksi 4 6 38.2... 1. 19.2 52.95. 31.8 31.8 68.2 31.8 9.5 35.35. 21.2 21.2 47. 53. 4,75 2.2 11.43.9 6.9 7.7 39.3 6.7 2.36 2.4.8..8 38.5 61.5 1.18 15.91 6.4. 6.4 32.1 67.9.6 33.85 13.5. 13.5 18.6 81.4.3 26.25 1.5. 1.5 8.1 91.9.15 18.1 7.2. 7.2.8 99.2 Fineness Modulus 5.47 1 Daerah Gradasi Agregat Campuran Dengan Butiran Maksimum 4 8 % Lolos 6 4 2.15.3.6 1.18 2.36 4.75 9.5 19.2 38.2 Diameter Ayakan koreksi penggunaan semen semen yang digunakan volume pasta volume agregat 1 kg/m 3 342,6 kg/m 3 295,4 liter 74,6 liter

Komposisi agregat Berat jenis SSD Komposisi agregat, % Berat jenis untuk agregat campuran Berat total agregat, kg Berat total tiap agregat, kg Komposisi Akhir Beton dalam Keadaan SSD Ag.halus Ag.kasar 2.481 2.51 4 6.993 1.56 673.3 11 Ag.campuran 2.5 1683.3 Semen 19,8 liter 342,6 kg/m 3 1. Pasir 271,3 liter 673,3 kg/m 3 1.97 Ag.Kasar 42,4 liter 11, kg/m 3 2.95 Air 185,5 liter 185,5 kg/m 3.54 Koreksi Air, Pasir, dan Ag.kasar Absorbsi air pada agregat halus (Ca) Absorsi air pada agregat kasar (Da) Kandungan air pada agregat halus (Ck) Kandungan air pada agregat kasar (Dk) 1.32% 1.54% 1.% 1.% Komposisi Adukan Beton Rencana dengan Agregat Semen 19,8 liter 342,6 kg/m 3 1. Pasir 27,1 liter 67,1 kg/m 3 1.96 Ag.kasar 42, liter 19, kg/m 3 2.94 Air 189,7 liter 189,7 kg/m 3.55 Komposisi beton untuk 1 zak semen: Semen 5 kg (1 zak) 4 liter Pasir 97,8 kg 78,8 liter Ag.kasar 147,2 kg 9, liter Air 27,7 kg 27,7 liter

LAMPIRAN III DATA PENGUJIAN

LEMBAR DATA PENGUJIAN ABSORBSI BETON Variasi Benda uji Berat basah Berat kering Absorbsi Rata-rata (%) (kg) (kg) (%) (%) 7 12.8 12.64 1.27 8 13.1 12.85 1.25 9 12.8 12.64 1.27 1 13.5 12.89 1.24 1.25 11 12.78 12.62 1.27 12 12.75 12.6 1.19 7 12.54 12.36 1.46 8 12.51 12.32 1.54 2 9 12.31 12.15 1.32 1 12.44 12.27 1.39 1.43 11 12.25 12.9 1.32 12 12.3 12.11 1.57 7 12.18 11.98 1.67 8 12.11 11.94 1.42 4 9 12.2 11.88 1.18 1 12.18 12. 1.5 1.61 11 12.16 11.94 1.84 12 12.14 11.9 2.2 7 11.83 11.6 1.98 8 11.59 11.46 1.13 6 9 11.74 11.54 1.73 1 11.57 11.4 1.49 1.61 11 11.77 11.59 1.55 12 11.66 11.46 1.75 7 11.37 11.18 1.7 8 11.42 11.2 1.96 8 9 11.37 11.19 1.61 1 11.26 11.1 1.44 1.66 11 11.22 11.6 1.45 12 11.24 11.4 1.81 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

