VARIASI KADAR PEREKAT PHENOL FORMALDEHIDA TERHADAP KUALITAS PAPAN PARTIKEL DARI CAMPURAN PARTIKEL KELAPA SAWIT DAN SERUTAN MERANTI
|
|
- Sri Lesmono
- 6 tahun lalu
- Tontonan:
Transkripsi
1 1 VARIASI KADAR PEREKAT PHENOL FORMALDEHIDA TERHADAP KUALITAS PAPAN PARTIKEL DARI CAMPURAN PARTIKEL KELAPA SAWIT DAN SERUTAN MERANTI SKRIPSI ANDRIAN TELAUMBANUA /TEKNOLOGI HASIL HUTAN PROGRAM STUDI KEHUTANAN FAKULTAS KEHUTANAN UNIVERSITAS SUMATERA UTARA 2016
2 2 ABSTRACT ANDRIAN TELAUMBANUA. Variations of Phenol Formaldehyde Adhesives Content towards the Quality of Particle Board Made from Particle Oil Palm and Shavings Meranti Mixtures. Supervised by RUDI HARTONO and APRI HERI ISWANTO. Palm oil plant is an oil producer. During this time the use of palm oil is only focused on the fruit, while the remaining part of the oil as the trunk is often regarded as wastes. Therefore, it is necessary to study the oil palm trunk to increase the value of palm trunks. The purpose of this study was to evaluate the physical and mechanical properties that results from particle board particle that made from particle oil palm and shavings meranti with some variation of the phenol formaldehyde adhesives content. The variations of phenol formaldehyde content were 8%, 10%, 12%, 14% dan 16%. The dimension of particle board was 25x25x1 cm with density target is 0,7 g/cm 3 using a pressure of 30 kg / cm2 for 8 minutes. The results will be compare with SNI The results showed that density, moisture content, water absorption for 2 and 24 hours, thickness swelling for 2 and 24 hours, internal bound, modulus of elasticity and modulus of rupture were 0,59-0,62 g/cm 3 ; 4,65-5,94%; 45,16-76,19% and 61,05-95,14%; 15,91-35,11% and 19,31-43,63%; 1,56-3,08 kg/cm 2 ; 9536, ,42 kg/cm 2 and 118,58-151,92 kg/cm 2. Physical properties (density, moisture content) has fulfilled SNI , while thickness swelling does not fulfill the standard. The entire value of IB and MOR testing have fulfilled the SNI , while the MOE not fulfill the standard. The best adhesives content from this study was 16%. Keywords: particle board, palm oil particle, shavings meranti, adhesive content, phenol formaldehyde.
3 3 ABSTRAK ANDRIAN TELAUMBANUA. Variasi Kadar Perekat Phenol Formaldehida Terhadap Kualitas Papan Partikel dari Campuran Partikel Kelapa Sawit dan Serutan Meranti. Dibimbing oleh RUDI HARTONO dan APRI HERI ISWANTO. Tanaman kelapa sawit merupakan tanaman penghasil minyak. Selama ini pemanfaatan kelapa sawit hanya terfokus pada bagian buah, sedangkan sisa bagian dari sawit seperti batang seringkali dianggap sebagai limbah. Oleh karena itu, perlu dilakukan penelitian terhadap batang kelapa sawit untuk meningkatkan nilai dari batang sawit. Tujuan dari penelitian ini adalah untuk mengevaluasi sifat fisis dan mekanis yang dihasilkan dari papan partikel yang terbuat dari partikel batang kelapa sawit dan serutan meranti dengan beberapa variasi kadar perekat phenol formaldehida. Variasi kadar perekat yang digunakan yaitu 8%, 10%, 12%, 14% dan 16%. Papan partikel dibuat berukuran 25x25x1 cm dengan target kerapatan 0,7 gr/cm 3 menggunakan tekanan 30 kg/cm 2 selama 8 menit. Hasil penelitian akan dibandingkan dengan SNI Hasil penelitian menunjukkan nilai kerapatan, kadar air, daya serap air 2 dan 24 jam, pengembangan tebal 2 dan 24 jam, keteguhan rekat internal, modulus elastis dan modulus patah berturut-turut ialah 0,59-0,62 g/cm 3 ; 4,65-5,94%; 45,16-76,19% dan 61,05-95,14%; 15,91-35,11% dan 19,31-43,63%; 1,56-3,08 kg/cm 2 ; 9536, ,42 kg/cm 2 dan 118,58-151,92 kg/cm 2. Sifat fisis (kerapatan, kadar air) telah memenuhi SNI , sedangkan pengembangan tebal tidak memenuhi standar. Seluruh pengujian IB dan MOR telah memenuhi SNI , sedangkan MOE belum memenuhi standar. Kadar perekat terbaik dalam penelitian ini adalah kadar perekat PF 16%. Kata kunci: papan partikel, partikel kelapa sawit, serutan meranti, kadar perekat, phenol formaldehida.
4 4 RIWAYAT HIDUP Penulis dilahirkan di Medan pada tanggal 23 November Penulis merupakan anak ketiga dari pasangan Samaeli Telaumbanua dan Tineke Puspawati Linanda. Penulis memulai pendidikan di SD Santo Thomas 1 Medan pada tahun , pendidikan tingkat Sekolah Menengah Pertama di SMP Santo Thomas 3 Medan pada tahun , pendidikan tingkat Sekolah Menengah Atas di SMA Sultan Iskandar Muda Medan pada tahun Pada tahun 2011, penulis lulus di Program Studi Kehutanan, Fakultas Pertanian USU melalui jalur Seleksi Nasional Masuk Perguruan Tinggi Negeri (SNMPTN). Penulis memilih minat studi Teknologi Hasil Hutan. Penulis telah mengikuti Praktik Pengenalan Ekosistem Hutan di Taman Hutan Rakyat Bukit Barisan dan Hutan Pendidikan USU pada tahun Pada tahun 2015 penulis juga telah menyelesaikan Praktik Kerja Lapang (PKL) di KPH Pekalongan Timur. Pada awal tahun 2015 penulis melaksanakan penelitian dengan judul Variasi Kadar Perekat Phenol Formaldehida terhadap Kualitas Papan Partikel dari Campuran Partikel Kelapa Sawit dan Serutan Meranti di bawah bimbingan Dr. Rudi Hartono, S.Hut, M.Si dan Dr. Apri Heri Iswanto, S.Hut, M.Si.
5 5 KATA PENGANTAR Puji dan syukur penulis panjatkan kepada Tuhan Yang Maha Esa karena atas rahmat-nya penulis dapat menyelesaikan skripsi yang berjudul Variasi Kadar Perekat Phenol Formaldehida terhadap Kualitas Papan Partikel dari Campuran Partikel Kelapa Sawit dan Serutan Meranti. Skripsi ini merupakan salah satu syarat untuk memperoleh gelar Sarjana Kehutanan di Program Studi Kehutanan, Fakultas Kehutanan,. Penelitian ini bertujuan untuk mengevaluasi pengaruh variasi kadar perekat phenol formaldehida, serta mengetahui kadar perekat terbaik terhadap kualitas papan partikel dari partikel kelapa sawit dan serutan meranti. Hasil penelitian ini diharapkan dapat meningkatkan nilai tambah dari limbah batang kelapa sawit sehingga masyarakat dapat beralih dari pemanfaatan kayu dalam bentuk log. Pada kesempatan ini, penulis mengucapkan terima kasih kepada: 1. Bapak Dr. Rudi Hartono, S.Hut, M.Si selaku ketua komisi pembimbing dan Bapak Dr. Apri Heri Iswanto, S.Hut, M.Si selaku anggota komisi pembimbing penulis yang dengan sabar dan tulus memberikan ilmu, masukan, bimbingan, serta arahan selama proses penulisan skripsi ini. 2. Keluarga tercinta, Ayahanda Samaeli Telaumbanua dan Ibunda Tineke Puspawati Linanda serta saudara-saudari penulis yang selalu memberikan dukungan, perhatian, doa, kasih sayang, serta pengorbanan baik moral maupun material kepada penulis.
