PENGARUH KANDUNGAN UNSUR Ag PADA PADUAN SOLDER BEBAS TIMBAL TERHADAP SIFAT MEKANIS DAN FISIS Sn-0.7Cu- X Ag
|
|
|
- Sudirman Makmur
- 6 tahun lalu
- Tontonan:
Transkripsi
1 PENGARUH KANDUNGAN UNSUR Ag PADA PADUAN SOLDER BEBAS TIMBAL TERHADAP SIFAT MEKANIS DAN FISIS Sn-0.7Cu- X Ag Erwin Siahaan Laboratorium Metalurgi Fisik, Program Studi Teknik Mesin, Universitas Tarumanagara erwins@ft.untar.ac.id Abstract: In this research was carried out of lead free solder sample of Sn-Cu-Ag to characterized how far the effect of Ag composition on Lead Free Solder of Sn0.7CuxAg to replace SnPb alloy. The research will be carried out such us specific gravity, melting point, micro structure, shear strength, and micro hardness value The impact was added Ag to Sn -Cu-Ag has shown that shear strength for each at 61% on material Sn-0.7Cu-1Ag,73% at material Sn-0.7Cu-1.5Ag and 94% on material Sn-Cu-2Ag. The results has shown that on Sn-0.7Cu-1Ag material getting melting point bellow Sn -Pb that is C. Key words: Material solder Sn-Cu-Ag, physical properties, mechanical properties PENDAHULUAN Penyolderan merupakan Proses penyambungan metalurgi suhu rendah yang pada umumnya reversible, merupakan suatu metode penggabungan dengan menggunakan logam pengisi yaitu logam solder yang memiliki temperatur leleh di bawah 315 C. Dalam penyambungan solder terjadi proses pembasahan (wetting) diikuti dengan reaksi kimia. Mampu basah merupakan fungsi dari material solder, flux, dan material yang akan disambung, seperti Cu. Reaksi kimia yang mengikuti proses pembasahan adalah antara solder cair dan material yang disambung untuk membentuk daerah fasa intermetalik pada antarmuka. Komposisi solder yang digunakan pada fabrikasi elektronik harus mempunyai mampu basah yang bagus dan mempunyai minimal satu komponen yang dapat membentuk intermetalik yang konduktif, stabil terhadap suhu, tidak getas, dan plastis dengan material dasar. Untuk alasan ini paduan solder yang paling umum adalah paduan berbasis Pb, misalnya Pb-Sn. Ada beberapa alasan sejarah untuk penggunaan yang luas dari paduan Pb-Sn sebagai paduan solder [1-4]. Alasan ini meliputi suhu solidus yang rendah, mampu bentuk yang bagus, dan membentuk intermetalik Cu-Sn pada selang suhu yang lebar, serta peralatan dan proses yang lebih murah. Akan tetapi Pb merupakan logam berat yang berbahaya (toxic) dan sudah ada peraturan pembatasan penggunaan Pb di negara-negara maju. Oleh karena itu berbagai usaha telah dilakukan di negaranegara tersebut untuk menggantikan solder berbasis Pb maupun paduan yang mengandung Pb lebih besar atau sama dengan 0.1% berat (ASTM B32-96 dan ISO 9453) dengan paduan lain yang ramah lingkungan [1,3,4]. Pengembangan paduan solder bebas Pb mulai dilakukan sejak diketahui bahwa Pb beracun bagi lingkungan dan berbahaya bagi manusia. Untuk itu di beberapa negara di Eropa, Asia maupun Amerika industri-industrinya mulai beralih menggunakan paduan-paduan yang bebas dari kandungan Pb [2-4]. Salah satunya penggunaan solder yang dulunya masih menggunakan Pb sebagai salah satu unsur pemadunya. Sebelum memulai dilakukan suatu studi tentang paduan solder bebas timbal (Pb) akan merujuk kepada hasil penelitian bebarapa peneliti sebelumnya [6-9]. METODE PENELITIAN Bahan dan Peralatan Untuk melakukan penelitian tentang Pengaruh Unsur Ag Pada Paduan Solder Bebas Timbal Sn-0.7 Cu- X Ag Terhadap Sifat Mekanis Dan Fisis. Digunakan bahan dan alat sebagai berikut: 1. Vickers Hardness Tester 2. Universal testing 3. Mikroskop Digital Jenco 4. Sn-0.7Cu 5. Ag Murni Pengaruh kandungan unsur Ag pada paduan solder bebas timbal terhadap sifat mekanis dan (E. Siahaan) 123
2 Gambar 1. Alat uji kekerasan Gambar 2. Alat uji geser Gambar 3. Alat uji struktur mikro Gambar 4. Sn-0.7Cu Gambar 5. Ag murni 124 Poros, Volume 15 Nomor 2, November 2017,
3 Mulai Persiapan Alat dan Bahan (SnCuAg) Material Balance Sn-0.7Cu- X Ag Peleburan dan Penuangan Sn-0.7Cu- X Ag Pengujian Karakteristik Paduan Solder Sifat mekanis: Uji Kekerasan (vickers) Uji Geser Pengamatan Struktur Mikro Sifat fisis: Melting point Berat Jenis Pengupulan Data dari Pengujian Perbandingan SnPb Analisa dan Pembahasan Kesimpulan dan Saran Selesai Gambar 6. Diagram alir penelitian HASIL DAN PEMBAHASAN Hasil Penelitian: Tabel 1. Material balance Berat (gram) No Paduan Material Total (gram) Sn-0.7Ag (gram) Ag (gram) 1 Sn-0.7Cu-1Ag Sn-0.7Cu-1.5Ag Sn-0.7Cu-2Ag Tabel 2. Data hasil pengukuran berat jenis paduan Sn-Cu-Ag Kode Sampel Berat Berat Jenis H (gram) 0 =ml H 1 =ml h=ml gr/ml Sn-Pb Sn-0.7Cu-1Ag Sn-0.7Cu-1.5Ag Sn-0.7Cu-2Ag Pengaruh kandungan unsur Ag pada paduan solder bebas timbal terhadap sifat mekanis dan (E. Siahaan) 125