LEMBAR DATA PENGUJIAN BERAT JENIS BETON Variasi Benda uji Diameter Panjang Volume Berat kering Berat jenis Berat jenis Rata-rata (%) (cm) (cm) (m 3 ) (kg) (kg/m 3 ) (kg/m 3 ) 1 15 3.53 12.64 2385.47 2 15 3.53 12.83 2421.33 3 15 3.53 12.76 248.12 4 15 3.53 12.68 2393.2 5 15 3.53 12.75 246.23 % 6 15 3.53 12.64 2385.47 7 15 3.53 12.64 2385.47 2398.99 8 15 3.53 12.85 2425.1 9 15 3.53 12.64 2385.47 1 15 3.53 12.89 2432.65 11 15 3.53 12.62 2381.69 12 15 3.53 12.6 2377.92 1 15 3.53 12.18 2298.66 2 15 3.53 12.15 2292.99 3 15 3.53 12.38 2336.4 4 15 3.53 12.11 2285.44 5 15 3.53 12.42 2343.95 2% 6 15 3.53 12.18 2298.66 7 15 3.53 12.36 2332.63 237.46 8 15 3.53 12.32 2325.8 9 15 3.53 12.15 2292.99 1 15 3.53 12.27 2315.64 11 15 3.53 12.9 2281.67 12 15 3.53 12.11 2285.44 1 15 3.53 12. 2264.69 2 15 3.53 12.2 2268.46 3 15 3.53 11.96 2257.14 4 15 3.53 11.9 2245.81 5 15 3.53 11.84 2234.49 4% 6 15 3.53 11.92 2249.59 7 15 3.53 11.98 226.91 2253.36 8 15 3.53 11.94 2253.36 9 15 3.53 11.88 2242.4 1 15 3.53 12. 2264.69 11 15 3.53 11.94 2253.36 12 15 3.53 11.9 2245.81 1 15 3.53 11.42 2155.23 2 15 3.53 11.78 2223.17 3 15 3.53 11.54 2177.87 6% 4 15 3.53 11.44 2159. 5 15 3.53 11.53 2175.98 2173.78 6 15 3.53 11.46 2162.77 7 15 3.53 11.6 2189.2 8 15 3.53 11.46 2162.77

Variasi Benda uji Diameter Panjang Volume Berat kering Berat jenis Berat jenis Rata-rata 9 15 3.53 11.54 2177.87 1 15 3.53 11.4 2151.45 11 15 3.53 11.59 2187.31 12 15 3.53 11.46 2162.77 1 15 3.53 11.8 291.6 2 15 3.53 11.18 219.93 3 15 3.53 1.86 249.54 4 15 3.53 1.6 2.47 5 15 3.53 11.16 216.16 8% 6 15 3.53 11. 275.96 7 15 3.53 11.18 219.93 286.18 8 15 3.53 11.2 2113.71 9 15 3.53 11.19 2111.82 1 15 3.53 11.1 294.83 11 15 3.53 11.6 287.28 12 15 3.53 11.4 283.51 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

LEMBAR DATA PENGUJIAN KUAT TEKAN BETON Variasi Umur Benda uji Berat Beban Tekan Luas Penampang Kuat tekan beton Rata-rata (%) (kg) (kn) ( 2 ) 1 12.64 384 17662.5 21.74 2 12.83 45 17662.5 25.48 % 3 12.76 368 17662.5 2.84 4 12.68 374 17662.5 21.17 22.1 5 12.75 428 17662.5 24.23 6 12.64 328 17662.5 18.57 1 12.18 28 17662.5 15.85 2 12.15 244 17662.5 13.81 2% 3 12.38 324 17662.5 18.34 4 12.11 348 17662.5 19.7 17.8 5 12.42 27 17662.5 15.29 6 12.18 344 17662.5 19.48 1 12. 198 17662.5 11.21 2 12.2 176 17662.5 9.96 4% 28 hari 3 11.96 186 17662.5 1.53 4 11.9 26 17662.5 11.66 1.74 5 11.84 148 17662.5 8.38 6 11.92 224 17662.5 12.68 1 11.42 136 17662.5 7.7 2 11.78 148 17662.5 8.38 6% 3 11.54 166 17662.5 9.4 4 11.44 114 17662.5 6.45 7.47 5 11.53 1 17662.5 5.66 6 11.46 128 17662.5 7.25 1 11.8 128 17662.5 7.25 2 11.18 96 17662.5 5.44 8% 3 1.86 84 17662.5 4.76 4 1.6 122 17662.5 6.91 5.81 5 11.16 118 17662.5 6.68 6 11. 68 17662.5 3.85 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

