LAMPIRAN I - PEMERIKSAAN MATERIAL ANALISA AYAKAN PASIR (ASTM C 136-84a) Nama : Muhammad Fauzi NIM : 10 0404 170 Diuji oleh : Muhammad Fauzi Diameter ayakan Berat Tertahan Berat Berat Total Kumulatif (mm) sampel 1 sampel 2 Weight (%) Terthan Lolos (gram) (gram) (gram) (%) (%) 9.52 mm 14,0 15,0 29,0 1,45 1,45 98,55 4.75 mm 23,0 20,0 43,0 2,15 3,60 96,40 2.36 mm 65,0 60,0 125,0 6,25 9,85 90,15 1.18 mm 131,0 130,0 261,0 13,05 22,90 77,10 0.60 mm 274,0 276,0 550,0 27,50 50,40 49,60 0.30 mm 304,0 300,0 604,0 30,20 80,60 19,40 0.15 mm 168,0 170,0 338,0 16,90 97,50 2,50 Pan 21,0 29,0 50,0 2,50 100,00 0,00 Total 1000,0 1000,0 2000 100 Modulus Kehalusan (FM) = 266,30 100 = 2,66 Persyaratan pasir halus pasir sedang pasir kasar 2.2<FM<2.6 2.6<FM<2.9 2.9<FM<3.2 Mengetahui, Asisten Laboratorium Beton ( Rahmadsyah Rangkuti )
Nama : Muhammad Fauzi NIM : 10 0404 170 Diuji oleh : Muhammad Fauzi BERAT ISI PASIR ASTM C 29/C 29M - 90 Suhu Ruangan ( 0 C) 28,00 Suhu Air ( 0 C) 26,00 Berat Bejana (kg) 0,46 Berat Air (kg) 1,86 Berat Isi Air (kg/m 3 ) 996,77 Faktor Koreksi' 535,90 Diamater maksimum agregat (mm) 10,00 Berat Isi Rojok Longgar Sampel 1 3,37 3,15 Sampel 2 3,40 3,20 Total 6,77 6,35 Rata - rata 3,38 3,18 Berat Bersih (kg) 2,92 2,71 Berat Isi [kg/m 3 ] 1564,83 1453,09 Mengetahui, Asisten laboratorium Beton ( Rahmadsyah Rangkuti )
BERAT JENIS DAN ABSORBSI PASIR (ASTM C 128-88) Nama NIM Diuji oleh : Muhammad Fauzi : 10 0404 170 : Muhammad Fauzi Sample I Sample II Average Berat pasir keadaan SSD (gram) 500,0 500,0 500,0 Berat pasir + air + piknometer (gram) 971,0 972,0 971,5 Berat pasir kering oven (gram) 488,0 490,0 489,0 Berat piknometer + air (gram) 671,0 672,0 671,5 Berat Jenis Kering 2,44 2,45 2,45 Berat Jenis SSD 2,50 2,50 2,50 Berat Jenis Jenuh Air 2,60 2,58 2,59 Absorbsi % 2,46 2,04 2,25 Mengetahui, Asisten laboratorium Beton ( Rahmadsyah Rangkuti )
KADAR LUMPUR PASIR (PENCUCIAN AGREGAT DENGAN AYAKAN NO. 200) ASTM C 117-90 : Muhammad Nama Fauzi NIM : 10 0404 170 : Muhammad Diuji oleh Fauzi sampel 1 sampel 2 rata - rata Berat Kering Mula-mula (gram) 500 500 500 Berat Kering Setelah Pencucian (gram) 497 496 496,5 Berat Lolos Ayakan No. 200 (gram) 3 4 3,5 Persentase Kadar Lumpur (%) 0,6 0,8 0,7 Mengetahui, Asisten laboratorium Beton Rahmadsyah Rangkuti
PENGUJIAN CLAY LUMP PASIR KADAR LIAT DALAM AGREGAT HALUS : Muhammad Nama Fauzi NIM : 10 0404 170 : Muhammad Diuji oleh Fauzi sampel 1 sampel 2 rata - rata Berat Kering Hasil Pengujian Kadar Lumpur (gram) 497 496 496,5 Berat Kering Setelah Pencucian (gram) 495 495 495 Berat Lolos Ayakan No. 200 (gram) 2 1 1,5 Persentase Kadar Lumpur (%) 0,40 0,20 0,30 Mengetahui, Asisten laboratorium Beton Rahmadsyah Rangkuti
PENGUJIAN COLORIMETRIC KANDUNGAN BAHAN ORGANIK AGREGAT HALUS : Muhammad Nama Fauzi NIM : 10 0404 170 : Muhammad Diuji oleh Fauzi Keterangan Sampel Lebih Terang Perbandingan Terhadap Warna Standard Gardner Sama No. 3 Lebih Gelap Mengetahui, Asisten laboratorium Beton Rahmadsyah Rangkuti
