PELAPISAN NIKEL PADA BAJA KARBON RENDAH DENGAN METODE ELEKTROPLATING SEBAGAI ANTI KOROSI SKRIPSI RUSDALENA

Transkripsi

1 PELAPISAN NIKEL PADA BAJA KARBON RENDAH DENGAN METODE ELEKTROPLATING SEBAGAI ANTI KOROSI SKRIPSI Diajukan untuk melengkapi tugas dan memenuhi syarat mencapai gelar Sarjana Sains RUSDALENA DEPARTEMEN FISIKA FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA MEDAN 2011

2 PERSETUJUAN Judul : PELAPISAN NIKEL PADA BAJA KARBON RENDAH DENGAN METODE ELEKTROPLATING SEBAGAI ANTI KOROSI Kategori : SKRIPSI Nama : RUSDALENA Nomor Induk Mahasiswa : Program Studi : SARJANA (S1) FISIKA Departemen : FISIKA Fakultas : MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) UNIVERSITAS SUMATERA UTARA Diluluskan di Medan, 9 Agustus 2011 Diketahui Departemen Fisika FMIPA USU Ketua Pembimbing DR. Marhaposan Situmorang Dr. Perdinan Sinuhaji, MS NIP NIP

3 PERNYATAAN PELAPISAN NIKEL PADA BAJA KARBON RENDAH DENGAN METODE ELEKTROPLATING SEBAGAI ANTI KOROSI SKRIPSI Saya mengakui bahwa skripsi ini adalah hasil kerja saya sendiri, kecuali beberapa kutipan dan ringkasan yang masing-masing disebutkan sumbernya. Medan, 9 Agustus 2011 RUSDALENA

4 PENGHARGAAN Puji dan syukur penulis haturkan kepada Allah SWT yang Maha Pengasih lagi Maha Penyayang yang telah memberikan rahmat dan hidayah-nya sehingga penulis dapat menyelesaikan skripsi yang berjudul Pelapisan Nikel pada Baja Karbon Rendah dengan Metode Elektroplating sebagai Anti Korosi, yang dilaksanakan di Laboratorium Electroplating Teknik Mesin Politeknik Negeri Medan dan pengujiannya di Pendidikan Teknologi Kimia Industri Medan. Ucapan terima kasih penulis sampaikan kepada Dr. Perdinan Sinuhaji, MS selaku Dosen Pembimbing penulis serta Drs. Infarizal dan Safitri selaku pembimbing di lapangan yang telah memberikan bimbingan, waktu dan tenaga kepada penulis dalam penyelesaian skripsi ini. Ucapan terima kasih juga penulis ucapkan kepada Dr. Luhut Sihombing, M.Si selaku Dosen Wali penulis selama mengikuti perkuliahan, kepada Ketua dan Sekretaris Jurusan Departemen Fisika DR. Marhaposan Situmorang dan Dra. Justinon, M.Si, Dekan FMIPA USU Dr. Sutarman, M.Sc serta semua Staf Pengajar dan Pegawai Departemen Fisika FMIPA USU. Tidak lupa penulis ucapkan terima kasih kepada yang paling kucintai dan kusayangi Ayahanda Sumarno dan Ibunda Tuminem yang telah memberikan dukungan baik moril maupun materil, kepada kakak-kakak ku tersayang Warni/Ali, Asiati/Usup, dan Idariati/Agus, Abang-abang ku tersayang Erdianto/Nita, Sutrisno dan Wahyudi, keponakan ku yang selalu membuatku tersenyum Nining dan Ery serta seluruh keluarga besar yang tidak dapat disebutkan namanya satu persatu, penulis ucapkan banyak terima kasih. Akhirnya tidak terlupakan untuk rekan seperjuangan ku Siska Futri Nst dan sahabat-sahabat ku (Juriah, Irna, Isma, Juli, Eva Pgb, Rahma, Angel, Ummi, Rini, Mora, Eva R, Suci, Dila, Delo) dan adik ku Wanda serta boy friend s (Oki, Iwan, Ichsan, Hilman dan Martin) yang selalu memberi motivasi dan semangat, buat abang-abang ku 2006 (Indra, Gilang, Riri, Deri dan Hakim) juga penulis ucapkan terima kasih, tidak terlupa juga buat semua pengurus UKMI AL- Falak yang mengajariku arti kehidupan dan semua mahasiswa Fisika USU khususnya stambuk 2007 yang is the best dan mengajariku arti sebuah kekeluargaan. Penulis menyadari bahwa dalam penulisan skripsi ini masih banyak kekurangan. Oleh karena itu, penulis mengharapkan adanya saran dan kritik yang bersifat konstruktif (membangun) demi kesempurnaan penyusunan skripsi ini. Akhirnya penulis berharap, semoga skripsi ini dapat membawa manfaat bagi kita semua.