6 6 3. Teman-teman satu perjuangan penelitian yaitu Evan Aritonang, Yeheskiel Simajuntak, Sabar Hutasoit, Fradika Siahaan, dan Shanty Sianturi atas suka duka yang telah terlalui selama penelitian serta teman-teman angkatan 2011 yang tidak bisa disebutkan namanya satu persatu. Penulis berharap skripsi ini bermanfaat bagi mahasiswa kehutanan maupun masyarakat umum. Akhir kata penulis mengucapkan terima kasih. Medan, Juli 2016 Penulis
7 7 DAFTAR ISI Halaman ABSTRACT... i ABSTRAK... ii RIWAYAT HIDUP... iii KATA PENGANTAR... iv DAFTAR ISI... vi DAFTAR TABEL... viii DAFTAR GAMBAR... ix DAFTAR LAMPIRAN... x PENDAHULUAN Latar Belakang... 1 Tujuan Penelitian... 3 Manfaat Penelitian... 3 TINJAUAN PUSTAKA Batang Kelapa Sawit... 4 Meranti... 5 Papan Partikel... 6 Perekat Phenol Formaldehida... 8 Variasi Kadar Perekat... 9 METODE PENELITIAN Waktu dan Tempat Alat dan Bahan Metode Penelitian Persiapan partikel BKS dan serutan Meranti Perhitungan bahan baku Pencampuran Perekat Pembentukan lembaran Hotpress/Pengempaan panas Pengkondisian Pemotongan contoh uji Pengujian papan partikel Pengujian sifat fisis dan mekanis Analisis data HASIL DAN PEMBAHASAN Sifat Fisis Papan Partikel Kerapatan Kadar Air Daya Serap Air... 23
8 8 Pengembangan Tebal Sifat Mekanis Papan Partikel Internal Bond (IB) Modulus of Elasticity (MOE) Modulus of Rupture (MOR) Kualitas papan Partikel KESIMPULAN DAN SARAN Kesimpulan Saran DAFTAR PUSTAKA LAMPIRAN
9 9 DAFTAR TABEL No. Halaman 1. Kebutuhan bahan baku partikel Standar Pengujian Sifat Fisis dan Mekanis Papan Partikel Rekapitulasi skoring kualitas sifat fisis dan mekanis papan partikel... 30
10 10 DAFTAR GAMBAR No. Halaman 1. Pola pemotongan untuk uji fisis dan mekanis papan Pengujian keteguhan rekat internal Cara pengujian MOR dan MOE Bagan alur penelitian Histogram rata-rata nilai kerapatan papan partikel Histogram rata-rata nilai spring back papan partikel Histogram rata-rata nilai kadar air papan partikel Histogram rata-rata nilai DSA pada perendaman 2 jam dan 24 jam Histogram rata-rata nilai PT pada perendaman 2 jam dan 24 jam Histogram rata-rata nilai IB papan partikel Histogram rata-rata nilai MOE papan partikel Histogram rata-rata nilai MOR papan partikel... 29
11 11 DAFTAR LAMPIRAN No. Halaman 1. Perhitungan bahan baku papan partikel Rekapitulasi nilai kerapatan dan kadar air papan partikel Rekapitulasi nilai daya serap air papan partikel Rekapitulasi hasil pengembangan tebal papan partikel Rekapitulasi nilai internal bond papan partikel Rekapitulasi nilai MOE papan partikel Rekapitulasi nilai MOR papan partikel Analisis keragaman kerapatan dan hasil uji duncan papan partikel Analisis keragaman kadar air dan hasil uji duncan papan partikel Analisis keragaman daya serap air 2 jam dan hasil uji duncan papan partikel Analisis keragaman daya serap air 24 jam dan hasil uji duncan papan partikel Analisis keragaman pengembangan tebal 2 jam dan hasil uji duncan papan partikel Analisis keragaman pengembangan tebal 24 jam dan hasil uji duncan papan partikel Analisis keragaman internal bond (IB) dan hasil uji duncan papan partikel Analisis keragaman keteguhan lentur (MOE) dan hasil uji duncan papan partikel Analisis keragaman keteguhan patah (MOR) dan hasil uji duncan papan partikel... 47
PEMBUATAN PAPAN PARTIKEL BERBAHAN DASAR SABUT KELAPA (Cocos nucifera L.) SKRIPSI
PEMBUATAN PAPAN PARTIKEL BERBAHAN DASAR SABUT KELAPA (Cocos nucifera L.) SKRIPSI OLEH : LISBETH DAMERIAHNI SIJABAT 110308031 PROGRAM STUDI KETEKNIKAN PERTANIAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA
Lebih terperinciPENGARUH PANJANG PARTIKEL TERHADAP KUALITAS ORIENTED PARTICLE BOARD DARI BAMBU TALI (Gigantochloa apus J.A & J.H. Schult.
PENGARUH PANJANG PARTIKEL TERHADAP KUALITAS ORIENTED PARTICLE BOARD DARI BAMBU TALI (Gigantochloa apus J.A & J.H. Schult. Kurz) SKRIPSI Oleh: RICKY HALOMOAN GEA 111201132/TEKNOLOGI HASIL HUTAN PROGRAM
Lebih terperinciPENGARUH KOMPOSISI PEREKAT UREA FORMALDEHIDA DAN BAHAN PENGISI STYROFOAM TERHADAP KUALITAS PAPAN PARTIKEL DARI LIMBAH BATANG KELAPA SAWIT SKRIPSI
PENGARUH KOMPOSISI PEREKAT UREA FORMALDEHIDA DAN BAHAN PENGISI STYROFOAM TERHADAP KUALITAS PAPAN PARTIKEL DARI LIMBAH BATANG KELAPA SAWIT SKRIPSI Oleh : ZAINAL ABIDIN SYAH POLEM 071203032 PROGRAM STUDI
Lebih terperinciPENGARUH PERENDAMAN SERUTAN KAYU DURIAN (Durio zibethinus) DALAM LARUTAN ASAM ASETAT DAN ACETIC ANHYDRIDE TERHADAP KUALITAS PAPAN PARTIKEL
i PENGARUH PERENDAMAN SERUTAN KAYU DURIAN (Durio zibethinus) DALAM LARUTAN ASAM ASETAT DAN ACETIC ANHYDRIDE TERHADAP KUALITAS PAPAN PARTIKEL SKRIPSI OLEH : RIZKY FEBRIANA BR LUBIS 121201126 Teknologi Hasil
Lebih terperinciPENGARUH RASIO SEMEN DAN PARTIKEL TERHADAP KUALITAS PAPAN SEMEN DARI LIMBAH PARTIKEL INDUSTRI PENSIL
PENGARUH RASIO SEMEN DAN PARTIKEL TERHADAP KUALITAS PAPAN SEMEN DARI LIMBAH PARTIKEL INDUSTRI PENSIL SKRIPSI Oleh: RIZQI PUTRI WINANTI 111201013 PROGRAM STUDI KEHUTANAN FAKULTAS KEHUTANAN UNIVERSITAS SUMATERA
Lebih terperinciVARIASI BERAT LABUR PEREKAT PHENOL FORMALDEHIDA TERHADAP KUALITAS PAPAN LAMINA DARI BATANG KELAPA SAWIT DENGAN PEMADATAN
VARIASI BERAT LABUR PEREKAT PHENOL FORMALDEHIDA TERHADAP KUALITAS PAPAN LAMINA DARI BATANG KELAPA SAWIT DENGAN PEMADATAN HASIL PENELITIAN Oleh: RAHMAD HIDAYAT DAULAY 091201012 PROGRAM STUDI KEHUTANAN FAKULTAS
Lebih terperinciKARAKTERISTIK PAPAN SEMEN DARI LIMBAH KERTAS KARDUS DENGAN PENAMBAHAN KATALIS KALSIUM KLORIDA
KARAKTERISTIK PAPAN SEMEN DARI LIMBAH KERTAS KARDUS DENGAN PENAMBAHAN KATALIS KALSIUM KLORIDA HASIL PENELITIAN Oleh: Zul Rahman Arief 061203037 / Teknologi Hasil Hutan PROGRAM STUDI KEHUTANAN FAKULTAS
