KETANGGUHAN RETAK DAN KEKUATAN IMPAK KOMPOSIT EPOXY-SERBUK KARET BAN BEKAS
|
|
- Adi Kurniawan
- 7 tahun lalu
- Tontonan:
Transkripsi
1 KETANGGUHAN RETAK DAN KEKUATAN IMPAK KOMPOSIT EPOXY-SERBUK KARET BAN BEKAS 1) Y. Suyoko, 2) Kurniawan Joko Nugroho 1) dan 2) Jurusan Teknik Mesin Politeknik Pratama Mulia Surakarta yesuyoko@gmail.com ABSTRACT This study aims to determine the mechanical properties of fracture toughness and impact strength of epoxy - powder composite rubber tires. The material is used as an epoxy resin matrix product Eposchon PT. Justus Chemical Kingdom and the amplifier material is scrap tire rubber powder particles with a mesh size of 40 passes. Composites made with conventional methods of scrap tire rubber powder which is mixed in with the epoxy resin weight fraction of the variation of 0 %, 5 %, 10 % and 15 %. Each composition is mixed with a mechanical stirrer at 500 rpm and a temperature of 40 C for 15 min. At last minute added hardener (catalyst). The mixture was then poured on the mold for further processing in a curing oven at a temperature of 50 C for 2 hours. Later in the impact test specimens and fracture toughness according to the standard ASTM D256 and ASTM D5045. The results show that an increase in impact strength and fracture toughness at all adding weight fraction of used tire rubber powder. The largest increase occurred in the addition of 15 % weight fraction, which increases the impact strength of % ( kj/mm2 ) and fracture toughness increased % ( 1.60 Mpa.m 1 / 2 ). Keywords : Composite polymers, epoxy resins, rubber powder Pendahuluan Rekayasa material terus dilakukan manusia guna mendapatkan material baru yang memiliki sifat-sifat tertentu yang umumnya tidak ditemukan pada material tunggal seperti logam, keramik dan polimer. Kombinasi antara dua atau beberapa material tunggal diharapkan mampu mengurangi keterbatasan sifat masing-masing material penyusunnya. Komposit partikulat terdiri dari fasa matrik yang diperkuat dengan fasa dispersi dalam bentuk partikel. Penguat dianggap sebagai partikel jika seluruh dimensinya secara kasar sama. Resin epoxy merupakan salah satu material thermoset yang dibentuk melalui reaksi kimia nonreversible dimana campuran mudah dan cepat mengeras pada Ketangguhan Retak dan Kekuatan... 55
2 temperatur 5 C sampai 150 C. Resin epoxy memiliki beberapa kelebihan diantaranya adalah tahan aus, tahan unsur kimia, penyusutan rendah, tahan terhadap fatik dan creep, kemampuan adhesi baik sekali dan mudah dibentuk. Kekurangan pada resin epoxy antara lain bersifat getas, sensitif terhadap takik (notch), kekuatan rendah, keterbatasan temperatur operasi ( 200 C), mudah menyerap uap air, koefisien ekspansi thermal tinggi. Aplikasi resin epoxy digunakan secara luas pada bidang transportasi, bidang olah raga, bidang kedokteran dan peralatan umum [2] Tyre rubber adalah bentuk lain dari karet alam yang dihasilkan sebagaibarang setengah jadi sehingga bisa langsung dipakai oleh konsumen, baik untuk pembuatan ban atau barang yang menggunakan bahan baku karet alam lainnya. Tyre rubber juga memiliki kelebihan pada daya campurnya yang baik sehingga mudah digabungkan dengan karet sintetis [3]. Limbah karet berupa ban bekas membutuhkan waktu yang cukup lama saat terdekomposisi oleh mikro-organisme yang hidup di alam, sehingga penumpukan dalam jumlah yang besar akan menimbulkan masalah lingkungan. Asosiasi Perusahaan Ban Indonesia (APBI) menyatakan bahwa produksi ban roda dua pada Januari-Desember 2011 mencapai 42 juta unit. APBI menargetkan petumbuhan penjualan ban di dalam negeri untuk tahun depan akan mencapai 54 juta unit [4]. Jumlah ban bekas pada satu atau dua tahun ke depan akan bertambah sebesar produksi ban pada tahun ini. Keterbatasan yang nyata dari matrik epoxy karena bersifat getas dan kekuatannya yang rendah dapat diatasi dengan penambahan serbuk karet ban bekas sebagai filler dalam ukuran mikro. Pembuatan komposit ini diharapkan menjadi produk inovatif baru sebagai salah satu cara mengatasi masalah lingkungan sekaligus menjadi material alternatif yang ringan dan kuat sebagai pengganti material logam pada berbagai aplikasi di bidang rekayasa. Penelitian ini bertujuan untuk mengetahui pengaruh kandungan serbuk karet ban bekas terhadap ketangguhan retak dan kekuatan impak komposit epoxyserbuk karet ban bekas. Metodologi Penelitian Bahan filler yang digunakan dalam penelitian ini adalah serbuk karet ban bekas dengan ukuran lolos 40 mesh. Resin epoxy Eposchon A dan hardener Eposchon B produk PT. Justus Kimia Raya digunakan sebagai matrik. Peralatan yang digunakan adalah cetakan komposit, timbangan digital, mechanical stirrer, kompor listrik, oven, Ketangguhan Retak dan Kekuatan... 56
3 mikroskop, mesin uji bending dan mesin uji impak. Tahapan penelitian dilakukan dengan pembuatanan serbuk karet dari bagian ban luar bekas yang tidak mengandungg kawat baja atau benang nilonn dengan alat kikir. Serbuk karet yang dihasilkan kemudian disaring dengan ayakan ukuran 40 mesh. Serbuk karet dengan fraksi berat 5% dicampur dengan resin epoxy menggunakan mechanical stirrer pada putaran 500 rpm sambil dipanaskan pada suhu 40 C selama 15 menit. Hardener dimasukkan ke dalam campuran dengan putaran yang diturunkan menjadi 100 rpm selama 1 menit. Campuran dituang ke dalam cetakan. Proses curing dilakukanan di dalam oven listrik pada 50 C selama 2 jam. Jumlah minimal spesimen untuk setiap satu variabel pengujian menurut standar ASTM adalah lima buah. Pengulangan proses pembuatanan komposit dengan fraksi berat serbuk karet sebesar 15% dan 25%. Untuk fraksi berat 0% %, campuran hanya terdiri dari resin epoxy dan hardener. Uji ketangguhan retak pada kondisi plane-strain, menggunakan spesimen single edge notch bend (SENB). Ketangguhan retak mode I menggunakan spesimen SENB diberikan dalam persamaan berikut [5] Dengan catatan P adalah beban kritis untuk perambatan retak (N), S adalah jarak antar tumpuan (m), a adalah panjang retak awal (m), B adalah tebal spesimen (m) dan W adalah lebar spesimen (m). Gambar 1. Skema uji ketangguhan retak dengan spesimen SENB [6] Uji kekuatan impak Charpy digunakan untuk mengetahui kemampuan material saat menyerap energi sebelum patah. Energi yang diserap material dihitung dengan persamaan [7] Dengan catatan m adalah massa pendulum (kg), g adalah percepatan gravitasi, L adalah panjang lengan (m), h0 adalah tinggi awal pendulum, h1 adalah tinggi akhir pendulum (m), sudut α adalah sudut awal lengan ( ), dan sudut β adalah sudut akhir lengan ( ). Ketangguhan Retak dan Kekuatan... 57
