PENGARUH FEEDING, KECEPATAN POTONG PAHAT CARBIDE TERHADAP KUALITAS PEMBUBUTAN BAHAN BAJA S45C. Rizwan Nur Agist, Joko Waluyo, Saiful Huda
|
|
- Ridwan Halim
- 6 tahun lalu
- Tontonan:
Transkripsi
1 E-Jurnal Teknik Mesin, Vol. 2 No. Desember 2014 ISSN: PENGARUH FEEDING, KECEPATAN POTONG PAHAT CARBIDE TERHADAP KUALITAS PEMBUBUTAN BAHAN BAJA S45C Rizwan Nur Agist, Joko Waluyo, Saiful Huda Jurusan Teknik Mesin, Fakultas Teknologi Industri, Institut Sains dan Teknologi AKPRIND Jl. Kalisahak No. 2 Yogyakarta, Indonesia, Waluyojok@yahoo.co.id ABSTRACT The lathe is a machine tool which plays an important role in the production process in the industry. In the process of turning the workpiece is gripped by rotating on its axis, while the cutting tool moves along the workpiece cut as a result there was an incision by a chisel to form grimly. In this process there are significant results due to surface roughness value of the incision. To get the ideal level of roughness is influenced by several parameters. In this study S45C steel workpiece as much as six pieces that will get different treatment in the course of the work, namely the variation of cutting speed of 145 m / min, 15 m / min and 15 m / min was used feeding 0.15 mm / rev and 0.2 mm / rev with the cutting depth of 0.5 mm to determine its effect on the quality of the surface roughness average lathe face. Then from workpiece to the workpiece respectively determined 3 points for the surface roughness test using test equipment surfcorder SE The results of the surface roughness of steel best quality and the lowest of 1.5 lm obtained from turning the cutting speed of 15 m / minutes, the engine turns 1000 rpm, depth of cut of 0.5 mm and 0.15 mm feeding / rev. While most high surface roughness of 5. lm sebersar obtained from the lathe with a cutting speed of 15 m / min, the engine turns 1400 rpm, and the feeding of 0.2 mm / put. Keywords: Lathe, cutting speed, Feeding, Roughness, quality 1. PENDAHULUAN Proses pembubutan merupakan salah satu metal cutting machine process dengan gerak utama berputar, benda kerja dicekam dan berputar pada sumbunya, sedangkan alat potong ( cutting tool) bergerak memotong sepanjang benda kerja akibatnya terjadilah penyayatan. Dalam proses ini terdapat pengaruh hasil nilai kekarasan permukaan akibat dari penyayatan tersebut. Sampai dengan saat ini proses pemesinan telah banyak digunakan oleh industri untuk membuat komponen atau bagian-bagian pada mesin automotive. Terutama banyak penggunaan mesin bubut pada proses pemesinan dikarenakan berbagai pekerjaan benda kerja untuk menghasilkan produk berbentuk silindris dapat dikerjakan dengan pembubutan Menurut Asyari Daryus (200:5) menyatakan bahwa parameter kecepatan penyayatan (cutting speed) terhadap kekasaran permukaan juga dipengaruhi oleh bahan dan jenis pahat. Tabel 1.1 Kecepatan Potong (Vc) Pahat HSS Pahat Karbida Bahan Halus Kasar Halus Kasar Baja perkakas Baja karbon rendah Baja karbon menengah Besi cor kelabu Kuningan Alumunium Keterangan : Halus = kedalaman pemotongan 0,3-2,2 mm, feed 0,13-0,3 mm/put Kasar = kedalaman pemotongan 4,75-,53 mm, feed 0,75-27 mm/put (Sumber : Asyari Daryus, Proses Produksi II, Universitas Darma Persada, Jakarta, Hal 5) Tarmawan mengatatakan bahwa pahat karbida mempunyai standar umum dengan untuk gerak makan f (feeding) 0,15-0,25 mm/rev seperti dapat dilihat pada Tabel 1.2 sebagai berikut. 2
2 E-Jurnal Teknik Mesin, Vol. 2 No. Desember 2014 ISSN: HSS 0,05-0,015 Tabel 1.2 Standart umum Feed (f) Carbide 0,15-0,25 (Sumber : Tarmawan, 1) Cooted Carbide 0,2-0,35 Dalam prosesnya menurut John A Schey pembubutan bahan S45C yang mempunyai kekerasan (< 275 BHN) dengan pahat karbida dapat dilakukan dengan beberapa proses pendinginan yaitu Dry (Kering), Emulsi minyak-mineral dan Fluida sintetis. Definisi Kekasaran permukaan adalah penyimpangan rata rata aritmetik dari garis rata-rata Profil. Dalam ISO definisi ini digunakan untuk menetapkan harga.rata-rata kekasaran permukaan. Setiap permukaan yang telah mengalami proses permesinan akan mengalami kekasaran permukaan tertentu, misalnya mengkilap, halus maupun kasar. Proses permesinan ini akan menentukan kekasaran permukaan pada level tertentu. Untuk bagian perencana kerja, bagian perhitungan biaya, maupun operator, harus mengetahui tingkat kekasaran permukaan, yang harus dicapai pada benda kerja. Proses pemesinan kualitas kekasaran permukaan yang paling umum adalah harga kekasaran rata-rata aritmatik (Ra) yaitu, seba gai standar kualitas permukaan dari hasil pemotongan maksimum yang diijinkan. Dimana posisi Ra dan parameter kekasaran yang lain, bentuk profil, panjang sampel dan panjang pengukuran yang dilakukan oleh mesin-mesikekasaran permukaan dapat dilihat seperti pada gambar ukur 1.1 METODE PENELITIAN Diagram Alir 1.1 Benda Uji Bahan matrial yang digunakann pada penelitian ini adalah baja S45C yang diproduksi oleh PT. BHINNEKA BAJANAS yang akan dikerjakan dengan proses pembubutan dengan spesifikasi sebagai berikut : Gambar 1.1 Parameter-parameter dalam profil permukaan. Gambar 3.2Benda kerja Tabel 3.1 Sifat- sifat Mekanikk Baja EMS 45 Sifat Mekanik Baja EMS 45 Kekerasan 10 HB Tegangan Luluh (σy) 43,44 ( kg/mm²) Tegangan Maksimal (σu) 7,74 (kg/mm²) Young s Modulus (GPa) 207 GPa (Sumber : PT. Bhineka Bajanas, 2014) Tabel 3.2 Komposisi Kimia Baja EMS 45 Komposisi C SI MN P S CR Ni Kadar 0,43 0,24 0, 0,,01 0,023 0,35 0,0 3