LEMBAR DATA PENGUJIAN KUAT TARIK BELAH BETON Variasi Benda Uji Umur Diameter Panjang Beban tekan Kuat Tarik Belah Rata - rata (%) (kn) 7 15 3 146 2.7 8 15 3 12 1.7 % 9 15 3 184 2.6 1 15 3 186 2.63 11 15 3 126 1.78 12 15 3 18 2.55 7 15 3 131 1.85 8 15 3 1 1.42 2.% 9 15 3 128 1.81 1 15 3 128 1.81 11 15 3 158 2.24 12 15 3 136 1.92 7 15 3 86 1.22 8 15 3 84 1.19 4% 9 15 3 18 1.53 28 hari 1 15 3 98 1.39 11 15 3 126 1.78 12 15 3 14 1.47 7 15 3 74 1.5 8 15 3 84 1.19 6% 9 15 3 56.79 1 15 3 96 1.36 11 15 3 5.71 12 15 3 7.99 7 15 3 6.85 8 15 3 5.71 8% 9 15 3 5.71 1 15 3 54.76 11 15 3 54.76 12 15 3 5.71 2.22 1.84 1.43 1.1.75 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

LEMBAR DATA PENGUJIAN ELASTISITAS BETON Variasi Umur Benda Uji Regangan Tegangan Elastisitas Rata-rata (%) 1.2 21.741 62842.843 2.23 25.478 62823.87 % 3.2 2.835 62574.328 4.19 21.175 65522.158 6346.635 5.23 24.232 61915.32 6.18 18.57 6261.641 1.36 15.853 47426.435 2.13 13.815 6741.764 2% 3.18 18.344 63652.428 4.19 19.73 63227.487 62537.992 5.16 15.287 66646.59 6.18 19.476 66873.779 1.26 11.21 3351.662 2.29 9.965 6327.252 4% 28 hari 3.27 1.531 3613.747 4.18 11.663 47532.575 45632.61 5.14 8.379 45469.11 6.18 12.682 488.315 1.12 7.7 45698.19 2.1 8.379 5322.99 6% 3.12 9.398 55742.727 4.13 6.454 39131.374 43159.678 5.12 5.662 3524.239 6.25 7.247 29961.518 1.52 7.247 141.723 2.51 5.435 871.477 8% 3.56 4.756 7629.832 4.5 6.97 1217.2 9812.717 5.49 6.681 1231.326 6.3 3.85 1254.743 Mengetahui, Asisten Lab.Beton USU Muhaad Fauzi