LAMPIRAN II - DATA BERAT ISI, ABSORBSI, DAN POROSITAS 1. BERAT ISI (KEADAAN SEIMBANG) NO. KODE SAMPEL BERAT KERING BERAT JENUH BERAT TERENDAM BERAT ISI gram gram gram kg/m³ 1 0% 9842 10294 5034 1865,49 2 0% 9898 10352 5041 1858,09 3 0% 9832 10280 5014 1861,47 4 0% 9874 10351 4981 1833,22 5 0% 9900 10381 5030 1844,57 rata - rata 9869,2 10331,6 5020 1852,57 1 15% 9785 10260 4983 1848,71 2 15% 9840 10325 4993 1839,92 3 15% 9814 10321 4930 1814,98 4 15% 9777 10250 4962 1843,36 5 15% 9840 10351 4985 1828,27 rata - rata 9811,2 10301,4 4970,6 1835,05 1 20% 9825 10340 4965 1822,42 2 20% 9759 10248 4952 1837,18 3 20% 9800 10311 4919 1812,05 4 20% 9768 10256 4968 1841,66 5 20% 9819 10314 4976 1833,93 rata - rata 9794,2 10293,8 4956 1829,45 1 25% 9808 10294 4946 1828,45 2 25% 9801 10295 4940 1824,76 3 25% 9758 10260 4934 1826,65 4 25% 9754 10258 4937 1827,61 5 25% 9786 10301 4948 1822,65 rata - rata 9781,4 10281,6 4941 1826,03
2. ABSORBSI KODE NO. SAMPEL MASSA MASSA BASAH KERING ABSORBSI gram gram % 1 0% 10294 9842 4,59 2 0% 10352 9898 4,59 3 0% 10280 9832 4,56 4 0% 10351 9874 4,83 5 0% 10381 9900 4,86 rata - rata 10331,6 9869,2 4,69 1 15% 10260 9785 4,85 2 15% 10325 9840 4,93 3 15% 10321 9814 5,17 4 15% 10250 9777 4,84 5 15% 10351 9840 5,19 rata - rata 10301,4 9811,2 5,00 1 20% 10340 9825 5,24 2 20% 10248 9759 5,01 3 20% 10311 9800 5,21 4 20% 10256 9768 5,00 5 20% 10314 9819 5,04 rata - rata 10293,8 9794,2 5,10 1 25% 10294 9808 4,96 2 25% 10295 9801 5,04 3 25% 10260 9758 5,14 4 25% 10258 9754 5,17 5 25% 10301 9786 5,26 rata - rata 10281,6 9781,4 5,11
3. POROSITAS NO. KODE SAMPEL MASSA VOLUME BENDA BASAH MASSA KERING UJI POROSITAS gram gram cm³ % 1 0% 10294 9842 5298,75 8,530 2 0% 10352 9898 5298,75 8,568 3 0% 10280 9832 5298,75 8,455 4 0% 10351 9874 5298,75 9,002 5 0% 10381 9900 5298,75 9,078 rata - rata 10331,6 9869,2 5298,75 8,727 1 15% 10260 9785 5298,75 8,964 2 15% 10325 9840 5298,75 9,153 3 15% 10321 9814 5298,75 9,568 4 15% 10250 9777 5298,75 8,927 5 15% 10351 9840 5298,75 9,644 rata - rata 10301,4 9811,2 5298,75 9,251 1 20% 10340 9825 5298,75 9,719 2 20% 10248 9759 5298,75 9,229 3 20% 10311 9800 5298,75 9,644 4 20% 10256 9768 5298,75 9,210 5 20% 10314 9819 5298,75 9,342 rata - rata 10293,8 9794,2 5298,75 9,429 1 25% 10294 9808 5298,75 9,172 2 25% 10295 9801 5298,75 9,323 3 25% 10260 9758 5298,75 9,474 4 25% 10258 9754 5298,75 9,512 5 25% 10301 9786 5298,75 9,719 rata - rata 10281,6 9781,4 5298,75 9,440
LAMPIRAN III - KUAT TEKAN BETON Nomor Subs. Tanggal Umur Berat Beban Kuat No. Benda Fly Ash (hari) uji Tekan Tekan cetak uji Uji (%) (kg) (kn) (MPa) 1 Variasi 1 0 27-Agust-14 24-Sep-14 28 9,842 280,0 15,85 2 Variasi 1 0 27-Agust-14 24-Sep-14 28 9,898 292,0 16,53 3 Variasi 1 0 27-Agust-14 24-Sep-14 28 9,832 274,0 15,51 4 Variasi 1 0 27-Agust-14 24-Sep-14 28 9,874 280,0 15,85 5 Variasi 1 0 27-Agust-14 24-Sep-14 28 9,900 292,0 16,53 Rata - rata 9,87 283,60 16,06 1 Variasi 2 15 