4 Tabel 3. Data hasil pengukuran temperatur leleh paduan Sn-Cu-Ag Kode Sampel Temperatur Leleh ( o C) Sn-Pb 183 Sn-0.7Cu-1Ag 182 Sn-0.7Cu-1.5Ag 191 Sn-0.7Cu-2Ag 198 Tabel 4. Data hasil pengujian kekerasan pada paduan Sn-Cu-Ag Kode Sampel Kekerasan (VHN) Sn-Pb 40 Sn-0.7Cu-1Ag Sn-0.7Cu-1.5Ag Sn-0.7Cu-2Ag Tabel 5. Data hasil pengujian kekuatan geser paduan Sn-Cu-Ag Kode Sampel Kekuatan Geser (N/mm 2 ) Sn-Pb Sn-0.7Cu-1Ag Sn-0.7Cu-1.5Ag Sn-0.7Cu-2Ag Gambar 7. Grafik pengaruh penambahan Ag terhadap perubahan berat jenis paduan Sn-0.7Cu Dari hasil pengukuran berat jenis yang dituangkan dalam Tabel 2 kemudian diubah ke dalam bentuk grafik, seperti dipaparkan dalam Gambar 7 terlihat bahwa penambahan unsur Ag berpengaruh terhadap nilai berat jenis dari paduan Sn-Cu. Semakin besar penambahan Ag, nilai berat jenis dari paduan Sn-Cu terlihat semakin naik. Hal ini disebabkan karena berat jenis Ag lebih tinggi dari berat jenis Sn dan Cu. Dari hasil pengujian temperature leleh yang dituangkan dalam Tabel 3 kemudian diubah ke dalam bentuk grafik, seperti dipaparkan pada Gambar 8 terlihat bahwa penambahan unsur Ag berpengaruh terhadap temperature leleh dari paduan Sn-0.7Cu terlihat bahwa semakin besar penambahan Ag, temperatur leleh dari paduan Sn-0.7Cu semakin meningkat. Hal ini disebabkan karena Ag memiliki titik leleh yang lebih tinggi dibandingkan dengan Sn-Cu. 126 Poros, Volume 15 Nomor 2, November 2017,
5 Gambar 8. Grafik pengaruh penambahan Ag terhadap temperatur leleh paduan Sn-0.7Cu Gambar 9. Grafik pengaruh penambahan Ag terhadap kekerasan paduan Sn-0.7Cu Gambar 10. Grafik pengaruh penambahan Ag terhadap kekuatan geser paduan Sn-0.7Cu Pengaruh kandungan unsur Ag pada paduan solder bebas timbal terhadap sifat mekanis dan (E. Siahaan) 127
6 Dari hasil pengujian kekerasan yang dituangkan dalam Tabel 4 kemudian diubah ke dalam bentuk grafik, seperti dipaparkan dalam Gambar 9 terlihat bahwa penambahan unsur Ag berpengaruh terhadap kekerasan dari paduan biner Sn-0.7Cu. Semakin besar penambahan Ag, nilai kekerasan dari paduan biner Sn-0.7Cu semakin meningkat. Dari hasil pengujian kekuatan geser yang dituangkan dalam Tabel 5 kemudian diubah kedalam bentuk grafik, seperti dipaparkan dalam Gambar 10 terlihat bahwa penambahan unsur Ag berpengaruh terhadap kekuatan geser pada paduan Sn-0,7Cu. Peningkatan kekuatan geser pada paduan Sn-0.7Cu yang mengandung Ag1% adalah , sedangkan pada paduan Sn-0.7Cu yang mengandung Ag 2% mengalami peningkatan kekuatan geser Hal ini menunjukkan bahwa peningkatan kekuatan geser diperoleh dari penambahan Ag. Gambar 11. Struktur mikro paduan Sn-0.7 Cu-1Ag Sn-0.7Cu-1Ag. pembesaran foto 500 Etsa: Asam Nitrat 2%, Akohol 98% Gambar 12. Struktur mikro paduan Sn-0.7Cu-2Ag. Pembesaran Foto500 Etsa: Asam Nitrat 2%, Akohol 98% 128 Poros, Volume 15 Nomor 2, November 2017,
7 Gambar 13. Struktur mikro paduan Sn-0.7Cu-1.5Ag. pembesaran foto 500 Etsa: Asam Nitrat 2%, Akohol 98% SIMPULAN 1. Pengaruh penambahan Ag pada paduan Sn-Cu-Ag dapat menaikkan berat jenis, yaitu pada material Sn-0.7Cu-1Ag diperoleh 7.36 gr/ml, pada material Sn-0.7Cu-1.5Ag diperoleh 8.9 gr/ml, dan pada material Sn-0.7Cu-2Ag diperoleh 9.45 gr/ml. 2. Pengaruh penambahan Ag pada paduan Sn-Cu-Ag dapat menaikkan temperatur leleh,182 C pada material Sn-0.7Cu-1Ag, 191 C pada material Sn-0.7Cu-1.5Ag dan 198 C pada material Sn-0.7Cu-2Ag. 3. Pengaruh penambahan Ag pada paduan Sn-Cu-Ag menaikkan nilai kekerasan, yaitu pada material Sn-0.7Cu-1Ag diperoleh VHN, pada material Sn-0.7Cu-1.5Ag diperoleh VHN, dan pada material Sn-0.7Cu-2Ag diperoleh VHN. 4. Pengaruh penambahan Ag pada paduan Sn-Cu-Ag dapat meningkatkan kekuatan geser, yaitu pada material Sn-0.7Cu-1Ag diperoleh N/mm 2, pada material Sn-0.7Cu-1.5Ag diperoleh N/mm 2, dan pada material Sn-0.7Cu-2Ag diperoleh N/mm Memiliki titik leleh ekuivalen dengan Sn-Pb(183 C). DAFTAR PUSTAKA [1]. Lee, Ning Cheng. Getting Ready for Lead Free Solders. USA: Indium Corporation of America Utica NY (2007) [2]. Yanfu, Yan et al. Influence of Temperature on Creep (2007). Behaviour of Ag Particle Enhancement SnCu Based Composite Solder, TSINGHUA SCIENCE AND TECHNOLOGY, ISSN /18 pp , Volume 12, number 3, June [3]. K.S. Bae, S.J. Kim, J Mater Res 17, 743 (2002). [4]. K. Suganuma, Curr Opin Solid State Mater Sci 5, 55 (2001) [5]. Lin, J.K.; DeSilva, A.; Frear, D.; Guo, Y.; Jang, J.;Li, L.; Mitchell, D.; Yeung, B.; Zhang, C. Characterization of lead free solders and under bump metallurgies for flip-chip package. Proc 51 ECTC, Orlando, FL, IEEE: Piscataway, NJ,; , May 2001 [6]. David E. Weisberg. Chapter 14 : Intergraph p. 14-8, [7]. Cho, M. G., Lee, H. M. Effects of Minor Additions of Zn on Interfacial Reactions of Sn-Ag-Cu and Sn-Cu Solders with Various Cu Substrates during Thermal Aging. Journal of ELECTRONIC MATERIALS, 36(11), , Pengaruh kandungan unsur Ag pada paduan solder bebas timbal terhadap sifat mekanis dan (E. Siahaan) 129
8 [8]. Mayappan, R. Wetting and Intermetallic Study between Sn-3.5Ag-1.0Cu-xZn Lead-Free Solders and Copper Substrate (x = 0, 0.1, 0.4,0.7). Advanced Materials Research, 501, , [9]. Mohd Salleh, M. A. A., Hazizi, M. H. Z., Ahmad, Z. A., Hussin, K., & Ahmad, K. R. Wettability, electrical and mechanical properties of 99.3Sn-0.7Cu/Si 3N4 novel lead-free nano composite solder. Advance Materials Research, 277, , Poros, Volume 15 Nomor 2, November 2017,