LEMBAR DATA PENGUJIAN ELASITISITAS BETON Sampel 1 Sampel 2 Sampel 3 Sampel 4 Sampel 5 Sampel 6 Substitusi Pembacaan Pembacaan Pembacaan Pembacaan Pembacaan Pembacaan P L P L P L P L P L P dial dial dial dial dial dial L (%) (kn) (kn) (kn) (kn) (kn) (kn) 5 16.16 2.8386.53 5 13.13 2.8386.43 5 14.14 2.8386.47 5 13.13 2.8386.43 5 15.15 2.8386.5 5 15.15 2.8386.5 1 3.3 5.66171.1 1 25.25 5.66171.83 1 28.28 5.66171.93 1 27.27 5.66171.9 1 28.28 5.66171.93 1 28.28 5.66171.93 15 42.42 8.49257.14 15 4.4 8.49257.133 15 4.4 8.49257.133 15 39.39 8.49257.13 15 39.39 8.49257.13 15 39.39 8.49257.13 2 5.5 11.3234.167 2 55.55 11.3234.183 2 51.51 11.3234.17 2 49.49 11.3234.163 2 5.5 11.3234.167 2 5.5 11.3234.167 25 63.63 14.1543.21 25 68.68 14.1543.227 25 67.67 14.1543.223 25 64.64 14.1543.213 25 65.65 14.1543.217 25 65.65 14.1543.217 3 76.76 16.9851.253 3 83.83 16.9851.277 3 82.82 16.9851.273 3 74.74 16.9851.247 3 8.8 16.9851.267 3 8.8 16.9851.267 35 9.9 19.816.3 35 99.99 19.816.33 35 93.93 19.816.31 35 87.87 19.816.29 35 95.95 19.816.317 328 95.95 18.574.317 384 12 1.2 21.741.34 4 112 1.12 22.6469.373 368 15 1.5 2.8351.35 374 11 1.1 21.1748.367 4 114 1.14 22.6469.38 - - - - - - - - - - 45 123 1.23 25.4777.41 - - - - - - - - - - 428 131 1.31 24.2321.437 - - - - - 2 4 5 9.9 2.8386.3 5 11.11 2.8386.37 5 13.13 2.8386.43 5 12.12 2.8386.4 5 11.11 2.8386.37 5 11.11 2.8386.37 1 23.23 5.66171.77 1 3.3 5.66171.1 1 23.23 5.66171.77 1 25.25 5.66171.83 1 2.2 5.66171.67 1 2.2 5.66171.67 15 38.38 8.49257.127 15 38.38 8.49257.127 15 39.39 8.49257.13 15 35.35 8.49257.117 15 38.38 8.49257.127 15 38.38 8.49257.127 2 55.55 11.3234.183 2 42.42 11.3234.14 2 52.52 11.3234.173 2 55.55 11.3234.183 2 55.55 11.3234.183 2 55.55 11.3234.183 25 86.86 14.1543.287 244 75.75 13.8146.25 25 67.67 14.1543.223 25 73.73 14.1543.243 25 7.7 14.1543.233 25 7.7 14.1543.233 28 94.94 15.8528.313 - - - - - 3 85.85 16.9851.283 3 88.88 16.9851.293 27 95.95 15.2866.317 3 83.83 16.9851.277 - - - - - - - - - - 324 15 1.5 18.3439.35 348 111 1.11 19.728.37 - - - - - 344 16 1.6 19.4763.353 5 1.1 2.8386.33 5 9.9 2.8386.3 5 9.9 2.8386.3 5 1.1 2.8386.33 5 11.11 2.8386.37 5 1.1 2.8386.33 1 18.18 5.66171.6 1 18.18 5.66171.6 1 25.25 5.66171.83 1 2.2 5.66171.67 1 26.26 5.66171.87 1 23.23 5.66171.77 15 75.75 8.49257.25 15 68.68 8.49257.227 15 66.66 8.49257.22 15 58.58 8.49257.193 148 6.6 8.37933.2 15 65.65 8.49257.217 198 1 1 11.212.333 176 84.84 9.96461.28 186 98.98 1.538.327 2 9.9 11.3234.3 - - - - - 2 92.92 11.3234.37 - - - - - - - - - - - - - - - 26 15 1.5 11.6631.35 - - - - - 224 115 1.15 12.6822.383 6 8 5 21.21 2.8386.7 5 18.18 2.8386.6 5 15.15 2.8386.5 5 26.26 2.8386.87 5 2.2 2.8386.67 5 25.25 2.8386.83 1 75.75 5.66171.25 1 77.77 5.66171.257 1 68.68 5.66171.227 1 8.8 5.66171.267 1 95.95 5.66171.317 1 9.9 5.66171.3 136 146 1.46 7.69993.487 148 165 1.65 8.37933.55 15 15 1.5 8.49257.5 114 121 1.21 6.45435.43 - - - - - 128 15 1.5 7.24699.5 - - - - - - - - - - 166 182 1.82 9.39844.67 - - - - - - - - - - - - - - - 5 88.88 2.8386.293 5 85.85 2.8386.283 5 9.9 2.8386.3 5 84.84 2.8386.28 5 89.89 2.8386.297 5 58.58 2.8386.193 1 167 1.67 5.66171.557 96 22 2.2 5.43524.733 84 245 2.45 4.75584.817 1 166 1.66 5.66171.553 1 154 1.54 5.66171.513 68 122 1.22 3.84996.47 128 211 2.11 7.24699.73 - - - - - - - - - - 122 21 2.1 6.9729.67 118 198 1.98 6.6882.66 - - - - -

