1 VOLUME 26 NOMOR 1, APRIL 2011 ISSN AKREDITASI : SK 187/AU1/P2MBI/08/2009 Penanggung Jawab: Kapuslit Metalurgi LIPI Dewan Redaksi : Ketua Merangkap Anggota: Ir. Ronald Nasoetion, MT Anggota: Dr. Ir. Rudi Subagja Dr. Ir. F. Firdiyono Dr. Agung Imadudin Dr. Ika Kartika, MT Ir. Yusuf Ir. Adil Jamali, M.Sc (UPT BPM LIPI) Prof. Riset. Dr. Ir. Pramusanto (Puslitbang TEKMIRA) Prof. Dr. Ir. Johny Wahyuadi, DEA (UI) Dr. Ir. Sunara, M.Sc (ITB) Sekretariat Redaksi: Pius Sebleku, ST Tri Arini, ST Arif Nurhakim, S.Sos Penerbit: Pusat Penelitian Metalurgi LIPI Kawasan PUSPIPTEK, Serpong, Gedung 470 Telp: (021) , Fax: (021) Alamat Sekretariat: Pusat Penelitian Metalurgi LIPI Kawasan PUSPIPTEK, Serpong, Gedung 470 Telp: (021) , Fax: (021) metalurgi_magz@yahoo.com Majalah ilmu dan teknologi terbit berkala setiap tahun, satu volume terdiri atas 3 nomor. Pengantar Redaksi. iii Abstrak.. v Metoda FZ pada Pembuatan Kristal Tunggal La2-2xSr1+2xMn2O7 Agung Imaduddin. 1 Kendala dan Kemungkinan Pengembangan Proses Caron untuk Bijih Nikel Laterit Kadar Rendah Indonesia Arifin Arif dan Edi Herianto... 7 Konsentrasi Pasir Besi Titan dari Pengotornya dengan Cara Magnetik Deddy Sufiandi.. 5 Pengaruh Penambahan Serat Polyvinyl Alcohol dan Superplastisizer Polycarboxylate Ethers terhadap Sifat Mekanik Material ECC Harsisto, dkk Percobaan Peningkatan Kadar Mangan Menggunakan Magnetic Separator Immanuel Ginting dan Deddy Sufiandi 27 Masih Terbukanya Peluang Penelitian Proses Caron untuk Mengolah Laterit Kadar Rendah di Indonesia Puguh Prasetiyo dan Ronald Nasoetion Adsorpsi Nikel dan Kobalt pada Resin Penukar Ion Lewatit Monoplus TP 207 XL dalam Beberapa Larutan Sulfat Frideni G.F Indeks
2 ii Majalah Metalurgi, V , ISSN
3 PENGANTAR REDAKSI Syukur Alhamdulillah Majalah Metalurgi Volume 26 Nomor 1, April 2011 kali ini menampilkan 6 buah tulisan. Tulisan pertama hasil penelitian disampaikan oleh Agung Imaduddin berjudul Metoda FZ pada Pembuatan Kristal Tunggal La2-2xSr1+2xMn2O7. Selanjutnya Arifin Arif dan Edi Herianto tentang Kendala dan Kemungkinan Pengembangan Proses Caron untuk Bijih Nikel Laterit Kadar Rendah Indonesia. Harsisto dan Kawan-Kawan juga menulis tentang Pengaruh Penambahan Serat Polyvinyl Alcohol dan Superplastisizer Polycarboxylate Ethers Terhadap Sifat Mekanik Material ECC. Immanuel Ginting dan Dedy Sufiandi menulis tentang Percobaan Peningkatan Kadar Mangan Menggunakan Magnetik Separator. Berikutnya Puguh P dan Ronald Nasoetion MT menulis tentang Masih Terbuka Peluang Penelitian Proses Caron untuk Mengolah Laterit Kadar Rendah di Indonesia. Pada bagian berikutnya ada 1 buah makalah terbaik pada Seminar Metalurgi 2009 yaitu Adsorpsi Nikel Dan Kobalt pada Resin Penukar Ion Lewatit Monoplus TP 207 XL dalam Beberapa Larutan Sulfat yang disampaikan oleh Frideni GF dan Kawan-Kawan. Semoga penerbitan Majalah Metalurgi volume ini dapat bermanfaat bagi perkembangan dunia penelitian di Indonesia. REDAKSI Pengantar Redaksi iii
4 iv Majalah Metalurgi, V , ISSN
5 METALURGI (Metallurgy) ISSN Vol 26 No. 1 April 2011 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya. UDC (OXDCF) 548 Agung Imaduddin (Pusat Penelitian Metalurgi LIPI) Metoda FZ pada Pembuatan Kristal Tunggal La 2-2x Sr 1+2x Mn 2 O Metalurgi, Volume 26 No.1 April 2011 La 2-2x Sr 1+2x Mn 2 O 7 (x=0,4) mempunyai CMR (Colossal Magnetoresistance) terbesar dibandingkan bahan Mn oxide lainnya [1]. Untuk menyelidiki sifat CMR ini, kita harus dapat membuat kristal tunggalnya. Untuk itu kami telah membuat kristal tunggal La 2-2x Sr 1+2x Mn 2 O 7 (x=0,4) atau disebut LSMO 327. Kristal tunggal kami buat dengan metoda FZ (Floating Zone). Sebelum pembuatan kristal tunggal dengan memakai metoda FZ, kami telah menganalisa hubungan suhu dan konsentrasi x dengan memakai thermocouple dan analisa EPMA (Electron Probe Microanalysis). Setelah penumbuhan dengan memakai metoda FZ, analisa struktur kristal dan sifat kristalisasinya pada hasil kristal tunggalnya dilakukan dengan memakai XRD dan rocking curve, kemudian kami juga memakai EPMA untuk mengetahui komposisi unsur yang terbentuk. Dari hasil metoda FZ ini diketahui bahwa permukaan cleave (permukaan kelupas) nya adalah bidang ab, dan memiliki nilai half full value width nya 0,115, yang menunjukkan kualitas kristal tunggal yang tinggi. Dari EPMA diketahui bahwa nilai x pada La 2-2x Sr 1+2x Mn 2 O 7 adalah 0,409. Kata kunci : CMR, Kristal tunggal, LSMO 327, Metoda floating zone 7 La 2-2x Sr 1+2x Mn 2 O 7 (x=0.4) has the most large CMR (Colossal Magnetoresistance) [1]. In order to research on CMR effect, we have to prepare high quality single crystals. We have grown La 2-2x Sr 1+2x Mn 2 O 7 single crystal of x = 0.4 (or LSMO 327). We have grown single crystals with FZ (Floating Zone) method. Before growing single crystals using the FZ method, we have analyzed the relation of temperature and concentration x by using thermo-couple and analysis of EPMA (Electron Probe Microanalysis). After growing using the FZ method, analysis of crystal structure and its crystallization properties were carried out using XRD and Rocking curve, then we were also using EPMA to determine its elemental composition. From the results of the FZ method, we know that the cleaved surface is the ab plane, and has a half full value width of 0.115, which indicates a high quality single crystal. From the EPMA result, we know that the value of x at the LA 2-2x Sr 1 +2 x Mn 2 O 7 is Keywords : CMR, Single crystal, LSMO, Floating zone method Abstrak v
6 METALURGI (Metallurgy) ISSN Vol 26 No. 1 April 2011 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya. UDC (OXDCF) Arifin Arif dan Edi Herianto (Pusat Penelitian Metalurgi LIPI) Kendala dan Kemungkinan Pengembangan Proses Caron untuk Bijih Nikel Laterit Kadar Rendah Indonesia Metalurgi, Volume 26 No.1 April 2011 Bagian terbesar dari bijih nikel laterit Indonesia yang cadangannya lebih dari 1 milyar ton termasuk pada klasifikasi bijih berkadar rendah. Komposisi bijih kadar rendah tersebut sangat bervariasi, dari bijih saprolit yang tinggi kandungan oksida magnesium dan silikatnya serta bijih limonit yang tinggi kandungan oksida besi dan aluminiumnya. Selain itu bijih limonit juga berpotensi mengandung silikat yang cukup tinggi. Oleh karena itu selalu ada kemungkinan dari suatu cebakan bijih, kandungan total magnesium dengan aluminium dan atau silikat dari bijih campuran tersebut masih melampaui dari batas kritis olahan proses HPAL. Oleh karena itu pengolahan optimal tidak dapat diharapkan hanya dari proses HPAL. Seperti diketahui walaupun kinerjanya tinggi tetapi proses HPAL cocok hanya untuk bijih yang kandungan magnesium dan atau silikatnya rendah seperti limonit murni. Untuk itu perlu disiapkan alternatif berupa proses yang komposisi bijih umpannya dapat lebih fleksibel. Kalau pilihannya adalah proses Caron tampaknya masih diperlukan langkah pendekatan terhadap beberapa kendala yang harus dihadapi oleh proses tersebut bila akan dikembangkan kedepan. Kata kunci : Bijih nikel, Laterit, Saprolit, Limonit, Proses HPAL, Proses Caron The largest portion of more than 1 billion ton Indonesian nickel laterite ore deposits can be classified as low grade. It is informed that the compositions of the ores varies in wide range, with high magnesium oxide and silicates contents for saprolite and high iron and aluminium oxides for limonite. The limonit ores are also potential in containing high enough silicate. Due to it always possible that the total magnesium and aluminium and or silicates contents of the mixed ores deposits are higher than the ore feed compositions critical limits of HPAL, so it is predicted that the optimal treatment would not be achieved if based only on HPAL process. As have been known even HPAL is high in performance but just only suitable for certain ores with low magnesium and low silicates contents such likes pure limonite. For that it requires to provide alternative processes which are more flexible toward ore feed compositions. If the selected process is Caron, still it needs some steps of problems approach that have to be faced for the future process development. Keywords : Nickel ore, Laterite, Saprolite, Limonite, HPAL process, Caron process vi Majalah Metalurgi, V , ISSN
7 METALURGI (Metallurgy) ISSN Vol 26 No. 1 April 2011 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya. UDC (OXDCF) Deddy Sufiandi (Pusat Penelitian Metalurgi LIPI) Konsentrasi Pasir Besi Titan dari Pengotornya dengan Cara Magnetik Metalurgi, Volume 26 No.1 April 2011 Pasir besi titan Indonesia cadangannya cukup besar terutama di daerah sekitar pantai Selatan Jawa. Salah satu potensi pasir besi titan yang akan di teliti adalah pasir besi dari daerah Tegal Buleud Pantai Selatan Sukabumi. Pemanfaatan pasir besi titan merupakan alternatif yang diperlukan untuk memenuhi kebutuhan bahan baku industri baja yang dalam perkembangan dan kebutuhannya semakin meningkat dengan terbatasnya cadangan bijih besi konvensional. Tujuan penelitian untuk mendapatkan kualitas pasir besi titan yang memenuhi persyaratan peleburan, perlu dilakukan konsentrasi untuk meningkatkan kadar besi dengan cara magnetik. Metode percobaan adalah melakukan identifikasi pasir besi titan dengan mengunakan analisa XRD. Kemudian dilakukan proses preparasi sampel dan pengayakan sebelum dimasukan kedalam peralatan pemisah magnetik dan dari pemisah magnet akan dihasilkan produk konsentrat, middling, dan tailing. Hasil percobaan menunjukkan produk konsentrat pasir besi titan mempunyai kandungan Fe % dan TiO 2 20 %. Dan pemisahan pasir besi titan dengan kondisi optimum diperoleh pada kondisi arus 3,5 ampere dan fraksi mesh dengan perolehan konsentrat rata-rata 90 %. Kata kunci : Pasir besi titan, Magnetic separator, Tegal Buleud - Sukabumi Selatan, Industri baja Titan iron sand has been found a lot in Indonesia especially around west coast of Java. One of titan iron sand used in this research is iron sand from Tegal Buleud area at Sukabumi west coast. The utilization of iron sand is an alternative to fill-up the rising demand of raw material for steel industry development due to limited amount of conventional iron ore. To obtain the quality of titan iron sand which is suitable with the requirement for smelting, it is needed to have concentration process by magnetic separator to increase iron content. The step of experiment were identification of titan iron sand composition, preparation of sample and sampling processes, and material separation using magnetic separator to get concentrate, middling, and tailing products. The result of experiment shown concentrate product of titan iron sand has Fe 2 O 3 and TiO2 with weight composition 80 % and 20 % respectively. And also The optimum condition in magnetic separator was 3.5 Ampere current and fraction -100 mesh got average concentrate yield about 90 %. Keywords : Titans iron sand, Magnetic separator, Tegal Buleud- South Sukabumi, Steel industry Abstrak vii