KARAKTERISTIK SIFAT MEKANIK DAN STRUKTUR MIKRO PADA MATERIAL Sn-0,7Cu- X Zn
KARAKTERISTIK SIFAT MEKANIK DAN STRUKTUR MIKRO PADA MATERIAL Sn-0,7Cu- X Zn Ridwan Adidarma, Erwin Siahaan dan Abrar Riza Jurusan Teknik Mesin, Fakultas Teknik Universitas Tarumanagara Abstract: Lead (Pb)
PENGARUH PENAMBAHAN UNSUR SILIKON (Si) PADA ALUMINIUM PADUAN HASIL REMELTING VELG SEPEDA MOTOR TERHADAP SIFAT FISIS DAN MEKANIS SKRIPSI
PENGARUH PENAMBAHAN UNSUR SILIKON (Si) PADA ALUMINIUM PADUAN HASIL REMELTING VELG SEPEDA MOTOR TERHADAP SIFAT FISIS DAN MEKANIS SKRIPSI Diajukan sebagai salah satu syarat untuk memperoleh gelar Sarjana
PENGARUH WAKTU PENGELASAN GMAW TERHADAP SIFAT FISIK MEKANIK SAMBUNGAN LAS LOGAM TAK SEJENIS ANTARA ALUMINIUM DAN BAJA KARBON RENDAH
PENGARUH WAKTU PENGELASAN GMAW TERHADAP SIFAT FISIK MEKANIK SAMBUNGAN LAS LOGAM TAK SEJENIS ANTARA ALUMINIUM DAN BAJA KARBON RENDAH Bi Asngali dan Triyono Jurusan Teknik Mesin Universitas Sebelas Maret
PENGARUH PENAMBAHAN TEMBAGA (Cu) TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PADA PADUAN ALUMINIUM-SILIKON (Al-Si) MELALUI PROSES PENGECORAN
Laporan Tugas Akhir PENGARUH PENAMBAHAN TEMBAGA (Cu) TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PADA PADUAN ALUMINIUM-SILIKON (Al-Si) MELALUI PROSES PENGECORAN Nama Mahasiswa : I Made Pasek Kimiartha NRP
Jl. Prof. Sudharto, SH., Tembalang-Semarang 50275, Telp * Abstrak. Abstract
PENGARUH PENAMBAHAN UNSUR TEMBAGA (Cu) TERHADAP SIFAT FISIS DAN MEKANIS MATERIAL CHASSIS BERBAHAN DASAR LIMBAH ALUMINIUM HASIL PENGECORAN HPDC YANG DISERTAI PERLAKUAN PANAS (HEAT TREATMENT) *Pandhu Madyantoro
KAJIAN PENDAHULUAN PEMBUATAN PADUAN Fe-Ni-Al DARI BAHAN BAKU FERRONIKEL PT. ANTAM Tbk. TUGAS AKHIR. Fiksi Sastrakencana NIM :
KAJIAN PENDAHULUAN PEMBUATAN PADUAN Fe-Ni-Al DARI BAHAN BAKU FERRONIKEL PT. ANTAM Tbk. TUGAS AKHIR Diajukan untuk memenuhi syarat kelulusan tahap pendidikan strata-1 pada Program Studi Teknik Metalurgi
BAB I PENDAHULUAN. Luasnya pemakaian logam ferrous baik baja maupun besi cor dengan. karakteristik dan sifat yang berbeda membutuhkan adanya suatu
BAB I PENDAHULUAN 1.1. Latar Belakang Penelitian Luasnya pemakaian logam ferrous baik baja maupun besi cor dengan karakteristik dan sifat yang berbeda membutuhkan adanya suatu penanganan yang tepat sehingga
BAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3.1.1. Tempat penelitian Penelitian dilakukan di Laboratorium Material Jurusan Teknik Mesin Universitas Sebelas Maret Surakarta 3.1.2. Alat dan bahan 3.2.1 Alat Alat yang dipergunakan
KARAKTERISTIK SIFAT MEKANIS DAN STRUKTUR MIKRO PROSES AUSTEMPER PADA BAJA KARBON S 45 C DAN S 60 C
KARAKTERISTIK SIFAT MEKANIS DAN STRUKTUR MIKRO PROSES AUSTEMPER PADA BAJA KARBON S 45 C DAN S 60 C Lim Richie Stifler, Sobron Y.L. dan Erwin Siahaan Jurusan Teknik Mesin, Fakultas Teknik Universitas Tarumanagara
KARAKTERISASI BAJA ARMOUR HASIL PROSES QUENCHING DAN TEMPERING
D.3 KARAKTERISASI BAJA ARMOUR HASIL PROSES QUENCHING DAN TEMPERING Padang Yanuar *, Sri Nugroho, Yurianto Jurusan Magister Teknik Mesin Fakultas Teknik UNDIP Jl. Prof. Sudharto SH Kampus Undip Tembalang
PENGARUH TEKANAN INJEKSI PADA PENGECORAN CETAK TEKANAN TINGGI TERHADAP KEKERASAN MATERIAL ADC 12
C.10. Pengaruh tekanan injeksi pada pengecoran cetak tekanan tinggi (Sri Harmanto) PENGARUH TEKANAN INJEKSI PADA PENGECORAN CETAK TEKANAN TINGGI TERHADAP KEKERASAN MATERIAL ADC 12 Sri Harmanto Jurusan
BAB IV ANALISA DAN PEMBAHASAN. Pembuatan spesimen dilakukan dengan proses pengecoran metode die
BAB IV ANALISA DAN PEMBAHASAN 4.1 Proses Pengecoran Hasil penelitian tentang pembuatan poros berulir (Screw) berbahan dasar 30% Aluminium bekas dan 70% piston bekas dengan penambahan unsur 2,5% TiB. Pembuatan
PENGARUH PERBEDAAN LAJU WAKTU PROSES PEMBEKUAN HASIL COR ALUMINIUM 319 DENGAN CETAKAN LOGAM TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS
PENGARUH PERBEDAAN LAJU WAKTU PROSES PEMBEKUAN HASIL COR ALUMINIUM 319 DENGAN CETAKAN LOGAM TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS Errens Lowther 1), Sofyan Djamil 1) dan Eddy S. Siradj 2) 1) Program
ANALISA PENGARUH AGING 400 ºC PADA ALUMINIUM PADUAN DENGAN WAKTU TAHAN 30 DAN 90 MENIT TERHADAP SIFAT FISIS DAN MEKANIS
TUGAS AKHIR ANALISA PENGARUH AGING 400 ºC PADA ALUMINIUM PADUAN DENGAN WAKTU TAHAN 30 DAN 90 MENIT TERHADAP SIFAT FISIS DAN MEKANIS Disusun : SUDARMAN NIM : D.200.02.0196 JURUSAN TEKNIK MESIN FAKULTAS
BAB I PENDAHULUAN. penting pada proses penyambungan logam. Pada hakekatnya. diantara material yang disambungkan. Ini biasanya dilakukan
BAB I PENDAHULUAN 1.1. Latar Belakang Pengelasan dalam industri manufaktur memiliki peranan penting pada proses penyambungan logam. Pada hakekatnya proses las atau pengelasan adalah penyambungan dua material