4 Kekuatan impak secara normal dihitung dengan persamaan [7] Hasil dan Pembahasan Uji ketangguhan retak dilakukan untuk mengetahui kemampuan material menahan perambatan terhadap retak awal yang sengaja diberikan. Pengujian dilakukan dengan spesimen Single Edge Notch Bend (SENB) dan metode Three Point Bending sesuai standar ASTM D5045. Dari pengujian ini didapat beban maksimum yang mampu diterima spesimen sebelum patah. Hasil perhitungan untuk masingmasing penambahan fraksi berat serbuk karet diberikan dalam Tabel 1 dan disajikan dalam bentuk grafik seperti Gambar 2. Tabel 1. Hasil uji ketangguhan retak No Fraksi berat serbuk karet (%) Ketangguhan Retak (MPa.m 1/2 ) 1 0 0, , , ,60 Tabel 1 dan Gambar 2 menunjukkan pengaruh penambahan fraksi berat serbuk karet terhadap ketangguhan retak komposit epoxy-serbuk karet ban bekas, dimana hasil uji ketangguhan retak memiliki kecenderungan naik pada semua penambahan fraksi berat serbuk karet. Peningkatan ketangguhan retak pada penambahan 5%, 10% dan 15% fraksi berat masingmasing adalah 21,62% (0,45 MPa.m 1/2 ), 45,95% (0,54 MPa.m 1/2 ) dan 332,43% (1,60 MPa.m 1/2 ). KIC rata-rata (MPa.m 1/2 ) Fraksi Berat Serbuk Karet Gambar 2. Kurva pengaruh fraksi berat serbuk karet terhadap ketangguhan retak komposit epoxy-serbuk karet ban bekas. Uji impak dilakukan untuk mengetahui ketangguhan material saat menerima beban secara tibatiba yang diwujudkan pada kemampuan material untuk menyerap energi sebelum patah. Pengujian dilakukan dengan metode Charpy sesuai standar ASTM D256. Hasil perhitungan untuk masing-masing penambahan fraksi berat serbuk karet diberikan Ketangguhan Retak dan Kekuatan... 58
5 dalam Tabel 2 dan disajikan dalam bentuk grafik seperti Gambar 3. Tabel 2. Hasil uji kekuatan impak No Fraksi berat serbuk karet (%) , , , ,27 Kekuatan Impak (kj/m 2 ) 14,26% (60,64 kj/m 2 ) dan 17,34% (62,27 kj/m 2 ). 0% 64 5% Kekuatan impak (kj/mm 2 ) Fraksi berat serbuk karet (%) 10% Gambar 3. Kurva pengaruh fraksi berat serbuk karet terhadap kekuatan impakkomposit epoxyserbuk karet ban bekas Tabel 2 dan Gambar 3 menunjukkan hasil uji impak yang memiliki kecenderungan naik pada semua penambahan fraksi berat serbuk karet. Peningkatan kekuatan impak pada penambahan 5%, 10% dan 15% fraksi berat serbuk karet masing-masing adalah 10,14% (58,45 kj/m 2 ), 15% Gambar 4. Fotomakro penampang patah spesimen Ketangguhan Retak dan Kekuatan... 59
6 Serbuk karet akan memuai seiring peningkatan suhu sehingga saat resin mengeras dan komposit menjadi lebih dingin maka serbuk karet juga akan menyusut. Hal tersebut menyebabkan ikatan antarmuka antara resin dengan serbuk karet menjadi lemah. Seiring peningkatan fraksi berat serbuk karet dalam matrik epoxy maka rongga yang terbentuk dalam komposit akan semakin sedikit sehingga komposit akan lebih kuat saat menerima beban. Penampang patah yang terlihat pada Gambar 4 untuk fraksi berat 5%, 10% dan 15% menunjukkan bahwa rongga yang terbentuk akan semakin berkurang seiring pertambahan fraksi berat serbuk karet. Sifat elastis karet berrpengaruh terhadap komposit saat menerima beban, hal ini ditunjukkan dari bentuk patahan yang lebih tidak beraturan dibanding bentuk patahan resin epoxy yang tidak diperkuat serbuk karet. Penampang patah berkilat pada Gambar 4 dengan fraksi berat 0% menunjukkan jenis patahan yang terjadi adalah patah getas. Kesimpulan Berdasarkan hasil penelitian dan pembahasan, dapat ditarik kesimpulan sebagai berikut : 1. Peningkatan terbesar kekuatan impak dan ketangguhan retak komposit epoxy-serbuk karet ban bekas dicapai pada penambahan 15% fraksi berat serbuk karet berturut-turut sebesar 62,27 kj/m 2 dan 1,60 MPa.m 1/2. 2. Struktur makro patahan spesimen uji menunjukkan bahwa komposit tanpa serbuk karet mengalami patah getas. 3. Serbuk karet akan berperan dalam membelokkan arah retak sehingga bentuk patahan komposit dengan serbuk karet cenderung tidak beraturan. Daftar Pustaka ASM Internatonal Composites, Vol 21. Harper, C.A Modern Plastics and Modern Plastics Handbook. New York: McGraw-Hill Companies. Hertzberg, R. W., 1989, Deformation and Fracture Mechanics of Engineering Materials, John Wiley & Sons, Inc. Broek, D., 1982, Elementary Engineering Fracture Mechanics, Martinus Nijhoff Publisher. Callister, Jr, W. D., Materials Science and Engineering an Introduction. New York: John Wiley & Sons. Ketangguhan Retak dan Kekuatan... 60
PENGARUH FRAKSI VOLUME PARTIKEL GENTENG SEBAGAI FILLER TERHADAP PERUBAHAN SIFAT KETAHANAN BAKAR MATERIAL KOMPOSIT POLYESTER RESIN.
PENGARUH FRAKSI VOLUME PARTIKEL GENTENG SEBAGAI FILLER TERHADAP PERUBAHAN SIFAT KETAHANAN BAKAR MATERIAL KOMPOSIT POLYESTER RESIN. 1) Siswanto, 2) Jumardi, 3) Basmal 1),2) Jurusan Teknik Mesin Politeknik
Lebih terperinciPENGARUH KEKUATAN BENDING DAN TARIK BAHAN KOMPOSIT BERPENGUAT SEKAM PADI DENGAN MATRIK UREA FORMALDEHIDE
PENGARUH KEKUATAN BENDING DAN TARIK BAHAN KOMPOSIT BERPENGUAT SEKAM PADI DENGAN MATRIK UREA FORMALDEHIDE Harini Program Studi Teknik Mesin Universitas 17 agustus 1945 Jakarta yos.nofendri@uta45jakarta.ac.id
Lebih terperinciPengaruh Penambahan Styrofoam dan Partikel Karet Terhadap Sifat Mekanik Resin Polyester Tak Jenuh
MAT - Universitas Gadjah Mada (UGM), Yogyakarta, 1-17 Oktober Pengaruh Penambahan Styrofoam dan Partikel Karet Terhadap Sifat Mekanik Resin Polyester Tak Jenuh Paryanto Dwi Setyawan a, Sugiman b a,b Jurusan
Lebih terperinciANALISA PENGARUH PENAMBAHAN CU PADA MATRIKS KOMPOSIT ALUMINIUM REMELTING
ANALISA PENGARUH PENAMBAHAN CU PADA MATRIKS KOMPOSIT ALUMINIUM REMELTING PISTON BERPENGUAT PASIR SILIKA TERHADAP KEKUATAN IMPAK DAN STUKTUR MIKRO PADA KOMPOSIT MATRIK ALUMINIUM DENGAN METODE STIR CASTING
Lebih terperinciPENGARUH FRAKSI VOLUME PARTIKEL TERHADAP KETAHANAN BAKAR KOMPOSIT FLY ASH-RIPOXY R-802
digilib.uns.ac.id PENGARUH FRAKSI VOLUME PARTIKEL TERHADAP KETAHANAN BAKAR KOMPOSIT FLY ASH-RIPOXY R-802 SKRIPSI Diajukan sebagai salah satu syarat untuk memperoleh gelar Sarjana Teknik Oleh: YOGA PRASETYA