8 METALURGI (Metallurgy) ISSN Vol 26 No. 1 April 2011 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya. UDC (OXDCF) 620 Harsisto, Hartati, Yulinda Lestari, Ari Yustisia Akbar (Pusat Penelitian Metalurgi - LIPI) Pengaruh Penambahan Serat Polyvinil Alcohol dan Superplastisizer Polycarboxylate Ethers terhadap Sifat Mekanik Material ECC Metalurgi, Volume 26 No.1 April 2011 Penelitian ini dilakukan untuk mempelajari pengaruh penambahan serat PVA dan superplastisizer tipe polycarboxylate ethers (tipe P) terhadap sifat mekanik material ECC. Tujuan dari penggunaan PVA adalah untuk meningkatkan kekuatan beton sehingga apabila dikenai beban, tipe retakan yang terjadi adalah retak rambut (microcrack). Superplasticizer ditambahkan untuk meningkatkan kelecakan (workability) ECC sehingga mudah dipadatkan dan didapatkan mutu yang lebih baik. Pengujian material ECC dilakukan dengan mengukur kuat tekan dan kuat lentur menggunakan universal testing machine. Dari variasi komposisi sampel ECC yang dilakukan, komposisi paling efektif terdapat pada perbandingan semen : air : pasir : fly ash : SP : PVA = 1 : 0,68 : 0,94 : 1,6 : 0,01 : 0,02 dengan kuat tekan 196 kg/cm 2 dan kuat lentur 145,3 kgf. Kata kunci : Self healing concrete, Engineered cement composite, Polyvinyl alcohol, Superplastisizer, Fly ash This research was conducted to study the effect of PVA fiber and polycarboxylate ethers typed superplastisizer (type P) to the mechanical properties of ECC materials. The purpose of the use of PVA is to increase the strength of the concrete so that when subjected to load, type of fracture is microcrack. Superplasticizer was added to enhance ECC workability so it was easily compressed and get better quality. ECC material testing was conducted by measuring the compressive and flexural strength using a universal testing machine. The most effective composition of ECC material on the ratio of cement: water: sand: fly ash: SP: PVA = 1 : 0.68 : 0.94 : 1.6 : 0.01 : 0.02 has compressive and flexural strength of 196 kg/cm 2 and kgf respectively. Keywords : Self healing concrete, Engineered cement composite, Polyvinyl alcohol, Superplastisizer, Fly ash viii Majalah Metalurgi, V , ISSN
9 METALURGI (Metallurgy) ISSN Vol 26 No. 1 April 2011 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya. UDC (OXDCF) Imanuel Ginting dan Deddy Sufiandi (Pusat Penelitian Metalurgi LIPI) Percobaan Peningkatan Kadar Mangan Menggunakan Magnetic Separator Metalurgi, Volume 25 No.2 Agustus 2010 Percobaan pemisahan besi dari mangan dengan magnetik seperator telah dilakukan terhadap bijih mangan dari daerah Trenggalek Jawa Timur dengan variabel percobaan yaitu rapat arus 2,5 ampere dengan tegangan atau voltage yang disesuaikan dengan kondisi alat. Umpan percobaan yang digunakan dalam pemisahan ini adalah bijih mangan yang telah melalui proses roasting sebelumnya. Kondisi optimal proses pemisahan diperoleh pada kuat arus 2,5 ampere dengan kandungan 50,99 % Mn dan kandungan besi 0,27 %. Kata kunci : Mangan, Pemanggangan, Magnetik separator, Produk The separation tests of roasted manganese ore by magnetic separator have been carried out. The test variables were the current densities such like 2,5 ampere and the voltage which suitable to the tool condition. The optimal condition of % content of Mn and 0.27 % Fe content achieved is current density 2.5 ampere. Keywords : Mangan, Roasting, Magnetic separator, Product Abstrak ix
10 METALURGI (Metallurgy) ISSN Vol 26 No. 1 April 2011 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya. UDC (OXDCF) Puguh Prasetiyo dan Ronald NNasoetion (Pusat Penelitian Metalurgi - LIPI) Masih Terbuka Peluang Penelitian Proses Caron untuk Mengolah Laterit Kadar Rendah di Indonesia Metalurgi, Volume 26 No.1 April 2011 Indonesia memiliki cadangan nikel pada peringkat dua dunia. Cadangan tersebut berupa bijih nikel oksida yang lazim disebut laterit, berada di Kawasan Timur Indonesia (KTI) terutama di Sulawesi Tenggara dan Halmahera. Adapun laterit terdiri dari limonit berkadar Ni<1,5 % dan saprolit berkadar Ni > 1,5 %. Laterit kadar tinggi saprolit berkadar Ni > 1,8 % sudah diolah di Sulawesi Tenggara dengan jalur pyrometalurgi oleh PT Antam (Aneka Tambang) untuk memproduksi FeNi (ferro nikel) di Pomalaa, dan PT INCO Canada untuk memproduksi nikel mattte (Ni-matte) di Soroako. Laterit kadar rendah yang terdiri dari limonit dan saprolit dengan kandungan Ni < 1,8 %, belum diolah di dalam negeri. Secara komersial untuk mengolah laterit kadar rendah digunakan proses Caron yang pertama kali dibangun di Nicaro Cuba oleh Freeport USA pada tahun Atau proses HPAL (High Pressure Acid Leaching) juga pertama kali dibangun di Moa Bay Cuba oleh Freeport USA pada tahun Kedua proses tersebut tergolong dalam jalur hydrometalurgi, dan pemilihan proses tergantung dari kondisi bijih terutama pada kandungan Mg (magnesium). Laterit kadar rendah dengan kandungan Mg (magnesium) rendah (Mg < 6 % atau MgO < 10 %) lebih sesuai untuk diolah dengan proses HPAL, dan magnesium tinggi (Mg > 6 % atau MgO > 10 %) diolah dengan proses Caron. Dalam perkembangannya setelah tahun 1990-an, proses Caron mulai ditinggalkan karena mengkonsumsi energi tinggi dengan perolehan yang rendah untuk nikel (Ni : %) maupun kobal (Co maks 50 %). Selanjutnya beralih ke proses HPAL karena proses ini mengkonsumsi energi rendah dengan perolehan tinggi untuk nikel (Ni > 90 %) maupun kobal (Co > 90 %). Dengan melihat kenyataan kegagalan tiga HPAL plant generasi kedua di Australia (Bulong tutup 2003, Cawse tutup 2008, dan Murrin Murrin berpindah kepemilikan ke Minara pada 2003/2004 dan beralih ke heap leach tahun 2007). Serta masih berlangsungnya Caron plant di Cuba (Nicaro dan Punta Gorda), Queensland Nickel di Yabulu Australia, dan Tocantin Brasilia. Maka proses Caron masih punya peluang untuk mengolah laterit kadar rendah di Indonesia. Peluang tersebut semakin terbuka apabila perolehan metal (recovery Ni dan Co) pada proses Caron bisa ditingkatkan setara dengan perolehan metal (recovery Ni dan Co) pada proses HPAL, dan ekonomis konsumsi energinya. Kata kunci : Laterit kadar rendah, Limonit, Saprolit, Hidrometalurgi, Proses Caron, Proses HPAL, Magnesium (Mg) Indonesia had the resources of nickel at the second in the world. The resources are nickel oxide which said laterite. The abundant of laterite locate at Sulawesi Tenggara (South-East Sulawesi) and Halmahera. There are two main mineral in laterite, limonit contains Ni<1,5% and saprolit contains Ni>1,5%. The high grade nickel saprolit contains Ni>1,8% has been processed in Sulawesi Tenggara to produce FeNi (ferro nickel) in Pomalaa by PT Antam, and to produce Ni-matte (nickel matte) in Sorowako by PT INCO Canada. The low grade laterite (limonit and saprolit contains Ni<1,8%) not yet processed in Indonesia. To process the low grade laterite are used Caron s process or HPAL s process (High Pressure Acid Leaching). The condition of laterite s ores are used to choice the process. The Caron s process is remained after 1990 s because it consume high energy with low metal recovery (Ni : % Co max 50 %). The choice to process low gradelaterite is HPAL because it consume low energy wiyh high recovery of metal (Ni > 90 % and Co > 90 %). The fact three HPAL plant in Australia unsuccessful (Bulong closed on 2003, Cawse closed on 2008, and Murrin Murrin taked over by Minara and change to heap leach on 2007) and the Caron plant still exist in Cuba (Nicaro and Punta Gorda), Queensland Nickel di Australia, and Tocantin Brasilia. Then Caron s process still have opportunity to process the low grade laterite in Indonesia if the recovery of metal can be increase as same as HPAL and the consume of energy can be decreased. Keywords : Low grade of laterite, Ilmonite, Saprolite, Hydrometallurgy, Caron process, HPAL process, Magnesium (Mg) x Majalah Metalurgi, V , ISSN
11 METALURGI (Metallurgy) ISSN Vol 26 No. 1 April 2011 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya. UDC (OXDCF) Frideni G. F, A. Wisma, M.Z. Mubarok, S. Purwadaria (Program Studi Sarjana Teknik Metalurgi, FTTM-ITB) Adsorpsi Nikel dan Kobal pada Resin Penukar Ion Lewatit Monoplus TP 207 XL dalam Beberapa Larutan Sulfat Metalurgi, Volume 26 No.1 April 2011 Resin penukar ion Lewatit Monoplus TP 207 XL adalah salah satu resin untuk memisahkan logam dari larutan hasil pelindian bijih nikel laterit. Resin ini tahan terhadap abrasi, dapat digunakan pada suhu diatas suhu kamar, memiliki kelarutan yang rendah dalam larutan hasil leaching sehingga dapat digunakan berulang-ulang. Tulisan ini membahas kinetika proses adsorpsi nikel dan kobalt pada resin penukar ion Lewatit Monoplus TP 207 XL dalam beberapa larutan nikel dan kobalt sintetik dengan ph 3, 4, dan 5 pada suhu kamar, 40 C, dan 50 C. Hasil dari percobaan menunjukkan bahwa dalam larutan nikel sulfat dan kobalt sulfat sintetik ph 5, persen adsorpsi nikel dan kobalt masing-masing dapat mencapai 92,19% dan 97,12% bila adsorpsinya dilakukan pada suhu 50 C. Berdasarkan studi kinetika yang telah dilakukan, laju adsorpsi pada resin saat awal proses ( 2 j am) cenderung terkendali oleh laju difusi ion-ion melalui lapis difusi dalam fluida. Hasil percobaan menunjukkan ph dan suhu larutan berpengaruh pada persen adsorpsi nikel dan kobalt dan resin lebih sesuai untuk adsorpsi logam-logam ini secara bersamaan, karena tidak cukup selektif untuk memisahkan keduanya. Kemungkinan penggunaan resin ini untuk mengadsorpsi nikel dan kobalt dari beberapa larutan hasil pelindian nikel laterit kadar rendah yang telah dikurangi kandungan ion besinya juga disajikan dalam tulisan ini. Kata kunci : Resin, Lewatit Monoplus TP 207 XL, Laterit, Pelindian, Difusi Lewatit Monoplus TP 207 XL ion exchange resin has a function to separate metal from nickel ore laterite in leaching solution. This resin has good wear ability and low solubility inside of solution after leaching process, therefore can be used at elevated temperature frequently. This study concern on kinetic of nickel and cobalt absorption of Lewatit Monoplus TP 207 XL ion exchange resin in nickel solution and synthetic cobalt, with potential hydrogen various around 3,4 and 5 at room temperature of 40 C and 50 C. Result shows that nickel and cobalt adsorption percentage can be obtained approximately around 92.19% and 97.12%, respectively, in nickel sulfide solution and 5 potential hydrogen of synthetic cobalt at temperature 50 C. Based on kinetic study which has been done, absorption rate of resin at the first process ( 2 h) effected by ions diffusion rate through diffusion layer in the fluid. Result shows that potential hydrogen and solution temperature affect in nickel and cobalt absorption percentages, and also resin more appropriate to absorb these metals simultaneously, due to difficulty to separate of them. This study also shows possibility to using this resin for absorption nickel and cobalt in various solutions which is obtained from low nickel laterite with low ferrous ions after leaching process. Keywords : Resin, Lewatit Monoplus TP 207 XL, Laterit, Leaching, Diffusion Abstrak xi
12 xii Majalah Metalurgi, V , ISSN