STUDI PENGARUH VARIASI KUAT ARUS PENGELASAN PELAT AISI 444 MENGGUNAKAN ELEKTRODA AWS E316L
EKSERGI Jurnal Teknik Energi Vol 13 No. 1 Januari 2017; 10-14 STUDI PENGARUH VARIASI KUAT ARUS PENGELASAN PELAT AISI 444 MENGGUNAKAN ELEKTRODA AWS E316L Ojo Kurdi Departement Teknik Mesin, Fakultas Teknik,
Perbaikan Sifat Mekanik Paduan Aluminium (A356.0) dengan Menambahkan TiC
Perbaikan Sifat Mekanik Paduan Aluminium (A356.0) dengan Menambahkan TiC Suhariyanto Jurusan Teknik Mesin FTI-ITS Kampus ITS Sukolilo Surabaya 60111 Telp. (031) 5922942, Fax.(031) 5932625, E-mail : d3mits@rad.net.id
PENGARUH UNSUR SILIKON PADA ALUMINIUM ALLOY (Al Si) TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO
PENGARUH UNSUR SILIKON PADA ALUMINIUM ALLOY (Al Si) TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO Ratih Ponco K.S., Erwin Siahaan dan Steven Darmawan Jurusan Teknik Mesin, Fakultas Teknik Universitas Tarumanagara
TUGAS SARJANA KARAKTERISASI SIFAT MEKANIK DAN STRUKTUR MIKRO PRODUK CORAN PADUAN ALUMINIUM DENGAN VARIASI KOMPOSISI TEMBAGA
TUGAS SARJANA KARAKTERISASI SIFAT MEKANIK DAN STRUKTUR MIKRO PRODUK CORAN PADUAN ALUMINIUM DENGAN VARIASI KOMPOSISI TEMBAGA Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Kesarjanaan Strata
pendinginan). Material Teknik Universitas Darma Persada - Jakarta
BAB V DIAGRAM FASE Komponen : adalah logam murni atau senyawa yang menyusun suatu logam paduan. Contoh : Cu - Zn (perunggu) komponennya adalah Cu dan Zn Solid solution (larutan padat) : terdiri dari beberapa
PENGARUH PENAMBAHAN Mg DAN PERLAKUAN PANAS TERHADAP SIFAT FISIK MEKANIK KOMPOSIT MATRIKS ALUMINIUM REMELTING PISTON BERPENGUAT SiO 2
PENGARUH PENAMBAHAN Mg DAN PERLAKUAN PANAS TERHADAP SIFAT FISIK MEKANIK KOMPOSIT MATRIKS ALUMINIUM REMELTING PISTON BERPENGUAT SiO 2 SKRIPSI Diajukan sebagai salah satu syarat untuk memperoleh gelar Sarjana
ISSN hal
Vokasi Volume IX, Nomor 2, Juli 2013 ISSN 193 9085 hal 134-140 PENGARUH KECEPATAN PUTAR DAN PENAMBAHAN INOKULAN AL-TiB PADA CENTRIFUGAL CASTING TERHADAP SIFAT FISIS DAN MEKANIS PADUAN ALUMINIUM COR A35
EVALUASI BESAR BUTIR TERHADAP SIFAT MEKANIS CuZn70/30 SETELAH MENGALAMI DEFORMASI MELALUI CANAI DINGIN
EVALUASI BESAR BUTIR TERHADAP SIFAT MEKANIS CuZn70/30 SETELAH MENGALAMI DEFORMASI MELALUI CANAI DINGIN Riyan Sanjaya 1) dan Eddy S. Siradj 2) 1) Program Studi Teknik Mesin, Fakultas Teknik Universitas
PENGARUH PUTARAN TERHADAP LAJU KEAUSAN Al-Si ALLOY MENGGUNAKAN METODE PIN ON DISK TEST
PENGARUH PUTARAN TERHADAP LAJU KEAUSAN Al-Si ALLOY MENGGUNAKAN METODE PIN ON DISK TEST Ikwansyah Isranuri (1),Jamil (2),Suprianto (3) (1),(2),(3) Departemen Teknik Mesin Fakultas Teknik USU Jl. Almamater,
SKRIPSI. PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM :
SKRIPSI PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM : 1104305004 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS UDAYANA
PEMBUATAN STRUKTUR DUAL PHASE BAJA AISI 3120H DARI BESI LATERIT
PEMBUATAN STRUKTUR DUAL PHASE BAJA AISI 3120H DARI BESI LATERIT Saefudin 1*, Toni B. Romijarso 2, Daniel P. Malau 3 Pusat Penelitian Metalurgi dan Material Lembaga Ilmu Pengetahuan Indonesia Kawasan PUSPIPTEK
ANALISA PENGARUH PENAMBAHAN CU PADA MATRIKS KOMPOSIT ALUMINIUM REMELTING
ANALISA PENGARUH PENAMBAHAN CU PADA MATRIKS KOMPOSIT ALUMINIUM REMELTING PISTON BERPENGUAT PASIR SILIKA TERHADAP KEKUATAN IMPAK DAN STUKTUR MIKRO PADA KOMPOSIT MATRIK ALUMINIUM DENGAN METODE STIR CASTING
TUGAS SARJANA ANALISIS KEKUATAN LULUH MINIMUM DITINJAU DARI STRUKTUR BUTIRAN LOGAM DASAR-HAZ-LOGAM LAS SAMBUNGAN PIPA GAS
TUGAS SARJANA ANALISIS KEKUATAN LULUH MINIMUM DITINJAU DARI STRUKTUR BUTIRAN LOGAM DASAR-HAZ-LOGAM LAS SAMBUNGAN PIPA GAS Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Kesarjanaan Strata Satu
Pengaruh Solution treatment Singkat pada Paduan Al-Si-Mg : Sebuah Studi Awal
Pengaruh Solution treatment Singkat pada Paduan Al-Si-Mg : Sebuah Studi Awal Indra Sidharta, Rahadian Firman P, Asri Kusumaningtyas, Wajan Berata, Sutikno Jurusan Teknik Mesin ITS Kampus ITS Sukolilo,
ANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIKS ALUMINIUM REMELTING
ANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIKS ALUMINIUM REMELTING PISTON BERPENGUAT SIO2 TERHADAP KEKUATAN IMPAK DAN STRUKTUR MIKRO DENGAN METODE STIR CASTING SKRIPSI Diajukan sebagai salah satu
PENGARUH MEDIA PENDINGIN PADA PROSES HARDENING MATERIAL BAJA S45C
PENGARUH MEDIA PENDINGIN PADA PROSES HARDENING MATERIAL BAJA S45C Syaifudin Yuri, Sofyan Djamil dan M. Sobrom Yamin Lubis Program Studi Teknik Mesin, Fakultas Teknik Universitas Tarumanagara, Jakarta e-mail:
SIFAT MEKANIK DAN STRUKTUR MIKRO SAMBUNGAN LAS ALUMINIUM 6061 HASIL FRICTION WELDING ABSTRACT
SIFAT MEKANIK DAN STRUKTUR MIKRO SAMBUNGAN LAS ALUMINIUM 6061 HASIL FRICTION WELDING Hendry Wicaksana S 1, Santoso Mulyadi 2, Ahmad Syuhri 2 1 Alumni Teknik Mesin Fakultas Teknik Universitas Jember, Jl.