Lebih terperinciKUALITAS PAPAN SEMEN DARI LIMBAH INDUSTRI PENSIL DENGAN BERBAGAI KOMPOSISI BAHAN BAKU DAN KONSENTRASI CaCl 2
KUALITAS PAPAN SEMEN DARI LIMBAH INDUSTRI PENSIL DENGAN BERBAGAI KOMPOSISI BAHAN BAKU DAN KONSENTRASI CaCl 2 SKRIPSI Fatmala Salmah 111201001 PROGRAM STUDI KEHUTANAN FAKULTAS KEHUTANAN UNIVERSITAS SUMATERA
Lebih terperinciLampiran 1. Perhitungan bahan baku papan partikel variasi pelapis bilik bambu pada kombinasi pasahan batang kelapa sawit dan kayu mahoni
Lampiran 1. Perhitungan bahan baku papan partikel variasi pelapis bilik bambu pada kombinasi pasahan batang kelapa sawit dan kayu mahoni Kadar perekat urea formaldehida (UF) = 12% Ukuran sampel = 25 x
Lebih terperinciSIFAT FISIS DAN MEKANIS PAPAN SEMEN DARI LIMBAH INDUSTRI PENSIL DENGAN BERBAGAI RASIO BAHAN BAKU DAN TARGET KERAPATAN
SIFAT FISIS DAN MEKANIS PAPAN SEMEN DARI LIMBAH INDUSTRI PENSIL DENGAN BERBAGAI RASIO BAHAN BAKU DAN TARGET KERAPATAN Oleh: Yunida Syafriani Lubis 111201033 PROGRAM STUDI KEHUTANAN FAKULTAS KEHUTANAN UNIVERSITAS
Lebih terperinciUniversitas Sumatera Utara
ERICK MARTHIN GULTOM (061203028) KEHUTANAN 2010 KUALITAS PAPAN PLASTIK KOMPOSIT PADA BERBAGAI TINGKAT PENDAURULANGAN PLASTIK ERICK MARTHIN GULTOM 061203028 DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS
Lebih terperinciPROGRAM STUDI KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA 2013
PENGARUH UKURAN PARTIKEL DAN KADAR PEREKAT TERHADAP SIFAT FISIS DAN MEKANIS PAPAN PARTIKEL DARI LIMBAH BATANG KELAPA SAWIT DENGAN PEREKAT UREA FORMALDEHIDA SKRIPSI Oleh: FRISKA SIMATUPANG 081203043/TEKNOLOGI
Lebih terperinciKUALITAS PAPAN SERAT BERKERAPATAN SEDANG DARI AKASIA DAN ISOSIANAT
KUALITAS PAPAN SERAT BERKERAPATAN SEDANG DARI AKASIA DAN ISOSIANAT HASIL PENELITIAN Oleh: Desi Haryani Tambunan 061203010/ Teknologi Hasil Hutan DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA
Lebih terperinciKARAKTERISTIK PAPAN SEMEN DARI LIMBAH KERTAS KARDUS DENGAN PENAMBAHAN KATALIS NATRIUM SILIKAT
KARAKTERISTIK PAPAN SEMEN DARI LIMBAH KERTAS KARDUS DENGAN PENAMBAHAN KATALIS NATRIUM SILIKAT SKRIPSI Oleh Ance Trisnawati Gultom 061203040/Teknologi Hasil Hutan PROGRAM STUDI KEHUTANAN FAKULTAS PERTANIAN
Lebih terperinciKARAKTERISTIK FISIS DAN MEKANIS PAPAN PARTIKEL BAMBU BETUNG
KARAKTERISTIK FISIS DAN MEKANIS PAPAN PARTIKEL BAMBU BETUNG HASIL PENELITIAN Oleh: Satria Muharis 071203013/Teknologi Hasil Hutan PROGRAM STUDI KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA 2011
Lebih terperinciPENGARUH KADAR PEREKAT UREA FORMALDEHIDA TERHADAP KUALITAS PAPAN PARTIKEL KULIT BUAHMARKISA (Passiflora edulis)
PENGARUH KADAR PEREKAT UREA FORMALDEHIDA TERHADAP KUALITAS PAPAN PARTIKEL KULIT BUAHMARKISA (Passiflora edulis) SKRIPSI OLEH: ELFRIDA ADLINA 121201084 PROGRAM STUDI KEHUTANAN FAKULTASKEHUTANAN UNIVERSITAS
Lebih terperinciKARAKTERISTIK PAPAN SEMEN DARI TIGA JENIS BAMBU DENGAN PENAMBAHAN KATALIS MAGNESIUM KLORIDA (MgCl 2 )
KARAKTERISTIK PAPAN SEMEN DARI TIGA JENIS BAMBU DENGAN PENAMBAHAN KATALIS MAGNESIUM KLORIDA (MgCl 2 ) SKRIPSI Oleh: Irvan Panogari Sibarani 071203007/ Teknologi Hasil Hutan PROGRAM STUDI KEHUTANAN FAKULTAS
Lebih terperinciKUALITAS FIBER PLASTIC COMPOSITE DARI KERTAS KARDUS DENGAN MATRIKS POLIETILENA (PE)
KUALITAS FIBER PLASTIC COMPOSITE DARI KERTAS KARDUS DENGAN MATRIKS POLIETILENA (PE) SKRIPSI Oleh: Reymon Fernando Cibro 071203026/ Teknologi Hasil Hutan PROGRAM STUDI KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS
Lebih terperinciSIFAT FISIS-MEKANIS PAPAN PARTIKEL DARI KOMBINASI LIMBAH SHAVING KULIT SAMAK DAN SERAT KELAPA SAWIT DENGAN PERLAKUAN TEKANAN BERBEDA
SIFAT FISIS-MEKANIS PAPAN PARTIKEL DARI KOMBINASI LIMBAH SHAVING KULIT SAMAK DAN SERAT KELAPA SAWIT DENGAN PERLAKUAN TEKANAN BERBEDA SKRIPSI MARIA YUNITA PROGRAM STUDI TEKNOLOGI HASIL TERNAK FAKULTAS PETERNAKAN
Lebih terperinciPENGARUH PENCAMPURAN IJUK TERHADAP KUALITAS PAPAN PARTIKEL DARI BATANG JAGUNG (Zea mays L)
PENGARUH PENCAMPURAN IJUK TERHADAP KUALITAS PAPAN PARTIKEL DARI BATANG JAGUNG (Zea mays L) SKRIPSI OLEH: WIDI FIORENTINA TARIGAN 131201128 DEPARTEMEN TEKNOLOGI HASIL HUTAN FAKULTAS KEHUTANAN UNIVERSITAS
Lebih terperinciMedan (Penulis Korespondensi : 2 Staf Pengajar Studi Kehutanan, Fakultas Pertanian, Universitas Sumatera Utara
VARIASI KOMPOSISI PEREKAT UREA FORMALDEHIDA DAN BAHAN PENGISI STYROFOAM TERHADAP KUALITAS PAPAN PARTIKEL DARI LIMBAH BATANG KELAPA SAWIT. (The Variation of Urea Formaldehyde Resin and Padding Styrofoam
Lebih terperinciPENGARUH UKURAN PELUPUH (ZEPHYR) DAN BUKU BAMBU (NODE) TERHADAP KUALITAS LAMINASI BAMBU BETUNG (Dendrocalamus asper)
PENGARUH UKURAN PELUPUH (ZEPHYR) DAN BUKU BAMBU (NODE) TERHADAP KUALITAS LAMINASI BAMBU BETUNG (Dendrocalamus asper) SKRIPSI Oleh: ANNISA NADIA 101201040 PROGRAM STUDI KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS
Lebih terperinciSIFAT FISIS DAN MEKANIS LAMINASI BAMBU BETUNG (Dendrocalamus asper BACKER EX. HEYNE) PADA BERBAGAI JUMLAH LAPISAN DAN POSISI PENGUJIAN
SIFAT FISIS DAN MEKANIS LAMINASI BAMBU BETUNG (Dendrocalamus asper BACKER EX. HEYNE) PADA BERBAGAI JUMLAH LAPISAN DAN POSISI PENGUJIAN SKRIPSI Oleh: MARIAH ULFA 101201035 PROGRAM STUDI KEHUTANAN FAKULTAS
Lebih terperinciKUALITAS PAPAN PARTIKEL DARI ECENG GONDOK (Eichhornia crassipes) DENGAN VARIASI KADAR PEREKAT UREA FORMALDEHIDA DAN UKURAN PARTIKEL
KUALITAS PAPAN PARTIKEL DARI ECENG GONDOK (Eichhornia crassipes) DENGAN VARIASI KADAR PEREKAT UREA FORMALDEHIDA DAN UKURAN PARTIKEL SKRIPSI OLEH: NOVITA OKTAVIANA 121201160/TEKNOLOGI HASIL HUTAN PROGRAM
Lebih terperinciAbstract. oil palm trunk waste, mahogany s, phenol formaldehyde, physical and mechanical properties, particle board.
