1 PENGARUH KUAT ARUS TERHADAP KEKERASAN, STRUKTUR MIKRO DAN LAJU KOROSI LAPISAN CHROMATE COATING PADA LOGAM ALUMINIUM Oleh: Bambang Hari P 1), Y. Yulianto K 2), Martinus Heru P 3) 1); 2); 3) Jurusan Teknik Mesin, Akademi Teknologi Warga Surakarta ABSTRACT The objective of this reseach is to find out the influence of currents in the process of chhromate coating on microstructure, hardness and corrosion rate of aluminium (Al). Aluminium is coated with copper (Cu), nickel (Ni) and chromium (Cr) variated with current (60 A, 90 A, and 120 A). Corrosion rate was tested with three-electrode cell method using 0.3% NaCl solution. Micro Vickers indentation was used for measuring surface hardness with load of 10 grams and an optical microscope is used to observe crosssectional microstructure. The highest value of surface hardness and the lowest corrosion rate are obtained on specimens of Al/Cu/Ni/Cr with the current 90 A. Increasing current can improve 1,10 mmpy corrosion rate and 571 VHN surface hardness of the specimen. However, the optimum currents is 90 A, if currents is increased again it can increase the corrosion rate and decrease the surface hardness of the specimen. Figures from microstructure observation of the specimen cross-section show tight thin layer on the specimen surface, so this layer can inhibit corrosion and increase the surface hardness of the specimen. Key words: Chromate coating, aluminium, corrosion resistance. I. PENDAHULUAN Sifat dari logam aluminium perlu ditingkatkan lagi dengan cara merekayasa sifat dari logam aluminium, salah satunya dengan proses perlakuan permukaan. Dengan proses perlakuan permukaan diharapkan sifat-sifat dari logam aluminium dapat ditingkatkan demikian juga dengan penampilannya. Salah satu cara dari proses perlakuan permukaan adalah dengan chromate coating. Proses chromate coating mempunyai keunggulan karena dapat dilakukan pada suhu kamar sehingga tidak menimbulkan distorsi atau perubahan struktur pada substrate. Permukaan dari substrate akan dikonversi dalam bentuk lapisan tipis chromate setelah dicelupkan ke dalam larutan chromic acid, chromic salt atau larutan kimia lainnya yang telah diberi aliran arus listrik DC. Arus listrik akan mengalir pada larutan ini sehingga ion-ion dari larutan akan menempel pada permukaan substrate. Untuk memperoleh hasil yang optimal, pada permukaan substrate harus dalam kondisi bersih saat proses pelapisan berlangsung. Dengan memberikan sirkulasi pada larutan elektrolit juga akan dapat memberikan hasil yang lebih optimal, karena proses pelekatan ion-ion dari larutan elektrolit pada permukaan substrate dapat berlangsung lebih merata. Substrate yang dipakai disini adalah logam aluminium dan penggunaan dari chromate coating bertujuan untuk proteksi terhadap korosi serta untuk keperluan decorative. Penelitian ini dilakukan dengan tujuan untuk : 1. Menganalisa pengaruh proses chromate coating pada logam aluminium dengan memvariasi kuat arus yang digunakan. 2. Mengetahui pengaruh lapisan chromate terhadap sifat-sifat dari logam aluminium ditinjau dari struktur mikro, kekerasan permukaan dan ketahanan korosinya. II. BAHAN DAN METODE A. BAHAN DAN PERALATAN Teknika ATW(2013) halaman 1
2 Bahan yang digunakan dalam penelitian : 1. Logam aluminium murni Digunakan sebagai spesimen yang berbentuk lingkaran dengan diameter 14 mm dan tebal 2 mm. Logam ini sebagai bahan yang dilapisi (katoda). 2. Amplas ukuran 600 sampai dengan 2000 mesh Digunakan untuk menghaluskan permukaan spesimen. 3. Autosol metal polish Digunakan untuk finishing dalam penghalusan permukaan spesimen agar diperoleh permukaan spesimen yang benar-benar halus dan mengkilap. 4. Alkohol Digunakan untuk membersihkan permukaan spesimen agar benar-benar bersih dari kotoran. 5. Larutan elektrolit Larutan cooper sulfate sebagai larutan elektrolit dalam proses pelapisan Cu. Larutan Watt s sebagai larutan elektrolit dalam proses pelapisan Ni. Larutan chromic acid sebagai larutan elektrolit dalam proses pelapisan Cr. 6. Anoda Tembaga (Cu), Nikel (Ni), Timbal (Pb) sebagai anoda dalam proses pelapisan. Peralatan yang digunakan dalam penelitian : 1. Alat punching berukuran diameter 14 mm Digunakan untuk memotong plat aluminium dengan tebal 2 mm, sehingga diperoleh spesimen berbentuk lingkaran berdiameter 14 mm dengan ketebalan 2 mm. 2. Alat proses chromate coating Gambar 1. Alat proses chromate coating 3. Alat uji kekerasan Menggunakan alat uji merk Buchler Micromet 2100 series, beban indentor 10 gr dengan waktu pembebanan 10 detik. 4. Alat uji korosi Menggunakan alat uji Potensiostat/Galvanostat PGS 201 T, dengan rentang tegangan mv s/d 2000 mv dan rentang arus 200 na s/d 2 A. 5. Alat uji komposisi bahan Pengujian komposisi bahan menggunakan alat Desktop Metals Analyser dengan merk Metalscan 2500 series. Elektron ditembakkan pada permukaan sampel, yang kemudian akan memancarkan X-Ray yang menunjukkan karakterisasi masing-masing unsur yang Teknika ATW(2013) halaman 2