13 ADSORPSI NIKEL DAN KOBALT PADA RESIN PENUKAR ION LEWATIT MONOPLUS TP 207 XL DALAM BEBERAPA LARUTAN SULFAT Frideni G.F, G. A Wisma, M.Z. Mubarok, dan S. Purwadaria Program Studi Sarjana Teknik Metalurgi, FTTM-ITB, Jl. Ganesa 10 Bandung, frideni_gf@yahoo.com / sunara_p@yahoo.com Intisari Resin penukar ion Lewatit Monoplus TP 207 XL adalah salah satu resin untuk memisahkan logam dari larutan hasil pelindian bijih nikel laterit. Resin ini tahan terhadap abrasi, dapat digunakan pada suhu diatas suhu kamar, memiliki kelarutan yang rendah dalam larutan hasil leaching sehingga dapat digunakan berulang-ulang. Tulisan ini membahas kinetika proses adsorpsi nikel dan kobalt pada resin penukar ion Lewatit Monoplus TP 207 XL dalam beberapa larutan nikel dan kobalt sintetik dengan ph 3, 4, dan 5 pada suhu kamar, 40 C, dan 50 C. Hasil dari percobaan menunjukkan bahwa dalam larutan nikel sulfat dan kobalt sulfat sintetik ph 5, persen adsorpsi nikel dan kobalt masing-masing dapat mencapai 92,19% dan 97,12% bila adsorpsinya dilakukan pada suhu 50 C. Berdasarkan studi kinetika yang telah dilakukan, laju adsorpsi pada resin saat awal proses ( 2 jam) cenderung terkendali oleh laju difusi ion-ion melalui lapis difusi dalam fluida. Hasil percobaan menunjukkan ph dan suhu larutan berpengaruh pada persen adsorpsi nikel dan kobalt dan resin lebih sesuai untuk adsorpsi logam-logam ini secara bersamaan, karena tidak cukup selektif untuk memisahkan keduanya. Kemungkinan penggunaan resin ini untuk mengadsorpsi nikel dan kobalt dari beberapa larutan hasil pelindian nikel laterit kadar rendah yang telah dikurangi kandungan ion besinya juga disajikan dalam tulisan ini. Kata kunci : Resin, Lewatit Monoplus TP 207 XL, Laterit, Pelindian, Difusi Abstract Lewatit Monoplus TP 207 XL ion exchange resin has a function to separate metal from nickel ore laterite in leaching solution. This resin has good wear ability and low solubility inside of solution after leaching process, therefore can be used at elevated temperature frequently. This study concern on kinetic of nickel and cobalt absorption of Lewatit Monoplus TP 207 XL ion exchange resin in nickel solution and synthetic cobalt, with potential hydrogen various around 3,4 and 5 at room temperature of 40 C and 50 C. Result shows that nickel and cobalt adsorption percentage can be obtained approximately around 92.19% and 97.12%, respectively, in nickel sulfide solution and 5 potential hydrogen of synthetic cobalt at temperature 50 C. Based on kinetic study which has been done, absorption rate of resin at the first process ( 2 h) effected by ions diffusion rate through diffusion layer in the fluid. Result shows that potential hydrogen and solution temperature affect in nickel and cobalt absorption percentages, and also resin more appropriate to absorb these metals simultaneously, due to difficulty to separate of them. This study also shows possibility to using this resin for absorption nickel and cobalt in various solutions which is obtained from low nickel laterite with low ferrous ions after leaching process. Keywords : Resin, Lewatit Monoplus TP 207 XL, Laterit, Leaching, Diffusion PENDAHULUAN Mengikuti Hellferich [1-2], proses adsorpsi nikel pada resin penukar ion Lewatit Monoplus TP 207 XL secara hipotetik diawali dengan perpindahan massa ion-ion nikel dari ruah latutan kepermukaan resin, adsorpsi nikel pada permukaan resin dan dilanjutkan dengan difusi nikel kebagian dalam resin. Proses adsorpsi ini ditunjukkan secara skematik seperti; Resin Permukaan Larutan kr K ks [Ni] r [Ni] l (1)
14 dengan l menyatakan larutan, r menyatakan resin, s menyatakan permukaan butiran resin, k s adalah koefisien perpindahan massa dalam larutan, k r adalah koefisien perpindahan massa dalam resin, dan K adalah konstanta kesetimbangan reaksi adsorpsi. Setelah kesetimbangan tercapai antara nikel yang teradsorpsi pada resin dengan nikel dalam larutan dimuka resin, akan diperoleh hubungan : = K (2) Laju pemuatan nikel pada resin sebelum kesetimbangan tercapai dapat dinyatakan oleh laju perpindahan massa nikel dari ruah larutan ke permukaan resin ; = (3) dan laju perpindahan massa nikel pada resin yang dapat dinyatakan dengan persamaan, Untuk mempelajari kinetika adsorpsi = (4) nikel dan/atau kobalt pada (4) resin penukar dengan A adalah luas antarmuka resinlarutan. larutan nikel dan/atau kobalt sulfat, ion Lewatit Monoplus TP 207 XL dari Apabila laju pemuatan resin terkendali dilakukan serangkaian percobaan adsorpsi oleh laju perpindahan massa ion-ion Ni dibawah tekanan atmosfer pada suhu dari ruah larutan kepermukaan resin, maka kamar, 40 C, dan 50 C, dengan pada keadaan tunak laju perpindahan massa dalam resin [ ] akan sama dengan laju perpindahan massa dalam larutan [ - ] Kondisi ini biasanya terjadi dalam larutan dengan konsentrasi nikel yang rendah. Dengan menyelesaikan kedua persamaan tersebut (Persamaan 3 = Persamaan 4) dan dengan mensubstitusikannya ke Persamaan (2), akan diperoleh relasi ; = (5) Subtitusi persamaan ini ke dalam Persamaan (4) memberikan, = k (K - ) (6) dengan k =k s k r A/(k s K+k s ) Bila konsentrasi nikel dalam larutan pada permukaan resin konstan, integrasi Persamaan 6 menghasilkan, ln = k t (7) Dengan memperhatikan bahwa pada keadaan kesetimbangan berlaku = dan adalah pemuatan nikel resin pada t = 0 yang nilainya = 0, persamaan diatas dapat disederhanakan menjadi, ln = k t (8) Persamaan ini menyatakan bahwa hubungan ln dengan t linier. PROSEDUR PERCOBAAN menggunakan larutan-larutan artifisial yang ph-nya 3, 4 dan 5. Keseluruhan percobaan dilakukan dengan menggunakan resin 4x atau 1x dari perkiraan kebutuhan teoritik. Percobaan adsorpsi nikel dan kobal juga dilakukan dengan menggunakan larutan hasil pelindian bijih nikel laterit yang ion besinya telah dikurangi. Pelindian dilakukan dalam larutan asam sulfat 1 M pada tekanan atmosfer dan percobaan adsorpsi ion-ion nikel dan kobalt dilakukan dalam larutan hasil pelindian pada temperatur 50 C dan 60 C, dengan menggunakan resin 4x teoritik. Nikel dan kobalt yang masih tertinggal dalam larutan, dianalisis dengan menggunakan flame AAS (Atomic Absorption Spectrophotometer) Shimadzu seri AA Majalah Metalurgi, V , ISSN / hal 45-52
15 HASIL DAN PEMBAHASAN Kinetika Adsorpsi Nikel pada Resin Penukar Ion Lewatit TP 207 XL dalam Larutan Sulfat Artifisial Dari data hasil pengujian adsorpsi nikel dalam larutan nikel sulfat dengan konsentrasi awal kurang lebih 280 ppm Ni, dialurkan hubungan antara % adsorpsi nikel dengan waktu sebagaimana disajikan pada Gambar-gambar 1, 2 dan 3 berturutturut dari hasil percobaan pada ph 3, ph 4 dan ph 5. Untuk perhitungan kinetika perlu diprediksi kondisi kesetimbangan (keadaan terminal proses adsorpsi), yaitu saat tidak lagi terjadi perubahan konsentrasi ion logam dalam resin. Oleh karena percobaan dilakukan selama 4 jam, kondisi kesetimbangan diasumsikan sebagai konsentrasi ion logam tertinggi dalam resin selama 4 jam pengamatan. Sedangkan data yang digunakan untuk perhitungan kinetika adalah data adsorpsi resin selama 2 jam, karena adsorpsi sudah tidak signifikan lagi setelah 2 jam proses adsorpsi. Gambar 2. Persen adsorpsi Ni sebagai fungsi waktu dalam larutan nikel sulfat ph 4 pada suhu kamar, 40 C, dan 50 C Gambar 3. Persen adsorpsi Ni sebagai fungsi waktu dalam larutan nikel sulfat ph 5 pada suhu kamar, 40 C, dan 50 C Hubungan ln dengan t untuk hasil-hasil percobaan di atas ditunjukkan pada Gambar 4, 5 dan 6. Keseluruhannya menunjukkan hubungan yang linier dengan koefisien korelasi (R) mendekati 1. Energi aktivasi proses (Tabel 1) < 4,46 kkal/mol menekankan bahwa proses terkendali oleh difusi melalui lapis difusi dalam fluida [3]. Tabel 1. Energi aktifasi proses adsorpsi nikel Gambar 1. Persen adsorpsi Ni sebagai fungsi waktu dalam larutan nikel sulfat ph 3 pada suhu kamar, 40 C, dan 50 C ph k / R (kalori/mol) (kkalori/mol) 3-154,2-154,2 306,395 0, ,825 4, ,4-646,4 1284,396 1,284 Adsorpsi Nikel dan../ Frideni G.F 47
16 Gambar 4. Kinetika proses adsorpsi nikel dalam larutan dengan ph 3 Hubungan ln dengan t untuk hasil-hasil percobaan di atas ditunjukkan pada Gambar 10, 11 dan 12. Keseluruhannya menunjukkan hubungan yang linear meskipun tidak sebaik pengaluran yang dilakukan pada adsorpsi nikel. Energi aktivasi proses (Tabel 2) < 4,4 kkal/mol menyatakan kembali bahwa proses terkendali oleh difusi melalui lapis difusi dalam fluida. Gambar 5. Kinetika proses adsorpsi nikel dalam larutan dengan ph 4 Gambar 7. Persen adsorpsi Co sebagai fungsi waktu dalam larutan kobalt sulfat ph 3 pada suhu kamar, 40 C dan 50 C Gambar 6. Kinetika proses adsorpsi nikel dalam larutan dengan ph 5 Kinetika Adsorpsi Kobalt pada Resin Penukar Ion Lewatit TP 207 XL dalam Larutan Sulfat Artifisial. Hubungan antara % adsorpsi kobal dengan waktu dari serangkaian percobaan yang dilakukan dalam larutan kobal sulfat 63,48 ppm Co, disajikan pada Gambar 7, 8 dan 9 berturut-turut dari hasil percobaan pada ph 3, ph 4 dan ph 5. Sama seperti perilaku adsorpsi nikel pada resin yang digunakan, laju adsorpsi pada resin menurun dengan peningkatan waktu adsorpsi. Gambar 8. Persen adsorpsi Co sebagai fungsi waktu dalam larutan kobalt sulfat ph 4 pada suhu kamar, 40 C, dan 50 C Gambar 9. Persen adsorpsi Co sebagai fungsi waktu dalam larutan kobalt sulfat ph 5 pada suhu kamar, 40 C, dan 50 C 48 Majalah Metalurgi, V , ISSN / hal 45-52
17 Gambar 10. Kinetika proses adsorpsi kobalt dalam larutan dengan ph 3 Kinetika Adsorpsi Nikel dan Kobalt pada Resin Penukar Ion Lewatit TP 207 XL dalam Larutan Nikel-Kobalt Sulfat Artifisial Untuk menentukan % adsorpsi Ni+Co dari larutan nikel-kobalt artifisial, konsentrasi nikel dan kobalt dalam larutan diubah dalam unit mol/l. Oleh karena itu hubungan antara % adsorpsi dengan waktu yang ditunjukkan pada Gambar 13 dan 14 didasarkan pada % mol (Ni+Co) yang teradsorpsi pada resin. Konsentrasi total awal Ni+Co yang digunakan dalam percobaan adalah sebesar 0,024 mol/l. Gambar 11. Kinetika proses adsorpsi kobalt dalam larutan dengan ph 4 Gambar 13. Persen adsorpsi Ni+Co sebagai fungsi waktu pada suhu kamar dengan resin 1x teoritik Gambar 12. Kinetika proses adsorpsi kobalt dalam larutan dengan ph 5 Tabel 2. Energi aktifasi proses adsorpsi kobalt ph k / R (Kalori/mole) (kkalori/mole) ,718 3, ,402 3, , ,449 4,363 Gambar 14. Persen adsorpsi Ni+Co sebagai fungsi waktu pada suhu kamar dengan resin 4x teoritik Dengan cara yang sama seperti yang dilakukan sebelumnya, laju adsorpsi Ni+Co dialurkan hubungan ln dengan t dari hasil-hasil percobaan di atas sebagaimana ditunjukkan pada Gambar 15 dan 16. Adsorpsi Nikel dan../ Frideni G.F 49
