Kajian Struktur Mikro Sambungan Las TIG Al-13,5Si
|
|
- Suryadi Iskandar
- 6 tahun lalu
- Tontonan:
Transkripsi
1 Kajian Struktur Mikro Sambungan Las TIG -13,5 Bayu Indriyanto 1), Hidayat Rudyanto 2) dan Wijoyo 3) 1,2,3 Teknik Mesin, Universitas Surakarta Jl. Raya Palur Km. 5 Surakarta bayu.indriyanto1993@gmail.com joyowi@yahoo.co.id ABSTRACT This study aims to investigate the influence of a strong electric current to microstructure that occurs in TIG welded joints of -13,5. Research using -13,5 materials and filler metals ER5356. TIG welding is done with strong variations in electrical current row is 90 A, 100 A and 110 A, AC TIG welding machine high frequency (ACHF) with alternating polarization, argon gas flow of 2.5 to 5 liters/min. Thick plates used are 10 mm, V-shape groove weld made double with 90 angle and weld multirun. Observation of microstructure on each specimen welding with an electric current variation obtained from micro photograph by using an optical microscope. The results show that the microstructure of metals welding currents of 100 A, a more refined grains compared with a current of 90 A and 110 A. In current 80 A, grain shape tends to be round while the current 110 A, grain shape tends to form a dendrite structure. Keywords: strong currents, TIG welding, microstructure, -13,5 1. PENDAHULUAN Logam memiliki berbagai jenis, banyak jenis logam yang digunakan oleh industri-industri besar. Salah satunya adalah aluminium dan paduannya, aluminium dan paduannya termasuk logam ringan yang mempunyai kekuatan tinggi, tahan terhadap karat dan merupakan konduktor listrik yang cukup baik. Logam ini dipakai secara luas dalam bidang kimia, listrik, bangunan, transpotasi, alat-alat penyimpanan. Kemajuan akhir-akhir ini dalam teknik pengelasan busur listrik dengan gas mulia menyebabkan pengelasan aluminium dan paduannya menjadi sederhana dan dapat dipercaya. Karena hal ini maka penggunaan aluminium dan paduannya di segala bidang telah berkembang. Awi Andoko, dkk., (2012), dalam penelitiannya yang bertujuan untuk mengetahui komposisi kimia paduan aluminium, struktur mikro, tingkat kekerasan dan kekuatan impak sebelum dan sesudah dilakukan pengelasan dengan metode pengelasan MIG pada cast wheel aluminium menggunakan elektroda ER 5356, menyimpulkan bahwa komposisi kimia cast wheel aluminium mengandung unsur 91,36%, 7,38% dan Fe 0,803% serta Cu dan Mg sekitar 0,05%. Hasil uji struktur mikro menunjukkan bahwa struktur butiran pada daerah HAZ menyatu dengan aluminium primer (α-) dan butiran membentuk paduan primer diantara α-. Hasil uji kekerasan pada spesimen pada raw material 57,56 kgf/mm², pada daerah las 44,20 kgf/mm² dan daerah HAZ 37,73 kgf/mm². Hasil uji impak pada raw material 0,118 Joule/mm² sedangkan daerah las adalah 0,067 Joule/mm². Kusmato, dkk., (2013), menyatakan bahwa kualitas hasil repair welding pada cast wheels aluminium silikon dengan metode pengelasan oksi asetilin, TIG dan MIG mempunyai komposisi kimia yang setara dengan paduan, karena unsur merupakan paduan terbesar yaitu 7,38%. Nilai kekerasan tertinggi yaitu hasil pengelasan oksi asetilin sebesar 54,80 BHN pada daerah lasan dan 38,69 BHN pada daerah HAZ. Nilai kekerasan terendah pada hasil pengelasan MIG yaitu 44,18 BHN pada daerah lassan dan hasil las TIG yaitu 30,47 BHN pada daerah HAZ. Nilai kekuatan impak tertinggi yaitu hasil pengelasan TIG dengan harga impak rata-ratanya 0,114 joule/mm². Harga impak terendah yaitu hasil pengelasan oksi asetilin dengan harga impak ratarata 0,085 joule/mm². I Dewa Made Krishna Muku, (2009), menyatakan bahwa kuat arus listrik mempunyai