3 akan ditangkap oleh detektor, kemudian secara otomatis akan diolah secara komputerisasi sehingga diperoleh data tentang unsur-unsur yang terkandung dalam sampel tersebut. 6. Alat uji struktur mikro Pengujian struktur mikro menggunakan mikroskop optik merk Olympus dan menggunakan larutan Asam Fluorida (HF 4,8 %) untuk mengetsa spesimen B. KAJIAN PUSTAKA Bhatt (2009) mengemukakan bahwa korosi adalah degradasi atau kerusakan komponen logam karena reaksi dengan lingkungan. Lapisan kromium konversi coating diterapkan untuk passivate permukaan logam agar dapat memperlambat dan mencegah proses korosi. Adnyani, dkk (2009) mengemukakan bahwa kekerasan permukaan berdasarkan hasil uji kekerasan Vickers akan semakin meningkat dengan naiknya kuat arus dan bertambahnya titik distribusi arus. Syamsa dan Santoso (2007) mengemukakan proses pelapisan nikel dengan menggunakan arus listrik (electroplating), semakin besar rapat arus dan semakin tinggi temperatur yang digunakan maka semakin tebal lapian nikel yang dihasilkan. Dobreva, dkk (2002) melakukan penelitian perlindungan korosi oleh lapisan tembaga, nikel dan krom. Superposisi dari tembaga, nikel dan krom membentuk pelindung multilayer yang bersifat dekoratif dan menjadi perlindungan terbaik terhadap korosi. Pengujian kekerasan bahan bertujuan untuk menentukan ketahanan suatu bahan terhadap deformasi plastis apabila bahan tersebut diberi beban dari luar. Pengujian kekerasan bahan pada penelitian ini menggunakan metode indentasi mikro Vickers, dimana pada permukaan material diberi bebas sebesar 10 gram. Indentor berbentuk piramida intan dengan sudut antara pemukaan berlawanan 136 o. Nilai kekerasan Vickers dinyatakan dengan rumus (ASM Metals HandBook Vol.8) P VHN 1,854 (kg/mm 2 ) 2 d Dimana, P = beban terpasang (kg) d = diagonal bekas injakan penetrator (mm) Pengujian laju korosi dilakukan dengan pengamatan intensitas arus korosi (Icorr) benda uji di dalam lingkungan Natrium Chlorida (NaCl) 0,3%. Ketepatan penentuan harga Icorr sangat penting karena Icorr berbanding langsung dengan besarnya laju korosi suatu logam di dalam lingkungannya. Perhitungan untuk mengetahui laju korosi dari percobaan ini dapat menggunakan metode berdasarkan kurva potensial vs log intensitas arus korosi (Muhammad, 2009). Gambar 2. Kurva potensial vs log intensitas arus Teknika ATW(2013) halaman 3
4 Harga laju korosi dapat ditentukan berdasarkan harga dari rapat arus korosi, dimana harga laju korosi suatu logam dalam lingkungannya sebanding dengan harga rapat arus korosi. Sesuai dengan persamaan laju korosi (Jones, 1991), seperti berikut ini: ai r 0, nd Dengan, r = laju korosi (mmpy) a = berat atom i = rapat arus korosi (µa/cm 2 ) n = valensi atom D = berat jenis spesimen (gr/cm 3 ) C. METODE PENELITIAN Bahan yang digunakan dalam penelitian ini adalah logam aluminium murni yang mempunyai komposisi (99,52 % Al; 0,102 % Si; 0,237 % Fe; 0,098 % Mn; 0,052 % Mg ; 0,066 % Ni; 0,051 % Sr; 0,217 % Ti; 0,146 % Ca; 0,166 % V dan 0,17 % Zr). Spesimen dipotong berbentuk lingkaran dengan diameter 14 mm dan tebal 2 mm menggunakan alat punch. Spesimen dilapisi dengan tiga lapisan yaitu: Cu, Ni dan Cr, menggunakan proses chromate coating dengan variasi kuat arus 60, 90 dan 120 A, menggunakan waktu pelapisan 5 detik dan tegangan 6 V. Pengujian komposisi bahan menggunakan Desktop Metals Analyser dengan merk Metalscan 2500 series. Mula Persiapan Spesimen Al d = 14 mm, Uji Tanpa pelapisan Pelapisan Cu V = 6 V; t = 5 detik; I = 60 A Pelapisan Cu/Ni V = 6 V; t = 10 menit; I = 60 A Pelapisan Cu/Ni/Cr V = 6 V; t = 5 detik; Uji Laju Korosi Uji Kekerasan P = 10 gr ; t = 10 Nilai Uji Struktur Analisis Data Kesimpulan Sele Gambar 3. Diagram alir penelitian Teknika ATW(2013) halaman 4
5 Pengujian kekerasan menggunakan alat dengan merk Buchler Micromet 2100 series, beban indentor 10 gram dengan waktu pembebanan 10 detik. Pengujian laju korosi menggunakan alat Potensiostat / Galvanostat PGS 201 T, dengan rentang tegangan mv s/d 2000 mv dan rentang arus 200 na s/d 2 A. Pengujian struktur mikro menggunakan mikroskop optik merk Olympus dan menggunakan larutan Asam Fluorida (HF 48 %) untuk mengetsa spesimen. III. ASIL DAN PEMBAHASAN A. Uji Kekerasan Spesimen Gambar 4. Perbandingan kekerasan permukaan spesimen Proses chromate coating dengan variasi kuat arus menyebabkan perbedaan nilai kekerasan pada spesimen. Kekerasan spesimen mempunyai nilai optimum pada spesimen Al-Cu-Ni-Cr dengan arus 90 A sebesar 571 VHN 0,01 yang ditunjukkan pada gambar 4. Dalam hal ini kuat arus berfungsi sebagai pemindah ion-ion krom menempel pada spesimen, semakin tinggi kuat arus maka semakin cepat ion-ion krom menempel pada permukaan spesimen, sehingga lapisan krom lebih padat yang menyebabkan kekerasan permukaan pada spesimen meningkat. Kuat arus mempunyai nilai yang optimal pada arus 90 A dan apabila dinaikkan lagi dapat mengurangi kekerasan permukaan spesimen. Hal ini disebabkan ion-ion krom yang menempel pada permukaan spesimen mempunyai sifat jenuh sehingga dapat merusak ikatan lapisan spesimen yang mengakibatkan penurunan kekerasan spesimen B. Pengujian Laju Korosi I cor Spesimen Gambar 5. Perbandingan Laju Korosi Teknika ATW(2013) halaman 5