18 Gambar 15. Kinetika adsorpsi Ni+Co dalam larutan yang mengandung resin 1 kali teoritik Gambar 16. Kinetika adsorpsi Ni+Co dalam larutan yang mengandung resin 4 kali teoritik Pengaruh Temperatur dan ph terhadap Kemampuan Adsorpsi Nikel dan Kobalt pada Resin Penukar Ion Lewatit TP 207 XL dari Larutan Artifisial Gambar 17 dan 18 berturut-turut menunjukkan pengaruh peningkatan ph terhadap persen adsorpsi nikel dan kobal pada pada temperatur kamar, 40 C, dan 50 C. Gambar 18. Pengaruh ph dan temperatur pada persen adsorpsi kobalt dalam larutan kobalt sulfat setelah selama 4 jam Proses adsorpsi Ni+Co berlangsung dengan energi aktifasi yang rendah, karena cenderung terkendali oleh laju pepindahan massa ion-ion nikel dalam larutan. Proses ini tidak sensitif terhadap kenaikan suhu. Laju adsorpsi nikel secara keseluruhan lebih lambat dari laju adsorpsi kobal, meskipun dari larutan dengan konsentrasi kobalt jauh lebih rendah dari nikel. Peningkatan jumlah nikel dan kobal yang dapat diadsorpsi pada suhu yang lebih tinggi kemungkinan berkaitan dengan peningkatan konsentrasi kesetimbangan ion-ion nikel dan kobalt pada resin. Adsorpsi pada ph yang lebih tinggi dari DpH (DpH nikel 2,2 dan DpH kobal 2,7) [4] meningkatkan laju adsorpsi nikel dan kobal serta jumlah nikel dan kobal yang dapat teradsorpsi selama 4 jam. Selektifitas Resin Penukar Ion Lewatit TP 207 XL Terhadap Nikel dan Kobalt Gambar 17. Pengaruh ph dan temperature pada persen adsorpsi nikel dalam larutan nikel sulfat setelah selama 4 jam Gambar 19. perbandingan persen adsorpsi nikel dan kobalt dalam larutan nikel-kobalt sulfat pada berbagai ph dengan suhu kamar selama 4 jam 50 Majalah Metalurgi, V , ISSN / hal 45-52
19 Gambar 20. Perbandingan persen adsorpsi nikel dan kobalt dalam larutan nikel-kobalt sulfat pada berbagai ph dengan suhu kamar selama 4 jam Nikel dan kobal memiliki DpH dengan rentang perbedaan yang kecil pada resin penukar ion Lewatit Monoplus TP 207 XL. Bersamaan dengan itu laju adsorpsi nikel lebih lambat dari laju adsorpsi kobalt. Sebagai konsekuensinya selektifitas resin terhadap nikel dan kobalt dalam larutan sulfat sangat rendah. Sebagai kesimpulannya resin penukar ion Lewatit TP Monoplus 207 XL lebih sesuai untuk digunakan mengadsorpsi nikel dan kobalt secara bersamaan. Adsorpsi Nikel dan Kobalt pada Resin Lewatit TP 207 XL dari Larutan Hasil Pelindian Larutan hasil pelindian yang digunakan adalah hasil pelindian dibawah tekanan atmosfer pada 95 C dengan menggunakan reagen pelindi larutan asam sulfat 1 M. Larutan hasil pelindian mengandung pengotor besi yang tinggi, sehingga besi harus dioksidasi terlebih dahulu menjadi ion Fe 3+ dengan berbagai metoda, dan selanjutnya dilakukan presipitasi besi dengan menaikkan ph. Ion-ion nikel dan kobalt dari larutan yang telah dipisahkan besinya di adsorpsi dengan resin Lewatit Monoplus TP 207 XL pada ph 4-4,5. Gambar-gambar 21, 22 dan 23 menunjukkan persen adsorpsi nikel, kobalt, dan/atau besi dari larutan hasil pelindian yang telah dikurangi kadar besinya. Gambar 21. Persen adsorpsi nikel, kobalt, dan besi dari larutan hasil pelindian (besi dioksidasi dengan H 2 O 2 ) pada ph 4 dengan suhu 50 C Gambar 22. Persen adsorpsi nikel dan besi dari larutan hasil pelindian (besi dioksidasi dengan aerasi 2 tahap) pada ph 4,5 dengan temperatur 60 C Gambar 23. Persen adsorpsi nikel dari larutan hasil pelindian (besi dioksidasi elektrokimia dengan beberapa variasi waktu) pada ph 4,5 dengan temperatur 60 C (adsorpsi besi sangat kecil dan diabaikan) Besi yang tertinggal cenderung ikut teradsorpsi saat adsorpsi nikel pada ph 4-4,5. Oleh karena itu besi dari larutan hasil pelindian harus dipisahkan sebanyak mungkin, sebelum dilakukan recovery Adsorpsi Nikel dan../ Frideni G.F 51
20 nikel dengan Lewatit Monoplus TP 207 XL. KESIMPULAN Dari percobaan adsorpsi yang telah dilakukan diketahui bahwa resin penukar ion Lewatit TP Monoplus 207 XL dapat digunakan untuk mengadsorpsi nikel, kobalt, dan besi pada ph sekitar 4. Keasaman larutan sangat mempengaruhi laju dan jumlah ion-ion nikel dan kobalt yang dapat di adsorpsi. Resin ini tidak selektif untuk memisahkan nikel dan kobalt dari larutan nikel-kobalt sulfat karena DpH untuk pemisahan kedua ion tersebut sangat berdekatan. Laju adsorpsi nikel lebih lambat dari laju adsorpsi kobalt dari larutan sulfat artifisial. Proses adsorpsi terkendali oleh laju difusi ion-ion melalui lapis difusi dalam fluida. Adsorpsi nikel dan kobalt dari larutan hasil pelindian berlangsung dengan laju yang lebih tinggi. DAFTAR PUSTAKA [1] Kunin, R., Ion Exchange Resin, Second Edition, John Wiley and Son, Inc., New York. [2] Zaimawati, Z Development of Resin in Pulp Process for Recovery Nickel and Cobalt from Laterite Leach Slurries, PhD Thesis, Murdoch Univ. WA. [3] Habashi, F Principle Of Extractive Metallurgy, Volume 2 (Hydrometallurgy), Gordon and Research, Science Publisher, Inc, New York. [4] Metal Winning by Hydrometallurgy, Lewatit, Bayer Chamicals. 52 Majalah Metalurgi, V , ISSN / hal 45-52
21 Indeks Penulis A Agung Imaduddin 1 Ari Yustisia Akbar 21 Arifin Arif 7 D Deddy Sufiandi 15, 27 E Edi Herianto 7 F Frideni G.F 45 G G. A Wisma 45 H Harsisto 21 Hartati Soeroso 21 I Immanuel Ginting 27 M M.Z. Mubarok 45 P Puguh Prasetiyo 35 R Ronald Nasoetion 3 S S. Purwadaria 45 Y Yulinda Lestari 21 Indeks
22 Majalah Metalurgi, V , ISSN
23 Indeks B Bijih nikel 7, 12, 13, 14, 35, 36, 43, 44, 45, 46 C Caron process 7, 13, 35, 44 CMR 1 D Difusi 45, 47, 48, 52 E Engineered cement composit 21., 22 F Floating zone method 1 Fly ash 21, 23, 24 H Hidrometalurgi 14, 35, 36 HPAL process 7, 35 Hydrometallurgy 35, 52 I Ilmonite 35 Industri baja 15, 16, 27 K Kristal tunggal 1, 2, 3, 4, 5 L Laterit 7, 10, 11, 12, 13, 14, 35, 36, 37, 38, 39, 40, 41, 42, 43, 45, 52 Laterite 7, 10, 13, 14, 35, 40, 43, 44, 52 Laterit kadar rendah 7, 13, 35, 36, 37, 38, 39, 40, 41, 43, 44, 45 Leaching 10, 20, 35, 36, 38, 39, 51, 43, 44, 45 Lewatit Monoplus TP 207 XL 45, 46, 51, 52 Limonit 7, 8, 11, 12, 13, 35, 36, 37, 41, 42, 43 Low grade of laterite 35 LSMO 1, 2 LSMO M Magnesium (Mg) 35, 37 Magnetic separator 15, 16, 17, 19, 27, 28, 29, 31, 32, 33 Mangan 27, 28, 29, 30, 31, 32, 33, 34, 38 Metoda floating zone 1 N Nickel ore 7 P Pasir besi titan 15, 16, 17, 18, 19, 20 Polyvinyl alcohol 21, 23, 24 Product 9, 14, 15, 27, 38 Produk 3, 7, 8, 9, 11, 14, 15, 16, 17, 18, 20, 23, 27, 28, 33, 35, 36, 38, 40, 41, 43 Proses Caron 7, 8, 9, 10, 12, 13, 35, 36, 37, 38, 41, 43 Proses HPAL 7, 8, 9, 13, 35, 36, 37, 39, 40, 41, 43 R Resin 45, 46, 47, 48, 49, 50, 51, 52 Roasting 27, 28, 30, 31, 32, 33 S Saprolite 7, 35, 42 Self healing concrete 21, 22, 23 Single crystal 1, 5 Steel industry 15 Superplastisize 21, 24 Indeks
24 T Tegal Buleud - Sukabumi Selatan 15 Tegal Buleud- South Sukabumi 15 Titans iron sand 15 Majalah Metalurgi, V , ISSN
25 LEMBAGA ILMU PENGETAHUAN INDONESIA P U S A T P E N E L I T I A N M E T A L U R G I Kawasan PUSPIPTEK Serpong 15314, Tlp Fax PANDUAN BAGI PENULIS 1. Penulis yang berminat menyumbangkan hasil karyanya untuk dimuat di dalam majalah Metalurgi, diharuskan mengirim naskah asli dalam bentuk final baik hardcopy atau softcopy (dalam file doc), disertai pernyataan bahwa naskah tersebut belum pernah diterbitkan atau tidak sedang menunggu penerbitannya dalam media tertulis manapun. 2. Penulis diminta mencantumkan nama tanpa gelar, afiliasi kedudukan dan alamat nya setelah judul karya tulisnya, dan ditulis dengan Times New Roman (TNR), jarak 1 spasi, font Naskah harus diketik dalam TNR font 12 dengan satu (1) spasi. Ditulis dalam bentuk hardcopy dengan kertas putih dengan ukuran A4 pada satu muka saja. Setiap halaman harus diberi nomor dan diusahakan tidak lebih dari 30 halaman 4. Naskah dapat ditulis dalam bahasa Indonesia atau bahasa Inggris, harus disertai dengan judul yang cukup ringkas dan dapat melukiskan isi makalah secara jelas. Judul ditulis dengan huruf kapital menggunakan TNR font 14 dan ditebalkan. Untuk yang berbahasa Indonesia, usahakanlah untuk menghindari penggunaan bahasa asing. 5. Isi naskah terdiri dari Judul naskah, Nama Pengarang dan Institusi beserta , Intisari/Abstract, Pendahuluan, Tata Kerja/Prosedur Percobaan, Hasil Percobaan, Pembahasan, Kesimpulan dan Saran, Daftar Pustaka, Ucapan Terimakasih dan Riwayat Hidup. Pakailah bahasa yang baik dan benar, singkat tapi cukup jelas, rapi, tepat dan informatif serta mudah dicerna/dimengerti. Sub judul ditulis dengan huruf kapital TNR font 12, ditebalkan tanpa penomoran urutan sub judul, misalnya : PENDAHULUAN PROSEDUR PERCOBAAN, dan seterusnya. 6. Naskah harus disertai intisari pendek dalam bahasa Indonesia dan abstract dalam bahasa Inggris ditulis TNR 10 jarak 1 spasi diikuti dengan kata kunci/keywords ditulis miring. Isi dari intisari/abstract merangkum secara singkat dan jelas tentang : Tujuan dan Ruang Lingkup Litbang Metoda yang Digunakan Ringkasan Hasil Kesimpulan 7. Isi pendahuluan menguraikan secara jelas tentang : Masalah dan Ruang Lingkup Status Ilmiah dewasa ini Hipotesis Cara Pendekatan yang Diharapkan Hasil yang Diharapkan 8. Tata kerja/prosedur percobaan ditulis secara jelas sehingga dapat dipahami langkahlangkah percobaan yang dilakukan. 9. Hasil dan pembahasan disusun secara rinci sebagai berikut : Data yang disajikan telah diolah, dituangkan dalam bentuk tabel atau gambar, serta diberi keterangan yang mudah dipahami. Penulisan keterangan tabel diletakkan di atas tabel, rata kiri dengan TNR 10 dengan spasi 1. Kata tabel ditulis tebal. Akhir ketrangan tidak diberi tanda titik.
26 LEMBAGA ILMU PENGETAHUAN INDONESIA P U S A T P E N E L I T I A N M E T A L U R G I Kawasan PUSPIPTEK Serpong 15314, Tlp Fax PANDUAN BAGI PENULIS Contoh : Tabel 1. Harga kekerasan baja SS 316L Penulisan keterangan gambar ditulis di bawah gambar, rata kiri dengan TNR 10 jarak 1 spasi, format in line with text. Kata gambar ditulis tebal. Akhir ketrangan tidak diberi tanda titik. Contoh : Gambar 1. Struktur mikro baja SS 316L Pada bagian pembahasan terlihat adanya kaitan antara hasil yang diperoleh dengan konsep dasar dan atau hipotesis Kesesuaian atau pertentangan dengan hasil litbang lainnya Implikasi hasil litbang baik secara teoritis maupun penerapan 10. Kesimpulan berisi secara singkat dan jelas tentang : Esensi hasil litbang Penalaran penulis secara logis dan jujur, fakta yang diperoleh 11. Penggunaan singkatan atau tanda-tanda diusahakan untu memakai aturan nasional atau internasional. Apabila digunakan sistem satuan maka harus diterapkan Sistem Internasional (SI) 12. Kutipan atau Sitasi Penulisan kutipan ditunjukkan dengan membubuhkan angka (dalam format superscript) sesuai urutan. Angka kutipan ditulis sebelum tanda titik akhir kalimat tanpa spasi, dengan tanda kurung siku dan tidak ditebalkan (bold). Jika menyebut nama, maka angka kutipan langsung dibubuhkan setelah nama tersebut. Tidak perlu memakai catatan kaki. Urutan dalam Daftar Pustaka ditulis sesuai dengan nomor urut kutipan dalam naskah. Contoh: Struktur mikro baja SS 316L [2]. 13. Penyitiran pustaka dilakukan dengan memberikan nomor di dalam tanda kurung. Daftar pustaka itu sendiri dicantumkan pada bagian akhir dari naskah. Susunan penulisan dari pustaka sebagai berikut : 1. Buku dengan satu pengarang atau dua pengarang (hanya nama pengarang yang dibalik) : [1] Peristiwady, Teguh Ikan-ikan Laut Ekonomis Penting di Indonesia : Petunjuk Identifikasi. Jakarta : LIPI Press. [2] Bambang, Dwiloka dan Ratih Riana Teknik Menulis Karya Ilmiah. Jakarta : Rineka Cipta. 2. Buku dengan tiga pengarang atau lebih [1] Suwahyono, Nurasih dkk Pedoman Penampilan Majalah Ilmiah Indonesia. Jakarta : Pusat Dokumentasi dan Informasi Ilmiah, LIPI. 3. Buku tanpa nama pengarang, tapi nama editor dicantumkan. [1] Brojonegoro, Arjuno dan Darwin (Ed.) Pemberdayaan UKM melalui Program Iptekda LIPI, Jakarta : LIPI Press. 4. Buku tanpa pengarang, tapi ditulis atas nama Lembaga. [1] Pusat Bahasa Departemen Pendidikan dan Nasional Kamus Besar bahasa Indonesia Jakarta : Balai Pustaka.