2 pengaruh yang nyata terhadap kekuatan tarik sambungan las aluminium seri 100 dengan proses las MIG; pola hubungan yang paling mendekati antara kuat arus dengan kekuatan tarik sambungan las aluminium seri 100 dengan proses las MIG adalah model hubungan polinomial orde 2; kekuatan sambungan las tertinggi diperoleh pada pengelasan dengan menggunakan kuat arus 180 Ampere, dengan kekuatan sambungan las yang dihasilkan sebesar 11,900 kgf/mm 2. jufri, (2008), melakukan penelitian tentang pengaruh variasi sudut kampuh V tunggal dan kuat arus pada sambungan logam aluminium mg 5083 terhadap kekuatan tarik hasil pengelasan TIG. Dari keempat tersebut tersebut akan dapat diketahui sejauh mana pengaruh sudut kampuh dan kuat arus hasil pengelasan TIG. Hasil pengujian menunjukkan pengelasan dengan kuat arus 100 A, 125 A dan 150 A berdasarkan variasi sudut kampuh dengan kuat arus 100 A sudut kampuh 90 o mempunyai tegangan tarik rata-rata lebih baik dibandingkan sudut kampuh 80 o dan 70 o, tegangan yang dihasilkan untuk sudut kampuh 70 o = MPa, 80 o = MPa dan 90 o = MPa. Pengujian pada pengelasan TIG untuk paduan - Mg 5083, faktor kuat arus sangat mempengaruhi hasil lasan (kekuatan tarik). Disini terlihat kuat arus 100 A dapat menghasilkan kekuatan las yang lebih baik dibandingkan 125 A dan 150 A. Secara umum penampakan struktur makro pada setiap variasi arus pengelasan dan sudut kampuh memiliki bentuk butir yang sama, pengamatan dilakukan pada bagian tengah dan tepi pada Material Unsur patahan -Mg 5083 hasil pengujian tarik dengan pembesaran 50 x. Mayus S., (2013), menyatakan bahwa pengelasan dari tiga arus las yang digunakan 70 A, 75 A dan 80 A, kuat arus 75 A mempunyai hasil pengelasan yang optimal baik dari struktur mikro dan sifat mekaniknya. Tujuan penelitian ini adalah menyelidiki pengaruh kuat arus listrik terhadap struktur mikro yang terjadi pada sambungan las TIG -13,5. 2. METODE PENELITIAN Bahan Bahan material yang digunakan adalah uminium licon (-13,5). Sedangkan filler yang digunakan adalah Tabel 1, menunjukkan komposi material yang digunakan dalam penelitian ini. Proses Pengelasan Pengelasan menggunakan pelat uminium AL-13,5 dan filler Pengelasan TIG dilakukan dengan variasi kuat arus listrik berturutturut adalah 90 A, 100 A dan 110 A, mesin las TIG AC frekuensi tinggi (ACHF) dengan polarisasi bolak-balik, debit gas argon 2,5 sampai 5 ltr/menit. Tebal pelat yang digunakan adalah 10 mm, alur las dibuat bentuk V ganda dengan sudut 90 o dan las multirun seperti terlihat pada Gambar 1. Dimensi plat adalah 300 mm x 100 mm x 10 mm. Pengujian Pengamatan struktur mikro pada masingmasing spesimen las dengan variasi arus listrik yang diperoleh dari hasil foto mikro dengan menggunakan mikroskop optic. Tabel 1. Komposisi kimia material induk logam las dan filler 5356 dalam % berat Fe Cu Mn Mg Cr Zn Be Ti Sn Pb Ca V Zr Ni Sr Material Induk Balance 13,5 0,202 0,147 <0,020 <0,050 <0, ,000 <0,010 0,0715 <0,030 0,005 <0,010 <0,003 <0,020 0,0384 Filler ER5356 Balance 0,25 0,40 0,01 0,05-0,20 4,5-5,5 0,05-0,20 0,10 0,0008 0,06-0, o ,5 Gambar 1. Bentuk alur las