Kualitas Papan Partikel dari Limbah Batang Kelapa Sawit dan Mahoni pada Variasi Kadar Perekat Phenol Formaldehida (Quality of Particle Board Made from Waste of Oil Palm Trunk and Mahogany s on Variations
Lebih terperinciKARAKTERISTIK PAPAN SEMEN DARI LIMBAH KARDUS DENGAN PENAMBAHAN KATALIS ALUMUNIUM SULFAT SKRIPSI
KARAKTERISTIK PAPAN SEMEN DARI LIMBAH KARDUS DENGAN PENAMBAHAN KATALIS ALUMUNIUM SULFAT SKRIPSI Oleh: Dedi Saputra 061203015/ Teknologi Hasil Hutan DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA
Lebih terperinciMETODOLOGI PENELITIAN
METODOLOGI PENELITIAN Waktu dan Lokasi Penelitian Penelitian ini dilaksanakan pada bulan Mei sampai Agustus 204 di Workshop Program Studi Kehutanan Fakultas Kehutanan Universitas Sumatera Utara untuk membuat
Lebih terperinciSIFAT FISIS MEKANIS PAPAN GIPSUM DARI TANDAN KOSONG KELAPA SAWIT (Elaeis guineensis Jacq.) DENGAN PERLAKUAN PERENDAMAN DAN VARIASI KADAR GIPSUM
SIFAT FISIS MEKANIS PAPAN GIPSUM DARI TANDAN KOSONG KELAPA SAWIT (Elaeis guineensis Jacq.) DENGAN PERLAKUAN PERENDAMAN DAN VARIASI KADAR GIPSUM SKRIPSI Oleh : FAUZAN KAHFI 031203035 PROGRAM STUDI TEKNOLOGI
Lebih terperinciVARIASI SUHU DAN WAKTU PENGEMPAAN TERHADAP KUALITAS PAPAN PARTIKEL DARI LIMBAH BATANG KELAPA SAWIT DENGAN PEREKAT PHENOL FORMALDEHIDA
VARIASI SUHU DAN WAKTU PENGEMPAAN TERHADAP KUALITAS PAPAN PARTIKEL DARI LIMBAH BATANG KELAPA SAWIT DENGAN PEREKAT PHENOL FORMALDEHIDA (The variation of Temperature and Pressing Time on Particle Board Quality
Lebih terperinciPOLA PENYEBARAN VASCULAR BUNDLES DAN KADAR AIR BATANG KELAPA SAWIT (Elaeis guineensis Jacq)
POLA PENYEBARAN VASCULAR BUNDLES DAN KADAR AIR BATANG KELAPA SAWIT (Elaeis guineensis Jacq) SKRIPSI OLEH: ZULFRIDEN SIREGAR 101201072/TEKNOLOGI HASIL HUTAN PROGRAM STUDI KEHUTANAN FAKULTAS KEHUTANAN UNIVERSITAS
Lebih terperinciKUALITAS PAPAN PARTIKEL DARI KOMPOSISI PARTIKEL BATANG KELAPA SAWIT DAN MAHONI DENGAN BERBAGAI VARIASI KADAR PEREKAT PHENOL FORMALDEHIDA
KUALITAS PAPAN PARTIKEL DARI KOMPOSISI PARTIKEL BATANG KELAPA SAWIT DAN MAHONI DENGAN BERBAGAI VARIASI KADAR PEREKAT PHENOL FORMALDEHIDA (Quality of Composition Particle Board of Oil Palm Trunk and Mahogany
Lebih terperinciSIFAT FISIS, MEKANIS DAN PEMESINAN KAYU RARU (Cotylelobium melanoxylon) SKRIPSI
ii SIFAT FISIS, MEKANIS DAN PEMESINAN KAYU RARU (Cotylelobium melanoxylon) SKRIPSI Oleh: Agnesia Claudia Agita Putri Siregar 071203012 PROGRAM STUDI KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA
Lebih terperinciSIFAT FISIS KAYU LAPIS BATANG KELAPA SAWIT
SIFAT FISIS KAYU LAPIS BATANG KELAPA SAWIT SKRIPSI ARIF BUDIMAN 031203027 DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA 2009 Arif Budiman. Sifat Fisis Kayu Lapis Batang Kelapa Sawit.
Lebih terperinciPENGARUH PERENDAMAN PANAS DAN DINGIN SABUT KELAPA TERHADAP KUALITAS PAPAN PARTIKEL YANG DIHASILKANNYA SISKA AMELIA
i PENGARUH PERENDAMAN PANAS DAN DINGIN SABUT KELAPA TERHADAP KUALITAS PAPAN PARTIKEL YANG DIHASILKANNYA SISKA AMELIA DEPARTEMEN HASIL HUTAN FAKULTAS KEHUTANAN INSTITUT PERTANIAN BOGOR 2009 i PENGARUH PERENDAMAN
Lebih terperinciKETAHANAN FIBER-PLASTIC
KETAHANAN FIBER-PLASTIC COMPOSITE DARI KERTAS KARDUS DAN POLIETILENA (PE) DENGAN PENAMBAHAN MALEAT ANHIDRIDA (MAH) DAN BENZOIL PEROKSIDA (BP) TERHADAP CUACA SKRIPSI Oleh: VICKY FADLIANSAH SIHOMBING 091201115/
Lebih terperinciKAJIAN BEBERAPA SIFAT DASAR BATANG PINANG (Areca catechu L.)