3 E-Jurnal Teknik Mesin, Vol. 2 No. Desember 2014 ISSN: (Sumber : PT. Bhineka Bajanas, 2014) 1.2 Pahat Penelitian ini menggunakan jenis pahat yang disesuaikan dengan jenis matrial yaitu pahat karbide dengan kode TNMG TF dalam standar ISO termasuk dalam kelompok P dengan sudut pahat 0 Kode h = h1 l1 l2 F B Gambar 3.4 Tool Holder (Sumber : Iscar s, C24) Tabel 3.4 Ukuran Tool Holder Satuan 20 mm 125 mm 2 mm 25 mm 20 mm (Sumber : Iscar s, C3) Gambar 3.3 Pahat Sisipan Tabel 3.3 Geometri Pahat Bentuk Geometr i Pahat Satua n 1.4 Waktu dan Tempat Penelitian Tempat untuk melakukan kegiatan penelitian skripsi ini dilakukan dengan beberapa proses dan dibeberapa tempat yaitu : 1. Proses pemotongan dan pembubutan dilaksanakan di Laboraturium Teknologi Mekanik IST AKPRIND Yogykarta 2. Pengujian Kekasaran benda uji dilaksanakan di Laboraturium Pengujian Bahan UGM Yogyakarta 1.3 Holder (Sumber : Iscar s) Insert Shape Clereanc e Angel Cutting Edge Length Thicknes s Corner Radius mm S = 4,7 mm 0,4 mm Pada penelitian ini pemegang pahat (tool holders) yang berfungsi untuk menopang sisipan pahat kelompok P maka digunakan PTGNR 2020 K 1. PEMBAHASAN Pengujian kekasaran permukaan menghasilkan data berupa angka (nilai) kekasaran permukaan. Data tersebut diperoleh dari pengukuran dengan menggunakan alat ukur kekasaran Surfcorder SE Pengukuran dilakukan setelah pengerjaan benda kerja menggunakan mesin bubut PINNACHO type S0/10. Namun sebelumnya, proses penimbangan pahat sebelum dan sesudah digunakan dilakukan guna mengetahui berapa pengurangan bobot pahat setelah di gunakan. Pengerjaan benda kerja dilakukan dengan membubut rata permukaannya, denagn spesifikasi dan kodefikasi sebagai berikut agartidak terjadikekeliruan dan memudahkan dalam pengamatannya. A1 = Kecepatan Potong (Cs) 145 m/menit, Putaran Mesin (n) 0 rpm dan Feeding 0,15 mm/put A2 = Kecepatan Potong (Cs) 145 m/menit, Putaran Mesin (n) 0 rpm dan Feeding 0,2 mm/put B1 = Kecepatan Potong (Cs) 15 m/menit, Putaran Mesin (n) 1000 rpm dan Feeding 0,15 B2 = Kecepatan Potong (Cs) 15 m/menit, Putaran Mesin (n) 1000 rpm dan Feeding 0,2 C1 = Kecepatan Potong (Cs) 15 m/menit, Putaran Mesin (n) 1400 rpm dan Feeding 0,15 C2 = Kecepatan Potong (Cs) 15 m/menit, Putaran Mesin (n) 1400 rpm dan Feeding 0,2 Kemudian diambil 3 titik untuk pengujian kekasaran dari tiap-tiap spesimen. Adapun hasil pengujian kekasaran Permukaan menggunakan variasi kecepatan potong, feeding dan kedalaman pemakanan 4
4 E-Jurnal Teknik Mesin, Vol. 2 No. Desember 2014 ISSN: dari spesimen S45C dalam penelitian ini dapat dilihat pada Tabel 3.1 di bawah ini. Spesi men Tabel 3.1. Data Hasil Uji Kekasaran Dalam Pemak anan (a) Laju Pemak anan (f) Kecep atan Poton g (Vc) Respon Ra T1 A1 0,5 0, , 4 A2 0,5 0, B1 0,5 0,15 15 B2 0,5 0,2 15 4, C1 0,5 0, , 0 C2 0,5 0,2 15 2, 4, Keterangan : T1 T2 T3 Ra : Titik Pertama : Titik kedua : Titik Ketiga : Rata-rata T 2 7 4, T , 7, R a ,1 Pengaruh Feeding dan Gaya Pemotongan Terhadap Kekasaran Permukan Untuk mengetahui pengaruh feeding terhadap kekasaran permukaan maka dilakukan perbandingan melalui grafik di bawah dari berbagai spesimen dengan variasi kecepatan potong yang berbeda. Pengaruh Feeding Terhadap Kekasaran Permukaan Kekasaran permukaan (µm) T1 T2 T3 Titik Pengujian Grafik 4.1 Pengaruh Feeding Terhadap Kekasaran permukaan Pengaruh Kecepatan Potong dan Keausan Pahat terhadap Kekasaran Permukaan A1 A2 B1 B2 c1 c2 Untuk mengetahui pengaruh Kecepatan Potong dan feeding terhadap kekasaran permukaan maka dilakukan perbandingan melalui grafik di bawah untuk memudahkan pengamatan dan menghindari kekeliruan : Kekasaran Permukaan (µm) Grafik 4.2 Pengaruh kecepatan Potong Terhadap Kekasaran Permukaan PENUTUP Kesimpulan Saran 1. Kualitas pembubutan muka rata dengan kecepatan potong 145 m/menit dengan sebesar. 2. Kualitas pembubutan muka rata dengan kecepatan potong 15 m/menit dengan sebesar Kualitas pembubutan muka rata dengan kecepatan potong 15 m/menit dengan sebesar 2,1. Dari pertimbangan hasil penelitian maka disarankan untuk memperoleh kualitas pembubutan dengan tingkat kekasaran permukaan yang baik pada proses pembubutan bahan S45C angka parameter feeding diperkecil yaitu 0,15 mm/put. Untuk variasi kecepatan potong diambil dari tabel berdasarkan jenis pahat dan matrial dalam pemotongan halus 14 1 dan 15 m/menit dan pilih mesin yang mempnyai kecepatan spindel yang paling mendekati hasil perhitungan. PUSTAKA Pengaruh Kecepatan Potong (Vc) Terhadap Kekasaran Permukaan Kecepatan Pemotongan (m/menit) A.Schey, John Proses Manufaktur. Terjemahan oleh Ir. Rines M.T., Edisi ketiga. Penerbit Andi. Yogyakarta. Feed 5
5 E-Jurnal Teknik Mesin, Vol. 2 No. Desember 2014 ISSN: Daryus, Asyari [2007], Diktat Kuliah Proses Produksi II, Fakultas Teknik Universitas Darma Persada, Jakarta ISCAR s untrmodern facilities for the manufacturing of tooling and boreng products are certified QS-000 adan ISO 00 Complete Machining Solution Turning Tools PT. Bhineka Bajanas. 2014, Produksi Besi S45C bersertifikat, Semarang. Tarmawan, Buku Panduan OperatorMachining, Departement Of Training, PT Texmaco Perkasa Engineering kaliwungu,kendal