27-Agust-14 24-Sep-14 28 9,787 270,0 15,29 2 Variasi 2 15 27-Agust-14 24-Sep-14 28 9,843 284,0 16,08 3 Variasi 2 15 27-Agust-14 24-Sep-14 28 9,777 262,0 14,83 4 Variasi 2 15 27-Agust-14 24-Sep-14 28 9,819 276,0 15,63 5 Variasi 2 15 27-Agust-14 24-Sep-14 28 9,845 266,0 15,06 Rata - rata 9,81 271,60 15,38 1 Variasi 3 20 27-Agust-14 24-Sep-14 28 9,767 240,0 13,59 2 Variasi 3 20 27-Agust-14 24-Sep-14 28 9,823 238,0 13,47 3 Variasi 3 20 27-Agust-14 24-Sep-14 28 9,757 264,0 14,95 4 Variasi 3 20 27-Agust-14 24-Sep-14 28 9,799 278,0 15,74 5 Variasi 3 20 27-Agust-14 24-Sep-14 28 9,825 240,0 13,59 Rata - rata 9,79 252,00 14,27 1 Variasi 4 25 27-Agust-14 24-Sep-14 28 9,754 198,0 11,21 2 Variasi 4 25 27-Agust-14 24-Sep-14 28 9,810 226,0 12,80 3 Variasi 4 25 27-Agust-14 24-Sep-14 28 9,744 210,0 11,89 4 Variasi 4 25 27-Agust-14 24-Sep-14 28 9,786 228,0 12,91 5 Variasi 4 25 27-Agust-14 24-Sep-14 28 9,812 222,0 12,57 Rata - rata 9,78 216,80 12,27
LAMPIRAN IV - KUAT TEKAN BETON Variasi Beban Tegangan Rekah Beton (MPa) Tegangan Substitusi Rekah Rekah D ¾ D ½ D ¼ D Fly Ash (kn) (MPa) 112 1,5852795 2,1137061 3,1705591 6,3411182 3,302665723 122 1,7268224 2,3024298 3,4536447 6,9072895 3,597546591 0% 98 1,3871196 1,8494928 2,7742392 5,5484784 2,889832508 112 1,5852795 2,1137061 3,1705591 6,3411182 3,302665723 130 1,8400566 2,4534088 3,6801132 7,3602265 3,833451286 Rata - rata 114,80 1,62 2,17 3,25 6,50 3,39 108 1,5286624 2,0382166 3,0573248 6,1146497 3,184713376 112 1,5852795 2,1137061 3,1705591 6,3411182 3,302665723 15% 90 1,2738854 1,6985138 2,5477707 5,0955414 2,653927813 100 1,4154282 1,8872376 2,8308563 5,6617127 2,948808681 96 1,358811 1,8117481 2,7176221 5,4352442 2,830856334 Rata - rata 101,20 1,43 1,91 2,86 5,73 2,98 86 1,2172682 1,6230243 2,4345364 4,8690729 2,535975466 78 1,104034 1,4720453 2,2080679 4,4161359 2,300070771 20% 80 1,1323425 1,50979 2,2646851 4,5293701 2,359046945 58 0,8209483 1,0945978 1,6418967 3,2837933 1,710309035 76 1,0757254 1,4343005 2,1514508 4,3029016 2,241094598 Rata - rata 75,60 1,07 1,43 2,14 4,28 2,23 48 0,6794055 0,905874 1,358811 2,7176221 1,415428167 62 0,8775655 1,1700873 1,7551309 3,5102619 1,828261382 25% 58 0,8209483 1,0945978 1,6418967 3,2837933 1,710309035 60 0,8492569 1,1323425 1,6985138 3,3970276 1,769285209 50 0,7077141 0,9436188 1,4154282 2,8308563 1,474404341 Rata - rata 55,60 0,79 1,05 1,57 3,15 1,64
LAMPIRAN V - DOKUMENTASI Gambar 1. Fly Ash Gambar 2. Bubuk Kertas
Gambar 3. Penuangan bahan dengan substitusi fly ash Gambar 4. Penuangan bahan bubur kertas
Gambar 5. Pengujian slump Gambar 6. Penuangan adukan beton kertas dengan substitusi fly ash
Gambar 7. Pemadatan benda uji dengan vibrator Gambar 8. Benda uji yang telah di cetak
Gambar 9. Penimbangan berat benda uji terendam Gambar 10. Penimbangan berat benda uji
Gambar 11. Pengujian kuat tekan beton kertas Gambar 12. Benda uji setelah diuji
Gambar 13. Pengujian kuat tarik belah Gambar 14. Benda uji setelah diuji tarik belah