STRUKTUR MIKRO DAN SIFAT MEKANIS ALUMINIUM PADUAN SERI 6063 HASIL COR DARI CETAKAN LOGAM, PASIR RESIN FURAN DAN PASIR KOMOSSA
STRUKTUR MIKRO DAN SIFAT MEKANIS ALUMINIUM PADUAN SERI 6063 HASIL COR DARI CETAKAN LOGAM, PASIR RESIN FURAN DAN PASIR KOMOSSA Chris Marvin A., Eddy S. Siradj dan Sobron Y.L. Jurusan Teknik Mesin, Fakultas
PEMBUATAN MATERIAL DUAL PHASE DARI KOMPOSISI KIMIA HASIL PELEBURAN ANTARA SCALING BAJA DAN BESI LATERIT KADAR NI RENDAH YANG DIPADU DENGAN UNSUR SIC
PEMBUATAN MATERIAL DUAL PHASE DARI KOMPOSISI KIMIA HASIL PELEBURAN ANTARA SCALING BAJA DAN BESI LATERIT KADAR NI RENDAH YANG DIPADU DENGAN UNSUR SIC Daniel P. Malau 1*, Saefudin 2 *12 Pusat Penelitian
PENGARUH PENAMBAHAN NIKEL TERHADAP KEKUATAN TARIK DAN KEKERASAN PADA BESI TUANG NODULAR 50
PENGARUH PENAMBAHAN NIKEL TERHADAP KEKUATAN TARIK DAN KEKERASAN PADA BESI TUANG NODULAR 50 Sudarmanto Prodi Teknik Mesin Sekolah Tinggi Teknologi Adisutjipto Jalan Janti Blok R Lanud Adisutjipto, Yogyakarta
BAB IV HASIL DAN PEMBAHASAN. Struktur mikro adalah gambaran dari kumpulan fasa-fasa yang dapat diamati
BAB IV HASIL DAN PEMBAHASAN 4.1 Pengujian Struktur Mikro Struktur mikro adalah gambaran dari kumpulan fasa-fasa yang dapat diamati melalui teknik metalografi. Struktur mikro suatu logam dapat dilihat dengan
ANALISIS SIFAT FISIS DAN MEKANIS ALUMINIUM (Al) PADUAN DAUR ULANG DENGAN MENGGUNAKAN CETAKAN LOGAM DAN CETAKAN PASIR
ANALISIS SIFAT FISIS DAN MEKANIS ALUMINIUM (Al) PADUAN DAUR ULANG DENGAN MENGGUNAKAN CETAKAN LOGAM DAN CETAKAN PASIR Masyrukan Teknik Mesin Universitas Muhammadiyah Surakarta JL. A.Yani Tromol Pos I Pabelan
PEMBENTUKAN FASA INTERMETALIK α-al 8 Fe 2 Si DAN β-al 5 FeSi PADA PADUAN Al-7wt%Si DENGAN PENAMBAHAN UNSUR BESI DAN STRONSIUM SKRIPSI
PEMBENTUKAN FASA INTERMETALIK α-al 8 Fe 2 Si DAN β-al 5 FeSi PADA PADUAN Al-7wt%Si DENGAN PENAMBAHAN UNSUR BESI DAN STRONSIUM SKRIPSI Oleh ALI DARMAWAN 04 04 04 006 2 SKRIPSI INI DIAJUKAN UNTUK MELENGKAPI
BAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN 3.1. DIAGRAM ALIR PENELITIAN Gambar 3.1 Diagram Alir Penelitian 38 3.2. ALAT DAN BAHAN 3.2.1 Alat Gambar 3.2 Skema Peralatan Penelitian Die Soldering 3.2.2 Bahan Bahan utama
PENGARUH TEMPERATUR PADA PENGELASAN DIFUSI LOGAM LAS TAK SEJENIS ANTARA ALUMINIUM DAN BAJA DENGAN METODE THERMAL SPRAY TESIS.
PENGARUH TEMPERATUR PADA PENGELASAN DIFUSI LOGAM LAS TAK SEJENIS ANTARA ALUMINIUM DAN BAJA DENGAN METODE THERMAL SPRAY TESIS Disusun untuk memenuhi sebagai persyaratan mencapai derajat magister Program
BAB I PENDAHULUAN 1.1 Latar Belakang
1 BAB I PENDAHULUAN 1.1 Latar Belakang Teknik pengerasan permukaan merupakan suatu proses untuk meningkatkan sifat kekerasan serta kinerja dari suatu komponen atau material. Kerusakan suatu material biasanya
DYAN YOGI PRASETYO I
ANALISA PENGARUH KECEPATAN PENGADUKAN DAN TEMPERATUR TUANG PADA AMC BERPENGUAT PASIR SILICA TERHADAP KEKUATAN IMPAK DAN TARIK DENGAN METODE STIR CASTING SKRIPSI Diajukan sebagai salah satu syarat untuk
1 BAB I PENDAHULUAN. Salah satu industri yang cukup berkembang di Indonesia saat ini adalah
1 BAB I PENDAHULUAN 1.1 Latar Belakang Salah satu industri yang cukup berkembang di Indonesia saat ini adalah industri baja. Peningkatan jumlah industri di bidang ini berkaitan dengan tingginya kebutuhan
PENGARUH PERLAKUAN PANAS TERHADAP SIFAT FISIS DAN MEKANIS MATERIAL MODEL CHASSIS BERBASIS Al-Si-Mg HASIL PENGECORAN HIGH PRESSURE DIE CASTING
PENGARUH PERLAKUAN PANAS TERHADAP SIFAT FISIS DAN MEKANIS MATERIAL MODEL CHASSIS BERBASIS Al-Si-Mg HASIL PENGECORAN HIGH PRESSURE DIE CASTING *Dedas Agusta 1, Athanasius Priharyoto Bayuseno 2 1 Mahasiswa
BAB 1 PENDAHULUAN 1.1. LATAR BELAKANG
BAB 1 PENDAHULUAN 1.1. LATAR BELAKANG Paduan Fe-Al merupakan material yang sangat baik untuk digunakan dalam berbagai aplikasi terutama untuk perlindungan korosi pada temperatur tinggi [1]. Paduan ini
BAB 3 METODOLOGI PENELITIAN
BAB 3 METODOLOGI PENELITIAN 3.1.DIAGRAM ALIR PENLITIAN Persiapan Benda Uji Material Sand Casting Sampel As Cast Perlakuan Quench/ Temper Preheat 550 O C 10 menit Austenisasi 920 O C 40 menit Quenching
ANALISA LANJUT PERUBAHAN SIFAT MEKANIK BAHAN PEWTER DENGAN REDUKSI 50% PADA PROSES PENGEROLAN BAHAN
17 ANALISA LANJUT PERUBAHAN SIFAT MEKANIK BAHAN PEWTER DENGAN REDUKSI % PADA PROSES PENGEROLAN BAHAN Firlya Rosa. S.S.T., M.T. 1 Jurusan Teknik Mesin, Fakultas Teknik Universitas Bangka Belitung firlya@ubb.ac.id
Eksperimen Pembentukan Kristal BPSCCO-2223 dengan Metode Self-Flux
Berkala Fisika ISSN : 1410-9662 Vol.8, No.2, April 2005, hal 53-60 Eksperimen Pembentukan Kristal BPSCCO-2223 dengan Metode Self-Flux Indras Marhaendrajaya Laboratorium Fisika Zat Padat Jurusan Fisika
BAB IV PROSES PERLAKUAN PANAS PADA ALUMINIUM
BAB IV PROSES PERLAKUAN PANAS PADA ALUMINIUM 4.1. Proses Perlakuan Panas pada Aluminium Proses perlakuan panas merupakan suatu proses yang mengacu pada proses pemanasan dan pendinginan, dengan tujuan untuk
Karakterisasi Material Sprocket
BAB III PENGUMPULAN DATA 3.1 Diagram Alir Penelitian Mulai Spesimen & Studiliteratur Gambar teknik & Pengambilan sample pengujian Metalografi: Struktur Makro & Mikro Uji Kekerasan: Micro Vickers komposisi
BAB I PENDAHULUAN. Aluminium (Al) adalah salah satu logam non ferro yang memiliki. ketahanan terhadap korosi, dan mampu bentuk yang baik.