Pengaruh Jenis Pahat dan Cairan Pendingin
Pengaruh Jenis Pahat dan Cairan Pendingin PENGARUH JENIS PAHAT DAN CAIRAN PENDINGIN SERTA KEDALAMAN PEMAKANAN TERHADAP TINGKAT KEKASARAN DAN KEKERASAN PERMUKAAN BAJA ST 60 PADA PROSES BUBUT KONVENSIONAL
Lebih terperinciEFFECT OF CUTING SPEED USING MATERIAL HSS TOOL AND CARBIDE TOOL FOR LATHE PRICESS OF MATERIAL AISI 1010 FOR QUALITY LATHE TOOL WEAR
EFFECT OF CUTING SPEED USING MATERIAL HSS TOOL AND CARBIDE TOOL FOR LATHE PRICESS OF MATERIAL AISI 1010 FOR QUALITY LATHE TOOL WEAR Joko Waluyo 1 1 Jurusan Teknik Mesin, Fakultas Teknik Industri, Institut
Lebih terperinciAnalisa Pengaruh Gerak Makan Dan Putaran Spindel Terhadap Keausan Pahat Pada Proses Bubut Konvensional
R E.M. (Rekayasa Energi Manufaktur) Jurnal "" # $ $ % & %" % ' " () http://dx.doi.org/0.2070/r.e.m.v2i.842 Analisa Pengaruh Gerak Makan Dan Putaran Spindel Terhadap Keausan Pahat Pada Proses Bubut Konvensional
Lebih terperinciMachine; Jurnal Teknik Mesin Vol. 3 No. 2, Juli 2017 P-ISSN : E-ISSN :
PENGARUH GERAK PEMAKANAN (FEEDING) PADA PROSES PEMOTONGAN BENDA KERJA S45C TERHADAP HASIL KEKASARAN PERMUKAAN BENDA KERJA MENGGUNAKAN PAHAT BUBUT HSS DI MESIN BUBUT KONVENSIONAL Rizan Afringga, R.Priyoko
Lebih terperinciPENGUKURAN KEKASARAN PROFIL PERMUKAAN BAJA ST37 PADA PEMESINAN BUBUT BERBASIS KONTROL NUMERIK
PENGUKURAN KEKASARAN PROFIL PERMUKAAN BAJA ST37 PADA PEMESINAN BUBUT BERBASIS KONTROL NUMERIK Zulfikar Akbar Mohammad *, Naufal Abdurrahman * and Mutiarani Politeknik Negeri Batam Jurusan Teknik Mesin
Lebih terperinciPengaruh Jenis Pahat, Kecepatan Spindel dan Kedalaman Pemakanan terhadap Tingkat Kekasaran Permukaan Baja S45C
Pengaruh Jenis Pahat, Kecepatan Spindel dan Kedalaman Pemakanan terhadap Tingkat Kekasaran Permukaan Baja S45C PENGARUH JENIS PAHAT, KECEPATAN SPINDEL DAN KEDALAMAN PEMAKANAN TERHADAP TINGKAT KEKASARAN
Lebih terperinciPENGARUH TEBAL PEMAKANAN DAN KECEPATAN POTONG PADA PEMBUBUTAN KERING MENGGUNAKAN PAHAT KARBIDA TERHADAP KEKASARAN PERMUKAAN MATERIAL ST-60
PENGARUH TEBAL PEMAKANAN DAN KECEPATAN POTONG PADA PEMBUBUTAN KERING MENGGUNAKAN PAHAT KARBIDA TERHADAP KEKASARAN PERMUKAAN MATERIAL ST-60 Hasrin Jurusan Teknik Mesin Politeknik Negeri Lhokseumawe Jl.Banda
Lebih terperinciPengaruh Kecepatan Putar Terhadap Kekasaran Permukaan Kayu Medang pada Proses Pembubutan
Pengaruh Kecepatan Putar Terhadap Kekasaran Permukaan Kayu Medang pada Proses Pembubutan Vivien Diawani*, Ihsan Saputra, Nidia Yuniarsih *Batam Polytechnics Mechanical Engineering Study Program Jl. Ahmad
Lebih terperinciStudi Eksperimental tentang Pengaruh Parameter Pemesinan Bubut terhadap Kekasaran Permukaan pada Pemesinan Awal dan Akhir
Studi Eksperimental tentang Pengaruh Parameter Pemesinan Bubut terhadap Kekasaran Permukaan pada Pemesinan Awal dan Akhir Agung Premono 1, a *, Triyono 1, R. Ramadhani 2, N. E. Fitriyanto 2 1 Dosen, Jurusan
Lebih terperinciPENGARUH LAJU PEMAKANAN DAN KECEPATAN POTONG PAHAT CARBIDE TERHADAP KEKASARAN PERMUKAAN BENDA BUBUT S45C KONDISI NORMAL DAN DIKERASKAN
POLITEKNOLOGI VOL. 11 NO. 3, SEPTEMBER 2012 PENGARUH LAJU PEMAKANAN DAN KECEPATAN POTONG PAHAT CARBIDE TERHADAP KEKASARAN PERMUKAAN BENDA BUBUT S45C KONDISI NORMAL DAN DIKERASKAN Darius Yuhas Dosen Teknik
Lebih terperinciPENGARUH FEEDING DAN SUDUT POTONG UTAMA TERHADAP KEKASARAN PERMUKAAN LOGAM HASIL PEMBUBUTAN RATA PADA MATERIAL BAJA ST 37
PENGARUH FEEDING DAN SUDUT POTONG UTAMA TERHADAP KEKASARAN PERMUKAAN LOGAM HASIL PEMBUBUTAN RATA PADA MATERIAL BAJA ST 37 ADENG PRIANA 2011 / 1106805 PENDIDIKAN TEKNIK MESIN JURUSAN TEKNIK MESIN FAKULTAS
Lebih terperinciKata kunci: Proses Milling, Variasi Kecepatan Putar dan Kedalaman Makan, Surface Roughness
Uji Kekasaran Permukaan Benda Kerja Pada Baja ST 37 Hasil Proses Milling Akibat Variasi Kecepatan Putar dan Kedalaman Makan Menggunakan Surface Roughness Tester Widson*, Naufal Abdurrahman P, Cahyo Budi
Lebih terperinciPengaruh Kedalaman Potong, Kecepatan Putar Spindel, Sudut Potong Pahat Terhadap Kekasaran Permukaan Hasil Bubut Konvensional Bahan Komposit
Pengaruh Kedalaman Potong, Kecepatan Spindel, Sudut Potong Pahat Terhadap Kekasaran Permukaan Komposit Pengaruh Kedalaman Potong, Kecepatan Putar Spindel, Sudut Potong Pahat Terhadap Kekasaran Permukaan
Lebih terperinciPROSES FREIS ( (MILLING) Paryanto, M.Pd.
PROSES FREIS ( (MILLING) Paryanto, M.Pd. Jur.. PT. Mesin FT UNY Proses pemesinan freis (milling) adalah penyayatan benda kerja menggunakan alat dengan mata potong jamak yang berputar. proses potong Mesin
Lebih terperinciAlfian Eko Hariyanto S1 Pendidikan Teknik Mesin, Fakultas Teknik, Universitas Negeri Surabaya
Pengaruh Jenis Pahat, Jenis Pendingin dan Kecepatan Pemakanan terhadap kekasaran permukaan Baja ST 42 PENGARUH JENIS PAHAT, JENIS PENDINGIN DAN KECEPATAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN BAJA ST
Lebih terperinciANALISIS TOPOGRAFI PERMUKAAN LOGAM DAN OPTIMASI PARAMETER PEMOTONGAN PADA PROSES MILLING ALUMINIUM ALLOY
ANALISIS TOPOGRAFI PERMUKAAN LOGAM DAN OPTIMASI PARAMETER PEMOTONGAN PADA PROSES MILLING ALUMINIUM ALLOY Sobron Yamin Lubis & Agustinus Christian Jurusan Teknik Mesin, Fakultas Teknik Universitas Tarumanagara
Lebih terperinciKAJIAN UMUR PAHAT PADA PEMBUBUTAN KERING DAN KERAS BAJA AISI 4340 MENGGUNAKAN PAHAT KARBIDA PVD BERLAPIS