6 Pada gambar 5, nilai ketahanan korosi optimum pada spesimen Al-Cu-Ni-Cr diperoleh pada penggunaan arus 90 A, yaitu sebesar 1,10 mmpy. Hal ini disebabkan spesimen mempunyai lapisan yang lebih rapat, sehingga logam induk akan lebih terlindung dari korosi dimana larutan pengkorosif sukar masuk untuk mengkorosi logam induk. C. Pengujian Struktur Mikro substrat 100µm Gambar 6. Struktur mikro penampang melintang pada spesimen Berdasarkan hasil uji laju korosi dan uji kekerasan diperoleh spesimen Al-Cu-Ni-Cr dengan arus 90 A yang mempunyai nilai optimum. Gambar 6, menunjukkan penampang melintang dari spesimen, dimana setiap satu strip mempunyai ketebalan 10 µm sehingga tebal lapisan sekitar 15 µm. Dengan adanya lapisan plating diatas permukaan specimen/logam alumunium menyebabkan permukaan spesimen lebih rapat sehingga dapat meningkatkan ketahanan terhadap korosi. IV. SIMPULAN 1. Proses chromate coating pada logam aluminium dapat meningkatkan kekerasan permukaan alumunium. Nilai kekerasan permukaan pada spesimen Al sebesar 35 VHN0,01. Peningkatan nilai kekerasan optimum sebesar 571 VHN0,01 terjadi pada spesimen Al yang dilapisi Cu, Ni dan Cr dengan arus 90 A. 2. Proses chromate coating pada logam aluminium dapat menurunkan laju korosi dalam media larutan 0,3% NaCl. Nilai laju korosi pada spesimen Al sebesar 3,31 mmpy. Penurunan nilai laju korosi optimum sebesar 1,10 mmpy terjadi pada spesimen Al yang dilapisi Cu, Ni dan Cr dengan arus 90 A. Struktur mikro pada spesimen Al yang dilapisi Cu, Ni dan Cr dengan arus 90 A menunjukkan adanya lapisan pasif yang rapat dengan ketebalan sekitar 15 µm. Dengan adanya lapisan pasif ini dapat meningkatkan kekerasan permukaan logam aluminium dan menurunkan laju korosi. V. DAFTAR PUSTAKA [1] Adnyani, I.A.S., Triadi, A. A. A., 2009, Pengaruh Kuat Dan Distribusi Arus Terhadap Ketebalan dan Kekerasan Lapisan Krom pada Stoneware Dan Earthenware, Jurnal Publikasi Vol. 8 No.2 Juli- Desember [2] ASM Metals HandBook Volume 8, 2000, Mechanical Testing and Evaluation. [3] ASM, 1987, Metals Handbooks Corrosion, Vol 13, Ninth Edition, ASM International Park, Ohio. [4] Bhatt H.2009,Trivalent Chromium Conversion Coating for Corrosion Protection of Aluminum Surface. [5] Jones, D.A.1991, Principles and Prevention of Corrosion, Mc Milman Publishing Company, New York. [6] Muhammad, 2009, Pengaruh Implantasi Ion Titanium Nitride (TiN) terhadap Laju Korosi pada baja VCL 140 dalam Lingkungan NaCI 0,5 %. [7] Syamsa, M., Santoso, B., 2007, Pengaruh Parameter Proses Pelapisan Nikel Terhadap Ketebalan Lapisan, Jurnal Teknik Mesin Vol. 9, No. 1, April 2007: Teknika ATW(2013) halaman 6
PENGARUH WAKTU ELEKTROPLATING NIKEL-CHROM TERHADAP KEKERASAN BAJA STAINLESS STEEL AISI 304
PENGARUH WAKTU ELEKTROPLATING NIKEL-CHROM TERHADAP KEKERASAN BAJA STAINLESS STEEL AISI 304 Nani Mulyaningsih 1, Priyo Tri Iswanto 2, Soekrisno 2 1 Mahasiswa Pasca Sarjana Jurusan Teknik Mesin dan Industri,
Lebih terperinciPENGARUH KONSENTRASI LARUTAN DAN WAKTU PELAPISAN NIKEL PADA ALUMINIUM TERHADAP KEKERASAN
PENGARUH KONSENTRASI LARUTAN DAN WAKTU PELAPISAN NIKEL PADA ALUMINIUM TERHADAP KEKERASAN Reny Afriany 1, Kusmono 2, R. Soekrisno 2 1 Mahasiswa Pasca Sarjana Teknik Mesin, Jurusan Teknik Mesin dan Industri,
Lebih terperinciVARIASI WAKTU HARD CHROMIUM PLATING TERHADAP KARAKTERISTIK STRUKTUR MIKRO, NILAI KEKERASAN DAN LAJU KOROSI BAJA KARBON RENDAH
C.11. Variasi waktu hard chromium plating (Sutrisno) VARIASI WAKTU HARD CHROMIUM PLATING TERHADAP KARAKTERISTIK STRUKTUR MIKRO, NILAI KEKERASAN DAN LAJU KOROSI BAJA KARBON RENDAH Sutrisno Program Studi
Lebih terperinciBAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3.1. Diagram Alir Penelitian Untuk mempermudah penelitian proses anodizing maka dibuat diagram alir penelitian proses anodizing, dapat ditunjukkan pada Gambar 3.1. Mulai Observasi
Lebih terperinciPENGARUH VARIASI TEGANGAN DAN WAKTU PELAPISAN TERHADAP KEKILAPAN, KEKERASAN DAN KEKASARAN PERMUKAAN ALUMINIUM
KURVATEK Vol.1. No.1, April, pp.1-6 e-issn: 2477-7870 1 PENGARUH VARIASI TEGANGAN DAN WAKTU PELAPISAN TERHADAP KEKILAPAN, KEKERASAN DAN KEKASARAN PERMUKAAN ALUMINIUM Ade Irvan Tauvana 1,a 1. Politeknik
Lebih terperinciPENINGKATAN KUALITAS PRODUK INDUSTRI KECIL PERALATAN RUMAH TANGGA DENGAN PELAPISAN LOGAM
PENINGKATAN KUALITAS PRODUK INDUSTRI KECIL PERALATAN RUMAH TANGGA DENGAN PELAPISAN LOGAM Nani Mulyaningsih Program Studi Teknik Mesin, Fakultas Teknik, Universitas Tidar Jl. Kapten Suparman No 39 Magelang
Lebih terperinciDAFTAR ISI LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL...
DAFTAR ISI Halaman LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL... DAFTAR LAMPIRAN... i ii iii iv v vi ix xi xii BAB 1
Lebih terperinciTUGAS AKHIR KARAKTERISASI PERMUKAAN MULTILAPIS KROM DAN TEMBAGA PADA BAJA KARBON HASIL PROSES ELECTROPLATING
TUGAS AKHIR KARAKTERISASI PERMUKAAN MULTILAPIS KROM DAN TEMBAGA PADA BAJA KARBON HASIL PROSES ELECTROPLATING Disusun Sebagai Syarat Untuk Mencapai Gelar Sarjana Teknik Jurusan Teknik Mesin Fakultas Teknik
Lebih terperinciBAB IV HASIL DAN ANALISA. pengujian komposisi material piston bekas disajikan pada Tabel 4.1. Tabel 4.1 Hasil Uji Komposisi Material Piston Bekas
BAB IV HASIL DAN ANALISA 4.1 Hasil Pengujian Komposisi Bahan Hasil uji komposisi menunjukan bahwa material piston bekas mempunyai unsur paduan utama 81,60% Al dan 13,0910% Si. Adapun hasil lengkap pengujian
Lebih terperinciBAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3.1.1. Tempat penelitian Penelitian dilakukan di Laboratorium Material Jurusan Teknik Mesin Universitas Sebelas Maret Surakarta 3.1.2. Alat dan bahan 3.2.1 Alat Alat yang dipergunakan
Lebih terperinciBAB IV ANALISA DAN PEMBAHASAN
BAB IV ANALISA DAN PEMBAHASAN 4.1. Hasil Anodizing Hasil anodizing aluminium 1XXX dengan variasi intensitas arus 0,016A/mm 2, 0,022A/mm 2, 0,028A/mm² dan waktu pencelupan 10 menit, terdapat kegagalan atau
Lebih terperinciPUBLIKASI ILMIAH. Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan Teknik Mesin Fakultas Teknik.