BAB I PENDAHULUAN 1.1. Latar Belakang Aluminium (Al) adalah salah satu logam non ferro yang memiliki beberapa keunggulan, diantaranya adalah memiliki berat jenis yang ringan, ketahanan terhadap korosi,
Available online at Website
Available online at Website http://ejournal.undip.ac.id/index.php/rotasi Pengaruh PWHT dan Preheat pada Kualitas Pengelasan Dissimilar Metal antara Baja Karbon (A-106) dan Baja Sri Nugroho, Wiko Sudiarso*
Kekuatan Tarik Dan Porositas Silinder Al-Mg-Si Hasil Die Casting Dengan Variasi Tekanan
Kekuatan Tarik Dan Porositas Silinder Al-Mg-Si Hasil Die Casting Dengan Variasi Tekanan Yudy Surya Irawan, Tjuk Oerbandono, Dian Fitria Agus Aristiyono, Pratikto Laboratorium Pengecoran Logam, Jurusan
BAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1 Hasil Pengelasan Pada FSW Pengelasan menggunakan metode friction stir welding ditunjukkan pada Gambar 4.1. Pengelasan dengan metode FSW ini merupakan pengelasan yang terjadi
ANALISIS KEKUATAN TARIK DAN STRUKTUR MIKRO PADA SAMBUNGAN T-JOINT DAN BUTT JOINT PIPA ALUMUNIUM DENGAN METODE SOLDERING
ANALISIS KEKUATAN TARIK DAN STRUKTUR MIKRO PADA SAMBUNGAN T-JOINT DAN BUTT JOINT PIPA ALUMUNIUM DENGAN METODE SOLDERING Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan
BAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3.1 Tempat Penelitian Penelitian dilakukan di INLASTEK (Institut Las Teknik) Surakarta dan Laboratorium Material Jurusan Teknik Mesin Fakultas Teknik Universitas Sebelas Maret
PENGARUH PROSES ROLLING TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS PADA KUNINGAN SETELAH DI PROSES ECAP
PENGARUH PROSES ROLLING TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS PADA KUNINGAN SETELAH DI PROSES ECAP Julyadi 1), Suryadi 2), Erwin Siahaan 1) dan Eddy S. Siradj 1) 1) Program Studi Teknik Mesin, Fakultas
ANALISIS SIFAT FISIS DAN MEKANIS PADA PELAPISAN KOMPOSIT MENGGUNAKAN TIMAH PUTIH
TUGAS AKHIR ANALISIS SIFAT FISIS DAN MEKANIS PADA PELAPISAN KOMPOSIT MENGGUNAKAN TIMAH PUTIH Disusun : SARYANTO NIM : D 200 040 103 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH SURAKARTA
BAB I PENDAHULUAN. mengenai hubungan antara komposisi dan pemprosesan logam, dengan
1 BAB I PENDAHULUAN 1.1. Latar Belakang Ilmu dan teknologi bahan merupakan penerapan teknologi mengenai hubungan antara komposisi dan pemprosesan logam, dengan sifat-sifat dan pemakaian yang sesuai dengan
BAB III METODOLOGI PENELITIAN. Studi Literatur. Persiapan Alat dan Bahan bahan dasar piston bekas. Proses pengecoran dengan penambahan Ti-B 0,05%
BAB III METODOLOGI PENELITIAN 3.1 Diagram Alir Mulai Studi Literatur Persiapan Alat dan Bahan bahan dasar piston bekas Proses pengecoran dengan penambahan Ti-B 0,05% Pengecoran suhu cetakan 250 C Pengecoran
UNIVERSITAS DIPONEGORO KARAKTERISASI PROSES PEMBUATAN AXLE BOTTOM BRACKET THREE PIECES PADA SEPEDA TUGAS AKHIR ARYO KUSUMOPUTRO L2E
UNIVERSITAS DIPONEGORO KARAKTERISASI PROSES PEMBUATAN AXLE BOTTOM BRACKET THREE PIECES PADA SEPEDA TUGAS AKHIR ARYO KUSUMOPUTRO L2E 605 308 FAKULTAS TEKNIK JURUSAN TEKNIK MESIN SEMARANG JUNI 2012 i ii
PENGARUH KECEPATAN PUTARANDAN DWELL TIME FLAT TOOL TERHADAP SIFAT FISIK DAN MEKANIK SAMBUNGAN FSSW AA5083DANGALVANIZED STEEL
PENGARUH KECEPATAN PUTARANDAN DWELL TIME FLAT TOOL TERHADAP SIFAT FISIK DAN MEKANIK SAMBUNGAN FSSW AA5083DANGALVANIZED STEEL SKRIPSI DiajukanSebagai Salah SatuSyaratUntukMemperolehGelar SarjanaTeknik Oleh
Analisis Sifat Fisis dan Mekanis Pada Paduan Aluminium Silikon (Al-Si) dan Tembaga (Cu) Dengan Perbandingan Velg Sprint
TUGAS AKHIR Analisis Sifat Fisis dan Mekanis Pada Paduan Aluminium Silikon (Al-Si) dan Tembaga (Cu) Dengan Perbandingan Velg Sprint Tugas Akhir ini disusun Guna Memenuhi Sebagian Syarat Memperoleh Derajat
PENGARUH TEMPERATUR TUANG DAN KANDUNGAN SILICON TERHADAP NILAI KEKERASAN PADUAN Al-Si
Pengaruh Temperatur Tuang dan Kandungan Silicon Terhadap Nilai Kekerasan Paduan Al-Si (Bahtiar & Leo Soemardji) PENGARUH TEMPERATUR TUANG DAN KANDUNGAN SILICON TERHADAP NILAI KEKERASAN PADUAN Al-Si Bahtiar
BAB III METODE PENELITIAN. 3.1 Diagram Alir Penelitian Pada penelitian ini langkah-langkah pengujian mengacu pada diagram alir pada Gambar 3.1.