27 LEMBAGA ILMU PENGETAHUAN INDONESIA P U S A T P E N E L I T I A N M E T A L U R G I Kawasan PUSPIPTEK Serpong 15314, Tlp Fax PANDUAN BAGI PENULIS 5. Artikel dari Jurnal/majalah dan koran (bila tanpa pengarang) [1] Haris, Syamsudin ,,Demokratisasi Partai dan Dilema Sistem Kepartaian di Indonesia. Jurnal Penelitian Politik.: Jakarta. 6. Artikel dari bunga rampai [1] Oetama, Yacob ,, Tradisi Intelektualitas, Taufik Abdullah, Jurnalisme Makna. Dalam A.B. Lapian dkk. (Ed.), Sejarah dan Dialog Peradaban. Jakarta : LIPI Press. 7. Bahan yang belum dipublikasikan atau tidak diterbikan [1] Wijana, I dewa Putu ,,Bias Gender pada Bahasa Majalah Remaja. Tesis, Fakultas Ilmu Budaya Yogyakarta : Universitas Gajah Mada. 8. Bahan yang belum dipublikasikan atau tidak diterbikan [1] Wijana, I dewa Putu ,,Bias Gender pada Bahasa Majalah Remaja. Tesis, Fakultas Ilmu Budaya Yogyakarta : Universitas Gajah Mada. 9. Tulisan Bersumber dari Internet [1] Rustandy, Tandean Tekan Korupsi Bangun Bangsa. ( diakses 14 Januari 2007) 14. Ucapan terimakasih ditulis dengan huruf kapital TNR font 12 dan ditebalkan. Isi dari ucapan terimakasih ditulis dengan TNR 12 dan spasi Naskah yang dinilai kurang tepat untuk dimuat di dalam majalah akan dikirim kembali kepada penulis. Saran-saran akan diberikan apabila ketidak tepatan tersebut hanya disebabkan oleh format atau cara penyajian. 16. Penulis bertanggung jawab penuh atas kebenaran naskahnya. 17. Setiap penerbitan tidak ada dua kali atau lebih penulis utama yang sama. Apabila ada, salah satu naskahnya penulis utama tersebut ditempatkan pada penulis kedua. Serpong, 8 Juni 2009 Redaksi Majalah Metalurgi
ADSORPSI NIKEL DAN KOBALT PADA RESIN PENUKAR ION LEWATIT MONOPLUS TP 207 XL DALAM BEBERAPA LARUTAN SULFAT
ADSORPSI NIKEL DAN KOBALT PADA RESIN PENUKAR ION LEWATIT MONOPLUS TP 207 XL DALAM BEBERAPA LARUTAN SULFAT Frideni G.F, G. A Wisma, M.Z. Mubarok, dan S. Purwadaria Program Studi Sarjana Teknik Metalurgi,
Lebih terperinciAKREDITASI : SK 187/AU1/P2MBI/08/2009
VOLUME 26 NOMOR 1, APRIL 2011 ISSN 0126 3188 AKREDITASI : SK 187/AU1/P2MBI/08/2009 Penanggung Jawab: Kapuslit Metalurgi LIPI Dewan Redaksi : Ketua Merangkap Anggota: Ir. Ronald Nasoetion, MT Anggota: Dr.
Lebih terperinciAKREDITASI : SK 187/AU1/P2MBI/08/2009
VOLUME 26 NOMOR 1, APRIL 2011 ISSN 0126 3188 AKREDITASI : SK 187/AU1/P2MBI/08/2009 Penanggung Jawab: Kapuslit Metalurgi LIPI Dewan Redaksi : Ketua Merangkap Anggota: Ir. Ronald Nasoetion, MT Anggota: Dr.
Lebih terperinciKONSENTRASI PASIR BESI TITAN DARI PENGOTORNYA DENGAN CARA MAGNETIK
KONSENTRASI PASIR BESI TITAN DARI PENGOTORNYA DENGAN CARA MAGNETIK Deddy Sufiandi Pusat Penelitian Metalurgi LIPI Kawasan PUSPIPTEK Serpong-Tangerang 15314 E-mail : deddy.sufiandi@lipi.go.id Intisari Pasir
Lebih terperinciMETODA FZ PADA PEMBUATAN KRISTAL TUNGGAL La 2-2x Sr 1+2x Mn 2 O 7
METODA FZ PADA PEMBUATAN KRISTAL TUNGGAL La 2-2x Agung Imaduddin Puslit Metalurgi LIPI Kawasan Puspiptek Serpong, Tangerang 15314 E-mail: agungi@gmail.com Intisari La 2-2x (x=0,4) mempunyai CMR (Colossal
Lebih terperinciPERILAKU PELARUTAN LOGAM NIKEL DAN BESI DARI BIJIH NIKEL KADAR RENDAH SULAWESI TENGGARA
PERILAKU PELARUTAN LOGAM NIKEL DAN BESI DARI BIJIH NIKEL KADAR RENDAH SULAWESI TENGGARA Solihin 1,* dan F. Firdiyono 2 1 Pusat Penelitian Geoteknologi-LIPI Komplek LIPI, Jl. Sangkuriang, Bandung 2 Pusat
Lebih terperinciPENINGKATAN KADAR NIKEL BIJIH LIMONIT MELALUI PROSES REDUKSI SELEKTIF DENGAN VARIASI WAKTU DAN PERSEN REDUKTOR
PENINGKATAN KADAR NIKEL BIJIH LIMONIT MELALUI PROSES REDUKSI SELEKTIF DENGAN VARIASI WAKTU DAN PERSEN REDUKTOR Muhammad Ikhwanul Hakim 1,a, Andinnie Juniarsih 1, Iwan Setiawan 2 1 Jurusan Teknik Metalurgi,
Lebih terperinciLembaga Ilmu Pengetahuan Indonesia
I.102 PENGOLAHAN BIJIH NIKEL KADAR RENDAH UNTUK MENDUKUNG INDUSTRI BAJA TAHAN KARAT Dr. Solihin, M.Env., Ir. Puguh Prasetiyo, Dr. Ir. Rudi Subagja, Dedy Sufiandi ST, Immanuel Ginting ST Lembaga Ilmu Pengetahuan
Lebih terperinciKENDALA DAN KEMUNGKINAN PENGEMBANGAN PROSES CARON UNTUK BIJIH NIKEL LATERIT KADAR RENDAH INDONESIA
KENDALA DAN KEMUNGKINAN PENGEMBANGAN PROSES CARON UNTUK BIJIH NIKEL LATERIT KADAR RENDAH INDONESIA Arifin Arif dan Edi Herianto Pusat Penelitian Metalurgi LIPI Kawasan PUSPIPTEK Serpong-Tangerang 15314
Lebih terperinciPENINGKATAN KADAR NIKEL (Ni) DAN BESI (Fe) DARI BIJIH NIKEL LATERIT KADAR RENDAH JENIS SAPROLIT UNTUK BAHAN BAKU NICKEL CONTAINING PIG IRON (NCPI/NPI)
PENINGKATAN KADAR NIKEL (Ni) DAN BESI (Fe) DARI BIJIH NIKEL LATERIT KADAR RENDAH JENIS SAPROLIT UNTUK BAHAN BAKU NICKEL CONTAINING PIG IRON (NCPI/NPI) Agus Budi Prasetyo dan Puguh Prasetiyo Pusat Penelitian
Lebih terperinciBAB I PENDAHULUAN. Nikel merupakan logam berwarna perak keputihan yang mempunyai kemampuan
BAB I PENDAHULUAN 1.1. Latar Belakang Mineral logam merupakan kekayaan alam tak terbarukan yang mempunyai peranan penting sebagai penopang perekonomian Indonesia. Salah satu mineral logam yang banyak dimanfaatkan
Lebih terperinciKARAKTERISTIK SIFAT MEKANIS BAJA LATERIT TERHADAP PROSES PENGEROLAN
KARAKTERISTIK SIFAT MEKANIS BAJA LATERIT TERHADAP PROSES PENGEROLAN Roy Hasudungan, Erwin Siahaan, Rosehan dan Bintang Jurusan Teknik Mesin, Fakultas Teknik Universitas Tarumanagara, LIPI-Metalurgi e-mail:
Lebih terperinciPENGGUNAAN TERAK NIKEL SEBAGAI AGREGAT PADA BETON MUTU TINGGI
PENGGUNAAN TERAK NIKEL SEBAGAI AGREGAT PADA BETON MUTU TINGGI T 624. 183 4 KHO ABSTRAK Beton merupakan material konstruksi bangunan yang sering digunakan karena mudah dibentuk dan biaya pemeliharaan yang
Lebih terperinciMASIH TERBUKANYA PELUANG PENELITIAN PROSES CARON UNTUK MENGOLAH LATERIT KADAR RENDAH DI INDONESIA
MASIH TERBUKANYA PELUANG PENELITIAN PROSES CARON UNTUK MENGOLAH LATERIT KADAR RENDAH DI INDONESIA Puguh Prasetiyo dan Ronald Nasoetion Pusat Penelitian Metalurgi-LIPI Kawasan Puspiptek Gd.470, Serpong
Lebih terperinciKARAKTERISASI PELINDIAN PRODUK PEMANGGANGAN ALKALI (FRIT) DALAM MEDIA AIR DAN ASAM SULFAT
KARAKTERISASI PELINDIAN PRODUK PEMANGGANGAN ALKALI (FRIT) DALAM MEDIA AIR DAN ASAM SULFAT Vanessa I. Z. Nadeak 1, Suratman 2, Soesaptri Oediyani 3 [1]Mahasiswa Jurusan Teknik Metalurgi Universitas Sultan
Lebih terperinciDAFTAR ISI LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL...