STUDI PELAPISAN KROM PADA BAJA KARBON DENGAN RAPAT ARUS 5 AMPERE TEGANGAN 12 VOLT DAN VARIASI WAKTU PENCELUPAN 10, 20, 30, 40 DAN 50 MENIT UNIVERSITAS MUHAMMADIYAH SURAKARTA PUBLIKASI ILMIAH Disusun sebagai
Lebih terperinciBAB I PENDAHULUAN. material lainnya yang dipergunakan sehari-hari memerlukan proses. penyelesaian akhir sebelum digunakan. Proses ini disebut dengan
BAB I PENDAHULUAN 1.1 Latar Belakang Setiap benda logam baik baja, besi maupun aluminium dan material lainnya yang dipergunakan sehari-hari memerlukan proses penyelesaian akhir sebelum digunakan. Proses
Lebih terperinciBAB I PANDAHULUAN. Berbagai industri barang perhiasan, kerajinan, komponen sepeda. merupakan pelapisan logam pada benda padat yang mempunyai
BAB I PANDAHULUAN 1.1 Latar Belakang Kehidupan modern tak lepas dari peranan industri elektroplating. Berbagai industri barang perhiasan, kerajinan, komponen sepeda motor, mobil, mesin, barang elektronik,
Lebih terperinciPENGARUH CAIRAN TUBUH MANUSIA TERHADAP KOROSI PADA PLAT PENYAMBUNG TULANG
Pengaruh Cairan Tubuh Manusia... (Nani Mulyaningsih) PENGARUH CAIRAN TUBUH MANUSIA TERHADAP KOROSI PADA PLAT PENYAMBUNG TULANG Nani Mulyaningsih Dosen Jurusan Teknik Mesin, Fakultas Teknik, Universitas
Lebih terperinciPengaruh Jarak Anoda-Katoda dan Durasi Pelapisan Terhadap Laju Korosi pada Hasil Electroplating Hard Chrome
JTERA - Jurnal Teknologi Rekayasa, Vol. 1, No. 1, Desember 2016, Hal. 1-6 ISSN 2548-737X Pengaruh Jarak Anoda-Katoda dan Durasi Pelapisan Terhadap Laju Korosi pada Hasil Electroplating Hard Chrome Abid
Lebih terperinciBAB I PENDAHULUAN. 1.1 Latar Belakang. Proses akhir logam (metal finishing) merupakan bidang yang sangat luas,
BAB I PENDAHULUAN 1.1 Latar Belakang Proses akhir logam (metal finishing) merupakan bidang yang sangat luas, yang dimana tujuan utamanya adalah untuk mencegah logam dengan korosifnya, namun juga mendapatkan
Lebih terperinciPENINGKATAN KETAHANAN KOROSI BAJA JIS S45C HASIL ELECTROPLATING NIKEL PADA APLIKASI MATERIAL CRYOGENIC
PENINGKATAN KETAHANAN KOROSI BAJA JIS S45C HASIL ELECTROPLATING NIKEL PADA APLIKASI MATERIAL CRYOGENIC Mirza Pramudia 1 1 Fakultas Teknik, Universitas Trunojoyo, Madura Jl. Raya Telang, Po. Box 2 Kamal,
Lebih terperinciPENGARUH KUAT ARUS PADA PROSES ANODIZING TERHADAP KARAKTERISTIK VELG MOBIL MERK BSA
34 PENGARUH KUAT ARUS PADA PROSES ANODIZING TERHADAP KARAKTERISTIK VELG MOBIL MERK BSA Hanung Hermawan 1), Nani Mulyaningsih 2), Catur Pramono 3) 1 Jurusan Teknik Mesin, Fakultas Teknik, Universitas Tidar
Lebih terperinciBAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN 3.1 Tempat Penelitian Proses pelapisan plastik ABS dengan menggunakan metode elektroplating dilaksanakan di PT. Rekayasa Plating Cimahi, sedangkan pengukuran kekasaran, ketebalan
Lebih terperinciBAB III METODE PENELITIAN. 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik
BAB III METODE PENELITIAN 3.1 Tempat dan Waktu Pelaksanaan Waktu dan tempat analisis sebagai berikut : 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik Departemen Teknik Mesin Sekolah
Lebih terperinciSTUDI EKSPERIMENTAL TENTANG PENGARUH VARIASI RAPAT ARUS PADA HARD CHROME ELECTROPLATING TERHADAP KARAKTERISTIK PERMUKAAN BAJA KARBON RENDAH
STUDI EKSPERIMENTAL TENTANG PENGARUH VARIASI RAPAT ARUS PADA HARD CHROME ELECTROPLATING TERHADAP KARAKTERISTIK PERMUKAAN BAJA KARBON RENDAH Harnowo Supriadi Staf Pengajar Jurusan Teknik Mesin, Fakultas
Lebih terperinciSTUDI PELAPISAN KROM PADA BAJA KARBON DENGAN VARIASI WAKTU PENCELUPAN 10, 20, 30, 40, 50 MENIT DAN TEGANGAN 9 VOLT DENGAN ARUS 5 AMPERE
STUDI PELAPISAN KROM PADA BAJA KARBON DENGAN VARIASI WAKTU PENCELUPAN 10, 20, 30, 40, 50 MENIT DAN TEGANGAN 9 VOLT DENGAN ARUS 5 AMPERE Disusun Sebagai Syarat Untuk Mencapai Gelar Sarjana Teknik Jurusan
Lebih terperinciBAB III METODOLOGI PENELITIAN. 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik
BAB III METODOLOGI PENELITIAN 3.1.Tempat dan Waktu Pelaksanaan Waktu dan tempat analisis sebagai berikut : 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik Departemen Teknik Mesin Sekolah
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
39 BAB IV HASIL DAN PEMBAHASAN 4.1. Hasil Pengujiaan 4.1.1. Pengujian Ketebalan Lapisan Dengan Coating Gauge Pengujian ini dilakukan untuk mengetahui tebal lapisan yang terdapat pada spesimen dengan menggunakan
Lebih terperinciBAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN 3.1 Persiapan sampel Sampel yang digunakan adalah pelat baja karbon rendah AISI 1010 yang dipotong berbentuk balok dengan ukuran 55mm x 35mm x 8mm untuk dijadikan sampel dan
Lebih terperinciBAB I PENDAHULUAN 1.1 Latar belakang
BAB I PENDAHULUAN 1.1 Latar belakang Dalam proses pembuatan komponen-komponen atau peralatan-peralatan permesinan dan industri, dibutuhkan material dengan sifat yang tinggi maupun ketahanan korosi yang
Lebih terperinciBAB I PENDAHULUAN. Dalam teknologi pengerjaan logam, proses electroplating. dikategorikan sebagai proses pengerjaan akhir (metal finishing).
BAB I PENDAHULUAN 1.1. Latar Belakang Masalah Dalam teknologi pengerjaan logam, proses electroplating dikategorikan sebagai proses pengerjaan akhir (metal finishing). Secara sederhana, electroplating dapat
Lebih terperinciGambar 4.1 Hasil anodizing aluminium 1XXX dengan suhu elektrolit o C dan variasi waktu pencelupan (a) 5 menit. (b) 10 menit. (c) 15 menit.