Lebih terperinciImpact Toughness Test. Sigit Ngalambang
Impact Toughness Test Sigit Ngalambang Definisi Ketangguhan (Toughness) Dalam ilmu material dan metalurgi, ketangguhan adalah kemampuan suatu material untuk menyerap energi pembebanan dari material tanpa
Lebih terperinciPengaruh Fraksi Volume Filler terhadap Kekuatan Bending dan Ketangguhan Impak Komposit Nanosilika Phenolic
Jurnal Rekayasa Mesin Vol.5, No.1 Tahun 2014: 27-32 ISSN 0216-468X Pengaruh Fraksi Volume Filler terhadap Kekuatan Bending dan Ketangguhan Impak Komposit Kuncoro Diharjo 1, Ischiadica Elharomy 1, Agus
Lebih terperinciSINTESIS DAN KARAKTERISASI SIFAT MEKANIK SERTA STRUKTUR MIKRO KOMPOSIT RESIN YANG DIPERKUAT SERAT DAUN PANDAN ALAS (Pandanus dubius)
SINTESIS DAN KARAKTERISASI SIFAT MEKANIK SERTA STRUKTUR MIKRO KOMPOSIT RESIN YANG DIPERKUAT SERAT DAUN PANDAN ALAS (Pandanus dubius) Citra Mardatillah Taufik, Astuti Jurusan Fisika FMIPA Universitas Andalas
Lebih terperinciek SIPIL MESIN ARSITEKTUR ELEKTRO
ek SIPIL MESIN ARSITEKTUR ELEKTRO EFEK WAKTU PERLAKUAN PANAS TEMPER TERHADAP KEKUATAN TARIK DAN KETANGGUHAN IMPAK BAJA KOMERSIAL Bakri* dan Sri Chandrabakty * Abstract The purpose of this paper is to analyze
Lebih terperinciANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIKS ALUMINIUM REMELTING
ANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIKS ALUMINIUM REMELTING PISTON BERPENGUAT SIO2 TERHADAP KEKUATAN IMPAK DAN STRUKTUR MIKRO DENGAN METODE STIR CASTING SKRIPSI Diajukan sebagai salah satu
Lebih terperinciPENGARUH FRAKSI VOLUME SERBUK GENTING TERHADAP PERUBAHAN KEKUATAN LENTUR DAN KEKUATAN IMPAK PADA KOMPOSIT POLYESTER RESIN.
PENGARUH FRAKSI VOLUME SERBUK GENTING TERHADAP PERUBAHAN KEKUATAN LENTUR DAN KEKUATAN IMPAK PADA KOMPOSIT POLYESTER RESIN. 1) Basmal, 2) Jumardi, 3) Siswanto 1).Jurusan Teknik Otomotif Politeknik Pratama
Lebih terperinciTUGAS AKHIR PENELITIAN SIFAT FISIS DAN MEKANIS KOMPOSIT SERBUK TIMAH PEREKAT EPOXY UKURAN SERBUK 100 MESH DENGAN FRAKSI VOLUME (20, 35, 50) %
TUGAS AKHIR PENELITIAN SIFAT FISIS DAN MEKANIS KOMPOSIT SERBUK TIMAH PEREKAT EPOXY UKURAN SERBUK 100 MESH DENGAN FRAKSI VOLUME (20, 35, 50) % Diajukan untuk Memenuhi Tugas dan Syarat-syarat Guna Memperoleh
Lebih terperinciKOMPOSIT BERBASIS POLYMER DENGAN MATRIK EPOXY YANG DIPERKUAT SERBUK ALUMINA
KOMPOSIT BERBASIS POLYMER DENGAN MATRIK EPOXY YANG DIPERKUAT SERBUK ALUMINA Rusnoto Progdi Teknik Mesin Fakultas Teknik Universitas Pancasakti Tegal Kontak Person: Rusnoto Rusnoto74@gmail.com Abstrak Menggabungan
Lebih terperinciMETODOLOGI PENELITIAN. Penelitian dilakukan di Laboratorium Material Teknik Mesin Jurusan Teknik
III. METODOLOGI PENELITIAN A. Tempat Penelitian Penelitian dilakukan di Laboratorium Material Teknik Mesin Jurusan Teknik Mesin dan Laboratorium Ilmu Tanah Jurusan Teknik Sipil Universitas Lampung serta
Lebih terperinciSINTESIS DAN KARAKTERISASI SIFAT MEKANIK BAHAN NANOKOMPOSIT EPOXY-TITANIUM DIOKSIDA
SINTESIS DAN KARAKTERISASI SIFAT MEKANIK BAHAN NANOKOMPOSIT EPOXY-TITANIUM DIOKSIDA Firmansyah, Astuti Jurusan Fisika FMIPA Universitas Andalas Kampus Unand, Limau Manis, Padang, 25163 e-mail: firman_bond007@yahoo.com
Lebih terperinciPengaruh Rendaman Terhadap Perubahan Sifat Mekanik Komposit Polyester Resin - Partikel Arang Sekam Padi
8 POLITEKNOSAINS, Vol. XV, No 2, September 2016 Pengaruh Rendaman Terhadap Perubahan Sifat Mekanik Komposit Polyester Resin - Partikel Arang Sekam Padi Siswanto 1, Fahmi Eka Saputra 2, Basmal 3 1&2 Jurusan
Lebih terperinciKOMPOSIT CORE HYBRID BERPENGUAT SERBUK KAYU JATI DAN MAHONI BERMATRIK POLYESTER
KOMPOSIT CORE HYBRID BERPENGUAT SERBUK KAYU JATI DAN MAHONI BERMATRIK POLYESTER Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan Teknik Mesin Fakultas Teknik Oleh: MUHAMMAD
Lebih terperinciPengaruh Variasi Fraksi Volume, Temperatur, Waktu Curing dan Post-Curing Terhadap Karakteristik Tekan Komposit Polyester - Hollow Glass Microspheres
JURNAL TEKNIK ITS Vol. 6, No. 1, (2017) ISSN: 2337-3539 (2301-9271 Print) F 196 Pengaruh Variasi Fraksi Volume, Temperatur, Waktu Curing dan Post-Curing Terhadap Karakteristik Tekan Komposit Polyester
Lebih terperinciPENGARUH KANDUNGAN DAN UKURAN PARTIKEL SERBUK GENTENG SOKKA TERHADAP KETANGGUHAN IMPAK KOMPOSIT GEOPOLIMER SKRIPSI
PENGARUH KANDUNGAN DAN UKURAN PARTIKEL SERBUK GENTENG SOKKA TERHADAP KETANGGUHAN IMPAK KOMPOSIT GEOPOLIMER SKRIPSI Diajukan sebagai salah satu syarat untuk memperoleh gelar Sarjana Teknik Disusun oleh
Lebih terperinciPENGARUH MEDIA PENDINGIN TERHADAP BEBAN IMPAK MATERIAL ALUMINIUM CORAN
PENGARUH MEDIA PENDINGIN TERHADAP BEBAN IMPAK MATERIAL ALUMINIUM CORAN Mukhtar Ali 1*, Nurdin 2, Mohd. Arskadius Abdullah 3, dan Indra Mawardi 4 1,2,3,4 Jurusan Teknik Mesin Politeknik Negeri Lhokseumawe
Lebih terperinciMETODOLOGI PENELITIAN. Penelitian dilakukan di Laboratorium Material Teknik Mesin Jurusan Teknik
34 III. METODOLOGI PENELITIAN A. Tempat Penelitian Penelitian dilakukan di Laboratorium Material Teknik Mesin Jurusan Teknik Mesin Universitas Lampung dan Laboratorium Teknik Mesin Politeknik Universitas
Lebih terperinciKevin Yoga Pradana Dosen Pembimbing: Prof. Dr. Ir. Wajan Berata, DEA
PENGARUH VARIASI FRAKSI VOLUME, TEMPERATUR DAN WAKTU POST-CURING TERHADAP KARAKTERISTIK BENDING KOMPOSIT POLYESTER - PARTIKEL HOLLOW GLASS MICROSPHERES Kevin Yoga Pradana 2109 100 054 Dosen Pembimbing:
Lebih terperinciTUGAS AKHIR PENELITIAN SIFAT FISIS DAN MEKANIS KOMPOSIT SERBUK TIMAH PEREKAT EPOXY UKURAN SERBUK 60 MESH DENGAN FRAKSI VOLUME (20, 35, 50) %
TUGAS AKHIR PENELITIAN SIFAT FISIS DAN MEKANIS KOMPOSIT SERBUK TIMAH PEREKAT EPOXY UKURAN SERBUK 60 MESH DENGAN FRAKSI VOLUME (20, 35, 50) % Diajukan untuk Memenuhi Tugas dan Syarat-syarat Guna Memperoleh
Lebih terperinciFajar Nugroho Sekolah Tinggi Teknologi Adisutjipto, Yogyakarta. Jl. Janti Blok R Lanud Adisutjipto
Seminar SENATIK Nasional Vol. II, 26 Teknologi November Informasi 2016, ISSN: dan 2528-1666 Kedirgantaraan (SENATIK) Vol. II, 26 November 2016, ISSN: 2528-1666 MdM- 41 STUDI PENGARUH PROSES MANUFAKTUR
Lebih terperinciPENGARUH RENDAMAN TERHADAP PERUBAHAN SIFAT MEKANIK KOMPOSIT POLIESTER RESIN-ARANG SEKAM PADI UNTUK MATERIAL BOARD PANEL.