KAJIAN UMUR PAHAT PADA PEMBUBUTAN KERING DAN KERAS BAJA AISI 4340 MENGGUNAKAN PAHAT KARBIDA PVD BERLAPIS SKRIPSI Skripsi Yang Diajukan Untuk Melengkapi Syarat Memperoleh Gelar Sarjana Teknik PIETER 120401043
Lebih terperinciOPTIMASI PARAMETER PEMESINAN TANPA FLUIDA PENDINGIN TERHADAP MUTU BAJA AISI Jl. Jend. Sudirman Km 3 Cilegon,
OPTIMASI PARAMETER PEMESINAN TANPA FLUIDA PENDINGIN TERHADAP MUTU BAJA AISI 1045 Haryadi 1, Slamet Wiyono 2, Iman Saefuloh 3, Muhamad Rizki Mutaqien 4 1,2,3,4 Jurusan Teknik Mesin, Fakultas Teknik, Universitas
Lebih terperinciPENGUJIAN KEBULATAN HASIL PEMBUBUTAN POROS ALUMINIUM PADA LATHE MACHINE TYPE LZ 350 MENGGUNAKAN ALAT UKUR ROUNDNESS TESTER MACHINE
PENGUJIAN KEBULATAN HASIL PEMBUBUTAN POROS ALUMINIUM PADA LATHE MACHINE TYPE LZ 350 MENGGUNAKAN ALAT UKUR ROUNDNESS TESTER MACHINE Rachman Saputra 1, Dodi Sofyan Arief 2, Adhy Prayitno 3 1 Mahasiswa Jurusan
Lebih terperinciPENGARUH VARIASI PUTARAN SPINDEL DAN KEDALAMAN PEMOTONGAN TERHADAP KEKASARAN PERMUKAAN BAJA ST 60 PADA PROSES BUBUT KONVENSIONAL
PENGARUH VARIASI PUTARAN SPINDEL DAN KEDALAMAN PEMOTONGAN TERHADAP KEKASARAN PERMUKAAN BAJA ST 60 PADA PROSES BUBUT KONVENSIONAL Muhammad Sabil 1, Ilyas Yusuf 2, Sumardi 2, 1 Mahasiswa Prodi D-IV Teknik
Lebih terperinciPENGARUH VARIASI PUTARAN BENDA KERJA DAN PUTARAN TOOL MENGGUNAKAN METODE PEMAKANAN TANGENSIAL PADA PROSES TURN-MILLING TERHADAP KEKASARAN PERMUKAAN
PENGARUH VARIASI PUTARAN BENDA KERJA DAN PUTARAN TOOL MENGGUNAKAN METODE PEMAKANAN TANGENSIAL PADA PROSES TURN-MILLING TERHADAP KEKASARAN PERMUKAAN Gusmardani Jefryanto 1 dan Yohanes 2 Laboratorium Teknologi
Lebih terperinciPENGARUH KETEBALAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN PADA MATERIAL S45C
Budha Maryanti (2016), TRANSMISI, Vol-XII Edisi-2/ Hal. 73-78 PENGARUH KETEBALAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN PADA MATERIAL S45C Budha Maryanti 1 Abstract Process that uses a CNC lathe is required
Lebih terperinciJTM. Volume 01 Nomor 03 Tahun 2013, 48-55
JTM. Volume 01 Nomor 03 Tahun 2013, 48-55 PENGARUH JENIS PAHAT, KECEPATAN SPINDEL, DAN KEDALAMAN PEMAKANAN TERHADAP TINGKAT KEKASARAN DAN KEKERASAN PERMUKAAN BAJA ST. 42 PADA PROSES BUBUT KONVENSIONAL
Lebih terperinciPENGARUH KECEPATAN POTONG PADA PROSES PEMBUBUTAN TERHADAP SURFACE ROUGHNESS DAN TOPOGRAFI PERMUKAAN MATERIAL ALUMINIUM ALLOY
PENGARUH KECEPATAN POTONG PADA PROSES PEMBUBUTAN TERHADAP SURFACE ROUGHNESS DAN TOPOGRAFI PERMUKAAN MATERIAL ALUMINIUM ALLOY Sobron Yamin Lubis 1, Erwin Siahaan 2 dan Kevin Brian 3 1,2,3 Jurusan Teknik
Lebih terperinciPENGARUH KECEPATAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN MATERIAL JIS G-3123 SS 41 DENGAN METODE TAGUCHI
PENGARUH KECEPATAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN MATERIAL JIS G-3123 SS 41 DENGAN METODE TAGUCHI Mustaqim 1, Kosjoko 2, Asmar Finali 3 1 Mahasiswa, 2 Dosen Pembimbing I, 3 Dosen Pembimbing II
Lebih terperinciPENGARUH PENGARUH JENIS COOLANT DAN VARIASI SIDE CUTTING EDGE ANGLE TERHADAP KEKASARAN PERMUKAAN BUBUT TIRUS BAJA EMS 45
PENGARUH PENGARUH JENIS COOLANT DAN VARIASI SIDE CUTTING EDGE ANGLE TERHADAP KEKASARAN PERMUKAAN BUBUT TIRUS BAJA EMS 45 Ma ruf Mujahid 1, Wirawan Sumbodo 2, Pramono 3 1.2.3 Prodi PendidikanTeknik Mesin,
Lebih terperinciANALISIS PENGARUH CUTTING SPEED DAN FEEDING RATE MESIN BUBUT TERHADAP KEKASARAN PERMUKAAN BENDA KERJA DENGAN METODE ANALISIS VARIANS
ANALISIS PENGARUH CUTTING SPEED DAN FEEDING RATE MESIN BUBUT TERHADAP KEKASARAN PERMUKAAN BENDA KERJA DENGAN METODE ANALISIS VARIANS Rakian Trisno Valentino Febriyano 1), Agung Sutrisno ), Rudy Poeng 3)
Lebih terperinciANALISIS PEMOTONGAN RODA GILA (FLY WHEEL) PADA PROSES PEMESINAN CNC BUBUT VERTIKAL 2 AXIS MENGGUNAKAN METODE PEMESINAN KERING (DRY MACHINING)
ANALISIS PEMOTONGAN RODA GILA (FLY WHEEL) PADA PROSES PEMESINAN CNC BUBUT VERTIKAL 2 AXIS MENGGUNAKAN METODE PEMESINAN KERING (DRY MACHINING) IRVAN YURI SETIANTO NIM: 41312120037 PROGRAM STUDI TEKNIK MESIN
Lebih terperinciPENGARUH PARAMETER PEMOTONGAN TERHADAP KEKASARAN PERMUKAAN PADA PROSES BUBUT BAJA AISI 1045
PENGARUH PARAMETER PEMOTONGAN TERHADAP KEKASARAN PERMUKAAN PADA PROSES BUBUT BAJA AISI 1045 Yuni Hermawan Jurusan Teknik Mesin -Fakultas Teknik - Universitas Jember Email: yunikaka@yahoo.co.id ABSTRAK
Lebih terperinciANALISIS KEAUSAN PAHAT TERHADAP KUALITAS PERMUKAAN BENDA KERJA PADA PROSES PEMBUBUTAN
ANALISIS KEAUSAN PAHAT TERHADAP KUALITAS PERMUKAAN BENDA KERJA PADA PROSES PEMBUBUTAN Eko Prasetyo, Hendri Sukma 2, Agri Suwandi 2 Jurusan Teknik Mesin Universitas Pancasila, Srengseng Sawah Jagakarsa,
Lebih terperinciPENGARUH VARIASI SUDUT UJUNG MATA POTONG KARBIDA TERHADAP KEKASARAN DAN TOPOGRAFI PERMUKAAN LOGAM Al 6061 PADA PROSES PEMBUBUTAN
PENGARUH VARIASI SUDUT UJUNG MATA POTONG KARBIDA TERHADAP KEKASARAN DAN TOPOGRAFI PERMUKAAN LOGAM Al 6061 PADA PROSES PEMBUBUTAN Sobron Lubis, Rosehan dan Rico Wiguna Program Studi Teknik Mesin Fakultas
Lebih terperinciANALISIS UMUR PAHAT DAN BIAYA PRODUKSI PADA PROSES DRILLING TERHADAP MATERIAL S 40 C
ANALISIS UMUR PAHAT DAN BIAYA PRODUKSI PADA PROSES DRILLING TERHADAP MATERIAL S 40 C 1 Azwinur, 2 Taufiq 1 Jurusan Teknik Mesin, Politeknik Negeri Lhokseumawe Jl. Banda Aceh-Medan Km.280 Buketrata Lhokseumawe.
