BERAT ISI AGREGAT HALUS UNTUK MATERIAL BETON. Calibration Of Measure ASTM C 29/C 29M 90 Suhu Ruangan o C 28 Suhu Air o C 26 Bejana Kg 0.46 Air Kg.85 Isi Air Kg/m 3 996.78 Faktor Koreksi, K=(B/A) 538.8 2. Hasil Pemeriksaan Cara Merojok Cara Longgar Sampel (kg) 3.0 2.86 Sampel 2 (kg) 3.06 2.84 Total (kg) 6.07 5.7 Rata-rata (kg) 3.035 2.85 Net Wwight (G), kg 2.575 2.386 Isi (G*K), kg/m 3 387.4 287.7
ANALISA AYAKAN PASIR UNTUK MATERIAL BETON Diameter Ayakan. (mm) Sampel (gr) (ASTM C 36 84a) Fraksi Tertahan Sampel 2 (gr) Ratarata (gr) Tertahan (%) Kumulatif Lolos (%) 9.50 0.00 0.00 0.00 0.00 00 4.75.67 9.83 0.75.08 98.93 2.36 28.76 26.44 27.60 3.84 96.7.8 27.89 2.54 24.72 6.3 83.69 0.60 275 242.88 258.94 42.20 57.80 0.30 28.42 289.54 285.48 70.75 29.25 0.5 256.76 298.56 277.66 98.5.49 Pan 8.5.2 4.86 00 0 Total 000 000 000 Fineness Modulus (FM) = 232.68 00 = 2.33 Klasifikasi psir yang baik: Halus Sedang Kasar : 2.2<FM<2.6 : 2.6<FM<2.9 : 2.9<FM<3.2
BERAT JENIS DAN ABSORBSI AGREGAT HALUS UNTUK MATERIAL BETON ASTM C 28 88 agregat dalam keadaan SSD di udara, g (S) piknometer + agregat + air yang dikalibrasi, g (C) kering oven agregat di udara,g (A) piknometer yang terisi air, g (B) Jenis Kering = Jenis SSD = Jenis Semu = Absorbsi, % A (B+S C) S (B+S C) A (B+A C) = (S A)X00 A Sampel Sampel 2 Rata-rata 500 500 500 968 972 970 466 464 465 668 666 667 2.33 2.39 4.72 2.5 2.58 2.54 2.8 2.94 2.875 7.296 7.76 7.528
PEMERIKSAAN KADAR LUMPUR AGREGAT HALUS UNTUK MATERIAL BETON ASTM C 7 90 Sampel Sampel 2 Rata-rata agregat mula-mula + pan, g 633 633 633 kering agregat setelah dicuci + pan, g 627 624 625.5 lumpur yang telah dicuci dengan ayakan No.200, g 6 9 7.5 Kadar lumpur pada agregat yang telah dicuci No.200, %.2.8.5
PENGUJIAN COLORIMETRIC KANDUNGAN BAHAN ORGANIK AGREGAT HALUS (ASTM c40 84) Perbandingan Terhadap Organic Plate Lebih Terang Sama Lebih Gelap Sampel No.3
UJI BERAT JENIS SEMEN PORTLAND Jenis Semen : Semen Padang Tipe I I II III, gr B 60. 60.06 63.9 Volume Awal, gr V 0. 0. 0 Volume Akhir, gr V2 20.7 20.6 2.4 Jenis Semen B*d/(V2-V) 3.0 3.02 3.08 3.03
HASIL PENGUJIAN PENYIMPANGAN UKURAN BATAKO NORMAL No. Panjang (mm) Lebar (mm) Tinggi (mm) SNI 03- SNI 03-0349- 0349-989 989 SNI 03-0349- 989 402 + 2 200 0 0 + 2 40 + 200 0 00 0 3 40 + 200. +0. 0 + 4 402 +2 200 0 0 + 5 40 + 200 0 00 0 Rata-rata 40.4 +.4 200.2 +0.2 00.6 +0.6 * Ukuran batako yang menjadi acuan: Panjang = 400mm; Lebar = 200mm; Tebal = 00mm * Selisih antara ukuran acuan terdapat pada kolom.