BAB IV ANALISA DAN PEMBAHASAN 1.1. Hasil Anodizing Hasil anodizing spesimen aluminium 1XXX dengan suhu elektrolit yang dijaga antara 40-45 o C dan waktu pencelupan anodizing selama 5, 10 dan 15 menit dapat
Lebih terperinciPengaruh Parameter Proses Pelapisan Nikel Terhadap Ketebalan Lapisan
Pengaruh Parameter Proses Pelapisan Nikel Terhadap Ketebalan Lapisan Bambang Santosa dan Martijanti Syamsa Jurusan Teknik Mesin, Universitas Jenderal Achmad Yani, Bandung Email: martijanti@yahoo.co.id
Lebih terperinciPENGARUH VARIASI WAKTU ANODIZING TERHADAP STRUKTUR PERMUKAAN, KETEBALAN LAPISAN OKSIDA DAN KEKERASAN ALUMINIUM 1XXX. Sulaksono Cahyo Prabowo
1 PENGARUH VARIASI WAKTU ANODIZING TERHADAP STRUKTUR PERMUKAAN, KETEBALAN LAPISAN OKSIDA DAN KEKERASAN ALUMINIUM 1XXX Sulaksono Cahyo Prabowo Jurusan Teknik Mesin Fakultas Teknik Universitas Muhammadiyah
Lebih terperinciPENGARUH SUHU LARUTAN ELEKTROLIT DAN WAKTU PELAPISAN TEMBAGA PADA PLAT BAJA LUNAK TERHADAP NILAI KETEBALAN ABSTRACT
PENGARUH SUHU LARUTAN ELEKTROLIT DAN WAKTU PELAPISAN TEMBAGA PADA PLAT BAJA LUNAK TERHADAP NILAI KETEBALAN B a s m a l Teknik Otomotif, Politeknik Pratama Mulia, Surakarta 57149, Indonesia ABSTRACT Effect
Lebih terperinciVARIASI RAPAT ARUS DALAM PROSES PELAPISAN KHROMIUM KERAS PADA CINCIN TORAK. Yusep Sukrawan 1
VARIASI RAPAT ARUS DALAM PROSES PELAPISAN KHROMIUM KERAS PADA CINCIN TORAK Yusep Sukrawan 1 ABSTRAK VARIASI RAPAT ARUS DALAM PROSES PELAPISAN KHROMIUM KERAS PADA CINCIN TORAK. Pelapisan khromium keras
Lebih terperinciMomentum, Vol. 13, No. 2, Oktober 2017, Hal ISSN
Momentum, Vol. 13, No. 2, Oktober 217, Hal. 19-24 ISSN 216-7395 PENGARUH TEGANGAN PELAPISAN NIKEL PADA TEMBAGA DALAM PELAPISAN KHROM DEKORATIF TERHADAP KETEBALAN, KEKERASAN DAN KEKASARAN LAPISAN Musa Assegaff
Lebih terperinciSTUDI EKONOMIS PENGARUH POST WELD HEAT TREATMENT TERHADAP UMUR PIPA
STUDI EKONOMIS PENGARUH POST WELD HEAT TREATMENT TERHADAP UMUR PIPA OLEH : NICKY ERSANDI NRP. 4105 100 041 DOSEN PEMBIMBING : DONY SETYAWAN, ST., M.Eng 1. PENDAHULUAN A. Latar belakang Material kapal harus
Lebih terperinciPELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL
PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL Firlya Rosa. S.S.T., M.T. 1 Jurusan Teknik Mesin, Fakultas Teknik Universitas Bangka Belitung firlya@ubb.ac.id 1 Rodiawan, S.T.,
Lebih terperinciBAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN 3.1. DIAGRAM ALIR PENELITIAN Penelitian yang dilakukan sesuai dengan diagram alir yang ditunjukkan pada gambar 3.1 Gambar 3.1. Diagram alir penelitian 3.2. ALAT DAN BAHAN
Lebih terperinciPELAPISAN STAINLESS STEEL AISI 304 MENGGUNAKAN NIKEL (Ni) MELALUI PROSES ELEKTROPLATING
PELAPISAN STAINLESS STEEL AISI 4 MENGGUNAKAN NIKEL (Ni) MELALUI PROSES ELEKTROPLATING Yoga Setiawan Ady N, Sulistyo Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik, Universitas Diponegoro Dosen Jurusan
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN. a) b) c) d)
BAB IV HASIL DAN PEMBAHASAN 4.1 Hasil dan Pembahasan Permukaan Spesimen Shot Peening Spesimen SS AISI 316 yang diberi perlakuan shot peening memiliki pengaruh terhadap permukaan sesuai dengan variasi yang
Lebih terperinciBAB IV METODE PENELITIAN. Start
BAB IV METODE PENELITIAN 4.1 Rancangan Penelitian Secara umum rancangan penelitian dapat digambarkan sebagai berikut : Start Studi literatur Jurnal, Text book Persiapan alat dan bahan Pembentukan spesimen
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1 Hasil Proses Shot peening Perlakuan shot peening pada material stainlees steel 304 memiliki pengaruh yang dapat dilihat pada gambar 4.1.(a) raw material, material sebelum
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1. Analisa Laju Korosi Stainless Steel AISI 304 Pengujian terhadap impeller dengan material baja tahan karat AISI 304 dengan media limbah pertambangan batu bara di BATAN Puspitek
Lebih terperinciPeningkatan Ketahanan Korosi Pada Material Biomedik Plat Penyambung Tulang SS 304 Dengan Gabungan Metode Shot peening dan Electroplating Ni-Cr
160 JURNAL ILMIAH SEMESTA TEKNIKA Vol. 18, No. 2, 160-167, November 2015 Peningkatan Ketahanan Korosi Pada Material Biomedik Plat Penyambung Tulang SS 304 Dengan Gabungan Metode Shot peening dan Electroplating
Lebih terperinciANALISA PERBEDAAN SIFAT MEKANIK DAN STRUKTUR MIKRO PADA PISTON HASIL PROSES PENGECORAN DAN TEMPA
ANALISA PERBEDAAN SIFAT MEKANIK DAN STRUKTUR MIKRO PADA PISTON HASIL PROSES PENGECORAN DAN TEMPA Ahmad Haryono 1*, Kurniawan Joko Nugroho 2* 1 dan 2 Jurusan Teknik Mesin, Politeknik Pratama Mulia Surakarta
Lebih terperinciPELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL
1 PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL Firlya Rosa. S. 1 Jurusan Teknik Mesin, Fakultas Teknik Universitas Bangka Belitung firlya@ubb.ac.id 1 Rodiawan, 2 Jurusan Teknik
Lebih terperinciPENGARUH PENGERJAAN DINGIN TERHADAP KETAHANAN KOROSI AISI 1020 HASIL ELEKTROPLATING Zn DI MEDIA NaCl. Oleh : Shinta Risma Ingriany ( )
SIDANG TUGAS AKHIR PENGARUH PENGERJAAN DINGIN TERHADAP KETAHANAN KOROSI AISI 1020 HASIL ELEKTROPLATING Zn DI MEDIA NaCl Oleh : Shinta Risma Ingriany (2706100025) Dosen Pembimbing : Prof. Dr. Ir. Sulistijono,
Lebih terperinciBAB III METODE PENELITIAN
BAB III METODE PENELITIAN Pada penelitian ini penulis meneliti tentang pengaruh penahanan waktu pemanasan (holding time) terhadap kekerasan baja karbon rendah pada proses karburasi dengan menggunakan media
Lebih terperinciBAB I PENDAHULUAN. ragam, oleh sebab itu manusia dituntut untuk semakin kreatif dan produktif dalam
BAB I PENDAHULUAN 1.1 Latar Belakang Penerapan teknologi rekayasa material saat ini semakin bervariasi hal ini disebabkan oleh tuntutan untuk memenuhi kebutuhan manusia yang beraneka ragam, oleh sebab
Lebih terperinciPENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH
PENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH NASKAH PUBLIKASI Diajukan guna memenuhi sebagian syarat memperoleh derajat sarjana S1
Lebih terperinciIII. METODOLOGI PENELITIAN. Penelitian ini dilaksanakan dari bulan Oktober 2014 sampai Juni 2015di
III. METODOLOGI PENELITIAN A. Tempat dan Waktu Penelitian Penelitian ini dilaksanakan dari bulan Oktober 2014 sampai Juni 2015di Laboratorium Material Teknik Mesin Fakultas Teknik Universitas Lampung.