Lebih terperinciPENGARUH KEKASARAN PERMUKAAN TERHADAP KEKUATAN TARIK BAJA AISI 4140 AFRIANGGA PRATAMA 2011/ PENDIDIKAN TEKNIK MESIN
PENGARUH KEKASARAN PERMUKAAN TERHADAP KEKUATAN TARIK BAJA AISI 4140 AFRIANGGA PRATAMA 2011/1102520 PENDIDIKAN TEKNIK MESIN JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS NEGERI PADANG 2016 PENGARUH
Lebih terperinciAplikasi Cairan Pelumas Pada Pengeboran Pelat ASTM A1011 Menggunakan Mata Bor HSS
Jurnal Mechanical, Volume 5, Nomor 2, September 214 Aplikasi Cairan Pelumas Pada Pengeboran Pelat ASTM A111 Menggunakan Mata Bor HSS Arinal Hamni, Anjar Tri Gunadi, Gusri Akhyar Ibrahim Jurusan Teknik
Lebih terperinciOPTIMASI PARAMETER PROSES BUBUT PADA BAJA St 60 DENGAN MENGGUNAKAN METODE TAGUCHI
OPTIMASI PARAMETER PROSES BUBUT PADA BAJA St 60 DENGAN MENGGUNAKAN METODE TAGUCHI *Fonsa Careca 1, Rusnaldy 2 1 Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik, Universitas Diponegoro 2 Dosen Jurusan Teknik
Lebih terperinciPengaruh Kedalaman Pemakanan, Jenis Pendinginan dan Kecepatan Spindel
Pengaruh Kedalaman Pemakanan, Jenis Pendinginan dan Kecepatan Spindel PENGARUH KEDALAMAN PEMAKANAN, JENIS PENDINGINAN DAN KECEPATAN SPINDEL TERHADAP KERATAAN DAN KEKASARAN PERMUKAAN BAJA ST 42 PADA PROSES
Lebih terperinciBAB I PENDAHULUAN 1.1 Latar Belakang
BAB I PENDAHULUAN 1.1 Latar Belakang Kaca banyak digunakan dalam kehidupan sehari-hari terutama untuk peralatan optik dan biochips akan tetapi proses fabrikasi kaca sangat terbatas, terutama untuk proses-proses
Lebih terperinciPENGARUH JENIS PAHAT, JENIS PENDINGINAN DAN KEDALAMAN PEMAKANAN TERHADAP KERATAAN DAN KEKASARAN PERMUKAAN BAJA ST 42 PADA PROSES BUBUT RATA MUKA
Pengaruh Jenis Pahat, Jenis Pendinginan dan Kedalaman Pemakanan PENGARUH JENIS PAHAT, JENIS PENDINGINAN DAN KEDALAMAN PEMAKANAN TERHADAP KERATAAN DAN KEKASARAN PERMUKAAN BAJA ST 42 PADA PROSES BUBUT RATA
Lebih terperinciJTM. Volume 03 Nomor 01 Tahun 2014,
JTM. Volume 03 Nomor 01 Tahun 2014, 120-125 PENGARUH VARIASI KEDALAMAN PEMAKANAN DAN KECEPATAN PUTAR SPINDLE TERHADAP TINGKAT KEKASARAN PERMUKAAN ALUMINIUM 6061 PADA MESIN CNC TU- 2A DENGAN PROGRAM ABSOLUT
Lebih terperinciOPTIMASI PARAMETER PROSES BUBUT PADA BERBAGAI JENIS BAJA DENGAN MEDIA PENDINGIN COOLED AIR JET COOLING
OPTIMASI PARAMETER PROSES BUBUT PADA BERBAGAI JENIS BAJA DENGAN MEDIA PENDINGIN COOLED AIR JET COOLING *Muhammad Taufik Fitriadi Febrianto 1, Rusnaldy 2 1 Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik,
Lebih terperinciPROSES PEMBUBUTAN LOGAM. PARYANTO, M.Pd.
PROSES PEMBUBUTAN LOGAM PARYANTO, M.Pd. Jur.. PT. Mesin FT UNY Proses bubut adalah proses pemesinan untuk menghasilkan bagian-bagian mesin (komponen) berbentuk silindris yang dikerjakan dengan menggunakan
Lebih terperinciTUGAS SARJANA PENGUKURAN GAYA PEMOTONGAN PADA PROSES BUBUT DENGAN MENGGUNAKAN DYNAMOMETER
TUGAS SARJANA PENGUKURAN GAYA PEMOTONGAN PADA PROSES BUBUT DENGAN MENGGUNAKAN DYNAMOMETER Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Kesarjanaan Strata Satu (S-1) di Jurusan Teknik Mesin
Lebih terperinciOptimasi Cutting Tool Carbide pada Turning Machine dengan Geometry Single Point Tool pada High Speed
ISBN 978-979-3541-50-1 IRWNS 2015 Optimasi Cutting Tool Carbide pada Turning Machine dengan Geometry Single Point Tool pada High Speed Badruzzaman a, Dedi Suwandi b a Jurusan Teknik Mesin,Politeknik Negeri
Lebih terperinciGambar I. 1 Mesin Bubut
BAB I PENDAHULUAN Latar Belakang Kata manufaktur berasal dari bahasa latin manus dan factus yang berarti dibuat dengan tangan. Kata manufacture muncul pertama kali tahun 1576, dan kata manufacturing muncul
Lebih terperinciOPTIMASI PROSES PEMBUATAN MOBIL KAYU DENGAN MESIN CNC ROUTER PADA INDUSTRI BATIK KAYU
OPTIMASI PROSES PEMBUATAN MOBIL KAYU DENGAN MESIN CNC ROUTER PADA INDUSTRI BATIK KAYU Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan Teknik Mesin Fakultas Teknik Oleh
Lebih terperinciMATERI KULIAH PROSES PEMESINAN KERJA BUBUT. Dwi Rahdiyanta FT-UNY
MATERI KULIAH PROSES PEMESINAN KERJA BUBUT Pengoperasian Mesin Bubut Dwi Rahdiyanta FT-UNY Kegiatan Belajar Pengoperasian Mesin Bubut a. Tujuan Pembelajaran. 1.) Siswa dapat memahami pengoperasian mesin
Lebih terperinciSTUDI PENGARUH SUDUT POTONG (Kr) PAHAT KARBIDA PADA PROSES BUBUT DENGAN TIPE PEMOTONGAN OBLIQUE TERHADAP KEKASARAN PERMUKAAN
NASKAH PUBLIKASI TUGAS AKHIR STUDI PENGARUH SUDUT POTONG (Kr) PAHAT KARBIDA PADA PROSES BUBUT DENGAN TIPE PEMOTONGAN OBLIQUE TERHADAP KEKASARAN PERMUKAAN Diajukan Untuk Memenuhi Tugas Dan Syarat - Syarat
Lebih terperinciPENERAPAN PENILAIAN KEKASARAN PERMUKAAN (SURFACE ROUGHNESS ASSESSMENT) BERBASIS VISI PADA PROSES PEMBUBUTAN BAJA S45C
PENERAPAN PENILAIAN KEKASARAN PERMUKAAN (SURFACE ROUGHNESS ASSESSMENT) BERBASIS VISI PADA PROSES PEMBUBUTAN BAJA S45C Yanuar Burhanuddin, Suryadiwansa Harun, Evans Afriant N., Tomy D.A. Jurusan Teknik
Lebih terperinciJTM. Volume 03 Nomor 02 Tahun 2014, 38-43
JTM. Volume 03 Nomor 02 Tahun 2014, 38-43 PENGARUH JUMLAH MATA SAYAT ENDMILL CUTTER, KEDALAMAN PEMAKANAN DAN KECEPATAN PEMAKANAN (FEEDING) TERHADAP TINGKAT KEKASARAN PERMUKAAN BENDA KERJA PADA MESIN MILING
Lebih terperinciPERBANDINGAN TINGKAT KEKASARAN DAN GETARAN PAHAT PADA PEMOTONGAN ORTHOGONAL DAN OBLIQUE AKIBAT SUDUT POTONG PAHAT
Perbandingan Tingkat Kekasaran dan Getaran Pahat Pada Pemotongan Orthogonal dan Oblique Akibat Sudut Pahat PERBANDINGAN TINGKAT KEKASARAN DAN GETARAN PAHAT PADA PEMOTONGAN ORTHOGONAL DAN OBLIQUE AKIBAT
Lebih terperinciKerataan Permukaan dan Bentuk Geram