HASIL PENGUJIAN PENYIMPANGAN UKURAN BATAKO 20% BIJI PLASTIK No. Panjang (mm) Lebar (mm) Tinggi (mm) SNI 03- SNI 03-0349- 0349-989 989 SNI 03-0349- 989 402 +2 20 + 02 +2 2 402 +2 202 +2 00 0 3 40 + 20 + 0 + 4 40 + 20 + 0 + 5 402 +2 20 + 0 + Rata-rata 40.6 +.6 20.2 +.2 0 + * Ukuran batako yang menjadi acuan: Panjang = 400mm; Lebar = 200mm; Tebal = 00mm * Selisih antara ukuran acuan terdapat pada kolom.
No. HASIL PENGUJIAN KUAT TEKAN BATAKO 20% BIJI PLASTIK LDPE Pembacaan Dial Ratarata SNI 03-0349-989 402 28 20 280 43.70 35 3 2 4004 28 8 280 42.97 35 3 3 3956 28 5 280 4.88 35 3 4 5063 28 20 280 43.70 35 3 5 4460 28 8 280 42.97 35 3 Rata-rata 437 28 8.2 280 43.05 40 3 Mutu
No. HASIL PENGUJIAN KUAT TEKAN BATAKO NORMAL Pembacaan Dial Ratarata SNI 03-0349-989 323 28 280 280 0.97 90 2 2749 28 270 280 98.33 90 3 2640 28 275 280 00.5 90 4 2836 28 278 280 0.24 90 5 2879 28 272 280 99.06 90 Rata-rata 2845 28 275 280 00.5 00 Mutu
No. HASIL PENGUJIAN TRIAL PERBANDINGAN :8:0.2 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9320 7 70 76.625 48.69 74.9 2 9220 7 65 76.625 45.2 69.56 Rata-rata 9270 7 67.5 76.625 46.95 72.23 243 7 24 25 97.89 50.6 2 Kubus Kecil 248 7 22 25 89.73 38.05 3 250 7 20 25 8.58 25.5 Rata-rata 247 7 22 25 89.73 38.05 No. HASIL PENGUJIAN TRIAL PERBANDINGAN :8:0.24 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9300 7 70 76.625 48.69 74.9 2 9340 7 72 76.625 50.08 77.05 Rata-rata 9320 7 7 76.625 49.39 75.98 246 7 24 25 97.89 50.6 2 Kubus Kecil 253 7 24 25 97.89 50.6 3 244 7 22 25 89.73 38.05 Rata-rata 247.67 7 23.33 25 95.72 46.42
No. HASIL PENGUJIAN TRIAL PERBANDINGAN :8:0.28 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9245 7 68 76.625 47.30 72.77 2 9267 7 70 76.625 48.69 74.9 Rata-rata 9256 7 69 76.625 47.99 73.84 247 7 22 25 89.73 38.05 2 Kubus Kecil 252 7 24 25 97.89 50.6 3 240 7 22 25 89.73 38.05 Rata-rata 247.67 7 22.67 25 92.45 42.24
No. HASIL PENGUJIAN TRIAL PERBANDINGAN :7:0.2 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 93 7 72 76.625 50.08 77.05 2 9445 7 75 76.625 52.7 80.26 Rata-rata 9378 7 73.5 76.625 5.2 78.65 257 7 25 25 0.97 56.88 2 Kubus Kecil 254 7 22 25 89.73 38.05 3 264 7 28 25 4.2 75.7 Rata-rata 258.33 7 25 25 0.97 56.88 No. HASIL PENGUJIAN TRIAL PERBANDINGAN :7:0.24 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9350 7 78 76.625 54.25 83.47 2 9468 7 80 76.625 55.65 85.6 Rata-rata 9409 7 79 76.625 54.95 84.54 267 7 28 25 4.2 75.7 2 Kubus Kecil 252 7 25 25 0.97 56.88 3 260 7 25 25 0.97 56.88 Rata-rata 259.67 7 26 25 06.05 63.5