5 PELAPISAN NIKEL PADA BAJA KARBON RENDAH DENGAN METODE ELEKTROPLATING SEBAGAI ANTI KOROSI ABSTRAK Telah dilakukan penelitian tentang pelapisan nikel pada baja karbon rendah DIN ST 37 dengan metode elektroplating. Dalam penelitian ini dilakukan pengujian kekerasan, ketebalan, korosi dan mengamati mikrostruktur. Pelapisan nikel pada baja karbon rendah divariasikan terhadap arus; 4; 5; 6; 7; dan 8 Amp, kekerasan maksimum 1212,897 MPa pada arus 8 Amp, ketebalan maksimum 0,058 mm pada arus 8 Amp, laju korosi pada masing-masing larutan NaCl (3%), H 2 SO 4 (20%), di air dan udara, pelapisan nikel pada baja karbon rendah yang paling baik digunakan di udara daripada di air, larutan NaCl (3%) dan H 2 SO 4 (20%), pada arus 8 Amp dengan laju korosi 0,00168 mm/thn. Mikrostruktur dari baja karbon rendah adalah ferrit dan pearlite.

6 NICKEL COATING ON LOW CARBON STEEL WITH ELECTROPLATING METHOD AS ANTI-CORROSION ABSTRACT Research has been conducted on the nickel coating on low carbon steel DIN ST 37 with the method of electroplating. In this research was tested about hardness, thickness, corrosion and observed microstructure. Nickel coating on low carbon steel is varied on current; 4; 5; 6; 7, and 8 Amp, maximum hardness MPa at 8 Amp current, maximum thickness of mm at 8 Amp current, the corrosion rate at each NaCl (3%), H 2 SO 4 (20%), in water and air, the nickel coating on low carbon steel is best used in air than in water, NaCl solution (3%) and H 2 SO 4 (20%), in the current 8 Amp with corrosion rate of mm / year. Microstructure of low carbon steel is ferrite and pearlite.

7 DAFTAR ISI Halaman Persetujuan... ii Pernyataan... iii Penghargaan... iv Abstrak... v Abstract... vi Daftar Isi... vii Daftar Tabel... ix Daftar Gambar... x Bab I Bab II Pendahuluan 1.1 Latar Belakang Rumusan Masalah Batasan Masalah Tujuan Penelitian Manfaat Penelitian Tempat Penelitian Sistematika Penulisan... 4 Tinjauan Pustaka 2.1 Metode-metode Pelapisan dengan Logam Elektroplating Unsur-unsur Pokok Proses Elektroplating Fungsi Elektroplating Pencelupan Panas (hot dipping) Pelapisan dengan Penyemprotan Sifat-sifat Bahan Pelapis Baja Pengertian Baja Sifat-sifat Baja Klasifikasi Baja Nikel Sifat-sifat Nikel Nikel dan Paduannya Karakteristik Pengujian Material Ketebalan Korosi Korosi dalam Air atau Lingkungan Berair Korosi Udara Prinsip-prinsip Dasar Pengendalian Korosi Pengukuran Kekerasan Vickers Keuntungan dan Kerugian Kekerasan Vickers Analisa Struktur Mikro... 18