DAFTAR ISI Halaman LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL... DAFTAR LAMPIRAN... i ii iii iv v vi ix xi xii BAB 1
Lebih terperinciBAB I PENDAHULUAN 1.1 L atar Belakang
BAB I PENDAHULUAN 1.1 Latar Belakang PT Aneka Tambang (Antam), Tbk. Unit Bisnis Pertambangan Emas (UBPE) Pongkor adalah salah satu industri penambangan dan pengolahan bijih emas. Lingkup kegiatannya adalah
Lebih terperinciPENGARUH LOGAM TEMBAGA DALAM PROSES PENYISIHAN LOGAM NIKEL DARI LARUTANNYA DENGAN MENGGUNAKAN METODE ELEKTRODEPOSISI TUGAS AKHIR
PENGARUH LOGAM TEMBAGA DALAM PROSES PENYISIHAN LOGAM NIKEL DARI LARUTANNYA DENGAN MENGGUNAKAN METODE ELEKTRODEPOSISI THE EFFECT OF COPPER IN NICKEL REMOVAL PROCESS BY ELECTRODEPOSITION METHOD TUGAS AKHIR
Lebih terperinciBAB I PENDAHULUAN. bidang perindustrian. Salah satu konsumsi nikel yang paling besar adalah sebagai
BAB I PENDAHULUAN I.1 Latar Belakang Nikel merupakan salah satu bahan penting yang banyak dibutuhkan dalam bidang perindustrian. Salah satu konsumsi nikel yang paling besar adalah sebagai bahan baku pembuatan
Lebih terperinciPEMBUATAN MATERIAL DUAL PHASE DARI KOMPOSISI KIMIA HASIL PELEBURAN ANTARA SCALING BAJA DAN BESI LATERIT KADAR NI RENDAH YANG DIPADU DENGAN UNSUR SIC
PEMBUATAN MATERIAL DUAL PHASE DARI KOMPOSISI KIMIA HASIL PELEBURAN ANTARA SCALING BAJA DAN BESI LATERIT KADAR NI RENDAH YANG DIPADU DENGAN UNSUR SIC Daniel P. Malau 1*, Saefudin 2 *12 Pusat Penelitian
Lebih terperinciPENENTUAN TINGKAT KEMAGNETAN DAN INDUKSI MAGNETIK TOTAL ENDAPAN PASIR LAUT PANTAI PADANG SEBAGAI FUNGSI KEDALAMAN
Jurnal Komunikasi Fisika Indonesia http://ejournal.unri.ac.id./index.php/jkfi Jurusan Fisika FMIPA Univ. Riau Pekanbaru. http://www.kfi.-fmipa.unri.ac.id Edisi April 217. p-issn.1412-296.; e-2579-521x
Lebih terperinciRECOVERY NIKEL DARI BIJIH LIMONITE TEREDUKSI OLEH LEACHING AMONIUM BIKARBONAT SKRIPSI
RECOVERY NIKEL DARI BIJIH LIMONITE TEREDUKSI OLEH LEACHING AMONIUM BIKARBONAT SKRIPSI Oleh SUGANTA HANDARU S 04 04 04 0682 DEPARTEMEN TEKNIK METALURGI & MATERIAL FAKULTAS TEKNIK UNIVERSITAS INDONESIA GENAP
Lebih terperinciANALISIS KADAR LOGAM KOBALT(Co) DAN NIKEL (Ni) DALAM ABU TERBANG HASIL PEMBAKARAN BATUBARA DARI DUA LOKASI DENGAN METODE SPEKTROFOTOMETRI SERAPAN ATOM
ANALISIS KADAR LOGAM KOBALT(Co) DAN NIKEL (Ni) DALAM ABU TERBANG HASIL PEMBAKARAN BATUBARA DARI DUA LOKASI DENGAN METODE SPEKTROFOTOMETRI SERAPAN ATOM SKRIPSI RICCA JASMINE 070802037 DEPARTEMEN KIMIA FAKULTAS
Lebih terperinciSTUDI PENENTUAN KADAR Cu, MG, MN, ZN DALAM TABLET MULTIVITAMIN-MINERAL SECARA SPEKTROFOTOMETRI SERAPAN ATOM
STUDI PENENTUAN KADAR Cu, MG, MN, ZN DALAM TABLET MULTIVITAMIN-MINERAL SECARA SPEKTROFOTOMETRI SERAPAN ATOM ABSTRAK Telah dilakukan penelitian tentang penentuan kadar Ca. Mg, Mn, Zn dalam contoh tiruan
Lebih terperinciPEMBUATAN ASAM OKSALAT DARI PELEPAH KELAPA SAWIT ( Elaeis guineensis ) MENGGUNAKAN METODE PELEBURAN ALKALI SKRIPSI M. HIDAYAT HASIBUAN
PEMBUATAN ASAM OKSALAT DARI PELEPAH KELAPA SAWIT ( Elaeis guineensis ) MENGGUNAKAN METODE PELEBURAN ALKALI SKRIPSI Oleh : M. HIDAYAT HASIBUAN 130425020 DEPARTEMEN TEKNIK KIMIA FAKULTAS TEKNIK UNIVERSITAS
Lebih terperinciPEMANFAATAN LIMBAH LUMPUR INDUSTRI PENGOLAHAN BAJA SEBAGAI PENGGANTI PARSIAL PASIR UNTUK BAHAN BANGUNAN
NO. Urut : 070/S2-TL/TPL/1997 PEMANFAATAN LIMBAH LUMPUR INDUSTRI PENGOLAHAN BAJA SEBAGAI PENGGANTI PARSIAL PASIR UNTUK BAHAN BANGUNAN TESIS Sebagai Salah Satu Persyaratan untuk Menyelesaikan Program Magister
Lebih terperinciBAB I PENDAHULUAN. 1.1 Latar Belakang
BAB I PENDAHULUAN 1.1 Latar Belakang Pada tahun 2005 menurut penelitian South East Asia Iron and Steel Institute, tingkat konsumsi baja per kapita di Indonesia sebesar 26,2 kg yang lebih rendah dibandingkan
Lebih terperinciKAJIAN DESALINASI LARUTAN SIMULASI TETES SECARA EKSKLUSI ION
KAJIAN DESALINASI LARUTAN SIMULASI TETES SECARA EKSKLUSI ION T 547.781 0465 BUN ABSTRAK Proses desalinasi merupakan salah satu tahap utama pada pengolahan tetes menjadi gula cair ataupun dalam mempersiapkan
Lebih terperinciSTUDI PENINGKATAN KADAR BESI TERHADAP BIJIH BESI LATERITIK ASAL KABUPATEN TASIKMALAYA MENGGUNAKAN METODE FLOTASI KEBALIKAN
STUDI PENINGKATAN KADAR BESI TERHADAP BIJIH BESI LATERITIK ASAL KABUPATEN TASIKMALAYA MENGGUNAKAN METODE FLOTASI KEBALIKAN TUGAS AKHIR Dibuat untuk memenuhi syarat mendapatkan gelar Sarjana Teknik Metalurgi
Lebih terperinciTESIS. Oleh : Nama : Rina Martsiana Nim : Pembimbing
PENGUKURAN MODULUS RESILIEN CAMPURAN BETON ASPAL YANG MENGANDUNG ROADCEL-50 DENGAN BEBAN STATIS DAN BEBAN BERULANG TESIS Oleh : Nama : Rina Martsiana Nim : 250 99 100 Pembimbing PROGRAM STUDI TEKNIK SIPIL
Lebih terperinciPROGRAM STUDI DIPLOMA III TEKNIK KIMIA FAKULTAS TEKNIK UNIVERSITAS SEBELAS MARET SURAKARTA 2013 commit to user
LAPORAN TUGAS AKHIR PEMBUATAN TITANIA PASTA SEBAGAI BAHAN BAKU SEL SURYA Disusun Oleh: ASTRI KURNIAWATI I 8310011 DEVI AYU ANTASARI I 8310021 PROGRAM STUDI DIPLOMA III TEKNIK KIMIA FAKULTAS TEKNIK UNIVERSITAS
Lebih terperinciPENGARUH UKURAN PARTIKEL BATU APUNG TERHADAP KEMAMPUAN SERAPAN CAIRAN LIMBAH LOGAM BERAT
PENGARUH UKURAN PARTIKEL BATU APUNG TERHADAP KEMAMPUAN SERAPAN CAIRAN LIMBAH LOGAM BERAT Aditiya Yolanda Wibowo, Ardian Putra Laboratorium Fisika Bumi, Jurusan Fisika FMIPA Universitas Andalas Kampus Unand,
Lebih terperinciPENGARUH WAKTU PELINDIAN PADA PROSES PEMURNIAN SILIKON TINGKAT METALURGI MENGGUNAKAN LARUTAN HCl
PENGARUH WAKTU PELINDIAN PADA PROSES PEMURNIAN SILIKON TINGKAT METALURGI MENGGUNAKAN LARUTAN HCl Bintang Adjiantoro dan Efendi Mabruri Pusat Penelitian Metalurgi LIPI Kawasan Puspiptek Serpong, Gedung
Lebih terperinciPELUANG PENELITIAN UNTUK MEMPERBAIKI TEKNOLOGI PROSES UNTUK MENGOLAH BIJIH NIKEL LATERIT KADAR RENDAH INDONESIA
PELUANG PENELITIAN UNTUK MEMPERBAIKI TEKNOLOGI PROSES UNTUK MENGOLAH BIJIH NIKEL LATERIT KADAR RENDAH INDONESIA Puguh Prasetiyo Pusat Penelitian Metalurgi LIPI Kawasan Puspiptek Serpong Tangerang 15314
Lebih terperinciMEMPELAJARI PENGARUEI TEKANAN KEMPA DAN SUHU TERHADAP KARAKTERISTIK MINYAK KEMIRI SUNAN (Aleurites frisperma)
MEMPELAJARI PENGARUEI TEKANAN KEMPA DAN SUHU TERHADAP KARAKTERISTIK MINYAK KEMIRI SUNAN (Aleurites frisperma) Oleh Berry F34104035 2008 DEPARTEMEN TEKNOLOGI INDUSTRI PERTANlAN FAKULTAS TEKNOLOGI PERTANIAN
Lebih terperinciSOLIDIFIKASI/STABILISASI LIMBAH TAILING YANG MENGANDUNG MERKURI (Hg) DARI PERTAMBANGAN EMAS SEBAGAI CAMPURAN DALAM PEMBUATAN CONCRETE (BETON) SKRIPSI
SOLIDIFIKASI/STABILISASI LIMBAH TAILING YANG MENGANDUNG MERKURI (Hg) DARI PERTAMBANGAN EMAS SEBAGAI CAMPURAN DALAM PEMBUATAN CONCRETE (BETON) SKRIPSI Oleh SUSI VIVIANA SIGIRO 130425009 DEPARTEMEN TEKNIK
Lebih terperinciSTUDI PENGARUH PROSES DELEADING TERHADAP DISTRIBUSI ARSENIK DI DALAM TANUR ANODA PT. SMELTING, GRESIK TUGAS AKHIR
STUDI PENGARUH PROSES DELEADING TERHADAP DISTRIBUSI ARSENIK DI DALAM TANUR ANODA PT. SMELTING, GRESIK TUGAS AKHIR Dibuat untuk memenuhi salah satu syarat memperoleh Gelar Sarjana Teknik Metalurgi Di Institut
Lebih terperinciPOLA RESPIRASI BUAH TOMAT (Lycopersicum esculentum) YANG DI-COATING DENGAN GEL LIDAH BUAYA (Aloe vera barbadensis Miller) SELAMA PENYIMPANAN SKRIPSI
POLA RESPIRASI BUAH TOMAT (Lycopersicum esculentum) YANG DI-COATING DENGAN GEL LIDAH BUAYA (Aloe vera barbadensis Miller) SELAMA PENYIMPANAN SKRIPSI OLEH: FELANY SUTANTO NRP 6103013025 PROGRAM STUDI TEKNOLOGI
Lebih terperinciMAJALAH METALURGI (2015) 3: Available online at
MAJALAH METALURGI (2015) 3: 115-124 Available online at www.ejurnalmaterialmetalurgi.com STUDI PERILAKU PELINDIAN BIJIH BESI NIKEL LIMONIT DARI PULAU HALMAHERA DALAM LARUTAN ASAM NITRAT Muhammad Wildanil
Lebih terperinciSKRIPSI. PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM :
SKRIPSI PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM : 1104305004 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS UDAYANA
Lebih terperinciKARAKTERISTIK DAN AKTIVASI CAMPURAN TANAH ANDISOL / LEMPUNG BAYAT / ABU SEKAM SEBAGAI PENJERAP LOGAM BERAT KROMIUM (Cr) TESIS
KARAKTERISTIK DAN AKTIVASI CAMPURAN TANAH ANDISOL / LEMPUNG BAYAT / ABU SEKAM SEBAGAI PENJERAP LOGAM BERAT KROMIUM (Cr) TESIS Disusun untuk memenuhi sebagian persyaratan mencapai derajat Magister Program
Lebih terperinciSTUDI GANGGUAN KOBALT, NIKEL DAN TEMBAGA PADA PENETAPAN BESI DENGAN SPEKTROFOTOMETRI SERAPAN ATOM DALAM NYALA UDARA - ASETILEN
STUDI GANGGUAN KOBALT, NIKEL DAN TEMBAGA PADA PENETAPAN BESI DENGAN SPEKTROFOTOMETRI SERAPAN ATOM DALAM NYALA UDARA - ASETILEN T 546.621 65 BUD ABSTRAK Terdapatnya gangguan dalam analisa secara spektroskopi