PENGARUH RENDAMAN TERHADAP PERUBAHAN SIFAT MEKANIK KOMPOSIT POLIESTER RESIN-ARANG SEKAM PADI UNTUK MATERIAL PENGARUH RENDAMAN TERHADAP PERUBAHAN SIFAT MEKANIK KOMPOSIT POLIESTER RESIN-ARANG SEKAM PADI
Lebih terperinciUNIVERSITAS DIPONEGORO
UNIVERSITAS DIPONEGORO PENGARUH PENAMBAHAN MAGNESIUM (Mg) TERHADAP KARAKTERISTIK KOMPOSIT ALUMINIUM DIPERKUAT SILIKON KARBIDA (SiC) DENGAN METODE STIR CASTING TUGAS AKHIR MUHAMMAD MUSTAGHFIRI L2E 606 040
Lebih terperinciPENGARUH PENAMBAHAN SERBUK LOGAM/NON-LOGAM TERHADAP KEKUATAN DAN PERILAKU RAMBAT RETAK PADA SAMBUNGAN LEM EPOXY
Journal of Environmental Engineering & Sustainable Technology Vol. No., November 5, Pages 67-7 JEEST http://jeest.ub.ac.id PENGARUH PENAMBAHAN SERBUK LOGAM/NON-LOGAM TERHADAP KEKUATAN DAN PERILAKU RAMBAT
Lebih terperinciPENGARUH FRAKSI VOLUME DAN UKURAN PARTIKEL KOMPOSIT POLYESTER RESIN BERPENGUAT PARTIKEL GENTING TERHADAP KEKUATAN TARIK DAN KEKUATAN BENDING ABSTRACT
PENGARUH FRAKSI VOLUME DAN UKURAN PARTIKEL KOMPOSIT POLYESTER RESIN BERPENGUAT PARTIKEL GENTING TERHADAP KEKUATAN TARIK DAN KEKUATAN BENDING Siswanto 1, Kuncoro Diharjo 2. 1. Mahasiswa Pasca Sarjana Teknik
Lebih terperinciPENGARUH KOMPOSISI CAMPURAN HARDENER DENGAN RESIN POLYESTER TERHADAP KUAT TARIK DAN BENDING POLIMER TERMOSET
PENGARUH KOMPOSISI CAMPURAN HARDENER DENGAN RESIN POLYESTER TERHADAP KUAT TARIK DAN BENDING POLIMER TERMOSET La Maaliku 1, Yuspian Gunawan 2, Aminur 2 1 Mahasiswa Program Studi Teknik Mesin Fakultas Teknik
Lebih terperinciKEKUATAN IMPAK KOMPOSIT HIBRID UNSATURATED POLYESTER / CLAY / SERAT GELAS Husaini Program Studi Teknik Sipil Fakultas Teknik Universitas Almuslim
KEKUATAN IMPAK KOMPOSIT HIBRID UNSATURATED POLYESTER / CLAY / SERAT GELAS Husaini Program Studi Teknik Sipil Fakultas Teknik Universitas Almuslim ABSTRAK Pengujian kekuatan impak digunakan untuk mengukur
Lebih terperinciSKRIPSI KARAKTERISASI KEAUSAN KAMPAS REM BERBASIS HYBRID KOMPOSIT MENGGUNAKAN METODE PIN ON DISC. Oleh :
SKRIPSI KARAKTERISASI KEAUSAN KAMPAS REM BERBASIS HYBRID KOMPOSIT MENGGUNAKAN METODE PIN ON DISC Oleh : ENDEN PERDANA CANDRA SETIAWAN NIM : 1104305023 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS UDAYANA
Lebih terperinciANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIK ALUMINIUM REMELTING
ANALISA PENGARUH PENAMBAHAN MG PADA KOMPOSIT MATRIK ALUMINIUM REMELTING PISTON BERPENGUAT SIO2 MENGGUNAKAN METODE STIR CASTING TERHADAP KEKERASAN DAN DENSITAS SKRIPSI Diajukan sebagai salah satu syarat
Lebih terperinciSTUDI SIFAT MEKANIK KOMPOSIT HIBRID EPOKSI /SERBUK KULIT TELUR AYAM BURAS/SERAT GELAS
STUDI SIFAT MEKANIK KOMPOSIT HIBRID EPOKSI /SERBUK KULIT TELUR AYAM BURAS/SERAT GELAS Heribertus Sukarja Jurusan Teknik Mesin Fakultas Teknik Universitas Proklamasi 45 Telp. +62274-485517 Jl.Proklamasi
Lebih terperinciDYAN YOGI PRASETYO I
ANALISA PENGARUH KECEPATAN PENGADUKAN DAN TEMPERATUR TUANG PADA AMC BERPENGUAT PASIR SILICA TERHADAP KEKUATAN IMPAK DAN TARIK DENGAN METODE STIR CASTING SKRIPSI Diajukan sebagai salah satu syarat untuk
Lebih terperinciKARAKTERISASI SIFAT MEKANIS DAN FISIS KOMPOSIT E-GLASS DAN RESIN ETERNAL 2504 DENGAN VARIASI KANDUNGAN SERAT, TEMPERATUR DAN LAMA CURING
144 KARAKTERISASI SIFAT MEKANIS DAN FISIS KOMPOSIT E-GLASS DAN RESIN ETERNAL 2504 DENGAN VARIASI KANDUNGAN SERAT, TEMPERATUR DAN LAMA CURING Viktor Malau 1 1 Staf Pengajar Jurusan Teknik Mesin dan Industri
Lebih terperinciBAB III METODOLOGI PENELITIAN
BAB III METODOLOGI PENELITIAN Laporan Tugas Akhir 3.1 Diagram Alir Proses Gambar 3.1. Diagram alir penelitian 25 Penelitian ini ditunjang dengan simulasi komputer dari hasil penelitian komposit PE-serbuk
Lebih terperinciJurusan Teknik Mesin, Universitas Brawijaya Jl. MT Haryono 167, Malang
Karakteristik Kekuatan Bending dan Impact akibat Variasi Unidirectional Pre-Loading pada serat penguat komposit Polyester Tjuk Oerbandono*, Agustian Adi Gunawan, Erwin Sulistyo Jurusan Teknik Mesin, Universitas
Lebih terperinciPENGARUH PENAMBAHAN CLAY TERHADAP SIFAT MEKANIK KOMPOIT HIBRID EPOKSI /SERAT GELAS
PENGARUH PENAMBAHAN CLAY TERHADAP SIFAT MEKANIK KOMPOIT HIBRID EPOKSI /SERAT GELAS PENGARUH PENAMBAHAN CLAY TERHADAP SIFAT MEKANIK KOMPOIT HIBRID EPOKSI /SERAT GELAS Heribertus Sukarja Jurusan Teknik Mesin
Lebih terperinciPengaruh Fraksi Volume Dan Panjang Serat Pelepah Lontar (Borassus Flabellifer) Terhadap Kekuatan Tarik Dan Kekuatan Impak Komposit Bermatrik Epoksi
Jurnal Rekayasa Mesin Vol.6, No.1 Tahun 215:33-38 ISSN 2477-641 Pengaruh Dan Panjang Serat Pelepah Lontar (Borassus Flabellifer) Terhadap Kekuatan Tarik Dan Kekuatan Impak Komposit Bermatrik Epoksi Amros
Lebih terperinciPENINGKATAN KEKUATAN TARIK DAN IMPAK PADA REKAYASA DAN MANUFAKTUR BAHAN KOMPOSIT HYBRID
C.1 PENINGKATAN KEKUATAN TARIK DAN IMPAK PADA REKAYASA DAN MANUFAKTUR BAHAN KOMPOSIT HYBRID BERPENGUAT SERAT E-GLASS DAN SERAT KENAF BERMATRIK POLYESTER UNTUK PANEL INTERIOR AUTOMOTIVE Agus Hariyanto Jurusan
Lebih terperinciBAB I PENDAHULUAN. Salah satu material yang sangat penting bagi kebutuhan manusia adalah
1 BAB I PENDAHULUAN 1.1 Latar Belakang Salah satu material yang sangat penting bagi kebutuhan manusia adalah logam. Seiring dengan jaman yang semakin maju, kebutuhan akan logam menjadi semakin tinggi.