No. HASIL PENGUJIAN TRIAL PERBANDINGAN :7:0.28 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9440 7 72 76.625 50.08 77.05 2 9452 7 75 76.625 52.7 80.26 Rata-rata 9446 7 73.5 76.625 5.2 78.65 266 7 26 25 06.05 63.5 2 Kubus Kecil 265 7 24 25 97.89 50.6 3 258 7 24 25 97.89 50.6 Rata-rata 263 7 24.67 25 00.6 54.79
No. HASIL PENGUJIAN TRIAL PERBANDINGAN :6:0.2 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9200 7 75 76.625 52.7 80.26 2 9345 7 78 76.625 54.25 83.47 Rata-rata 9272.5 7 76.5 76.625 53.2 8.86 246 7 25 25 0.97 56.88 2 Kubus Kecil 245 7 24 25 97.89 50.6 3 247 7 28 25 4.2 75.7 Rata-rata 246 7 25.67 25 04.69 6.06 No. HASIL PENGUJIAN TRIAL PERBANDINGAN :6:0.24 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9505 7 92 76.625 63.99 98.45 2 9589 7 95 76.625 66.08 0.67 Rata-rata 9547 7 93.5 76.625 65.04 00.06 252 7 30 25 22.36 88.25 2 Kubus Kecil 250 7 25 25 0.97 56.88 3 250 7 28 25 4.2 75.7 Rata-rata 259.67 7 27.67 25 2.85 73.6
No. HASIL PENGUJIAN TRIAL PERBANDINGAN :6:0.28 Pembacaan Dial Ratarata Estimasi 28 hari Silinder 9384 7 88 76.625 6.2 94.7 2 9276 7 85 76.625 59.2 90.96 Rata-rata 9330 7 86.5 76.625 60.7 92.56 248 7 28 25 4.2 75.7 2 Kubus Kecil 248 7 25 25 0.97 56.88 3 246 7 25 25 0.97 56.88 Rata-rata 247.33 7 26 25 06.049 63.5
HASIL PENGUJIAN TRIAL PERBANDINGAN :6:0.24 20% BIJI PLASTIK LDPE No. Pembacaan Dial Rata-rata 7866 7 60 76.625 4.73 2 802 7 60 76.625 4.73 3 7904 7 58 76.625 40.34 Rata-rata 7957.33 7 59.33 76.625 4.27 HASIL PENGUJIAN TRIAL PERBANDINGAN :6:0.24 25% BIJI PLASTIK LDPE No. Pembacaan Dial Rata-rata 7280 7 50 76.625 34.78 2 7647 7 55 76.625 38.26 3 7570 7 52 76.625 36.7 Rata-rata 7499 7 52.33 76.625 36.40
HASIL PENGUJIAN TRIAL PERBANDINGAN :6:0.24 30% BIJI PLASTIK LDPE No. Pembacaan Dial Rata-rata 7322 7 50 76.625 34.78 2 7805 7 48 76.625 33.39 3 7509 7 45 76.625 3.30 Rata-rata 7545.33 7 47.67 76.625 33.6 HASIL PENGUJIAN TRIAL PERBANDINGAN :6:0.24 25% BIJI PLASTIK LDPE No. Pembacaan Dial Rata-rata 6335 7 48 76.625 33.39 2 6659 7 45 76.625 3.30 3 6605 7 42 76.625 29.2 Rata-rata 6533 7 45 76.625 3.30