Kerataan Permukaan dan Bentuk Geram PENGARUH JENIS PAHAT, KECEPATAN SPINDEL, DAN KEDALAMAN PEMAKANAN TERHADAP TINGKAT KERATAAN PERMUKAAN DAN BENTUK GERAM BAJA ST. 60 PADA PROSES BUBUT KONVENSIONAL MUHAMMAD
Lebih terperinciSTUDI EKSPERIMENTAL PENGARUH KEMIRINGAN SISI POTONG PAHAT DAN KECEPATAN POTONG TERHADAP KUALITAS KEKASARAN PERMUKAAN MATERIAL PADA SHAPING MACHINE
STUDI EKSPERIMENTAL PENGARUH KEMIRINGAN SISI POTONG PAHAT DAN KECEPATAN POTONG TERHADAP KUALITAS KEKASARAN PERMUKAAN MATERIAL PADA SHAPING MACHINE Disusun oleh : H a r i y a n t o Politeknik Perkapalan
Lebih terperinciPoliteknik Negri Batam Program Studi Teknik Mesin Jl. Ahmad Yani, Batam Centre, Batam 29461, Indonesia
Pengaruh Kecepatan Putar Alat Potong (Spindle ) dan Kedalaman Pemakanan (Depth Of Cut) Proses Milling pada Aluminium Alloy Terhadap Kehalusan Permukaan Produk Muhammad Irwan Arinanda *, Hanifah Widyastuti
Lebih terperinciPengaruh Perubahan Parameter Pemesinan Terhadap Surface Roughness Produk Pada Proses Pemesinan dengan Single Cutting Tool
Pengaruh Perubahan Parameter Pemesinan Terhadap Surface Roughness Produk Pada Proses Pemesinan dengan Single Cutting Tool Sally Cahyati 1,a, Triyono, 2,b M Sjahrul Annas 3,c, A.Sumpena 4,d 1,2,3 Jurusan
Lebih terperinciOPTIMASI KEKASARAN PADA COPY TURNING DENGAN VARIASI PARAMETER KEDALAMAN PEMAKANAN, KECEPATAN POTONG DAN GERAK MAKAN
OPTIMASI KEKASARAN PADA COPY TURNING DENGAN VARIASI PARAMETER KEDALAMAN PEMAKANAN, KECEPATAN POTONG DAN GERAK MAKAN 1 Widodo, 2 Mahros Darsin 1 Jurusan Teknik Mesin Politeknik Negeri Batam Parkway Street
Lebih terperinciKAJIAN GAYA PEMOTONGAN DAN KEKASARAN PERMUKAAN PADA PROSES PEMBUBUTAN BERBAGAI MATERIAL MENGGUNAKAN PAHAT HSS
KAJIAN GAYA PEMOTONGAN DAN KEKASARAN PERMUKAAN PADA PROSES PEMBUBUTAN BERBAGAI MATERIAL MENGGUNAKAN PAHAT HSS SKRIPSI Diajukan sebagai salah satu syarat Untuk memperoleh gelar Sarjana Teknik Oleh : ANZIZAN
Lebih terperinciPengaruh Kemiringan Benda Kerja dan Kecepatan Pemakanan terhadapgetaran Mesin Frais Universal Knuth UFM 2
Pengaruh Kemiringan Benda Kerja dan Kecepatan Pemakanan terhadapgetaran Mesin Frais Universal Knuth UFM 2 Romiyadi 1 1 Program Studi Perawatan dan Perbaikan Mesin, Politeknik Kampar Jl. Tengku Muhammad
Lebih terperinciSimulasi Komputer untuk Memprediksi Besarnya Daya Pemotongan pada Proses Pembubutan Silindris
Seminar Nasional Tahunan Teknik Mesin, SNTTM-VI, 2007 Jurusan Teknik Mesin, Universitas Syiah Kuala Simulasi Komputer untuk Memprediksi Besarnya Daya Pemotongan pada Proses Pembubutan Silindris Muhammad
Lebih terperinciBAB I PENDAHULUAN. Pentingnya proses permesinan merupakan sebuah keharusan. mesin dari logam. Proses berlangsung karena adanya gerak
BAB I PENDAHULUAN 1.1. Latar Belakang Pentingnya proses permesinan merupakan sebuah keharusan dalam industri manufaktur terutama untuk pembuatan komponenkomponen mesin dari logam. Proses berlangsung karena
Lebih terperinciBEKERJA DENGAN MESIN BUBUT
BEKERJA DENGAN MESIN BUBUT STANDAR KOMPETENSI KERJA NASIONAL INDONESIA (SKKNI) BIDANG KOMPETENSI 1. KELOMPOK DASAR / FOUNDATION 2. KELOMPOK INTI 3. PERAKITAN (ASSEMBLY) 4. PENGECORAN DAN PEMBUATAN CETAKAN
Lebih terperinciPENGUJIAN KEBULATAN HASIL PEMBUATAN POROS ALUMINIUM MENGGUNAKAN EMCO T.U CNC -2A SMKN2 PEKANBARU DENGAN ROUNDNESS TESTER MACHINE
PENGUJIAN KEBULATAN HASIL PEMBUATAN POROS ALUMINIUM MENGGUNAKAN EMCO T.U CNC -2A SMKN2 PEKANBARU DENGAN ROUNDNESS TESTER MACHINE Erizal Hamdi 1,Dodi Sofyan Arief 2, Adhy Prayitno 3 1 Mahasiswa Jurusan
Lebih terperinciPENGARUH KECEPATAN PUTAR SPINDLE (RPM) DAN JENIS SUDUT PAHAT PADA PROSES PEMBUBUTAN TERHADAP TINGKAT KEKASARAN BENDA KERJA BAJA EMS 45
PENGARUH KECEPATAN PUTAR SPINDLE (RPM) DAN JENIS SUDUT PAHAT PADA PROSES PEMBUBUTAN TERHADAP TINGKAT KEKASARAN BENDA KERJA BAJA EMS 45 Mohammad Farokhi 1, Wirawan Sumbodo 2, Rusiyanto 3 1.2.3 Pendidikan
Lebih terperinciMomentum, Vol. 12, No. 1, April 2016, Hal. 1-8 ISSN , e-issn
Momentum, Vol. 12, No. 1, April 2016, Hal. 1-8 ISSN 0216-7395, e-issn 2406-9329 PENGARUH ARAH PEMAKANAN DAN SUDUT PERMUKAAN BIDANG KERJA TERHADAP KEKASARAN PERMUKAAN MATERIAL S45C PADA MESIN FRAIS CNC
Lebih terperinciTUGAS SARJANA OPTIMASI PARAMETER PEMESINAN PROSES CNC FREIS TERHADAP HASIL KEKASARAN PERMUKAAN DAN KEAUSAN PAHAT MENGGUNAKAN METODE TAGUCHI
TUGAS SARJANA OPTIMASI PARAMETER PEMESINAN PROSES CNC FREIS TERHADAP HASIL KEKASARAN PERMUKAAN DAN KEAUSAN PAHAT MENGGUNAKAN METODE TAGUCHI Diajukan sebagai Salah Satu Syarat untuk Memperoleh Gelar Kesarjanaan
Lebih terperinciBAB II LANDASAN TEORI
BAB II LANDASAN TEORI 2.1 Proses Pemesinan Untuk membuat suatu alat atau produk dengan bahan dasar logam haruslah di lakukan dengan memotong bahan dasarnya. Proses pemotongan ini dapat dilakukan dengan
Lebih terperinciPENGARUH PERUBAHAN KECEPATAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN PADA PROSES PEMBUBUTAN
PENGARUH PERUBAHAN KECEPATAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN PADA PROSES PEMBUBUTAN Hadimi Jurusan Teknik Mesin Politeknik Negeri Pontianak Email: had_imi@yahoo.co.id, hadimi.mr@gmail.com Hp: 05613038462
Lebih terperinciIman Saefuloh 1, Ipick Setiawan 2 Panji Setyo Aji 3
Pengaruh Lapisan TiN (Titanium Nitrida), TiAlN (Titanium Aluminium Nitrida) dan Non Coating Pahat Karbida Terhadap Kualitas Permukaan dan Ketahanan Keausan Pada Proses Pembubutan Baja Aisi 1045 Iman Saefuloh
Lebih terperinciPENGARUH PROSES BURNISHING TERHADAP KEKASARAN DAN KEKERASAN MILD STEEL MENGGUNAKAN MESIN BUBUT KONVENSIONAL
111 PENGARUH PROSES BURNISHING TERHADAP KEKASARAN DAN KEKERASAN MILD STEEL MENGGUNAKAN MESIN BUBUT KONVENSIONAL Guruh Purwanto 1, Didik Djoko Susilo 2, Budi Santoso 2 1 Mahasiswa Jurusan Teknik Mesin Universitas