Lebih terperinciBAB III PROSEDUR PENELITIAN. Penelitian ini dilakukan sesuai dengan diagram alir berikut ini : Pelat Baja Tipe SPHC JIS G Pembuatan Spesimen Uji
BAB III PROSEDUR PENELITIAN Penelitian ini dilakukan sesuai dengan diagram alir berikut ini : Mulai Pelat Baja Tipe SPHC JIS G 3131 Pembuatan Spesimen Uji Proses Pretreatment Proses Hot Dip Galvanis :
Lebih terperinciPENGARUH TEMPERATUR PERLAKUAN PANAS HASIL PELAPISAN Cu-Ni PADA BAJA KARBON ST-37 TERHADAP SIFAT MEKANIK
PENGARUH TEMPERATUR PERLAKUAN PANAS HASIL PELAPISAN Cu-Ni PADA BAJA KARBON ST-37 TERHADAP SIFAT MEKANIK Ir. Agus Solehudin, M.T. 1) Drs. H. Uum Sumirat, M.Pd., M.T. 1) ABSTRAK Peningkatan karakteristik
Lebih terperinciBAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3.1 Tempat Penelitian Penelitian dilakukan di INLASTEK (Institut Las Teknik) Surakarta dan Laboratorium Material Jurusan Teknik Mesin Fakultas Teknik Universitas Sebelas Maret
Lebih terperinciPENGARUH VARIASI RAPAT ARUS TERHADAP KETEBALAN LAPISAN ELEKTROPLATING SENG PADA BAJA KARBON RENDAH. Nizam Effendi *)
PENGARUH VARIASI RAPAT ARUS TERHADAP KETEBALAN LAPISAN ELEKTROPLATING SENG PADA BAJA KARBON RENDAH Nizam Effendi *) Abstrak Tujuan penelitian ini adalah untuk mengetahui pengaruh variasi rapat arus terhadap
Lebih terperinciBAB III METODE PENELITIAN dan dilaksanakan di Laboratorium Fisika Material Departemen Fisika
BAB III METODE PENELITIAN 3.1. Tempat dan Waktu Penelitian Kegiatan penelitian ini dilakukan pada bulan Maret sampai dengan Juli 2011 dan dilaksanakan di Laboratorium Fisika Material Departemen Fisika
Lebih terperinciBAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN 3.1. DIAGRAM ALIR PENELITIAN Gambar 3.1 Diagram Alir Penelitian 38 3.2. ALAT DAN BAHAN 3.2.1 Alat Gambar 3.2 Skema Peralatan Penelitian Die Soldering 3.2.2 Bahan Bahan utama
Lebih terperinciPengaruh Rapat Arus Terhadap Ketebalan Dan Struktur Kristal Lapisan Nikel pada Tembaga
ISSN:2089 0133 Indonesian Journal of Applied Physics (2012) Vol.2 No.1 halaman 1 April 2012 Pengaruh Rapat Arus Terhadap Ketebalan Dan Struktur Kristal Lapisan Nikel pada Tembaga ABSTRACT Setyowati, Y.
Lebih terperinciPENGARUH ARUS PADA PROSES ANODISASI ALUMINUM TERHADAP KETEBALAN LAPISAN OKSIDA DAN LAJU KOROSI
PENGARUH ARUS PADA PROSES ANODISASI ALUMINUM TERHADAP KETEBALAN LAPISAN OKSIDA DAN LAJU KOROSI Agung Setyo Darmawan 1, Tri Widodo Besar Riyadi 2 1 Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah
Lebih terperinciJURNAL MER-C NO. 10/VOL. 1/2018
PENGARUH VARIASI BEBAN INDENTOR VICKERS HARDNESS TESTER TERHADAP HASIL UJI KEKERASAN MATERIAL ALUMINIUM DAN BESI COR Nizar Bagas Maulana Universitas Tidar Jl. Kapten Suparman No.39 e-mail: nizar.bagas.nb@gmail.com,
Lebih terperinciSidang TUGAS AKHIR. Dosen Pembimbing : Prof. Dr.Ir.Sulistijono,DEA
Sidang TUGAS AKHIR Dosen Pembimbing : Prof. Dr.Ir.Sulistijono,DEA Latar Belakang Abdul Latif Murabbi / 2708.100.088 Batasan Masalah Abdul Latif Murabbi / 2708.100.088 PERMASALAHAN Abdul Latif Mrabbi /
Lebih terperinciANALISIS STRESS CORROSION CRACKING LOGAM TEMBAGA DENGAN METODE U-BEND PADA MEDIA KOROSI NH4OH 1M
ANALISIS STRESS CORROSION CRACKING LOGAM TEMBAGA DENGAN METODE U-BEND PADA MEDIA KOROSI NH4OH 1M *Ardia Wanandi Suwarno 1, Athanasius Priharyoto Bayuseno 2 1 Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik,
Lebih terperinciBAB IV ANALISA DAN PEMBAHASAN. Setelah dilakukan pengujian anodizing pada aluminium seri 6, maka
BAB IV ANALISA DAN PEMBAHASAN Setelah dilakukan pengujian anodizing pada aluminium seri 6, maka diperoleh data-data pengujian yang kemudian dijabarkan melalui beberapa subsub pembahasan dari masing-masing
Lebih terperinciPENGARUH WAKTU PADA ELEKTROPLATING KROM DEKORATIF DENGAN LOGAM BASIS TEMBAGA TERHADAP LAJU KOROSI
PENGARUH WAKTU PADA ELEKTROPLATING KROM DEKORATIF DENGAN LOGAM BASIS TEMBAGA TERHADAP LAJU KOROSI Citra Ayu Dewi 1 & Ahmadi 2 1&2 Dosen Program Studi Pendidikan Kimia FPMIPA IKIP Mataram E-mail: Ayudewi_citra@yahoo.co.id
Lebih terperinciBAB I PENDAHULUAN. Melihat kerugian yang terjadi yang akan ditimbulkan oleh korosi. ini maka berbagai usaha dilakukan untuk dapat mencegah korosi
BAB I PENDAHULUAN 1.1. Latar Belakang Melihat kerugian yang terjadi yang akan ditimbulkan oleh korosi ini maka berbagai usaha dilakukan untuk dapat mencegah korosi salah satu cara untuk mencegah korosi
Lebih terperinciPENGARUH KONSENTRASI ELEKTROLIT DAN WAKTU ANODISASI TERHADAP KETAHANAN AUS DAN KEKERASAN PADA LAPISAN OKSIDA PADUAN ALUMINIUM ADC12
PENGARUH KONSENTRASI ELEKTROLIT DAN WAKTU ANODISASI TERHADAP KETAHANAN AUS DAN KEKERASAN PADA LAPISAN OKSIDA PADUAN ALUMINIUM ADC12 Bambang Wahyu Sidharta 1, R. Soekrisno 2, Priyo Tri Iswanto 2 1 Mahasiswa
Lebih terperinciPENGARUH SURFACE TREATMENT METODA PLASMA NITRIDING TERHADAP KEKERASAN DAN KETAHANAN AUS PAHAT BUBUT BAHAN BAJA KECEPATAN TINGGI
D.17. Pengaruh Surface Treatment Metoda Plasma Nitriding Terhadap Kekerasan (Sunarto) D.98 PENGARUH SURFACE TREATMENT METODA PLASMA NITRIDING TERHADAP KEKERASAN DAN KETAHANAN AUS PAHAT BUBUT BAHAN BAJA
Lebih terperinciPENGARUH VARIASI VOLTASE, WAKTU DENGAN TEMPERATUR PROSES PELAPISAN KROM 50 0 C TERHADAP KARAKTERISTIK LOGAM ALUMINIUM
PENGARUH VARIASI VOLTASE, WAKTU DENGAN TEMPERATUR PROSES PELAPISAN KROM 50 0 C TERHADAP KARAKTERISTIK LOGAM ALUMINIUM Purgiyanto 1), Viktor Malau 2) 1) Program Pasca Sarjana jurusan Teknik Mesin dan Industri