No. HASIL PENGUJIAN KUAT TEKAN KUBUS NORMAL Pembacaan Dial Ratarata SNI 03-0349-989 250 28 28 25 4.2 90 2 245 28 26 25 06.05 90 3 244 28 26 25 06.05 90 4 246 28 26 25 06.05 90 5 245 28 24 25 97.89 90 6 250 28 28 25 4.2 90 7 236 28 22 25 89.73 90 8 24 28 24 25 97.89 90 9 239 28 24 25 97.89 90 0 242 28 26 25 06.05 90 237 28 22 25 89.73 90 2 240 28 24 25 97.89 90 Rata-rata 242.92 28 25 25 0.97 00 Mutu
No. HASIL PENGUJIAN KUAT TEKAN KUBUS 20% BIJI PLASTIK LDPE Pembacaan Dial Ratarata SNI 03-0349-989 207 28 5 25 6.82 35 3 2 25 28 5 25 6.82 35 3 3 95 28 0 25 40.79 35 3 4 22 28 5 25 6.8 35 3 5 202 28 2 25 48.95 35 3 6 203 28 2 25 48.95 35 3 7 204 28 2 25 48.95 35 3 8 80 28 0 25 40.79 35 3 9 202 28 2 25 48.95 35 3 0 203 28 2 25 48.95 35 3 20 28 5 25 6.8 35 3 2 22 28 5 25 6.8 35 3 Rata-rata 203.75 28 2.92 25 52.68 40 3 Mutu
HASIL PENGUJIAN KUAT TARIK BREQUETTE 20% BIJI PLASTIK LDPE No. Kuat Tarik Kuat Tarik (Kg/cm 2 ) 02 28 0.65 7.84 8.45 2 0 28 0.7 7.29 9.79 3 09 28 0.85 8.96 9.67 4 08 28 0.75 8.4 9.0 5 05 28 0.9 0.53 8.72 6 99 28 0.6 8.37 7.3 7 09 28 0.65 7.7 8.6 8 08 28.025 7.56 3.82 9 04 28 0.75 7.28 0.5 0 28 0.8 7.83 0.42 08 28 0.95 7.6 3.54 2 0 28 0.7 7.5 9.98 Rata-rata 06.7 28 0.78 9.99
HASIL PENGUJIAN KUAT TARIK BREQUETTE NORMAL No. Kuat Tarik Kuat Tarik (Kg/cm 2 ) 26 28.2 8.6 4.2 2 22 28.05 8.02 3.35 3 23 28. 7.40 5.6 4 7 28.35 7.05 9.53 5 2 28.5 8.52 7.95 6 23 28.5 7.07 2.64 7 23 28.25 7.02 8.6 8 28 28.5 7.23 2.5 9 25 28.6 7.9 20.62 0 28 28.45 6.89 2.46 27 28 2.74 7.37 2 24 28.58 8.9 8.023 Rata-rata 23.92 28 0.78 8.22
FOTO DOKUMENTASI Biji Plastik Semen Tipe Pasir Cetakan Brequette Cetakan Silinder Cetakan Batako
Cetakan Kubus Penumbuk Batako Penumbuk Silinder Analisa Ayakan Mengayak Pasir Mengayak Dengan ayakan No 4
Pengujian Kadar Lumpur Pengujian Isi Pasir Pengujian Jenis Pasir Pengujian Kalorimetrik Pembuatan Sampel Trial Sampel Trial Silinder dan Kubus
Pengujian Kuat Tekan Retakan Hasil Kuat Tekan 20% Biji Plastik LDPE Retakan Hasil Kuat Tekan 25% Biji Plastik LDPE Retakan Hasil Kuat Tekan 25% Biji Plastik LDPE Retakan Hasil Kuat Tekan 25% Biji Plastik LDPE
Pengecoran Sampel Pembuatan Sampel Batako Pembuatan Kubus & Brequette Kubus & Brequette Batako Curing Batako dengan Cara Disiram
Pengujian Absorbsi Direndam Batako Direndam Pengujian Ukuran Pada Batako Pengujian Kuat Tarik Brequtte Pengujian Kuat Tekan Kubus Kecil Pengujian Kuat Tekan Batako