Lebih terperinciPENGARUH GRADE BATU GERINDA, KECEPATAN MEJA LONGITUDINAL, DAN KEDALAMAN PEMAKANAN TERHADAP KEKASARAN PERMUKAAN PADA PROSES GERINDA PERMUKAAN SKRIPSI
//digilib.unej.a //digilib.unej.ac. //digilib.unej.a //digilib.unej.ac. //digilib.unej.a //digilib.unej.ac. //digilib.unej.a //digilib.unej.ac. //digilib.unej.a //digilib.unej.ac. //d //d //d //d PENGARUH
Lebih terperinciOLEH : I PUTU AGUNG MAHAPUTRA NIM
SKRIPSI PENGARUH VARIASI GERAK MAKAN DAN KEDALAMAN POTONG TERHADAP KEKASARAN PERMUKAAN TIRUS POROS BERTINGKAT PADA PROSES BUBUT DENGAN MESIN CNC LEADWELL TURNING CENTER OLEH : I PUTU AGUNG MAHAPUTRA NIM
Lebih terperinciJURNAL PENGARUH VARIASI GERAK MAKAN, KEDALAMAN POTONG DAN JENIS CAIRAN PENDINGIN TERHADAP TINGKAT KEKASARAN PERMUKAAN PEMBUBUTAN BAJA ST 37
JURNAL PENGARUH VARIASI GERAK MAKAN, KEDALAMAN POTONG DAN JENIS CAIRAN PENDINGIN TERHADAP TINGKAT KEKASARAN PERMUKAAN PEMBUBUTAN BAJA ST 37 EFFECT OF FEEDING VARIATION, CUT DEPTH AND LEVEL OF LIQUID COOLING
Lebih terperinciSTUDI PENGARUH SUDUT POTONG PAHAT HSS PADA PROSES BUBUT DENGAN TIPE PEMOTONGAN ORTHOGONAL TERHADAP KEKASARAN PERMUKAAN
NASKAH PUBLIKASI TUGAS AKHIR STUDI PENGARUH SUDUT POTONG PAHAT HSS PADA PROSES BUBUT DENGAN TIPE PEMOTONGAN ORTHOGONAL TERHADAP KEKASARAN PERMUKAAN Diajukan Untuk Memenuhi Tugas Dan Syarat-Syarat Guna
Lebih terperinciPENGARUH KECEPATAN SPINDEL, KECEPATAN PEMAKANAN DAN
digilib.uns.ac.id PENGARUH KECEPATAN SPINDEL, KECEPATAN PEMAKANAN DAN KEDALAMAN PEMAKANAN TERHADAP TINGKAT KEKASARAN PERMUKAAN BENDA KERJA HASIL PEMESINAN BUBUT CNC PADA BAJA ST 40 S K R I P S I Oleh :
Lebih terperinciBAB II MESIN BUBUT. Gambar 2.1 Mesin bubut
BAB II MESIN BUBUT A. Prinsip Kerja Mesin Bubut Mesin bubut merupakan salah satu mesin konvensional yang umum dijumpai di industri pemesinan. Mesin bubut (gambar 2.1) mempunyai gerak utama benda kerja
Lebih terperinciPENGARUH VARIABEL PEMOTONGAN PADA PEMESINAN KERING BAJA AISI 1045 MENGGUNAKAN PAHAT KARBIDA TAK BERLAPIS
PENGARUH VARIABEL PEMOTONGAN PADA PEMESINAN KERING BAJA AISI 1045 MENGGUNAKAN PAHAT KARBIDA TAK BERLAPIS Ir. Abdul Haris Nasution, MT. Staf Pengajar Jurusan Teknik Mesin Fakultas Teknik UISU Medan ABSTRAK
Lebih terperinciUNIVERSITAS DIPONEGORO
UNIVERSITAS DIPONEGORO PENGARUH CRATER WEAR DAN FLANK WEAR PAHAT TUNGSTEN CARBIDE PADA GAYA MAKAN DAN GAYA POTONG PADA PEMBUBUTAN MATERIAL AL 2024-T4 TUGAS AKHIR GUNAWAN SETIAWAN KUSCAHYANTO L2E 007 039
Lebih terperinciBab IV Data Pengujian
Bab IV Data Pengujian 4.1 Data Benda Kerja Dalam pengujian ini, benda kerja yang digunakan adalah Alumunium 2024. Komposisi dari unsur penyusunnya dapat dilihat pada tabel 4.1. Tabel 4.1. Komposisi unsur
Lebih terperinciPENGARUH JENIS MATERIAL PAHAT POTONG DAN ARAH PEMAKANAN TERHADAP KEKASARAN PERMUKAAN BAJA EMS 45 PADA PROSES CNC MILLING
PENGARUH JENIS MATERIAL PAHAT POTONG DAN ARAH PEMAKANAN TERHADAP KEKASARAN PERMUKAAN BAJA EMS 45 PADA PROSES CNC MILLING Ana Wilda Widiantoro 1, Muhammad Khumaedi 2, Wirawan Sumbodo 3 1.2.3 Pendidikan
Lebih terperinciSimulasi Komputer Untuk Memprediksi Besarnya Daya Pemotongan Pada Proses Cylindrical Turning Berdasarkan Parameter Undeformed Chip Thickness
Simulasi Komputer Untuk Memprediksi Besarnya Daya Pemotongan Pada Proses Cylindrical Turning Berdasarkan Parameter Undeformed Chip Thickness Oegik Soegihardjo Dosen Fakultas Teknologi Industri, Jurusan
Lebih terperinciBAB 3 RANCANGAN DAN PELAKSANAAN PERCOBAAN
BAB 3 RANCANGAN DAN PELAKSANAAN PERCOBAAN 3.1 Instalasi Alat Percobaan Alat yang digunakan untuk melakukan percobaan adalah mesin CNC 5 axis buatan Deckel Maho, Jerman dengan seri DMU 50 evolution. Dalam
Lebih terperinciBAB III METODE PENELITIAN. Mulai. Studi Pustaka. Persiapan Spesimen dan Peralatan. Permesinan dengan Kondisi Permesinan Kering dan Basah
BAB III METODE PENELITIAN 3.1 Diagram Alir Penelitian Mulai Studi Pustaka Persiapan Spesimen dan Peralatan Permesinan dengan Kondisi Permesinan Kering dan Basah Permesinan dengan Pemakaian Jenis Pahat
Lebih terperinciSIMULASI UNTUK MEMPREDIKSI PENGARUH PARAMETER CHIP THICKNESS TERHADAP DAYA PEMOTONGAN PADA PROSES CYLINDRICAL TURNING
Simulasi untuk Memprediksi Pengaruh... Muhammad Yusuf, M. Sayuti SIMULASI UNTUK MEMPREDIKSI PENGARUH PARAMETER CHIP THICKNESS TERHADAP DAYA PEMOTONGAN PADA PROSES CYLINDRICAL TURNING Muhammad Yusuf 1)
Lebih terperinciStudi Pengaruh Sudut Potong Pahat Hss Pada Proses Bubut Dengan Tipe Pemotongan Orthogonal Terhadap Kekasaran Permukaan
TUGAS AKHIR Studi Pengaruh Sudut Potong Pahat Hss Pada Proses Bubut Dengan Tipe Pemotongan Orthogonal Terhadap Kekasaran Permukaan Diajukan Untuk Memenuhi Tugas Dan Syarat-Syarat Guna Memperoleh Gelar
Lebih terperinciOPTIMASI PARAMETER PROSES BUBUT BAJA St 60 DENGAN MEDIA PENDINGIN COOLED AIR JET COOLING
OPTIMASI PARAMETER PROSES BUBUT BAJA St 60 DENGAN MEDIA PENDINGIN COOLED AIR JET COOLING *Gama Cahaya Putera Su-Marna 1, Rusnaldy 2 1 Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik, Universitas Diponegoro
Lebih terperinciPengaruh Jenis Pahat Bubut Terhadap Kekasaran Permukaan Hasil Bubutan pada Bahan Stainless Steel
Pengaruh Jenis Pahat Bubut Terhadap Kekasaran Permukaan Hasil Bubutan pada Bahan Stainless Steel Ida Bagus Puspa Indra 1), Tjokorda Gde Tirta Nindhia 2)*, I Nyoman Gede Antara 2) 1) Politeknik Negeri Bali,
Lebih terperinciMelakukan Pekerjaan Dengan Mesin Frais
MATERI KULIAH PROSES PEMESINAN PROSES FRAIS Melakukan Pekerjaan Dengan Mesin Frais Oleh: Dwi Rahdiyanta Fakultas Teknik Universitas Negeri Yogyakarta Kegiatan Belajar Melakukan Pekerjaan Dengan Mesin Frais.