Lebih terperinciPerubahan Sifat Mekanis Komposit Hibrid Polyester yang Diperkuat Serat Sabut Kelapa dan Serat Ampas Empulur Sagu
Perubahan Sifat Mekanis Komposit Hibrid Polyester yang Diperkuat Serat Sabut Kelapa dan Serat Ampas Empulur Sagu Arthur Yanny Leiwakabessy, Anindito Purnowidodo, Sugiarto, Rudy Soenoko Jurusan Teknik Mesin
Lebih terperinciBAB I PENDAHULUAN. penduduknya menjadikan beras sebagai makanan pokoknya, serta. produksi berasnya merata di seluruh tanah air.
BAB I PENDAHULUAN 1.1. Latar Belakang Indonesia sebagai negara agraris yang mayoritas penduduknya menjadikan beras sebagai makanan pokoknya, serta produksi berasnya merata di seluruh tanah air. Berdasarkan
Lebih terperinciPENGARUH PERLAKUAN ALKALI TERHADAP KEKUATANBENDING KOMPOSIT SERAT RAMBUT MANUSIA DENGAN MATRIK POLYESTER. Suryanto, Yuyun Estriyanto, Budi Harjanto
PENGARUH PERLAKUAN ALKALI TERHADAP KEKUATANBENDING KOMPOSIT SERAT RAMBUT MANUSIA DENGAN MATRIK POLYESTER Suryanto, Yuyun Estriyanto, Budi Harjanto Pendidikan Teknik Mesin, Jurusan Pendidikan Teknik dan
Lebih terperinciPEMANFAATAN LIMBAH TANDAN KOSONG KELAPA SAWIT SEBAGAI PAPAN KOMPOSIT DENGAN VARIASI PANJANG SERAT
PEMANFAATAN LIMBAH TANDAN KOSONG KELAPA SAWIT SEBAGAI PAPAN KOMPOSIT DENGAN VARIASI PANJANG SERAT Rina Lusiani 1*, Sunardi 2, Yogie Ardiansah 3 1,2,3 Jurusan Teknik Mesin, Fakultas Teknik, Universitas
Lebih terperinciAnalisis Sifat Mekanik Komposit Polyester Berpenguat Biride Partikel Arang Sekam Padi dan Kalsit
Analisis Sifat Mekanik Komposit Polyester Berpenguat Biride Partikel Arang Sekam Padi dan Kalsit Basmal 1, Joko Sukarno 2,Siswanto 3. 1,2 Program Studi Mesin Otomotif Politeknik Pratama Mulia Surakarta
Lebih terperinciKata kunci : Serat batang pisang, Epoxy, Hand lay-up, perbahan temperatur.
KARAKTERISTIK EFEK PERUBAHAN TEMPERATUR PADA KOMPOSIT SERAT BATANG PISANG DENGAN PERLAKUAN NaOH BERMETRIK EPOXY Ngafwan 1, Muh. Al-Fatih Hendrawan 2, Kusdiyanto 3, Jurusan Teknik Mesin Fakultas Teknik
Lebih terperinciIII. METODOLOGI PENELITIAN. Penelitian ini dilakukan di Laboratorium Material Teknik Jurusan Teknik Mesin,
III. METODOLOGI PENELITIAN A. Tempat Penelitian Penelitian ini dilakukan di Laboratorium Material Teknik Jurusan Teknik Mesin, Laboratorium Mekanik Politeknik Negeri Sriwijaya. B. Bahan yang Digunakan
Lebih terperinciKAJIAN PERLAKUAN SERAT SABUT KELAPA TERHADAP SIFAT MEKANIS KOMPOSIT EPOKSI SERAT SABUT KELAPA
KAJIAN PERLAKUAN SERAT SABUT KELAPA TERHADAP SIFAT MEKANIS KOMPOSIT EPOKSI SERAT SABUT KELAPA Indra Mawardi 1, Azwar 2, Amir Rizal 3 1,2,3 Jurusan Teknik Mesin, Politeknik Negeri Lhokseumawe Jl. Banda
Lebih terperinciIII. METODE PENELITIAN. Penelitian ini dilakukan pada Bulan September 2012 sampai dengan November
III. METODE PENELITIAN 3.1 Waktu dan Tempat Penelitian Penelitian ini dilakukan pada Bulan September 2012 sampai dengan November 2012. Preparasi sampel dilakukan di Laboratorium Fisika Material Universitas
Lebih terperinciPENGARUH PENAMBAHAN Mg DAN PERLAKUAN PANAS TERHADAP SIFAT FISIK MEKANIK KOMPOSIT MATRIKS ALUMINIUM REMELTING PISTON BERPENGUAT SiO 2
PENGARUH PENAMBAHAN Mg DAN PERLAKUAN PANAS TERHADAP SIFAT FISIK MEKANIK KOMPOSIT MATRIKS ALUMINIUM REMELTING PISTON BERPENGUAT SiO 2 SKRIPSI Diajukan sebagai salah satu syarat untuk memperoleh gelar Sarjana
Lebih terperinciKARAKTERISASI BAJA ARMOUR HASIL PROSES QUENCHING DAN TEMPERING
D.3 KARAKTERISASI BAJA ARMOUR HASIL PROSES QUENCHING DAN TEMPERING Padang Yanuar *, Sri Nugroho, Yurianto Jurusan Magister Teknik Mesin Fakultas Teknik UNDIP Jl. Prof. Sudharto SH Kampus Undip Tembalang
Lebih terperinciPengaruh Moisture Content dan Thermal Shock Terhadap Sifat Mekanik Komposit Hibrid Berbasis Serat Gelas dan Coir (Aplikasi: Blade Turbin Angin)
Pengaruh Moisture Content dan Thermal Shock Terhadap Sifat Mekanik Komposit Hibrid Berbasis Serat Gelas dan Coir (Aplikasi: Blade Turbin Angin) Mastariyanto Perdana a ), Jamasri Jurusan Teknik Mesin dan
Lebih terperinciPENGARUH KOMPOSISI DAN UKURAN MIKRO SERBUK KULIT KERANG DARAH (ANADORA GRANOSA) TERHADAP KOMPOSIT EPOKSI-PS/SERBUK KULIT KERANG DARAH (SKKD) SKRIPSI