BAB III METODE PENELITIAN 3.1 Diagram Alir Penelitian Pada penelitian ini langkah-langkah pengujian mengacu pada diagram alir pada Gambar 3.1. Mulai Mempersiapkan Alat dan Bahan Proses Peleburan Proses
BAB V DIAGRAM FASE ISTILAH-ISTILAH
BAB V DIAGRAM FASE ISTILAH-ISTILAH Komponen : adalah logam murni atau senyawa yang menyusun suatu logam paduan. Contoh : Cu - Zn (perunggu), komponennya adalah Cu dan Zn Solid solution (larutan padat)
Pengaruh Variasi Komposisi Kimia dan Kecepatan Kemiringan Cetakan Tilt Casting Terhadap Kerentanan Hot Tearing Paduan Al-Si-Cu
Pengaruh Variasi Komposisi Kimia dan Kecepatan Kemiringan Cetakan Tilt Casting Terhadap Kerentanan Hot Tearing Paduan Cu Bambang Tjiroso 1, Agus Dwi Iskandar 2 Jurusan Teknik Industri, Fakultas Teknik
Perilaku Mekanik Tembaga Fosfor C1220T-OL Pada Proses Annealing dan Normalizing
Perilaku Mekanik Tembaga Fosfor C1220T-OL Pada Proses Annealing dan Normalizing R. Henny Mulyani 1,a), Ade Angga Bastian 2) 1,2 Universitas Jenderal Achmad Yani Teknik Metalurgi Fakultas Teknik Jl. Jenderal
Studi Eksperimen Pengaruh Durasi Gesek, Tekanan Gesek Dan Tekanan Tempa Pengelasan Gesek (FW) Terhadap Kekuatan Tarik dan Impact Pada Baja Aisi 1045
Studi Eksperimen Pengaruh Durasi Gesek, Tekanan Gesek Dan Tekanan Tempa Pengelasan Gesek (FW) Terhadap Kekuatan Tarik dan Impact Pada Baja Aisi 1045 Hari Subiyanto 1,*, Subowo 1, Gathot DW 1, Syamsul Hadi
BAB I PENDAHULUAN. Teknik Material dan Metalurgi FTI-ITS
BAB I PENDAHULUAN I.1 Latar Belakang Baja (steel) adalah material yang paling banyak dan umum digunakan di dunia industri, hal ini karena baja memberikan keuntungan keuntungan yang banyak yaitu pembuatannya
Diagram Fasa. Latar Belakang Taufiqurrahman 1 LOGAM. Pemaduan logam
Diagram Fasa Latar Belakang Umumnya logam tidak berdiri sendiri (tidak dalam keadaan murni Kemurnian Sifat Pemaduan logam akan memperbaiki sifat logam, a.l.: kekuatan, keuletan, kekerasan, ketahanan korosi,
ANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIK ALUMINIUM REMELTING
ANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIK ALUMINIUM REMELTING PISTON BERPENGUAT SIO2 MENGGUNAKAN METODE STIR CASTING TERHADAP KEKERASAN DAN DENSITAS SKRIPSI Diajukan sebagai salah satu syarat
PENGARUH PERLAKUAN PANAS TERHADAP KEKERASAN DAN STRUKTUR MIKRO BAJA JIS S45C
PENGARUH PERLAKUAN PANAS TERHADAP KEKERASAN DAN STRUKTUR MIKRO BAJA JIS S45C Kusdi Priyono 1), Muhammad Farid 2), Djuhana 2) 1) PPRN-BATAN Kawasan Puspiptek, Tangerang Selatan, Banten, INDONESIA 2) Program
BAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3.1 Diagram Alir Penelitian Proses karakterisasi material Bantalan Luncur dengan menggunakan metode pengujian merusak. Proses penelitian ini dapat dilihat dari diagram alir berikut
BAB III PENGUMPULAN DAN PENGOLAHAN DATA PENELITIAN
36 BAB III PENGUMPULAN DAN PENGOLAHAN DATA PENELITIAN 3.1 Peralatan yang Digunakan Peralatan yang digunakan dalam penelitian dan pengujian ini antara lain: 1. Tabung Nitridasi Tabung nitridasi merupakan
PENGARUH NITROGEN TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PADUAN IMPLAN Co-28Cr-6Mo-0,4Fe-0,2Ni YANG MENGANDUNG KARBON HASIL PROSES HOT ROLLING
PENGARUH NITROGEN TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PADUAN IMPLAN Co-28Cr-6Mo-0,4Fe-0,2Ni YANG MENGANDUNG KARBON HASIL PROSES HOT ROLLING Kafi Kalam 1, Ika Kartika 2, Alfirano 3 [1,3] Teknik Metalurgi
TUGAS AKHIR ANALISIS PENGARUH PROSES ARTIFICIAL AGEING TERHADAP SIFAT MEKANIK PADA ALUMINIUM SERI AA 7075 ( S1 )
TUGAS AKHIR ANALISIS PENGARUH PROSES ARTIFICIAL AGEING TERHADAP SIFAT MEKANIK PADA ALUMINIUM SERI AA 7075 Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Sarjana Strata satu ( S1 ) Di Fakultas
ANALISA PENGARUH PENGECORAN ULANG TERHADAP SIFAT MEKANIK PADUAN ALUMUNIUM ADC 12
D.20. Analisa Pengaruh Pengecoran Ulang terhadap Sifat Mekanik... (Samsudi Raharjo) ANALISA PENGARUH PENGECORAN ULANG TERHADAP SIFAT MEKANIK PADUAN ALUMUNIUM ADC 12 Samsudi Raharjo, Fuad Abdillah dan Yugohindra
Pengaruh Temperatur dan Waktu Tahan Aging Presipitasi Hardening terhadap Struktur Mikro dan Sifat Mekanik Paduan Mg-6Zn-1Y
JURNAL TEKNIK POMITS Vol. 3, No. 2, (2014) ISSN: 2337-3539 (2301-9271 Print) F-232 Pengaruh Temperatur dan Waktu Tahan Aging Presipitasi Hardening terhadap Struktur Mikro dan Sifat Mekanik Paduan Mg-6Zn-1Y
ANALISA PENGARUH KONDUKTIVITAS TERMAL BACKING PLATE TERHADAP SIFAT FISIK DAN MEKANIK SAMBUNGAN FRICTION STIR SPOT WELDING AA 5052-H32
ANALISA PENGARUH KONDUKTIVITAS TERMAL BACKING PLATE TERHADAP SIFAT FISIK DAN MEKANIK SAMBUNGAN FRICTION STIR SPOT WELDING AA 5052-H32 SKRIPSI Diajukan Sebagai Salah Satu Syarat untuk Memperoleh Gelar Sarjana
DAFTAR ISI LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL...