GRAFIK HUBUNGAN TEGANGAN-REGANGAN - Substitusi % 3 25 2 15 1 5 3 25 2 15 1 5.1.2.3.4.1.2.3.4.5 Benda uji 1 Benda uji 2 3 25 2 15 1 5 3 25 2 15 1 5.1.2.3.4.1.2.3.4 Benda uji 3 Benda uji 4 3 25 2 15 1 5 3 25 2 15 1 5.1.2.3.4.5.1.2.3.4 Benda uji 5 Benda uji 6

- Substitusi 2% 2 2 15 15 1 1 5 5.1.2.3.4.1.2.3.4 Benda uji 1 Benda uji 2 2 15 1 5 3 25 2 15 1 5.1.2.3.4.1.2.3.4 Benda uji 3 Benda uji 4 2 2 15 15 1 1 5 5.1.2.3.4.1.2.3.4 Benda uji 5 Benda uji 6

- Substitusi 4% 2 2 15 15 1 1 5 5.1.2.3.1.2.3.4 Benda uji 1 Benda uji 2 2 2 15 15 1 1 5 5.1.2.3.4.1.2.3.4 Benda uji 3 Benda uji 4 2 2 15 15 1 1 5 5.5.1.15.2.1.2.3.4.5 Benda uji 5 Benda uji 6

- Substitusi 6% 1 8 6 4 2 1 8 6 4 2.2.4.6.2.4.6 Benda uji 1 Benda uji 2 1 8 6 4 2 1 8 6 4 2.2.4.6.8.2.4.6 Benda uji 3 Benda uji 4 1 8 6 4 2 1 8 6 4 2.1.2.3.4.2.4.6 Benda uji 5 Benda uji 6

- Substitusi 8% 1 8 6 4 2 1 8 6 4 2.2.4.6.8.2.4.6.8 Benda uji 1 Benda uji 2 1 8 6 4 2 1 8 6 4 2.2.4.6.8.1.2.4.6.8 Benda uji 3 Benda uji 4 1 8 6 4 2 5 4 3 2 1.2.4.6.2.4.6 Benda uji 5 Benda uji 6

LAMPIRAN IV DOKUMENTASI

Gambar 1. Potongan bambu betung Gambar 2. Perendaman bambu selama 24 jam Gambar 3. Pengujian berat jenis bambu

Gambar 4. Persiapan bahan (a) (b) Gambar 5. Persiapan alat, (a) Cetakan silinder; (b) Mesin molen

(a) (b) (c) Gambar 6. (a),(b), dan (c) Proses pengecoran beton Gambar 7. Pengujian Slump

Gambar 8. Penuangan adukan ke dalam cetakan Gambar 9. Perawatan sampel beton selama 28 hari Gambar 1. Sampel benda uji beton

Gambar 11. Pengujian kuat tarik belah beton Gambar 12. Penimbangan benda uji Gambar 13. Pengujian kuat tekan dan elastisitas beton

Gambar 14. Compressor strain dial test Gambar 15. Penampakan agregat batu pecah dan potongan bambu pada beton