PENGARUH KOMPOSISI DAN UKURAN MIKRO SERBUK KULIT KERANG DARAH (ANADORA GRANOSA) TERHADAP KOMPOSIT EPOKSI-PS/SERBUK KULIT KERANG DARAH (SKKD) SKRIPSI Oleh TOMMY ARISSA PUTRA 090405039 DEPARTEMEN TEKNIK
Lebih terperinciSTUDI KEKUATAN IMPAK PADA PENGECORAN PADUAL Al-Si (PISTON BEKAS) DENGAN PENAMBAHAN UNSUR Mg
STUDI KEKUATAN IMPAK PADA PENGECORAN PADUAL Al-Si (PISTON BEKAS) DENGAN PENAMBAHAN UNSUR Mg Rusnoto Program Studi Teknik Mesin Unversitas Pancasakti Tegal E-mail: rusnoto74@gmail.com Abstrak Piston merupakan
Lebih terperinciPENGARUH MOISTURE CONTENT DAN THERMAL SHOCK TERHADAP SIFAT MEKANIK DAN FISIK KOMPOSIT HIBRID BERBASIS SERAT GELAS DAN COIR
PENGARUH MOISTURE CONTENT DAN THERMAL SHOCK TERHADAP SIFAT MEKANIK DAN FISIK KOMPOSIT HIBRID BERBASIS SERAT GELAS DAN COIR Oleh : Mastariyanto Perdana Jurusan Teknik Mesin, Fakultas Teknologi Industri
Lebih terperinciPENGARUH VARIASI FRAKSI VOLUME, TEMPERATUR CURING DAN POST-CURING TERHADAP KARAKTERISTIK TEKAN KOMPOSIT EPOXY - HOLLOW GLASS MICROSPHERES IM30K
PENGARUH VARIASI FRAKSI VOLUME, TEMPERATUR CURING DAN POST-CURING TERHADAP KARAKTERISTIK TEKAN KOMPOSIT EPOXY - HOLLOW GLASS MICROSPHERES IM30K Widyansyah Ritonga 2109100027 Dosen Pembimbing: Wahyu Wijanarko.
Lebih terperinciMohammad Bagus E. H. 1, Hari Arbiantara 2, Dedi Dwilaksana 2. Abstrak. Abstract. Pendahuluan
1 Pengaruh Variasi Fraksi Berat dan Panjang Serat Komposit Pelepah Kelapa dengan Matriks Polypropylene terhadap Kekuatan Tarik pada Proses Injection Moulding (The Effect of Weight Fraction Variations and
Lebih terperinciPERENCANAAN ELEMEN MESIN RESUME JURNAL BERKAITAN DENGAN POROS
Judul : PERENCANAAN ELEMEN MESIN RESUME JURNAL BERKAITAN DENGAN POROS ANALISA KEKUATAN PUNTIR DAN KEKUATAN LENTUR PUTAR POROS BAJA ST 60 SEBAGAI APLIKASI PERANCANGAN BAHAN POROS BALING-BALING KAPAL Pengarang
Lebih terperinciSTUDI KEKUATAN IMPAK DAN STRUKTUR MIKRO BALL MILL DENGAN PERLAKUAN PANAS QUENCHING
STUDI KEKUATAN IMPAK DAN STRUKTUR MIKRO BALL MILL DENGAN PERLAKUAN PANAS QUENCHING Sumpena Program Studi Teknik Mesin Universitas Proklamasi 45 Yogyakarta Email: sumpenast@yahoo.co.id Abstrak Proses akhir
Lebih terperinciBAB I PENDAHULUAN 1.1 Latar Belakang
BAB I PENDAHULUAN 1.1 Latar Belakang Perkembangan rekayasa teknologi saat ini tidak hanya bertujuan untuk membantu umat manusia, namun juga harus mempertimbangkan aspek lingkungan. Segala hal yang berkaitan
Lebih terperinciBAB III METODE PENELITIAN. Metode penelitian yang digunakan dalam penelitian ini adalah eksperimen,
BAB III METODE PENELITIAN 3.1 Metode Penelitian Metode penelitian yang digunakan dalam penelitian ini adalah eksperimen, dengan tujuan untuk mengetahui pengaruh suhu tempering terhadap sifat mekanik baja
Lebih terperinciPENGARUH PERENDAMAN (NaOH) TERHADAP KEKUATAN TARIK DAN BENDING BAHAN KOMPOSIT SERAT BAMBU TALI (GIGANTOCHLOA APUS) BERMATRIKS POLYESTER
INFO TEKNIK Volume 15 No. 2 Desember 2014 (139-148) PENGARUH PERENDAMAN (NaOH) TERHADAP KEKUATAN TARIK DAN BENDING BAHAN KOMPOSIT SERAT BAMBU TALI (GIGANTOCHLOA APUS) BERMATRIKS POLYESTER Kosjoko Fakutas
Lebih terperinciPENGARUH KOMPOSISI DAN UKURAN MAKRO SERBUK KULIT KERANG DARAH (ANADORA GRANOSA) TERHADAP KOMPOSIT EPOKSI-PS/SERBUK KULIT KERANG DARAH (SKKD) SKRIPSI
PENGARUH KOMPOSISI DAN UKURAN MAKRO SERBUK KULIT KERANG DARAH (ANADORA GRANOSA) TERHADAP KOMPOSIT EPOKSI-PS/SERBUK KULIT KERANG DARAH (SKKD) SKRIPSI Oleh ADDRIYANUS TANTRA 100405034 DEPARTEMEN TEKNIK KIMIA
Lebih terperinciREKAYASA DAN MANUFAKTUR RANDOM COCONUT FIBER COMPOSITES BERMATRIK EPOXY UNTUK PANEL INTERIOR AUTOMOTIVE
D.11 REKAYASA DAN MANUFAKTUR RANDOM COCONUT FIBER COMPOSITES BERMATRIK EPOXY UNTUK PANEL INTERIOR AUTOMOTIVE Agus Hariyanto*, Wahyu Fitrianto Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah
Lebih terperinciLaporan Praktikum Laboratorium Teknik Material 1 Modul D Uji Lentur dan Kekakuan
Laporan Praktikum Laboratorium Teknik Material 1 Modul D Uji Lentur dan Kekakuan oleh : Nama : Catia Julie Aulia NIM : Kelompok : 7 Anggota (NIM) : 1. Conrad Cleave Bonar (13714008) 2. Catia Julie Aulia
Lebih terperinciLAPORAN TUGAS AKHIR SIFAT MEKANIK KOMPOSIT SERAT TANGKAI ILALANG SEBAGAI BAHAN PANEL RAMAH LINGKUNGAN