KAJIAN BEBERAPA SIFAT DASAR BATANG PINANG (Areca catechu L.) HASIL PENELITIAN Oleh : TRISNAWATI 051203021 PROGRAM STUDI TEKNOLOGI HASIL HUTAN DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA
Lebih terperinciLIMBAH LINEAR. Oleh: NAN UNIVERSI Universitas Sumatera Utara
KARAKTERISTIK PAPAN KOMPOSIT BERBAHAN LIMBAH BATANG KELAPA SAWIT DENGANN MATRIKS LINEAR LOW DENSITY POLYETHYLENE (LLDPE) HASIL PENELITIAN Oleh: Janter Manik 061203026/ Teknologi Hasil Hutan H DEPARTEMEN
Lebih terperinciPENGARUH SUHU PEREBUSAN PARTIKEL JERAMI (STRAW) TERHADAP SIFAT-SIFAT PAPAN PARTIKEL RINO FARDIANTO
PENGARUH SUHU PEREBUSAN PARTIKEL JERAMI (STRAW) TERHADAP SIFAT-SIFAT PAPAN PARTIKEL RINO FARDIANTO DEPARTEMEN HASIL HUTAN FAKULTAS KEHUTANAN INSTITUT PERTANIAN BOGOR 2009 PENGARUH SUHU PEREBUSAN PARTIKEL
Lebih terperinciBAB III METODOLOGI PENELITIAN
7 BAB III METODOLOGI PENELITIAN 3.1 Waktu dan Tempat Penelitian Penelitian dilaksanakan di Laboratorium Biokomposit dan pengujian sifat fisis dan mekanis dilaksanakan di Laboratorium Rekayasa dan Desain
Lebih terperinciTINJAUAN PUSTAKA. Menurut Badan Standardisasi Nasional (2010) papan partikel merupakan
TINJAUAN PUSTAKA Papan Partikel Menurut Badan Standardisasi Nasional (2010) papan partikel merupakan papan yang terbuat dari bahan berlignoselulosa yang dibuat dalam bentuk partikel dengan menggunakan
Lebih terperinci(Penulis Korespondensi: 2 Dosen Program Studi Kehutanan, Fakultas Pertanian, Universitas Sumatera Utara
Kualitas Papan Partikel Batang Pisang Barangan Berdasarkan Variasi Kadar Perekat Phenol Formaldehida (Particle Board Quality from Barangan Banana Stem Variation Based On Phenol Formaldehyde Resin Levels)
Lebih terperinciSafrina Talenta Lumbangaol 1, Rudi Hartono 2, Tito Sucipto 2 1 Program Studi Kehutanan, Fakultas Pertanian, Universitas Sumatera Utara,
Variasi Lama Perendaman dan Phenol Formaldehida terhadap Kualitas Papan Lamina dari Batang Kelapa Sawit (Soaking Time Variation and Phenol Formaldehyde Consentration on Laminated Board Quality Made from
Lebih terperinciMETODE PENELITIAN. Penelitian ini dilaksanakan pada bulan Mei - Oktober Pembuatan
METODE PENELITIAN Waktu dan Tempat Penelitian ini dilaksanakan pada bulan Mei - Oktober 2015. Pembuatan papan dan pengujian sifat fisis dilakukan di Laboratorium Teknologi Hasil Hutan, Program Studi Kehutanan,
Lebih terperinci17 J. Tek. Ind. Pert. Vol. 19(1), 16-20
KUALITAS PAPAN KOMPOSIT DARI LIMBAH BATANG KELAPA SAWIT (Elaeis guineensis Jacq) DAN POLYETHYLENE (PE) DAUR ULANG THE QUALITY OF COMPOSITE BOARD MADE OF WASTE OIL PALM STEM (Elaeis guineensis Jacq) AND
Lebih terperinciDiajukan Sebagai Persyaratan Untuk Menyelesaikan Pendidikan Diploma III Jurusan Teknik Kimia Politeknik Negeri Sriwijaya. Oleh :
PENGARUH PEREKAT LIKUIDA KAYU KARET DAN PEREKAT UREA FORMALDEHID TERHADAP KUALITAS PAPAN PARTIKEL (PARTICLE BOARD) DARI TANDAN KOSONG SAWIT (Elaeis guineensis Jacq) Diajukan Sebagai Persyaratan Untuk Menyelesaikan
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
19 BAB IV HASIL DAN PEMBAHASAN 4.1 Sifat Akustik Papan Partikel Sengon 4.1.1 Koefisien Absorbsi suara Apabila ada gelombang suara bersumber dari bahan lain mengenai bahan kayu, maka sebagian dari energi
Lebih terperinciSIFAT FISIS MEKANIS PAPAN PARTIKEL DARI LIMBAH KAYU GERGAJIAN BERDASARKAN UKURAN PARTIKEL
SIFAT FISIS MEKANIS PAPAN PARTIKEL DARI LIMBAH KAYU GERGAJIAN BERDASARKAN UKURAN PARTIKEL NATURE OF FISIS MECHANICAL PARTICLE BOARD FROM RIPSAW WASTE OF PURSUANT TO SIZE MEASURE PARTICLE Saibatul Hamdi
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
17 BAB IV HASIL DAN PEMBAHASAN 4.1 Sifat Fisis Papan Partikel 4.1.1 Kerapatan Kerapatan merupakan perbandingan antara massa per volume yang berhubungan dengan distribusi partikel dan perekat dalam contoh
Lebih terperinciKARAKTERISTIK PAPAN COM-PLY DARI CAMPURAN KAYU SAWIT DAN KORAN BEKAS. Oleh/By :
1 KARAKTERISTIK PAPAN COM-PLY DARI CAMPURAN KAYU SAWIT DAN KORAN BEKAS (Characteristics of Com-ply Board Made from the Mixture of Oil-Palm Wood and Old Newsprint) Oleh/By : Sahwalita 1,Usia 2, Iwan Risnasari
Lebih terperinciPENGARUH BESARAN KEMPA TERHADAP SIFAT PAPAN PARTIKEL SERUTAN KAYU. (The Effect of Pressing Rate on Wood Shaving Particleboard Properties)
PENGARUH BESARAN KEMPA TERHADAP SIFAT PAPAN PARTIKEL SERUTAN KAYU (The Effect of Pressing Rate on Wood Shaving Particleboard Properties) 1, Oleh /By : 1 M.I.Iskandar & Achmad Supriadi Email: 19supriadi1@gmail.com
Lebih terperinciAnwar Kasim, Yumarni dan Ahmad Fuadi. Abstract. Key words: Elaeis guineensis Jacq., trunk, Uncaria gambir Roxb., adhesive, particleboard.