Lebih terperinciKESESUAIAN PENGGUNAAN CAMPURAN ASPAL MINYAK DAN ASBUTON MIKRO DENGAN PEN. 40 SEBAGAI BAHAN PENGIKAT DALAM HOT ROLLED SHEET
KESESUAIAN PENGGUNAAN CAMPURAN ASPAL MINYAK DAN ASBUTON MIKRO DENGAN PEN. 40 SEBAGAI BAHAN PENGIKAT DALAM HOT ROLLED SHEET RINGKASAN THE SUITABILITY OF A 40 PEN. BLEND OF REFINERY AND MICROASBUTON BITUMEN
Lebih terperinciPENGARUH SUBTITUSI ABU SERABUT KELAPA (ASK) DALAM CAMPURAN BETON. Kampus USU Medan
PENGARUH SUBTITUSI ABU SERABUT KELAPA (ASK) DALAM CAMPURAN BETON Nora Usrina 1, Rahmi Karolina 2, Johannes Tarigan 3 1 Departemen Teknik Sipil, Universitas Sumatera Utara, Jl. Perpustakaan No. 1 Kampus
Lebih terperinciKATA PENGANTAR. Ucapan terima kasih penulis haturkan kepada:
KATA PENGANTAR Alhamdulillah penulis panjatkan ke hadirat Allah SWT atas ridho, berkat rahmat dan perkenannya, tesis ini bisa diselesaikan dengan baik. Tesis ini disusun untuk memenuhi salah satu persyaratan
Lebih terperinciPERBANDINGAN KUAT TEKAN BETON MENGGUNAKAN AGREGAT JENUH KERING MUKA DENGAN AGREGAT KERING UDARA
Perbandingan Tekan.. Kering Udara PERBANDINGAN KUAT TEKAN BETON MENGGUNAKAN AGREGAT JENUH KERING MUKA DENGAN AGREGAT KERING UDARA Dosen Jurusan Teknik Sipil, Fakultas Teknik, Universitas Janabadra, Yogyakarta
Lebih terperinciPENGGUNAAN TEPUNG SAGU SEBAGAI PENGENTAL (THICKENER) PADA THICK TOMATO KETCHUP PROPOSAL SKRIPSI OLEH : SHERLY
PENGGUNAAN TEPUNG SAGU SEBAGAI PENGENTAL (THICKENER) PADA THICK TOMATO KETCHUP PROPOSAL SKRIPSI OLEH : SHERLY 6103006026 PROGRAM STUDI TEKNOLOGI PANGAN FAKULTAS TEKNOLOGI PERTANIAN UNIVERSITAS KATOLIK
Lebih terperinciPELINDIAN BIJIH NIKEL LATERIT SULAWESI TENGGARA DALAM MEDIA ASAM SULFAT
PROSIDING PEMAPARAN HASIL PENELITIAN PUSAT PENELITIAN GEOTEKNOLOGI LIPI TAHUN 2014 Peran Penelitian Geoteknologi untuk Menunjang Pembangunan Berkelanjutan di Indonesia PELINDIAN BIJIH NIKEL LATERIT SULAWESI
Lebih terperinciBROMINASI ASAM SINAMAT di BAWAH BEBERAPA KONDISI REAKSI
BROMINASI ASAM SINAMAT di BAWAH BEBERAPA KONDISI REAKSI ABSTRAK Dalam penelitian ini dilakukan reaksi transformasi ikatan rangkap olefinik dari asam sinamat dalam berbagai kondisi reaksi dengan tujuan
Lebih terperinciPERCOBAAN PENINGKATAN KADAR MANGAN MENGGUNAKAN MAGNETIC SEPARATOR
PERCOBAAN PENINGKATAN KADAR MANGAN MENGGUNAKAN MAGNETIC SEPARATOR Immanuel Ginting dan Deddy Sufiandi Pusat Penelitian Metalurgi LIPI Kawasan PUSPIPTEK Serpong-Tangerang 15314 E-mail : imma001@lipi.go.id
Lebih terperinciTHESIS Submitted to The Faculty of Agricultural Technology in partial fulfillment of the requirements for obtaining the Bachelor Degree
EFFECT OF SOAKING PRETREATMENTS ON THE DRYING KINETICS AND REHYDRATION CHARACTERISTICS OF PETAI BEANS (Parkia speciosa) EFEK PERLAKUAN AWAL PERENDAMAN PADA LAJU PENGERINGAN DAN KARAKTERISTIK REHIDRASI
Lebih terperinciA STUDY ON MANGANESE LEACHING FROM MANGANESE DIOXIDE ORES BY USING SULFURIC ACID
STUDI PELINDIAN MANGAN SECARA REDUKSI DENGAN MENGGUNAKAN LARUTAN ASAM SULFAT A STUDY ON MANGANESE LEACHING FROM MANGANESE DIOXIDE ORES BY USING SULFURIC ACID Ahmad Royani 1, Rudi Subagja 2 dan Azwar Manaf
Lebih terperinciStudi Pengaruh ph Proses Pelindian Pada Proses Ekstraksi Titanium Dioksida Dari Pasir Besi Tasikmalaya Dengan Menggunakan Metode Hidrometalurgi
Studi Pengaruh ph Proses Pelindian Pada Proses Ekstraksi Titanium Dioksida Dari Pasir Besi Tasikmalaya Dengan Menggunakan Metode Hidrometalurgi Ina Fajria dan Bambang Suharno Teknik Metalurgi dan Material
Lebih terperinciPengaruh Variasi Arus dan Jenis Elektrode pada Pengelasan Smaw Terhadap Sifat Mekanik Baja Karbon
Jurnal Ilmiah Teknik Mesin CakraM Vol. 3 No.2. Oktober 2009 (144-149) Pengaruh Variasi Arus dan Jenis Elektrode pada Pengelasan Smaw Terhadap Sifat Mekanik Baja Karbon I Made Gatot Karohika Jurusan Teknik
Lebih terperinci1 Departemen Fisika, Fakultas Sains dan Teknologi, Universitas Airlangga
Ekstraksi Titanium Dioksida (TiO 2 ) Berbahan Baku Pasir Besi dengan Metode Hidrometalurgi Luthfiana Dysi Setiawati 1, Drs. Siswanto, M.Si 1, DR. Nurul Taufiqu Rochman, M.Eng 2 1 Departemen Fisika, Fakultas
Lebih terperinciPENGARUH PENAMBAHAN FLY ASH DAN VOLUME FOAM TERHADAP KUAT TEKAN, DAYA SERAP AIR, DAN BERAT JENIS BETON RINGAN FOAM DENGAN PERBANDINGAN 1 PC : 1 PS
PENGARUH PENAMBAHAN FLY ASH DAN VOLUME FOAM TERHADAP KUAT TEKAN, DAYA SERAP AIR, DAN BERAT JENIS BETON RINGAN FOAM DENGAN PERBANDINGAN 1 PC : 1 PS SKRIPSI Oleh : MAHARANI K1512039 FAKULTAS KEGURUAN DAN
Lebih terperinciMENENTUKAN TINGKAT KEMATANGAN DAN TEGANGAN ORDINARY PORTLAND CEMENT DIBANDINGKAN DENGAN PORTLAND COMPOSITE CEMENT
MENENTUKAN TINGKAT KEMATANGAN DAN TEGANGAN ORDINARY PORTLAND CEMENT DIBANDINGKAN DENGAN PORTLAND COMPOSITE CEMENT Emsiakui E Sembiring 1, Ir. Besman Surbakti, MT 2 1 Departemen Teknik Sipil, Universitas
Lebih terperinciPEMBUATAN KERAMIK BETA ALUMINA (Na 2 O - Al 2 O 3 ) DENGAN ADITIF MgO DAN KARAKTERISASI SIFAT FISIS SERTA STRUKTUR KRISTALNYA.
PEMBUATAN KERAMIK BETA ALUMINA (Na 2 O - Al 2 O 3 ) DENGAN ADITIF MgO DAN KARAKTERISASI SIFAT FISIS SERTA STRUKTUR KRISTALNYA. Ramlan 1, Masno Ginting 2, Muljadi 2, Perdamean Sebayang 2 1 Jurusan Fisika
Lebih terperinciKETENTUAN CALL FOR PAPERS SEMIKNAS 2017
KETENTUAN CALL FOR PAPERS SEMIKNAS 2017 Sub Sub Tema untuk presentasi makalah : 1. Manajemen Informasi Kesehatan 2. Manajemen Mutu Informasi Kesehatan 3. Kodifikasi Klasifikasi Penyakit dan Tindakan 4.
Lebih terperinciPENGARUH GRADASI TERHADAP PARAMETER KOMPAKSI MATERIAL CRUSHED LIMESTONE ABSTRAK
PENGARUH GRADASI TERHADAP PARAMETER KOMPAKSI MATERIAL CRUSHED LIMESTONE AGUNG ROY NANDO NRP: 0921024 Pembimbing: Ir. Herianto Wibowo, M.Sc ABSTRAK Limestone di kenal sebagai batu kapur atau batu gamping
Lebih terperinciPemanfaatan Limbah Pelepah Pisang di Meteseh sebagai Bahan Baku pembuatan kertas dengan Proses Soda menggunakan Alat Digester
TUGAS AKHIR Pemanfaatan Limbah Pelepah Pisang di Meteseh sebagai Bahan Baku pembuatan kertas dengan Proses Soda menggunakan Alat Digester (Waste Utilization of Banana in Meteseh as Raw Material Soda Process
Lebih terperinciPEMISAHAN DAN PEROLEHAN KEMBALI Cr(VI) DARI ALIRAN LIMBAH ELEKTROPLATING DENGAN TEKNIK MEMBRAN CAIR EMULSI TESIS MAGIS'1'ER. .
hinta S No.: 129/S2-TL./TPL/1999 PEMISAHAN DAN PEROLEHAN KEMBALI Cr(VI) DARI ALIRAN LIMBAH ELEKTROPLATING DENGAN TEKNIK MEMBRAN CAIR EMULSI TESIS MAGIS'1'ER. Oleh Indah NIM25397032 BIDANG KHUSUS TEKNOLOGt
Lebih terperinciADSORPSI BERULANG DENGAN K ZEOLIT UNTUK KOMPONEN GULA REDUKSI DAN SUKROSA PADA TETES TEBU
ADSORPSI BERULANG DENGAN K ZEOLIT UNTUK KOMPONEN GULA REDUKSI DAN SUKROSA PADA TETES TEBU Jimmy Prasetya*, Dr.A.Koesdarminta Jurusan Teknik Kimia, Fakultas Teknologi Industri, Universitas Katolik Parahyangan
Lebih terperinciUji Kinerja Ekstraktan Cyanex 272 dalam Me-recovery Logam Nikel dari Limbah Ni-Cd dengan Metode Ekstraksi Cair-Cair
Uji Kinerja Ekstraktan Cyanex 272 dalam Me-recovery Logam kel dari Limbah - dengan Metode Ekstraksi Cair-Cair Ir.Rita Arbianti,Msi, Ir.Yuliusman,MEng, dan Hendra Syaifuddin Jurusan Teknik Gas dan Petrokimia,
Lebih terperinciPENGARUH INJEKSI POLIMER ATAS STRUKTUR DAN KOMPOSISI SERTA SIFAT FISIK BATUAN RESERVOIR
PENGARUH INJEKSI POLIMER ATAS STRUKTUR DAN KOMPOSISI SERTA SIFAT FISIK BATUAN RESERVOIR RINGRASAN Masalah penting yang dihadapi pada pendesakan dengan polimer adalah "penyumbatan", yang disebabkan oleh
Lebih terperinciPELINDIAN NIKEL DAN BESI PADA MINERAL LATERIT DARI KEPULAUAN BULIHALMAHERA TIMUR DENGAN LARUTAN ASAM KLORIDA
SEMINAR NASIONAL KIMIA DAN PENDIDIKAN KIMIA VII Penguatan Profesi Bidang Kimia dan Pendidikan Kimia Melalui Riset dan Evaluasi Program Studi Pendidikan Kimia Jurusan P.MIPA FKIP UNS Surakarta, 18 April
Lebih terperinciSINTESIS SILIKA AEROGEL BERBASIS WATERGLASS UNTUK PENYIMPAN HIDROGEN ABSTRAK
SINTESIS SILIKA AEROGEL BERBASIS WATERGLASS UNTUK PENYIMPAN HIDROGEN Nama : Esar Pramudityo (2305 100 032) Mustika Endahing Pertiwi (2305 100 097) Jurusan : Teknik Kimia FTI-ITS Dosen Pembimbing : Dr.
Lebih terperinciKelompok B Pembimbing
TK-40Z2 PENELITIAN Semester II 2007/2008 APLIKASI MEMBRAN CA/ZEOLIT UNTUK PEMISAHAN CAMPURAN ALKOHOL-AIR Kelompok B.67.3.13 Indria Gusmelli (13004106) Aziza Addina Permata (13004107) Pembimbing Dr. Irwan
Lebih terperinciTESIS. Disusun untuk memenuhi sebagian persyaratan mencapai derajat Magister Program Studi Ilmu Lingkungan. Oleh : TRI MURNIATI NIM.