Lebih terperinciIII. METODE PENELITIAN. Penelitian sekaligus pengambilan data dilakukan di Laboratorium Produksi dan
III. METODE PENELITIAN A. Tempat Penelitian Penelitian sekaligus pengambilan data dilakukan di Laboratorium Produksi dan Laboratorium Metrologi Universitas Lampung serta Laboratorium Material ITB Bandung
Lebih terperinciIII. METODOLOGI PENELITIAN. Penelitian ini dilakukan di Lab.Proses Produksi, CNC dan material teknik
III. METODOLOGI PENELITIAN A. Tempat Penelitian Penelitian ini dilakukan di Lab.Proses Produksi, CNC dan material teknik Jurusan Teknik mesin Universitas Lampung untuk pengukuran suhu luaran vortex tube,
Lebih terperinciBAB I PENDAHULUAN. Penggunaan mesin frais (milling) baik untuk keperluan produksi. maupun untuk kaperluan pendidikan, sangat dibutuhkan untuk
BAB I PENDAHULUAN 1.1. Latar Belakang Masalah Seiring dengan perkembangan jaman dan teknologi, Penggunaan mesin frais (milling) baik untuk keperluan produksi maupun untuk kaperluan pendidikan, sangat dibutuhkan
Lebih terperinciJURNAL KONSENTRASI TEKNIK PRODUKSI
PENGARUH CUTTING SPEED DAN RASIO L/D TERHADAP KESILINDRISAN BENDA KERJA HASIL FINISHING PADA PROSES PEMBUBUTAN TIRUS DIVERGEN DENGAN ALUMINIUM 6061 JURNAL KONSENTRASI TEKNIK PRODUKSI Diajukan untuk memenuhi
Lebih terperinciBAB III. METODOLOGI PENELITIAN. Penelitian ini akan dilaksanakan dalam 4 bulan yaitu dari bulan Oktober 2014
BAB III. METODOLOGI PENELITIAN 3.1 Waktu Dan Tempat Penelitian Penelitian ini akan dilaksanakan dalam 4 bulan yaitu dari bulan Oktober 2014 sampai dengan Januari 2014. Penelitian akan dilakukan di Laboratorium
Lebih terperinciBEKERJA DENGAN MESIN BUBUT
1 BEKERJA DENGAN MESIN BUBUT PENGERTIAN Membubut adalah proses pembentukan benda kerja dengan mennggunakan mesin bubut. Mesin bubut adalah perkakas untuk membentuk benda kerja dengan gerak utama berputar.
Lebih terperinci28 Gambar 4.1 Perancangan Produk 4.3. Proses Pemilihan Pahat dan Perhitungan Langkah selanjutnya adalah memilih jenis pahat yang akan digunakan. Karen
27 BAB IV SOP PENGOPERASIAN MESIN BUBUT KONVENSIONAL UNTUK MEMBUBUT PERMUKAAN 4.1. Ukuran Benda Kerja Sebelum melakukan proses pembubutan, langkah awal yang perlu dilakukan oleh seorang operator adalah
Lebih terperinciSAT. Pengaruh Kemiringan Spindel Dan Kecepatan Pemakanan Terhadap Getaran Mesin Frais Universal Knuth UFM 2. Romiyadi, Emon Azriadi. 1.
Teknobiologi JI SAT Jurnal Ilmiah Sains Terapan Lembaga Penelitian Universitas Riau Jurnal Teknobiologi, V(1) 2014: 31 36 ISSN : 2087 5428 Pengaruh Kemiringan Spindel Dan Kecepatan Pemakanan Terhadap Getaran
Lebih terperinciOPTIMASI PARAMETER PROSES PEMESINAN TERHADAP KEAUSAN PAHAT DAN KEKASARAN PERMUKAAN BENDA HASIL PROSES CNC TURNING DENGAN MENGGUNAKAN METODE TAGUCHI
TUGAS SARJANA OPTIMASI PARAMETER PROSES PEMESINAN TERHADAP KEAUSAN PAHAT DAN KEKASARAN PERMUKAAN BENDA HASIL PROSES CNC TURNING DENGAN MENGGUNAKAN METODE TAGUCHI Diajukan Sebagai Salah Satu Syarat Untuk
Lebih terperinciBudi Setiyana 1), Rusnaldy 2), Nuryanto 3)
PENGARUH KECEPATAN POTONG PADA PROSES PEMESINAN KECEPATAN TINGGI TERHADAP GEOMETRI DAN KEKERASAN GERAM UNTUK BEBERAPA LOGAM DENGAN VARIASI NILAI KEKUATAN TARIK Budi Setiyana 1), Rusnaldy 2), Nuryanto 3)
Lebih terperinciPENGARUH VARIASI CUTTING FLUID DAN VARIASI FEEDING PADA PROSES PEMOTONGAN ORTHOGONAL POROS BAJA TERHADAP KEKASARAN PERMUKAAN. Febi Rahmadianto 1)
PENGARUH VARIASI CUTTING FLUID DAN VARIASI FEEDING PADA PROSES PEMOTONGAN ORTHOGONAL POROS BAJA TERHADAP KEKASARAN PERMUKAAN Febi Rahmadianto 1) ABSTRAK Kondisi pemotongan yang optimum bagi suatu proses
Lebih terperinciJTM. Volume 03 Nomor 01 Tahun 2014, 40-48
PENGARUH JENIS PAHAT, KEDALAMAN PEMAKANAN, DAN JENIS CAIRAN PENDINGIN TERHADAP TINGKAT KEKASARAN DAN KERATAAN PERMUKAAN BAJA ST. 41 PADA PROSES MILLING KONVENSIONAL Navy A ang Assegaf S1 Pend Teknik Mesin,
Lebih terperinciI. PENDAHULUAN. Proses permesinan merupakan proses manufaktur dimana objek dibentuk
I. PENDAHULUAN A. Latar Belakang Proses permesinan merupakan proses manufaktur dimana objek dibentuk dengan cara membuang atau meghilangkan sebagian material dari benda kerjanya. Tujuan digunakan proses
Lebih terperinciPENGARUH JUMLAH MATA SAYAT END MILL CUTTER MENGGUNAKAN KODE PROGRAM G 02 Dan G 03 TERHADAP KERATAAN ALUMUNIUM 6061 PADA MESIN CNC TU-3A
Pengaruh Jumlah Mata Sayat End Mill Cutter Terhadap Kerataan Alumunium 6061 PENGARUH JUMLAH MATA SAYAT END MILL CUTTER MENGGUNAKAN KODE PROGRAM G 02 Dan G 03 TERHADAP KERATAAN ALUMUNIUM 6061 PADA MESIN
Lebih terperinci