DAFTAR ISI Halaman LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL... DAFTAR LAMPIRAN... i ii iii iv v vi ix xi xii BAB 1
TUGAS SARJANA. PROSES AGE HARDENING TERHADAP PERUBAHAN SIFAT MEKANIS DAN STRUKTUR MIKRO PADUAN Al-Cu
TUGAS SARJANA PROSES AGE HARDENING TERHADAP PERUBAHAN SIFAT MEKANIS DAN STRUKTUR MIKRO PADUAN Al-Cu Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Strata Satu (S-1) di Jurusan Teknik Mesin Fakultas
BAB III METODOLOGI PENELITIAN
3.1 DIAGRAM ALIR BAB III METODOLOGI PENELITIAN STUDI LITERATUR ALUMINIUM AC8H PROSES PELEBURAN PROSES GBF PENGUJIAN KOMPOSISI KIMIA PENAMBAHAN Sr (LADLE TREATMENT) PENAMBAHAN PHOSPOR (LADLE TREATMENT)
PENGARUH TEMPERATUR LAPISAN INTERMETALIK TERHADAP SIFAT FISIK MEKANIK PADA SAMBUNGAN DIFUSI LOGAM TAK SEJENIS ANTARA SS400 DENGAN AL6061 TESIS
PENGARUH TEMPERATUR LAPISAN INTERMETALIK TERHADAP SIFAT FISIK MEKANIK PADA SAMBUNGAN DIFUSI LOGAM TAK SEJENIS ANTARA SS400 DENGAN AL6061 TESIS Disusun untuk memenuhi sebagian persyaratan mencapai derajat
Journal of Mechanical Engineering Learning
JMEL 1 (1) (2012) Journal of Mechanical Engineering Learning http://journal.unnes.ac.id/sju/index.php/jmel PENGARUH PROSES ANNEALINGPADA SAMBUNGAN LAS SMAW TERHADAP STRUKTUR MIKRO DAN KEKERASAN BAJA S45C
BAB IV HASIL PENELITIAN DAN PEMBAHASAN
BAB IV HASIL PENELITIAN DAN PEMBAHASAN IV.1 FENOMENA FADING PADA KOMPOSISI PADUAN AC4B Pengujian komposisi dilakukan pada paduan AC4B tanpa penambahan Ti, dengan penambahan Ti di awal, dan dengan penambahan
ek SIPIL MESIN ARSITEKTUR ELEKTRO
ek SIPIL MESIN ARSITEKTUR ELEKTRO EFEK WAKTU PERLAKUAN PANAS TEMPER TERHADAP KEKUATAN TARIK DAN KETANGGUHAN IMPAK BAJA KOMERSIAL Bakri* dan Sri Chandrabakty * Abstract The purpose of this paper is to analyze
BAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN 3.1 Diagram Alir Penelitian Menyediakan Sampel Memotong blok / ingot Al Menyediakan Crusibel Menimbang blok Al, serbuk Mg, dan serbuk grafit Membuat Barrier dari campuran
Mohammad Bagus E. H. 1, Hari Arbiantara 2, Dedi Dwilaksana 2. Abstrak. Abstract. Pendahuluan
1 Pengaruh Variasi Fraksi Berat dan Panjang Serat Komposit Pelepah Kelapa dengan Matriks Polypropylene terhadap Kekuatan Tarik pada Proses Injection Moulding (The Effect of Weight Fraction Variations and
BAB IV HASIL DAN ANALISA. Gajah Mada, penulis mendapatkan hasil-hasil terukur dan terbaca dari penelitian
BAB IV HASIL DAN ANALISA 4.1 Hasil Pengujian Spesimen Dalam melakukan penelitian uji dilaboratorium bahan teknik Universitas Gajah Mada, penulis mendapatkan hasil-hasil terukur dan terbaca dari penelitian
KARAKTERISTIK SIFAT MEKANIS BAJA LATERIT TERHADAP PROSES PENGEROLAN
KARAKTERISTIK SIFAT MEKANIS BAJA LATERIT TERHADAP PROSES PENGEROLAN Roy Hasudungan, Erwin Siahaan, Rosehan dan Bintang Jurusan Teknik Mesin, Fakultas Teknik Universitas Tarumanagara, LIPI-Metalurgi e-mail:
PERBANDINGAN KUALITAS MATERIAL BEARING MERK SKF, FMB, NKK, DAN JAL TERHADAP TERHADAP SIFAT FISIS DAN MEKANIS
PERBANDINGAN KUALITAS MATERIAL BEARING MERK SKF, FMB, NKK, DAN JAL TERHADAP TERHADAP SIFAT FISIS DAN MEKANIS Masryukan, Ngafwan, dan Taufik Surya Nugroho Teknik Mesin Universitas Muhammadiyah Surakarta
UNIVERSITAS MUHAMMADIYAH SURAKARTA
TUGAS AKHIR SIFAT FISIS DAN MEKANIS BAJA KARBON RENDAH DENGAN PERLAKUAN CARBURIZING ARANG BAMBU Disusun Sebagai Syarat Untuk Mencapai Gelar Sarjana Teknik Jurusan Teknik Mesin Fakultas Teknik Universitas
STRUKTUR MIKRO DAN SIFAT MEKANIS ALUMINIUM (Al-Si) PADA PROSES PENGECORAN MENGGUNAKAN CETAKAN LOGAM, CETAKAN PASIR DAN CETAKAN CASTABLE
STRUKTUR MIKRO DAN SIFAT MEKANIS ALUMINIUM (Al-Si) PADA PROSES PENGECORAN MENGGUNAKAN CETAKAN LOGAM, CETAKAN PASIR DAN CETAKAN CASTABLE Martinus Mandala, Eddy S. Siradj dan Sofyan Djamil Program Studi
JURNAL SAINS DAN SENI POMITS Vol. 1, No. 1, (2012) 1-5 1
JURNAL SAINS DAN SENI POMITS Vol. 1, No. 1, (2012) 1-5 1 Studi Eksperimental Perbandingan Pengaruh Variasi Solution Treatment pada Perlakuan Panas Precipitation Hardening T6 terhadap Sifat Mekanik Paduan
Kata Kunci : Daerah lasan, Las oksi asetilin, Besi tuang kelabu, Fisis, Mekanis, Bahan tambah, HAZ, Kekuatan tarik, Kekerasan.
Analisis Sambungan Lasan Logam Besi Tuang Kelabu Dengan Menggunakan Las Oksi Asetilin Oleh : Tiwan, MT. Dosen Prodi Teknik Mesin FT UNY Penelitian ini menitikberatkan pada pengkajian hasil lasan logam
BAB IV HASIL DAN PEMBAHASAN. Foto Mikro dan Morfologi Hasil Pengelasan Difusi
BAB IV HASIL DAN PEMBAHASAN Penelitian sambungan logam tak sejenis antara Baja SS400 dan Aluminium AA5083 menggunakan proses pengelasan difusi ini dilakukan untuk mempelajari pengaruh ketebalan lapisan
KATA PENGANTAR. Sidoarjo, Desember Fakultas. Universitas Muhammadiyah Sidoarjo 1
KATA PENGANTAR Puji beserta syukur panjatkan kehadirat Tuhan yang Maha Esa. Karena berkat rahmat, hidayahnya, telah mampu menyelesaiakan sebuah makalah tentang pengaruh pengelsan FCAW tanpa dan dengan
PENGARUH PERLAKUAN TEMPERING TERHADAP KEKERASAN DAN KEKUATAN IMPAK BAJA JIS G 4051 S15C SEBAGAI BAHAN KONSTRUKSI. Purnomo *)
PENGARUH PERLAKUAN TEMPERING TERHADAP KEKERASAN DAN KEKUATAN IMPAK BAJA JIS G 4051 S15C SEBAGAI BAHAN KONSTRUKSI Purnomo *) Abstrak Baja karbon rendah JIS G 4051 S 15 C banyak digunakan untuk bagian-bagian
PENGARUH PERLAKUAN PANAS T6 TERHADAP SIFAT FISIS DAN MEKANIS MATERIAL MODEL PROPELLER SHAFT BERBAHAN DASAR ALUMINIUM SERI 6063 HASIL PENGECORAN HPDC
PENGARUH PERLAKUAN PANAS T6 TERHADAP SIFAT FISIS DAN MEKANIS MATERIAL MODEL PROPELLER SHAFT BERBAHAN DASAR ALUMINIUM SERI 6063 HASIL PENGECORAN HPDC *Farid Abdul Rahman 1, Athanasius Priharyoto Bayuseno