Lebih terperinciPENGARUH KUAT ARUS PADA PELAPISAN NICKEL DAN NICKEL-HARD CHROMIUM PLATING TERHADAP SIFAT FISIS DAN MEKANIS PERMUKAAN BAJA AISI 410
PENGARUH KUAT ARUS PADA PELAPISAN NICKEL DAN NICKEL-HARD CHROMIUM PLATING TERHADAP SIFAT FISIS DAN MEKANIS PERMUKAAN BAJA AISI 410 Noor Setyo *), Viktor Malau **) Jurusan Teknik Mesin Fakultas Teknik Universitas
Lebih terperinciPengaruh Variasi Tegangan dan Waktu Terhadap Kekerasan Lapisan Nikel dengan Metode Electroplating pada Coran Aluminium scrap
LJTMU: Vol. 03, No. 01, April 2016, (01-08) ISSN Print : 2356-3222 ISSN Online : 2407-3555 http://ejournal-fst-unc.com/index.php/ljtmu Pengaruh Variasi Tegangan dan Waktu Terhadap Kekerasan Lapisan Nikel
Lebih terperinciBAB IV ANALISA DAN PEMBAHASAN. Pembuatan spesimen dilakukan dengan proses pengecoran metode die
BAB IV ANALISA DAN PEMBAHASAN 4.1 Proses Pengecoran Hasil penelitian tentang pembuatan poros berulir (Screw) berbahan dasar 30% Aluminium bekas dan 70% piston bekas dengan penambahan unsur 2,5% TiB. Pembuatan
Lebih terperinciKarakterisasi Material Sprocket
BAB IV DATA DAN ANALISA 4.1 Pengamatan Metalografi 4.1.1 Pengamatan Struktur Makro Pengujian ini untuk melihat secara keseluruhan objek yang akan dimetalografi, agar diketahui kondisi benda uji sebelum
Lebih terperinciBAB I PENDAHULUAN 1.1. Latar Belakang
BAB I PENDAHULUAN 1.1. Latar Belakang Anodizing atau yang dikenal dengan nama pelapisan logam (plating) atau (surface treatment), adalah suatu perlakuan permukaan untuk melapisi permukaan logam agar terlindung
Lebih terperinciPENGARUH RAPAT ARUS DAN WAKTU PADA PULSE ELECTRODEPOSITION OF NICKEL TERHADAP MIKROSTRUKTUR LAPISAN DEPOSIT DAN LAJU KOROSI AISI 410
PENGARUH RAPAT ARUS DAN WAKTU PADA PULSE ELECTRODEPOSITION OF NICKEL TERHADAP MIKROSTRUKTUR LAPISAN DEPOSIT DAN LAJU KOROSI AISI 41 Rivaldo Ramadhana Saputra. 1,a, Soesaptri Oediyani, Ir., ME. 2, Dr. Efendi
Lebih terperinciBAB I PENDAHULUAN 1.1 Latar Belakang
BAB I PENDAHULUAN 1 Latar Belakang Penerapan teknologi rekayasa material saat ini semakin bervariasi. Hal ini disebabkan oleh tuntutan untuk memenuhi kebutuhan manusia yang beraneka ragam, sehingga manusia
Lebih terperinciBAB III METODE PENELITIAN
BAB III METODE PENELITIAN A. Tempat dan Waktu Penelitian 1. Tempat Penelitian Penelitian ini dilaksanakan di: a. Laboratorium Logam Politeknik Manufaktur Ceper yang beralamat di Batur, Tegalrejo, Ceper,
Lebih terperinciBAB II TINJAUAN PUSTAKA. (C), serta unsur-unsur lain, seperti : Mn, Si, Ni, Cr, V dan lain sebagainya yang
BAB II TINJAUAN PUSTAKA 2.1 Baja Baja merupakan paduan yang terdiri dari unsur utama besi (Fe) dan karbon (C), serta unsur-unsur lain, seperti : Mn, Si, Ni, Cr, V dan lain sebagainya yang tersusun dalam
Lebih terperinciGambar 3.1 Diagram alur Penelitian
BAB III METODE PENELITIAN 3.1. Diagram Alur Penelitian Penelitian dalam tugas akhir ini dilakukan dalam beberapa tahapan meliputi: menentukan tujuan penelitian, mengumpulkan landasan teori untuk penelitian,
Lebih terperinciFAKULTAS TEKNIK JURUSAN TEKNIK MESIN UNIVERSITAS MUHAMMADIYAH SURAKARTA
NASKAH PUBLIKASI PENGARUH WAKTU TAHAN CELUP PROSES ELEKTROPLATING TEMBAGA TERHADAP KETEBALAN PELAPISAN PADA PLAT BAJA KARBON TINGGI DENGAN VARIASI TAHAN 10,12 DAN 14 DETIK Naskah Publikasi Diajukan untuk
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1. Pengujian komposisi kimia Pengujian komposisi kimia dilakukan dengan mesin spektrum komposisi kimia Optical Emission Spectrometer dan memberikan hasil pembacaan secara
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1. Analisis Laju Korosi Baja Karbon Pengujian analisis dilakukan untuk mengetahui prilaku korosi dan laju korosi baja karbon dalam suatu larutan. Pengujian ini dilakukan dengan
Lebih terperinciPENGARUH KUAT ARUS LISTRIK TERHADAP KEKERASAN, KECERAHAN DAN KETEBALAN LAPISAN OKSIDA HASIL PROSES ANODIZING PADA ALUMINIUM
PENGARUH KUAT ARUS LISTRIK TERHADAP KEKERASAN, KECERAHAN DAN KETEBALAN LAPISAN OKSIDA HASIL PROSES ANODIZING PADA ALUMINIUM Wawan Hartanto Program Studi S-1 Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah
Lebih terperinciMEKANIKA Volume 11 Nomor 2, Maret 2013
109 PENGARUH ARUS DAN WAKTU PELAPISAN HARD CHROME TERHADAP KETEBALAN LAPISAN DAN TINGKAT KEKERASAN MIKRO PADA PLAT BAJA KARBON RENDAH AISI 1026 DENGAN MENGGUNAKAN CrO 3 250 gr/lt DAN H 2 SO 4 2,5 gr/lt
Lebih terperinciBAB II TINJAUAN PUSTAKA DAN DASAR TEORI
BAB II TINJAUAN PUSTAKA DAN DASAR TEORI 2.1 Tinjauan Pustaka Dalam metode pelapisan plastik ABS dengan elektroplating ada beberapa aspek yang harus diperhatikan, diantaranya adalah tingkat kecerahan suatu
Lebih terperinciElektrodeposisi Lapisan Kromium dicampur TiO 2 untuk Aplikasi Lapisan Self Cleaning
Jurnal Fisika Unand Vol. 5, No. 4, Oktober 2016 ISSN 2302-8491 Elektrodeposisi Lapisan Kromium dicampur TiO 2 untuk Aplikasi Lapisan Self Cleaning Ardi Riski Saputra*, Dahyunir Dahlan Jurusan Fisika FMIPA
Lebih terperinciANALISIS SIFAT FISIK LAPISAN TIPIS TITANIUM NITRIDA PADA BAJA AISI 410 YANG DILAPIS DENGAN METODE SPUTTERING
Analisis Sifat Fisik Lapisan Tipis Titanium Nitrida ANALISIS SIFAT FISIK LAPISAN TIPIS TITANIUM NITRIDA PADA BAJA AISI 410 YANG DILAPIS DENGAN METODE SPUTTERING Xander Salahudin Program Studi Teknik Mesin,
Lebih terperinciBAB III. dan RX-KING ditujukan pada diagram dibawah ini yaitu diagram alir penelitian. Rumah Kopling F1-ZR. Rumah Kopling RX-KING.