LAPORAN TUGAS AKHIR SIFAT MEKANIK KOMPOSIT SERAT TANGKAI ILALANG SEBAGAI BAHAN PANEL RAMAH LINGKUNGAN Diajukan Sebagai Syarat Memperoleh Gelar Sarjana Teknik Jurusan Teknik Industri Fakultas Teknik Universitas
Lebih terperinci2.2.9 Definisi Aluminium Klasifikasi Aluminium... 21
DAFTAR ISI HALAMAN JUDUL... i LEMBAR PENGESAHAN DOSEN... ii LEMBAR PENGESAHAN DOSEN PENGUJI... iii HALAMAN PERSEMBAHAN... iv HALAMAN MOTTO... v KATA PENGANTAR... vi ABSTRAK... viii DAFTAR ISI... x DAFTAR
Lebih terperinciIII. METODOLOGI PENELITIAN. Penelitian dilakukan di Laboratorium Material Teknik Mesin Jurusan Teknik
III. METODOLOGI PENELITIAN A. Tempat Penelitian Penelitian dilakukan di Laboratorium Material Teknik Mesin Jurusan Teknik Mesin Universitas Lampung. Adapun kegiatan penelitian yang dilakukan di laboratorium
Lebih terperinciStudi Experimental Pengaruh Fraksi Massa dan Orientasi Serat Terhadap Kekuatan Tarik Komposit Berbahan Serat Nanas
Studi Experimental Pengaruh Fraksi Massa dan Orientasi Serat Terhadap Kekuatan Tarik Komposit Berbahan Serat Nanas Andi Saidah, Helmi Wijanarko Program Studi Teknik Mesin,Fakultas Teknik, Universitas 17
Lebih terperinciPramuko Ilmu Purboputro Jurusan Teknik Mesin Universitas Muhammadiyah Surakarta
PENGARUH KOMPOSISI SERAT SABUT KELAPA TERHADAP KOEFISIEN GESEK DAN TEMPERATUR GESEK PADA BAHAN KOPLING CLUTCH KENDARAAN DARI KOMPOSIT SERAT SABUT KELAPA SERBUK TEMBAGA FIBERGLASS DENGAN MATRIK PHENOL Pramuko
Lebih terperinciAlasan pengujian. Jenis Pengujian merusak (destructive test) pada las. Pengujian merusak (DT) pada las 08/01/2012
08/01/2012 MATERI KE II Pengujian merusak (DT) pada las Pengujian g j merusak (Destructive Test) dibagi dalam 2 bagian: Pengujian di bengkel las. Pengujian skala laboratorium. penyusun: Heri Wibowo, MT
Lebih terperinciLaporan Praktikum Laboratorium Teknik Material 1 Modul A Uji Tarik
Laporan Praktikum Laboratorium Teknik Material 1 Modul A Uji Tarik oleh : Nama : Catia Julie Aulia NIM : Kelompok : 7 Anggota (NIM) : 1. Conrad Cleave Bonar (13714008) 2. Catia Julie Aulia () 3. Hutomo
Lebih terperinciLAPORAN PRAKTIKUM PRAKTIKUM PENGUJIAN MATERIAL MODUL 3 - PENGUJIAN IMPAK DELIANA RAMDANIAWATI KELOMPOK: 7
LAPORAN PRAKTIKUM PRAKTIKUM PENGUJIAN MATERIAL MODUL 3 - PENGUJIAN IMPAK DELIANA RAMDANIAWATI 1206217364 KELOMPOK: 7 LABORATORIUM METALURGI FISIK DEPARTEMEN TEKNIK METALURGI DAN MATERIAL FAKULTAS TEKNIK
Lebih terperinciBAB IV PEMBAHASAN. BAB IV Pembahasan 69
BAB IV PEMBAHASAN 4.1 ANALISA STRUKTUR MIKRO BAJA SETELAH HARDENING DAN TEMPERING Struktur mikro yang dihasilkan setelah proses hardening akan menentukan sifat-sifat mekanis baja perkakas, terutama kekerasan
Lebih terperinciSTUDI PENGARUH PENAMBAHAN SERAT TERHADAP KUAT TEKAN DAN KUAT LENTUR ATAP SERAT BULU AYAM
STUDI PENGARUH PENAMBAHAN SERAT TERHADAP KUAT TEKAN DAN KUAT LENTUR ATAP SERAT BULU AYAM Sri Handani dan Denia Efilusi Jurusan Fisika FMIPA Univesitas Andalas Email : shandani69@yahoo.com ABSTRAK Telah
Lebih terperinciPENGARUH KADAR CLAY PADA KOMPOSIT SERBUK AL-SI/CLAY
PENGARUH KADAR CLAY PADA KOMPOSIT SERBUK AL-SI/CLAY Nanang Endriatno Staf Pengajar Program Studi Teknik Mesin Fakultas Teknik Universitas Halu Oleo, Kendari Kampus Hijau Bumi Tridarma Andounohu Kendari
Lebih terperinciBAB III METODE PENELITIAN
BAB III METODE PENELITIAN 3. 1. DIAGRAM ALIR PENELITIAN Dikeringkan, Dipotong sesuai cetakan Mixing Persentase dengan Rami 15,20,25,30,35 %V f Sampel Uji Tekan Sampel Uji Flexural Sampel Uji Impak Uji
Lebih terperinciPengaruh Penguat Hibride Partikel Serbuk Arang Sekam Padi dan Kalsit Terhadap Sifat Mekanik Pada Komposit Polyester Resin.
POLITEKNOSAINS, Vol. XVI, No 1, Maret 2017 1 Pengaruh Penguat Hibride Partikel Serbuk Arang Sekam Padi dan Kalsit Terhadap Sifat Mekanik Pada Komposit Polyester Resin. Basmal 1, Joko Sukarno 2,Siswanto
Lebih terperinciUNIVERSITAS MUHAMMADIYAH SURAKARTA PUBLIKASI ILMIAH
KARAKTERISTIK KOMPOSIT SERBUK KAYU JATI DENGAN FRAKSI VOLUME 25%, 30%, 35% TERHADAP UJI BENDING, UJI TARIK DAN DAYA SERAP BUNYI UNTUK DINDING PEREDAM SUARA UNIVERSITAS MUHAMMADIYAH SURAKARTA PUBLIKASI
Lebih terperinciANALISA SIFAT MEKANIS KOMPOSIT METRIK EPOKSI DIPERKUAT SERBUK CANGKANG TELUR ITIK UNTUK RODA GIGI TRANSPORTIR PADA MESIN BUBUT.