Pengaruh Suhu dan Lama Pengempaan pada Pembuatan Papan Partikel dari Batang Kelapa Sawit (Elaeis guineensis Jacq.) dengan Perekat Gambir (Uncaria gambir Roxb.) terhadap Sifat Papan Partikel Influence of
Lebih terperinciLuthfi Hakim 1 dan Fauzi Febrianto 2. Abstract
21 KARAKTERISTIK FISIS PAPAN KOMPOSIT DARI SERAT BATANG PISANG (MUSA. SP) DENGAN PERLAKUAN ALKALI (PHYSICAL PROPERTIES OF COMPOSITE BOARD MADE FROM BANANA FIBER (MUSA SP.) WITH ALKALI TREATMENT) Luthfi
Lebih terperinciBAB III METODOLOGI 3.1 Waktu dan Tempat Penelitian 3.2 Alat dan Bahan Test Specification SNI
BAB III METODOLOGI 3.1 Waktu dan Tempat Penelitian Persiapan bahan baku, pembuatan dan pengujian sifat fisis papan partikel dilaksanakan di Laboratorium Bio-Komposit sedangkan untuk pengujian sifat mekanis
Lebih terperinciPengaruh Pelapisan Akrilik terhadap Kualitas Papan Partikel dari Limbah Batang Kelapa Sawit
Pengaruh Pelapisan Akrilik terhadap Kualitas Papan Partikel dari Limbah Batang Kelapa Sawit The Effect of Acrylic Coating on Oil Palm Trunk Waste Particle Board Merry Cristin Natalia Simaremare a, Tito
Lebih terperinciPENGARUH KADAR RESIN PEREKAT UREA FORMALDEHIDA TERHADAP SIFAT-SIFAT PAPAN PARTIKEL DARI AMPAS TEBU AHMAD FIRMAN ALGHIFFARI
PENGARUH KADAR RESIN PEREKAT UREA FORMALDEHIDA TERHADAP SIFAT-SIFAT PAPAN PARTIKEL DARI AMPAS TEBU AHMAD FIRMAN ALGHIFFARI DEPARTEMEN HASIL HUTAN FAKULTAS KEHUTANAN INSTITUT PERTANIAN BOGOR 2008 PENGARUH
Lebih terperinciPEMBUATAN BRIKET DARI SEKAM PADI DENGAN KOMBINASI BATUBARA
PEMBUATAN BRIKET DARI SEKAM PADI DENGAN KOMBINASI BATUBARA SKRIPSI Oleh : KASTA EFRATA BARUS 100308040 PROGRAM STUDI KETEKNIKAN PERTANIAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA 2016 PEMBUATAN BRIKET
Lebih terperinciPAPAN PARTIKEL DARI AMPAS TEBU (Saccharum officinarum)
KARYA TULIS PAPAN PARTIKEL DARI AMPAS TEBU (Saccharum officinarum) Disusun Oleh: APRI HERI ISWANTO, S.Hut, M.Si NIP. 132 303 844 DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA 2009
Lebih terperinciKARAKTERISTIK FISIS DAN MEKANIS PARTICLE BOARD DARI TANDAN KOSONG KELAPA SAWIT DENGAN VARIASI ZAT ADITIF DAN JENIS PEREKAT
KARAKTERISTIK FISIS DAN MEKANIS PARTICLE BOARD DARI TANDAN KOSONG KELAPA SAWIT DENGAN VARIASI ZAT ADITIF DAN JENIS PEREKAT Diajukan Sebagai Persyaratan Untuk Menyelesaikan Pendidikan Diploma III Jurusan
Lebih terperinciSTUDI KOMPARASI SNI DENGAN JIS A 5905 : 2003 PAPAN SERAT SKRIPSI. Oleh: Ulfah Hanum Nasution / Teknologi Hasil Hutan
STUDI KOMPARASI SNI 01-4449-2006 DENGAN JIS A 5905 : 2003 PAPAN SERAT SKRIPSI Oleh: Ulfah Hanum Nasution 071203014/ Teknologi Hasil Hutan PROGRAM STUDI KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA
Lebih terperinciOPTIMASI PEMANFAATAN SALAH SATU JENIS LESSER KNOWN SPECIES DARI SEGI SIFAT FISIS DAN SIFAT MEKANISNYA SKRIPSI OLEH: KRISDIANTO DAMANIK
OPTIMASI PEMANFAATAN SALAH SATU JENIS LESSER KNOWN SPECIES DARI SEGI SIFAT FISIS DAN SIFAT MEKANISNYA SKRIPSI OLEH: KRISDIANTO DAMANIK 121201056 PROGRAM STUDI KEHUTANAN FAKULTAS KEHUTANAN UNIVERSITAS SUMATERA
Lebih terperinciKETAHANAN PAPAN KOMPOSIT POLIMER DARI LIMBAH BATANG KELAPA SAWIT DAN PLASTIK POLIPROPILENA TERHADAP ORGANISME PENGGEREK KAYU DI LAUT HASIL PENELITIAN
KETAHANAN PAPAN KOMPOSIT POLIMER DARI LIMBAH BATANG KELAPA SAWIT DAN PLASTIK POLIPROPILENA TERHADAP ORGANISME PENGGEREK KAYU DI LAUT HASIL PENELITIAN Oleh: AZMI PRATAMA 051203043/Teknologi Hasil Hutan
Lebih terperinciSIFAT FISIS-MEKANIS PAPAN PARTIKEL DARI KOMBINASI LIMBAH SHAVING KULIT SAMAK DAN TANDAN KOSONG KELAPA SAWIT DENGAN KONSENTRASI PEREKAT BERBEDA
SIFAT FISIS-MEKANIS PAPAN PARTIKEL DARI KOMBINASI LIMBAH SHAVING KULIT SAMAK DAN TANDAN KOSONG KELAPA SAWIT DENGAN KONSENTRASI PEREKAT BERBEDA SKRIPSI N DIAN NURDIANI PROGRAM STUDI TEKNOLOGI HASIL TERNAK
Lebih terperinciSIFAT FISIK MEKANIK PAPAN PARTIKEL TANPA PEREKAT DARI TANDAN KOSONG KELAPA SAWIT (Elaeis Guineensis acq)
Sifat fisik dan mekanik papan partikel tanpa perekat dari tandan kosong kelapa sawit.budi Tri Cahyana SIFAT FISIK MEKANIK PAPAN PARTIKEL TANPA PEREKAT DARI TANDAN KOSONG KELAPA SAWIT (Elaeis Guineensis
Lebih terperinciPROTOTYPE PARQUET DARI LIMBAH BATANG AREN Arenga pinnata (Wurmb) Merrill SKRIPSI. Oleh: ANDRO TARIGAN
PROTOTYPE PARQUET DARI LIMBAH BATANG AREN Arenga pinnata (Wurmb) Merrill SKRIPSI Oleh: ANDRO TARIGAN 041203010 DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA MEDAN 2010 PROTOTYPE PARQUET
Lebih terperinciBAB III METODE PENELITIAN
8 BAB III METODE PENELITIAN 3.1 Bahan dan Alat Penelitian ini menggunakan bahan-bahan berupa tandan kosong sawit (TKS) yang diperoleh dari pabrik kelapa sawit di PT. Perkebunan Nusantara VIII Kertajaya,
Lebih terperinciPENGARUH COMPACTION RATIO TERHADAP SIFAT PAPAN LANTAI PARTIKEL KAYU JATI DAN SENGON
Forum Teknik Sipil No. XVII/2-Mei 2007 501 PENGARUH TERHADAP SIFAT PAPAN LANTAI PARTIKEL KAYU JATI DAN SENGON Widayanto 1), Morisco 2), T.A. Prayitno 3) 1) Mahasiswa Program MTBB Jurusan Teknik Sipil dan
Lebih terperinciPEMANFAATAN PELEPAH KELAPA SAWIT SEBAGAI BAHAN BAKU PAPAN PARTIKEL
PEMANFAATAN PELEPAH KELAPA SAWIT SEBAGAI BAHAN BAKU PAPAN PARTIKEL Rudianda Sulaeman, dan Evi Sribudiani Dosen Prodi Kehutanan Fakultas Pertanian UNRI. Email: sribudiani_unri@yahoo.co.id ABSTRACT Each