8 Bab III Bab IV Bab V Metodologi Penelitian 3.1 Peralatan dan Bahan-Bahan Peralatan Bahan-Bahan Diagram Alir Penelitian Variabel Eksperimen Variabel Penelitian Variabel Percobaan yang Diuji Prosedur Penelitian Cara Pembuatan Larutan Pelaksanaan Pembersihan Sampel Pelaksanaan Pelapisan Nikel Pengujian Sifat Fisis Ketebalan (Thikcness) Ketahanan Korosi (Corrosion Resistance) Sifat Mekanik Uji Kekerasan (Vickers Hardness Test) Analisa Mikrostruktur Mikroskop Optik (Microscope Optic) Hasil dan Pembahasan 4.1 Hasil Penelitian Sifat Fisis Hasil Pengujian Ketebalan Hasil Pengujian Korosi Sifat Mekanik Hasil Pengujian Kekerasan Analisa Mikrostruktur Mikroskop Optik Pembahasan Sifat Fisis Ketebalan (Thickness) Ketahanan Korosi (Corrosion Resistance) Sifat Mekanik Kekerasan (Vickers Hardness) Kesimpulan dan Saran 5.1 Kesimpulan Saran DAFTAR PUSTAKA LAMPIRAN

9 DAFTAR TABEL Tabel 3.1 Berat Pelapisan Nikel untuk Uji Korosi dalam Larutan NaCl Tabel 3.2 Berat Pelapisan Nikel untuk Uji Kekerasan, Ketebalan dan Mikrostruktur Tabel 3.3 Berat Pelapisan Nikel untuk Uji Korosi dalam Air Tabel 3.4 Berat Pelapisan Nikel untuk Uji Korosi dalam Larutan H 2 SO Tabel 3.5 Berat Pelapisan Nikel untuk Uji Korosi di Udara Tabel 4.1 Pengukuran Ketebalan Pelapisan Nikel Tabel 4.2 Data Laju Korosi dari Pengujian Korosi dalam NaCl (3%) Tabel 4.3 Data Laju Korosi dari Pengujian Korosi dalam H 2 O Tabel 4.4 Data Laju Korosi dari Pengujian Korosi dalam H 2 SO 4 (20%) Tabel 4.5 Data Laju Korosi dari Pengujian Korosi di Udara Tabel 4.6 Data Pengukuran Kekerasan Lapisan Nikel... 33

10 DAFTAR GAMBAR Gambar 2.1 Rangkaian dasar elektrik untuk electroplating... 6 Gambar 2.2 Kekerasan Vickers Test Gambar 3.1 Diagram Alir Penelitian Gambar 4.1 Mikrostruktur Baja Karbon Rendah Nikel Dengan Kuat Arus 4 Amp Gambar 4.2 Mikrostruktur Baja Karbon Rendah Nikel Dengan Kuat Arus 5 Amp Gambar 4.3 Mikrostruktur Baja Karbon Rendah Nikel Dengan Kuat Arus 6 Amp Gambar 4.4 Mikrostruktur Baja Karbon Rendah Nikel Dengan Kuat Arus 7 A Gambar 4.5 Mikrostruktur Baja Karbon Rendah Nikel Dengan Kuat Arus 8 A Gambar 4.6 Hubungan Ketebalan Pelapisan Nikel dengan Kuat Arus Gambar 4.7 Hubungan Laju Korosi dengan Kuat Arus dalam Larutan NaCl 3% Gambar 4.8 Hubungan Laju Korosi dengan Kuat Arus Pada Air Gambar 4.9 Hubungan Laju Korosi dengan Kuat Arus Pada Larutan H 2 SO 4 20% Gambar 4.10 Hubungan Laju Korosi dengan Kuat Arus Di Udara Gambar 4.11 Hubungan Kekerasan Pelapisan Nikel dengan Kuat Arus... 41