PENGELOLAAN LIMBAH CAIR INDUSTRI BATIK DENGAN METODE ELEKTROLISIS SEBAGAI ALTERNATIF PENURUNAN TINGKAT KONSENTRASI LOGAM BERAT DI SUNGAI JENES, KECAMATAN LAWEYAN, KOTA SURAKARTA TESIS Disusun untuk memenuhi
Lebih terperinciBAB V HASIL DAN PEMBAHASAN
BAB V HASIL DAN PEMBAHASAN Bentonit diperoleh dari bentonit alam komersiil. Aktivasi bentonit kimia. Aktivasi secara kimia dilakukan dengan merendam bentonit dengan menggunakan larutan HCl 0,5 M yang bertujuan
Lebih terperinciDIFFUSION TEST AS AN ALTERNATIVE INDICATOR FOR DURABILITY ASSESSMENT OF BITUMINOUS MIXTURES THESIS
T 615. 957 KC1 S DIFFUSION TEST AS AN ALTERNATIVE INDICATOR FOR DURABILITY ASSESSMENT OF BITUMINOUS MIXTURES THESIS by AINE KUSUMAWATI 26997032 PROGRAM SISTEM DAN TEKNIK JALAN RAYA PROGRAM PASCASARJANA
Lebih terperinciLAPORAN PENELITIAN HIBAH BERSAING
REKAYASA LAPORAN PENELITIAN HIBAH BERSAING OPTIMASI PROSES CHELATING DENGAN MENGGUNAKAN EDTA DAN H 2 SO 4 UNTUK MENINGKATKAN BLEACH ABILITY HIDROGEN PEROKSIDA PADA PROSES PULP BLEACHING Oleh: Ir Ahmad
Lebih terperinci- 3 - BAB I KETENTUAN UMUM
- 2-2. Undang-Undang Nomor 23 Tahun 2014 tentang Pemerintahan Daerah (Lembaran Negara Republik Indonesia Tahun 2014 Nomor 244, Tambahan Lembaran Negara Republik Indonesia Nomor 5587) sebagaimana telah
Lebih terperinciEksperimen Pembentukan Kristal BPSCCO-2223 dengan Metode Self-Flux
Berkala Fisika ISSN : 1410-9662 Vol.8, No.2, April 2005, hal 53-60 Eksperimen Pembentukan Kristal BPSCCO-2223 dengan Metode Self-Flux Indras Marhaendrajaya Laboratorium Fisika Zat Padat Jurusan Fisika
Lebih terperinciKriteria Kontributor. Materi Naskah dan Proses Seleksi
Kriteria Kontributor 1. Kontributor adalah individu atau kelompok dengan jumlah anggota 2 sampai 3 orang. 2. Mahasiswa Universitas Indonesia program S1 dan vokasi. 3. Masih berstatus mahasiswa aktif pada
Lebih terperinciANALISA KEKUATAN BAHAN STEEL 304 TERHADAP KEKUATAN IMPAK BENDA JATUH BEBAS ABSTRAK
ANALISA KEKUATAN BAHAN STEEL 304 TERHADAP KEKUATAN IMPAK BENDA JATUH BEBAS M Bima Syah Alam 1, Din Aswan Amran Ritonga, ST, MT 2 1,2 Jurusan Teknik Mesin Sekolah Tinggi Teknik Harapan Medan 2016 E-mail
Lebih terperinciLecture #6. Dioda Semikonduktor (Semiconductor Diode) Rangkaian Peredam Sinyal (Filter) Filter lolos rendah pasif Filter lolos tinggi pasif
Lecture #6 Rangkaian Peredam Sinyal (Filter) Filter lolos rendah pasif Filter lolos tinggi pasif Dioda Semikonduktor (Semiconductor Diode) Basic electronic / Yohandri Contents : Semiconductor Theory P-N
Lebih terperinciPENGARUH PERTUKARAN ION TERHADAP FLY ASH UNTUK MEMBUAT ADITIF OIL WELL CEMENT DARI SEMEN TIPE A. Rahmat Hidayat 1 dan M.Nasikin 2.
PENGARUH PERTUKARAN ION TERHADAP FLY ASH UNTUK MEMBUAT ADITIF OIL WELL CEMENT DARI SEMEN TIPE A Rahmat Hidayat 1 dan M.Nasikin 2 1 Teknik Kimia, Fakultas Teknik, Universitas Indonesia, Depok 16424, Indonesia
Lebih terperinciTESIS MAGISTER OLEH : RM. RUSTAMAJI NIM
STUDI ANALISIS DAN EKSPERIMENTASI PERBAIKAN TANAH GAMBUT DENGAN CLEANSET CEMENT SEBAGAI ALTERNATIF PERBAIKAN TANAH DASAR UNTUK KONSTRUKSI TIMBUNAN BADAN JALAN TESIS MAGISTER OLEH : RM. RUSTAMAJI NIM. 25095012
Lebih terperinciTESIS. Oleh : SUJATMIKO NUGROHO
KARAKTERISTIK TEKNIK AGREGAT BUATAN DARI ABU TERBANG DAN PENGGUNAANNYA DALAM CAMPURAN BETON ASPAL TESIS Oleh : SUJATMIKO NUGROHO 25099116 Pembimbing : Ir. BAMBANG ISMANTO SISWOSOEBROTHO, MSc, PhD. PROGRAM
Lebih terperinciATURAN PENULISAN NASKAH ILMIAH JURNAL TEKNOVASI
ATURAN PENULISAN NASKAH ILMIAH JURNAL TEKNOVASI I. UMUM 1. Jurnal Teknovasi adalah publikasi ilmiah berkala yang terbit setiap 2 (dua) kali setahun yaitu April dan Oktober. 2. Naskah ilmiah yang diterbitkan
Lebih terperinciTEKNIK VOLTAMETRI PELUCUTAN ANODIK UNTUK PENENTUAN KADAR LOGAM Pb, Cd, DAN Cu PADA AIR LAUT PELABUHAN BENOA
TEKNIK VOLTAMETRI PELUCUTAN ANODIK UNTUK PENENTUAN KADAR LOGAM Pb, Cd, DAN Cu PADA AIR LAUT PELABUHAN BENOA SKRIPSI Oleh : I Wayan Hermawan NIM. 1108105010 JURUSAN KIMIA FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN
Lebih terperinciSeminar Material Metalurgi 2009
Seminar Material Metalurgi 2009 Tema Seminar "Penguatan Riset Material dan Metalurgi Menuju Industri yang Ramah Lingkungan" Pendahuluan Indonesia merupakan negara yang kaya akan sumber daya alam yang merupakan
Lebih terperinciMETODA FOTO BACK-REFLECTION LAUE UNTUK MENENTUKAN ARAH SUMBU KRISTAL TUNGGAL La 2-2x Sr 1+2x Mn 2 O 7 (x=0,4)
METODA FOTO BACK-REFLECTION LAUE UNTUK MENENTUKAN ARAH SUMBU KRISTAL TUNGGAL La 2-2x Sr 1+2x Mn 2 O 7 (x=0,4) Agung Imaduddin Pusat Penelitian Metalurgi LIPI Kawasan Puspiptek Serpong, Tangerang 15314
Lebih terperinciATURAN PENULISAN NASKAH ILMIAH JURNAL BIS A (BISNIS ADMINISTRASI)
ATURAN PENULISAN NASKAH ILMIAH JURNAL BIS A (BISNIS ADMINISTRASI) I. UMUM 1. Jurnal Bisnis Administrasi (Jurnal BIS-A) adalah publikasi ilmiah berkala yang terbit 2 (dua) kali setahun yaitu Juni dan Desember.
Lebih terperinciAfdal, Elio Nora Islami. Jurusan Fisika FMIPA Universitas Andalas, Padang
KARAKTERISASI MAGNETIK BATUAN BESI DARI BUKIT BARAMPUANG, NAGARI LOLO, KECAMATAN PANTAI CERMIN, KABUPATEN SOLOK, SUMATERA BARAT (MAGNETIC CHARACTERIZATION OF IRON STONE OF BARAMPUANG HILL, NAGARI LOLO,
Lebih terperinciMaterial dengan Kandungan Karbon Tinggi dari Pirolisis Tempurung Kelapa untuk Reduksi Bijih Besi
Material dengan Kandungan Karbon Tinggi dari Pirolisis Tempurung Kelapa untuk Reduksi Bijih Besi Anton Irawan, Ristina Puspa dan Riska Mekawati *) Jurusan Teknik Kimia, Fak. Teknik, Universitas Sultan
Lebih terperinciBAB I PENDAHULUAN. 1.1 Latar Belakang
BAB I PENDAHULUAN 1.1 Latar Belakang Pemakaian batubara sebagai sumber energi telah menjadi salah satu pilihan di Indonesia sejak harga bahan bakar minyak (BBM) berfluktuasi dan cenderung semakin mahal.
Lebih terperinciLenny Marcillina, Erwin, dan Tengku Emrinaldi
PENENTUAN NILAI TINGKAT KEMAGNETAN DAN SUSEPTIBILITAS MAGNETIK ENDAPAN PASIR BESI SEBAGAI FUNGSI KEDALAMAN DI PANTAI ARTA DAN PANTAI KATA PARIAMAN SUMATERA BARAT Lenny Marcillina, Erwin, dan Tengku Emrinaldi
Lebih terperinciPENGEMBANGAN KURVA t-z PADA TANAH PASIRAN BERDASARKAN HASIL UJI GESER LANGSUNG DENGAN APLIKASI PADA PONDASI BOR BER-INSTRUMEN. Tesis.
PENGEMBANGAN KURVA t-z PADA TANAH PASIRAN BERDASARKAN HASIL UJI GESER LANGSUNG DENGAN APLIKASI PADA PONDASI BOR BER-INSTRUMEN Tesis Sebagai Salah Satu Syarat untuk Menyelesaikan Program Pendidikan Magister
Lebih terperinciPENGARUH TEGANGAN DAN KONSENTRASI NaCl TERHADAP KOROSI RETAK TEGANG PADA BAJA DARI SPONS BIJIH LATERIT SKRIPSI
PENGARUH TEGANGAN DAN KONSENTRASI NaCl TERHADAP KOROSI RETAK TEGANG PADA BAJA DARI SPONS BIJIH LATERIT SKRIPSI Oleh BUDI SETIAWAN 04 03 04 015 8 DEPARTEMEN METALURGI DAN MATERIAL FAKULTAS TEKNIK UNIVERSITAS
Lebih terperinciPENENTUAN SIFAT LISTRIK AIR PADA WADAH ALUMINIUM DAN BESI BERDASARKAN PENGARUH RADIASI MATAHARI
PENENTUAN SIFAT LISTRIK AIR PADA WADAH ALUMINIUM DAN BESI BERDASARKAN PENGARUH RADIASI MATAHARI Yusuf Syetiawan, Sugianto, Riad Syech Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas
Lebih terperinciHUBUNGAN ZONA SERPENTINISASI DENGAN PENYEBARAN NIKEL LATERIT DAERAH LOJI, KABUPATEN HALMAHERA SELATAN, PROVINSI MALUKU UTARA
HUBUNGAN ZONA SERPENTINISASI DENGAN PENYEBARAN NIKEL LATERIT DAERAH LOJI, KABUPATEN HALMAHERA SELATAN, PROVINSI MALUKU UTARA OLEH Boyke Muhammad Khadafi 211090017 PROGRAM PASCASARJANA MAGISTER TEKNIK GEOLOGI
Lebih terperinciEKSTRAKSI ALUMINA DARI RESIDU BAUKSIT UNTUK BAHAN BAKU ZEOLIT SINTETIS DENGAN PRODUK SAMPING KONSENTRAT BESI
EKSTRAKSI ALUMINA DARI RESIDU BAUKSIT UNTUK BAHAN BAKU ZEOLIT SINTETIS DENGAN PRODUK SAMPING KONSENTRAT BESI Muchtar Aziz Puslitbang Teknologi Mineral dan Batubara Jl. Jend.Sudirman No. 623, Bandung Email:
Lebih terperinciPENGARUH FRAKSI BERAT SERAT TERHADAP KEKUATAN IMPACT KOMPOSIT SERAT SERABUT KELAPA DENGAN MATRIKS POLIESTER
LAPORAN TUGAS SARJANA PENGARUH FRAKSI BERAT SERAT TERHADAP KEKUATAN IMPACT KOMPOSIT SERAT SERABUT KELAPA DENGAN MATRIKS POLIESTER Diajukan sebagai salah satu tugas dan syarat untuk memperoleh gelar Strata-1
Lebih terperinciPENGARUH KOMPOSISI LARUTAN TERHADAP KANDUNGAN Mo DALAM LAPISAN PADUAN Ni-Mo SECARA ELEKTROPLATING
PENGARUH KOMPOSISI LARUTAN TERHADAP KANDUNGAN Mo DALAM LAPISAN PADUAN Ni-Mo SECARA ELEKTROPLATING Sri Mulyaningsih dan Budi Priyono Pusat Penelitian Metalurgi-LIPI E-mail : srim006@lipi.go.id Intisari
Lebih terperinciTUGAS SARJANA. SINTESIS KOMPOSIT MATRIKS LOGAM Al/SiC PADA BAHAN REM KERETA API
TUGAS SARJANA SINTESIS KOMPOSIT MATRIKS LOGAM Al/SiC PADA BAHAN REM KERETA API Diajukan sebagai salah satu tugas dan syarat untuk memperoleh gelar Strata 1 (S-1) Jurusan Teknik Mesin Fakultas Teknik Universitas
Lebih terperinciANALISA SIFAT MEKANIK PERMUKAAN BAJA ST 37 DENGAN PROSES PACK CARBURIZING, MENGGUNAKAN ARANG KELAPA SAWIT SEBAGAI MEDIA KARBON PADAT
ANALISA SIFAT MEKANIK PERMUKAAN BAJA ST 37 DENGAN PROSES PACK CARBURIZING, MENGGUNAKAN ARANG KELAPA SAWIT SEBAGAI MEDIA KARBON PADAT Ir. Kaidir. M. Eng., M.Si, 1) Rizky Arman, ST. MT 2) Julisman 3) Jurusan
Lebih terperinciABSTRAK. Kata kunci: roster, serbuk kayu, kuat tekan, metode Taguchi.
ABSTRAK Pembangunan sektor perumahan/hunian memacu berkembangnya usaha bahan bangunan terutama industri pasir-semen di daerah Godean. Salah satu produk yang dihasilkan oleh industri pasir-semen adalah
Lebih terperinciSTUDI POTENSI SEMEN ALTERNATIF DENGAN BAHAN DASAR KAPUR PADALARANG DAN FLY ASH SURALAYA
STUDI POTENSI SEMEN ALTERNATIF DENGAN BAHAN DASAR KAPUR PADALARANG DAN FLY ASH SURALAYA ABSTRAK Studi Potensi Semen Alternatif dengan Bahan Dasar Kapur Padalarang dan Fly Ash Suralaya Oleh : Erlangga
Lebih terperinci