Lebih terperinciKUALITAS PAPAN KOMPOSIT DARI SABUT KELAPA DAN LIMBAH PLASTIK BERLAPIS BAMBU DENGAN VARIASI KERAPATAN DAN LAMA PERENDAMAN
KUALITAS PAPAN KOMPOSIT DARI SABUT KELAPA DAN LIMBAH PLASTIK BERLAPIS BAMBU DENGAN VARIASI KERAPATAN DAN LAMA PERENDAMAN NaOH Quality of Composite Board Made from Coconut Fiber and Waste Plastic with Bamboo
Lebih terperinciKAJIAN BEBERAPA SIFAT DASAR KAYU EKALIPTUS (Eucalyptus grandis) UMUR 5 TAHUN
KAJIAN BEBERAPA SIFAT DASAR KAYU EKALIPTUS (Eucalyptus grandis) UMUR 5 TAHUN SKRIPSI FRANS JANUARI HUTAGALUNG 051203045 DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVESITAS SUMATERA UTARA 2010 LEMBAR PENGESAHAN
Lebih terperinciPAPAN PARTIKEL DARI CAMPURAN LIMBAH ROTAN DAN PENYULINGAN KULIT KAYU GEMOR (Alseodaphne spp)
Papan partikel dari campuran limbah rotan dan penyulingan PAPAN PARTIKEL DARI CAMPURAN LIMBAH ROTAN DAN PENYULINGAN KULIT KAYU GEMOR (Alseodaphne spp) Particle Board from Mixture of Rattan Waste and Gemor
Lebih terperinciKARAKTERISTIK PAPAN PARTIKEL DARI BATANG PANDAN MENGKUANG (Pandanus atrocarpus Griff) BERDASARKAN UKURAN PARTIKEL DAN KONSENTRASI UREAFORMALDEHIDA
KARAKTERISTIK PAPAN PARTIKEL DARI BATANG PANDAN MENGKUANG (Pandanus atrocarpus Griff) BERDASARKAN UKURAN PARTIKEL DAN KONSENTRASI UREAFORMALDEHIDA The Characteristic of Particle Board Made From Pandan
Lebih terperinciPENGUJIAN SIFAT MEKANIS PANEL STRUKTURAL DARI KOMBINASI BAMBU TALI (Gigantochloa apus Bl. ex. (Schult. F.) Kurz) DAN KAYU LAPIS PUJA HINDRAWAN
1 PENGUJIAN SIFAT MEKANIS PANEL STRUKTURAL DARI KOMBINASI BAMBU TALI (Gigantochloa apus Bl. ex. (Schult. F.) Kurz) DAN KAYU LAPIS PUJA HINDRAWAN DEPARTEMEN HASIL HUTAN FAKULTAS KEHUTANAN INSTITUT PERTANIAN
Lebih terperinciPENINGKATAN MUTU PAPAN PARTIKEL MELALUI PENINGKATAN KADAR PEREKAT ( I mprovement of Particle Board Quality by Increasing Adhesive Content)
Penelitian Hasil Hutan Vol. 33 No., Juni 015: ISSN: 016-439 Terakreditasi No.: 443/AU/PMI-LIPI/0 8/01 PENINGKATAN MUTU PAPAN PARTIKEL MELALUI PENINGKATAN KADAR PEREKAT ( I mprovement of Particle Board
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
21 4.1 Geometri Strand pada Tabel 1. BAB IV HASIL DAN PEMBAHASAN Hasil pengukuran nilai rata-rata geometri strand pada penelitian ini tertera Tabel 1 Nilai rata-rata pengukuran dimensi strand, perhitungan
Lebih terperinciSIFAT FISIK MEKANIK PAPAN PARTIKEL JERAMI PADI Mechanical and physical properties of particleboard rice straw
SIFAT FISIK MEKANIK PAPAN PARTIKEL JERAMI PADI Mechanical and physical properties of particleboard rice straw Lastri Anita Gultom, Dirhamsyah, Dina Setyawati Fakultas Kehutanan Universitas Tanjungpura.
Lebih terperinciKUALITAS PAPAN KOMPOSIT BERLAPIS FINIR DARI SABUT KELAPA DAN PLASTIK POLIETILENA DAUR ULANG: VARIASI UKURAN PARTIKEL SABUT KELAPA
5 KUALITAS PAPAN KOMPOSIT BERLAPIS FINIR DARI SABUT KELAPA DAN PLASTIK POLIETILENA DAUR ULANG: VARIASI UKURAN PARTIKEL SABUT KELAPA The Quality of Veneered Composite Board Made of Coir and Recycled Polyethylene:
Lebih terperinciPEMBUATAN PAPAN PARTIKEL BERBAHAN DASAR KULIT DURIAN (Durio zibethinus murr.)
PEMBUATAN PAPAN PARTIKEL BERBAHAN DASAR KULIT DURIAN (Durio zibethinus murr.) (Manufacture of Particle Board Made from Durian Peel) Riska 1,3), Ainun Rohanah 1), Adian Rindang 1), Rudi Hartono 2) 1) Program
Lebih terperinciSIFAT FISIK DAN MEKANIK PAPAN KOMPOSIT DARI BATANG SINGKONG DAN LIMBAH PLASTIK BERDASARKAN PELAPISAN DAN KOMPOSISI BAHAN BAKU
SIFAT FISIK DAN MEKANIK PAPAN KOMPOSIT DARI BATANG SINGKONG DAN LIMBAH PLASTIK BERDASARKAN PELAPISAN DAN KOMPOSISI BAHAN BAKU Physical and Mechanical Properties of Composite Board Made from Singkong Trunk
Lebih terperinciKUALITAS SERAT DARI LIMBAH BATANG KELAPA SAWIT SEBAGAI BAHAN BAKU PAPAN SERAT SKRIPSI. Oleh : Rizki Syahputra Hasibuan
KUALITAS SERAT DARI LIMBAH BATANG KELAPA SAWIT SEBAGAI BAHAN BAKU PAPAN SERAT SKRIPSI Oleh : Rizki Syahputra Hasibuan 051203007 DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN UNIVERSITAS SUMATERA UTARA MEDAN
Lebih terperinciIII. METODOLOGI. 3.3 Pembuatan Contoh Uji
III. METODOLOGI 3.1 Waktu dan Tempat Penelitian Persiapan bahan baku dan pembuatan papan partikel dilaksanakan di Laboratorium Kimia Hasil Hutan dan Laboratorium Bio-Komposit sedangkan untuk pengujian
Lebih terperinciTINJAUAN PUSTAKA. perabot rumah tangga, rak, lemari, penyekat dinding, laci, lantai dasar, plafon, dan
TINJAUAN PUSTAKA A. Papan Partikel A.1. Definisi papan partikel Kayu komposit merupakan kayu yang biasa digunakan dalam penggunaan perabot rumah tangga, rak, lemari, penyekat dinding, laci, lantai dasar,
Lebih terperinciKarakteristik Papan Partikel dari Pelepah Salak Pondoh (Salacca sp) dengan Penambahan Asam Sitrat
Seminar Nasional XVIII MAPEKI Karakteristik Papan Partikel dari Pelepah Salak Pondoh (Salacca sp) dengan Penambahan Asam Sitrat Dayu Kemalasari Soraya dan Ragil Widyorini * Fakultas Kehutanan Universitas
Lebih terperinciLAMPIRAN. Lampiran 1. Nilai kerapatan papan semen pada berbagai perlakuan Anak petak
LAMPIRAN Lampiran 1. Nilai kerapatan papan semen pada berbagai perlakuan (S : F : A) Tanpa katalis (kg/cm 3 ) Katalis (kg/cm 3 ) 1:2,5:1,25 1 0,8503305 1,0959684 2 0,8294807 0,9763012 3 0,8943189 0,9229823
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