BAB III PENELITIAN 3.1. Diagram aliran Penelitian Secara skematis prosedur penelitian dan pengujian pada rumah kopling F1-ZR dan RX-KING ditujukan pada diagram dibawah ini yaitu diagram alir penelitian.
Lebih terperinciPENGARUH VARIASI KONSENTRASI LARUTAN NaCl TERHADAP KETAHANAN KOROSI HASIL ELEKTROPLATING Zn PADA COLDROLLED STEEL AISI 1020
SIDANG TUGAS AKHIR PENGARUH VARIASI KONSENTRASI LARUTAN NaCl TERHADAP KETAHANAN KOROSI HASIL ELEKTROPLATING Zn PADA COLDROLLED STEEL AISI 1020 Oleh: Pathya Rupajati (2706 100 039) Dosen Pembimbing: Prof.
Lebih terperinciSTUDI PELAPISAN KROM DENGAN PROSES ELEKTROPLATING PADA HANDEL REM SEPEDA MOTOR DENGAN VARIASI RAPAT ARUS
STUDI PELAPISAN KROM DENGAN PROSES ELEKTROPLATING PADA HANDEL REM SEPEDA MOTOR DENGAN VARIASI RAPAT ARUS NASKAH PUBLIKASI Untuk Memenuhi Sebagian Persyaratan Guna Mencapai Derajat Sarjana S-1 Teknik Mesin
Lebih terperinciANALISA PERBANDINGAN PELAPISAN GALVANIS ELEKTROPLATING DENGAN HOT DIP GALVANIZING TERHADAP KETAHANAN KOROSI DAN KEKERASAN PADA BAJA
ANALISA PERBANDINGAN PELAPISAN GALVANIS ELEKTROPLATING DENGAN HOT DIP GALVANIZING TERHADAP KETAHANAN KOROSI DAN KEKERASAN PADA BAJA Yoyok Wahyudi, A rasy Fahruddin Prodi Teknik Mesin Fakultas Teknik, Universitas
Lebih terperinciBAB IV ANALISIS DAN PEMBAHASAN
BAB IV ANALISIS DAN PEMBAHASAN Setelah dilakukan pengujian anodizing pada aluminium seri 1xxx, maka diperoleh data-data pengujian yang kemudian dijabarkan melalui beberapa sub-sub pembahasan dari masing-masing
Lebih terperinciPENGARUH PROSES NITRIDASI ION PADA BIOMATERIAL TERHADAP KEKERASAN DAN KETAHANAN KOROSI
PENGARUH PROSES NITRIDASI ION PADA BIOMATERIAL TERHADAP KEKERASAN DAN KETAHANAN KOROSI Wirjoadi, Lely Susita, Bambang Siswanto, Sudjatmoko BADAN TENAGA NUKLIR NASIONAL Pusat Teknologi Akselerator dan Proses
Lebih terperinciKARAKTERISASI SIFAT MEKANIK HASIL ELEKTROPLATING NIKEL KARBONAT (NiCO 3 ) PADA TEMBAGA (Cu)
KARAKTERISASI SIFAT MEKANIK HASIL ELEKTROPLATING NIKEL KARBONAT (NiCO 3 ) PADA TEMBAGA (Cu) Andrisel Putri, Sri Handani Jurusan Fisika FMIPA Universitas Andalas,Padang Kampus Unand Limau Manis, Pauh Padang
Lebih terperinciSIFAT FISIS DAN MEKANIS LAPISAN NIKEL-CHROMIUM PADA PERMUKAAN BAJA AISI 410
SIFAT FISIS DAN MEKANIS LAPISAN NIKEL-CHROMIUM PADA PERMUKAAN BAJA AISI 410 A. Noor Setyo HD *, Suheli ** Jurusan Teknik Mesin Fakultas Teknik Universitas Tidar Magelang Jl. Kapten S. Parman 39 Potrobangsan
Lebih terperinciBAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN 3.1 DIAGRAM ALIR Penambahan penghalus butir titanium Karakterisasi: Uji komposisi Uji kekerasan Karakterisasi: Uji kekerasan Mikrostruktur (OM) Penuaan (T4 dan T6) T = 28
Lebih terperinciANALISIS PENGARUH MEDIA PACK CARBURIZING TERHADAP KEAUSAN DAN KEKERASAN SPROKET SEPEDA MOTOR. Sigit Gunawan 1 dan Sigit Budi Harton 2
ANALISIS PENGARUH MEDIA PACK CARBURIZING TERHADAP KEAUSAN DAN KEKERASAN SPROKET SEPEDA MOTOR Sigit Gunawan 1 dan Sigit Budi Harton 2 ABSTRAK Penelitian ini bertujuan untuk mengkaji pengaruh media pack
Lebih terperinciPENGARUH VARIASI WAKTU BAJA KARBON RENDAH TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN, LAJU KOROSI DAN NILAI KEAUSAN SPESIFIK
PENGARUH VARIASI WAKTU BAJA KARBON RENDAH TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN, LAJU KOROSI DAN NILAI KEAUSAN SPESIFIK Sutrisno Teknik Mesin, Universitas Nahdlatul Ulama Surakarta E-mail : Trisnowmech_79@yahoo.co.id
Lebih terperinciBAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3.1. Diagram Alir Penelitian Mulai Identifikasi Masalah Kajian Pustaka Persiapan Alat dan Bahan Aluminium Seri 1XXX Cleaning Na 2CO 3 50 gram + 1 liter RO Waktu cleaning 2 menit
Lebih terperinciBAB IV HASIL PENGUJIAN
BAB IV HASIL PENGUJIAN 4.1 Komposisi Kimia Baja yang digunakan untuk penelitian ini adalah AISI 1010 dengan komposisi kimia seperti yang ditampilkan pada tabel 4.1. AISI 1010 Tabel 4.1. Komposisi kimia
Lebih terperinciJOB SHEET DAN LAPORAN PRAKTIKUM MATA KULIAH PRAKTIKUM METALURGI LAS
JOB SHEET DAN LAPORAN PRAKTIKUM MATA KULIAH PRAKTIKUM METALURGI LAS PENYUSUN : HERI WIBOWO, MT. PENYUSUN LAPORAN : NAMA... NIM... KELOMPOK/ KELAS... JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS NEGERI
Lebih terperinciMoch. Novian Dermantoro NRP Dosen Pembimbing Ir. Muchtar Karokaro, M.Sc. NIP
Pengaruh Variasi Bentuk dan Ukuran Scratch Polyethylene Wrap Terhadap Proteksi Katodik Anoda Tumbal Al-Alloy pada Baja AISI 1045 di Lingkungan Air Laut Moch. Novian Dermantoro NRP. 2708100080 Dosen Pembimbing
Lebih terperinci