ANALISA SIFAT MEKANIS KOMPOSIT METRIK EPOKSI DIPERKUAT SERBUK CANGKANG TELUR ITIK UNTUK RODA GIGI TRANSPORTIR PADA MESIN BUBUT Tri manunggal Utomo¹, Rusnoto², Drajat Samyono³ 1 Mahasiswa Jurusan Teknik
Lebih terperinciPEMANFAATAN PARTIKEL TEMPURUNG KEMIRI SEBAGAI BAHAN PENGUAT PADA KOMPOSIT RESIN POLIESTER
Jurnal Mechanical, Volume 3, Nomor 1,Maret 212 PEMANFAATAN PARTIKEL TEMPURUNG KEMIRI SEBAGAI BAHAN PENGUAT PADA KOMPOSIT RESIN POLIESTER Harnowo Supriadi Staf Pengajar Jurusan Teknik Mesin, Fakultas Teknik
Lebih terperinciPENGARUH FRAKSI VOLUME SERAT KAYU GELAM(MELALEUCE LEUCANDENDRA) KEKUATAN TARIK DAN IMPAK KOMPOSIT BERMATRIK POLYESTER
PENGARUH FRAKSI VOLUME SERAT KAYU GELAM(MELALEUCE LEUCANDENDRA) KEKUATAN TARIK DAN IMPAK KOMPOSIT BERMATRIK POLYESTER Saifullah Arief 1, Pratikto 2, Yudy Surya Irawan 2 1 Jurusan Teknik Mesin UNISKA, Jl
Lebih terperinciKOMPOSIT BERBASIS POLYMER DENGAN MATRIK EPOXY YANG DIPERKUAT SERBUK ALUMINA
KOMPOSIT BERBASIS POLYMER DENGAN MATRIK EPOXY YANG DIPERKUAT SERBUK ALUMINA Rusnoto Progdi Teknik Mesin Fakultas Teknik Universitas Pancasakti Tegal rusnoto74@gmail.com ABSTRAK Menggabungan dua material
Lebih terperinciPENGARUH BUTIRAN FILLER KAYU SENGON TERHADAP KARAKTERISTIK PAPAN PARTIKEL YANG BERPENGUAT SERAT TANDAN KOSONG KELAPA SAWIT
28 PENGARUH BUTIRAN FILLER KAYU SENGON TERHADAP KARAKTERISTIK PAPAN PARTIKEL YANG BERPENGUAT SERAT TANDAN KOSONG KELAPA SAWIT Sunardi, Moh. Fawaid, Rina Lusiani, Rumondang Parulian Jurusan Teknik Mesin
Lebih terperinciBAB I PENDAHULUAN. endemik. Bambu merupakan jenis rumput rumputan yang beruas. yang tinggi. Beberapa jenis bambu mampu tumbuh hingga sepanjang
BAB I PENDAHULUAN 1.1 Latar Belakang Di Indonesia terdapat berbagai jenis bambu diperkirakan sekitar 159 spesies dari total 1.250 jenis bambu yang terdapat di dunia. Bahkan sekitar 88 jenis bambu yang
Lebih terperinciANALISA KETANGGUHAN KOMPOSIT ALUMINIUM BERPENGUAT SERBUK SiC
ANALISA KETANGGUHAN KOMPOSIT ALUMINIUM BERPENGUAT SERBUK SiC Suyanto Program Studi Teknik Bangunan Kapal Akademi Teknik Perkapalan (ATP) Veteran Semarang Email: suyantoeste@yahoo.com ABSTRAK Produksi AMC
Lebih terperinciNASKAH PUBLIKASI KARYA ILMIAH
NASKAH PUBLIKASI KARYA ILMIAH SIFAT FISIS DAN MEKANIS AKIBAT PERUBAHAN TEMPERATUR PADA KOMPOSIT SERAT BATANG PISANG YANG DICUCI MENGGUNAKAN NaOH BERMATRIK EPOXY Disusun Untuk Memenuhi Tugas dan Syarat-Syarat
Lebih terperinciKekuatan tarik komposit lamina berbasis anyaman serat karung plastik bekas (woven bag)
Jurnal Kompetensi Teknik Vol. 8, No.2, Mei 2017 1 Kekuatan tarik komposit lamina berbasis anyaman serat karung plastik bekas (woven bag) Heri Yudiono 1, Rusiyanto 2, dan Kiswadi 3 1,2 Teknik Mesin, Fakultas
Lebih terperinciAnalisis Kegagalan pada Shaft Gearbox Mesin Palletizer di PT Holcim Tbk Tuban
F68 Analisis Kegagalan pada Shaft Gearbox Mesin Palletizer di PT Holcim Tbk Tuban Asia, Lukman Noerochim, dan Rochman Rochiem Departemen Teknik Material dan Metalurgi FTI-ITS, Kampus ITS-Keputih Sukolilo,
Lebih terperinciANALISA PENGARUH AGING 400 ºC PADA ALUMINIUM PADUAN DENGAN WAKTU TAHAN 30 DAN 90 MENIT TERHADAP SIFAT FISIS DAN MEKANIS
TUGAS AKHIR ANALISA PENGARUH AGING 400 ºC PADA ALUMINIUM PADUAN DENGAN WAKTU TAHAN 30 DAN 90 MENIT TERHADAP SIFAT FISIS DAN MEKANIS Disusun : SUDARMAN NIM : D.200.02.0196 JURUSAN TEKNIK MESIN FAKULTAS
Lebih terperinciPengaruh Penambahan Prosentase Fraksi Volume Hollow Glass Microsphere Komposit Hibrid Sandwich Terhadap Karakteristik Tarik dan Bending
JURNAL TEKNIK POMITS Vol. 2, No. 1, (2013) ISSN: 2337-3539 (2301-9271 Print) 1 Pengaruh Penambahan Prosentase Fraksi Volume Hollow Glass Microsphere Komposit Hibrid Sandwich Terhadap Karakteristik Tarik
Lebih terperinciPENGARUH SUHU PENCAMPURAN TERHADAP KEKUATAN TARIK DAN FRACTURE TOUGHNESS EPOXY RESIN - ORGANOCLAY MONTMORILLONITE NANOKOMPOSIT SKRIPSI
PENGARUH SUHU PENCAMPURAN TERHADAP KEKUATAN TARIK DAN FRACTURE TOUGHNESS EPOXY RESIN - ORGANOCLAY MONTMORILLONITE NANOKOMPOSIT SKRIPSI Diajukan sebagai salah satu syarat untuk memperoleh gelar Sarjana
Lebih terperinciANALISIS SIMULASI UJI IMPAK BAJA KARBON SEDANG (AISI 1045) dan BAJA KARBON TINGGI (AISI D2) HASIL PERLAKUAN PANAS. R. Bagus Suryasa Majanasastra 1)
ANALISIS SIMULASI UJI IMPAK BAJA KARBON SEDANG (AISI 1045) dan BAJA KARBON TINGGI (AISI D2) HASIL PERLAKUAN PANAS R. Bagus Suryasa Majanasastra 1) 1) Dosen Program Studi Teknik Mesin - Universitas Islam
Lebih terperinciJurusan Teknik Mesin, Fakultas Teknik, Universitas Jember 2
1 Pengaruh Variasi Panjang Serat Terhadap Kekuatan Tarik Dan Bending Komposit Matriks Polipropilena Dengan Penguat Serat Sabut Kelapa 10% Pada Proses Injection Moulding (The Effect Of Fiber Length Variation
Lebih terperinciBAB 3 METODE PENELITIAN
BAB 3 METODE PENELITIAN 3.1 Waktu dan Tempat Penelitian Penelitian dilaksanakan pada bulan di Laboratorium Penelitian DepartemenTeknik Kimia Universitas Sumatera Utara. Waktu penelitian selama 2 bulan,
Lebih terperinciBAB I PENDAHULUAN 1.1. Latar Belakang
BAB I PENDAHULUAN 1.1. Latar Belakang Penggunaan dan pemanfaatan karet sekarang ini semakin berkembang. Karet merupakan bahan atau material yang tidak bisa dipisahkan dari kehidupan manusia, sebagai bahan
Lebih terperinciPENGARUH PENAMBAHAN SERBUK SILIKA PADA MATRIK ALUMINIUM TERHADAP FRACTURE TUOGHNESS
PENGARUH PENAMBAHAN SERBUK SILIKA PADA MATRIK ALUMINIUM TERHADAP FRACTURE TUOGHNESS Oleh : Hendriwan Fahmi 1 dan Angga Prima Syokti 2 1 Dosen Jurusan Teknik Mesin, 2 Mahasiswa Jurusan Teknik Mesin Fakultas
Lebih terperinciANALISIS DAN PEMBUATAN GENTENG POLIMER DENGAN MEMANFAATKAN LIMBAH KARET INDUSTRI SERTA HIGH DENSITY POLYETHYLENE (HDPE) BEKAS
ANALISIS DAN PEMBUATAN GENTENG POLIMER DENGAN MEMANFAATKAN LIMBAH KARET INDUSTRI SERTA HIGH DENSITY POLYETHYLENE (HDPE) BEKAS Hafiz Arif Lubis, Kurnia Sembiring *), Achiruddin *) Jurusan Fisika, Fakultas
Lebih terperinciBAB IV ANALISIS DAN PEMBAHASAN
BAB IV ANALISIS DAN PEMBAHASAN 4.1 Hasil Pengujian Impak dan Pembahasan Dari hasil pengujian impak yang telah didapat data yaitu energi yang terserap oleh spesimen uji untuk material komposit serat pelepah