BAB IV HASIL DAN PEMBAHASAN 4.1. Sifat Fisis Papan Semen 4.1.1. Kadar Air Nilai rata-rata kadar air papan semen sekam hasil pengukuran disajikan pada Gambar 7. 12 Kadar air (%) 9 6 3 0 JIS A5417 1992:
Lebih terperinciPemanfaatan Limbah Kulit Buah Nangka sebagai Bahan Baku Alternatif dalam Pembuatan Papan Partikel untuk Mengurangi Penggunaan Kayu dari Hutan Alam
Pemanfaatan Limbah Kulit Buah Nangka sebagai Bahan Baku Alternatif dalam Pembuatan Papan Partikel untuk Mengurangi Penggunaan Kayu dari Hutan Alam Andi Aulia Iswari Syam un 1, Muhammad Agung 2 Endang Ariyanti
Lebih terperinciPAPAN PARTIKEL TANPA PEREKAT DARI BAMBU ANDONG DAN KAYU SENGON MENGGUNAKAN PERLAKUAN OKSIDASI SUHASMAN
PAPAN PARTIKEL TANPA PEREKAT DARI BAMBU ANDONG DAN KAYU SENGON MENGGUNAKAN PERLAKUAN OKSIDASI SUHASMAN SEKOLAH PASCASARJANA INSTITUT PERTANIAN BOGOR BOGOR 2011 PERNYATAAN MENGENAI DISERTASI DAN SUMBER
Lebih terperinciPENGARUH LAMA WAKTU PENUMPUKAN KAYU KARET (Hevea brasiliensis Muell. Arg.) TERHADAP SIFAT - SIFAT PAPAN PARTIKEL TRIDASA A SAFRIKA
PENGARUH LAMA WAKTU PENUMPUKAN KAYU KARET (Hevea brasiliensis Muell. Arg.) TERHADAP SIFAT - SIFAT PAPAN PARTIKEL TRIDASA A SAFRIKA DEPARTEMEN HASIL HUTAN FAKULTAS KEHUTANAN INSTITUT PERTANIAN BOGOR 2008
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
22 BAB IV HASIL DAN PEMBAHASAN 4.1 Geometri Strand Hasil pengukuran geometri strand disajikan pada Tabel 4. Berdasarkan data, nilai rata-rata dimensi strand yang ditentukan dengan menggunakan 1 strand
Lebih terperinciJonyal Periandi Sitanggang 1, Tito Sucipto 2, Irawati Azhar 2 1 Alumni Program Studi Kehutanan, Fakultas Kehutanan, Universitas Sumatera Utara,
Pengaruh Kadar Perekat Urea Formaldehida Terhadap Kualitas Papan Partikel dari Kayu Gamal (Gliricidia sepium) (The Effect of Urea Formaldehyde Adhesive Content on Quality of Gamal Wood Particleboard(Gliricidia
Lebih terperinciSIFAT SIFAT DASAR PAPAN COMPLY YANG MENGGUNAKAN PEREKAT POLIURETAN DAN MELAMINE FORMALDEHIDA TRY ANGGRAHINI KARANGAN
SIFAT SIFAT DASAR PAPAN COMPLY YANG MENGGUNAKAN PEREKAT POLIURETAN DAN MELAMINE FORMALDEHIDA TRY ANGGRAHINI KARANGAN DEPARTEMEN HASIL HUTAN FAKULTAS KEHUTANAN INSTITUT PERTANIAN BOGOR 2009 SIFAT SIFAT
Lebih terperinciPAPAN SEMEN-GYPSUM DARI CORE-KENAF (Hibiscus cannabinus L.) MENGGUNAKAN TEKNOLOGI PENGERASAN AUTOCLAVE
12 PAPAN SEMEN-GYPSUM DARI CORE-KENAF (Hibiscus cannabinus L.) MENGGUNAKAN TEKNOLOGI PENGERASAN AUTOCLAVE Cement-Gypsum Board from Core-Kenaf (Hibiscus cannabinus L.) Using Curing AutoclaveTechnology Rohny
Lebih terperinciVariasi Pelapis Luar dan Berat Labur Perekat Phenol Formaldehida terhadap Kualitas Papan Lamina dengan Inti dari Batang Kelapa Sawit
Variasi Pelapis Luar dan Berat Labur Perekat Phenol Formaldehida terhadap Kualitas Papan Lamina dengan Inti dari Batang Kelapa Sawit (Variation of Outer Layer and Phenol Formaldehyde Adhesive Glue Spread
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN
23 BAB IV HASIL DAN PEMBAHASAN 4.1 Geometri Strand Hasil pengukuran geometri strand secara lengkap disajikan pada Lampiran 1, sedangkan nilai rata-ratanya tertera pada Tabel 2. Tabel 2 Nilai pengukuran
Lebih terperinciKAJIAN LAJU INFILTRASI TANAH PADA BERBAGAI PENGGUNAAN LAHAN DI DESA SEMPAJAYA KECAMATAN BERASTAGI KABUPATEN KARO
KAJIAN LAJU INFILTRASI TANAH PADA BERBAGAI PENGGUNAAN LAHAN DI DESA SEMPAJAYA KECAMATAN BERASTAGI KABUPATEN KARO SKRIPSI OLEH : RIKA ISNAINI PROGRAM STUDI KETEKNIKAN PERTANIAN FAKULTAS PERTANIAN UNIVERSITAS
Lebih terperinciKiki Sinaga, M. Dirhamsyah Dan Ahmad Yani Fakultas Kehutanan Universitas Tanjungpura. Jalan Imam Bonjol Pontianak
JURNAL HUTAN LESTARI (217) KUALITAS PAPAN PARTIKEL PALEM EKOR TUPAI (Wodyetia bifurcata) DAN KAYU AKASIA (Acacia mangium) BERDASARKAN KOMPOSISI BAHAN BAKU DAN KONSENTRASI PEREKAT (Quality of Particle Board
Lebih terperinciBAB IV HASIL DAN PEMBAHASAN. Gambar 8 Histogram kerapatan papan.
17 BAB IV HASIL DAN PEMBAHASAN 4.1 Sifat Fisis Papan Komposit Anyaman Pandan 4.1.1 Kerapatan Sifat papan yang dihasilkan akan dipengaruhi oleh kerapatan. Dari pengujian didapat nilai kerapatan papan berkisar
Lebih terperinciSuherti, Farah Diba, Nurhaida Fakultas Kehutanan Universitas Tanjungpura. Jln Imam Bonjol Pontianak
SIFAT FISIK DAN MEKANIK PAPAN PARTIKEL DARI KULIT DURIAN (Durio sp) DENGAN KONSENTRASI UREA FORMALDEHID YANG BERBEDA Physical and Mechanical Properties of Particle Board from Durian Bark (Durio sp) with
Lebih terperinciSIFAT FISIK DAN MEKANIK PAPAN PARTIKEL DARI LIMBAH PLASTIK JENIS HDPE
Jurnal Riset Industri Hasil Hutan Vol., No.1, Juni 2011: 7 14 SIFAT FISIK DAN MEKANIK PAPAN PARTIKEL DARI LIMBAH PLASTIK JENIS HDPE (High Density Polyetylene) DAN RANTING/CABANG KARET (Hevea brasiliensis
Lebih terperinciIra Lestari Simbolon 1, Tito Sucipto 2, Rudi Hartono 2 1 Alumni Program Studi Kehutanan, Fakultas Kehutanan, Universitas Sumatera Utara, Jl.
Pengaruh Ukuran Partikel dan Komposisi Semen- Partikel terhadap Kualitas Papan Semen dari Cangkang Kemiri (Aleurites Moluccana Wild) ( Effect of Particle Size and Composition of Particles cement for quality
Lebih terperinciPengembangan Perekat Likuid dan Papan Partikel dari Limbah Tandan Kosong Sawit
Jurnal Ilmu Pertanian Indonesia (JIPI), Agustus 213 ISSN 853 4217 Vol. 18 (2): 115 124 Pengembangan Perekat Likuid dan Papan Partikel dari Limbah Tandan Kosong Sawit (Development of Wood Liquid and Particleboard
Lebih terperinci