3 Volume 10, Desember 2016 ISSN : HASIL DAN PEMBAHASAN Pemeriksaan visual dengan mikroskop bertujuan untuk mengungkap dan memperoleh informasi struktur dalam skala mikro yang tidak dapat diamati dengan mata biasa. Dengan pemeriksaan menggunakan mikroskop dapat diamati struktur mikro logam, baik itu berupa besar butirnya, arah dan susunan butir dan fasafasa yang ada di dalam kristal logam. Detail struktur mikro yang dapat diamati tergantung pada skala perbesarannya. Pada spesimen las metalografi yang diamati adalah pada raw material, daerah HAZ dan daerah lasan. Posisi pengambilan foto mikro seperti pada Gambar 2. Sedangkan hasil foto mikro ditunjukkan pada Gambar 3, 4 dan 5. Raw material Gambar 2. Titik pengujian kekerasan a) b) c) -Mg Gambar 3. Struktur mikro pada pengelasan 90 A: a) raw material, b) daerah HAZ, c) daerah las a) b)
4 c) -Mg Gambar 4. Struktur mikro pada pengelasan 100 A: a) raw material, b) daerah HAZ, c) daerah las a) b) c) -Mg Gambar 5. Struktur mikro pada pengelasan 110 A: a) raw material, b) daerah HAZ, c) daerah las Hasil pengamatan foto mikro pada tiap spesimen arus pengelasan di setiap titik raw material, daerah HAZ dan daerah las tidak mempunyai perbedaan begitu jauh pada setiap hasil uji foto mikro. Pada raw material terlihat struktur aluminium dan membentuk struktur dendrit, struktur aluminium terlihat berwarna terang mengkilap. Daerah raw material ini juga terlihat butiran-butiran silikon yang berwarna abu-abu gelap yang menyebar di sekeliling struktur aluminium. Butiran sebagai matrik diantara aluminium primer yang saling berdekatan. Pada daerah HAZ butiran-butiran dan terlihat lebih kecil daripada di daerah raw material, hal ini disebabkan struktur butir pada daerah HAZ mulai rusak karena disebabkan perlakuan panas dari pengelaasan yang dilakukan, karena struktur kristal logam akan rusak pada titik cairnya. Struktur kristal akan terbentuk kembali jika logam didinginkan. Bila pendinginan berlangsung secara perlahan-lahan, terbentuklah kelompok atom pada permukaan cairan yang kemudian menjadi inti butiran padat. Selama proses pendinginan dengan laju pendinginan lambat, inti pertama bertambah besar akibat kepindahan atom dari cairan kebahan padat.
5 Akhirnya, semua cairan bertransformasi dan butir bertambah besar. Batas butir merupakan titik pertemuan pertumbuhan berbagai inti. Bila pendinginan cepat, jumlah kelompok bertambah dan tiap-tiap kelompok tumbuh dengan cepat hingga akhirnya saling bertemu. Sebagai hasil akhir, diperoleh logam dengan jumlah butir yang banyak atau disebut logam padat berbutir halus. Pada daerah HAZ mengalami pendinginan yang lebih cepat daripada daerah las maka pada daerah HAZ butir dan terlihat menyebar dan merata. Karena pada daerah HAZ mengalami pendinginan yang lebih cepat hal ini juga mempengaruhi nilai kekerasannya yaitu nilai kekerasan pada daerah HAZ lebih kecil daripada daerah raw material. Pada daerah las terdapat penambahan unsur dari filler las yang digunakan yaitu 5356 dimana unsur dasar dari filler yang digunakan adalah magnesium sehingga membentuk paduan -Mg. Magnesium dan aluminium pada daerah las terlihat berwarna mengkilap dengan struktur yang lebih rapat. Pada struktur mikro daerah las arus 100 A butir lebih halus dibandingkan dengan arus 90 A dan 110 A. Pada arus 80 A bentuk butir cenderung lebih bulat sedangkan pada arus 110 bentuk butir cenderung masih membentuk struktur dendrit. Hasil pengelasan pada arus 100 A, struktur mikronya dengan butir lebih halus, hal ini sangat dimungkinkan mempunyai sifat mekanik yang lebih baik dibanding dengan hasil pengelasan pada arus 90A dan 110 A. Hasil pengamatan struktur mikro ini sejalan dengan Awi Andoko, dkk., (2012), struktur butiran pada daerah HAZ menyatu dengan aluminium primer (α-) dan butiran membentuk paduan primer diantara α-., juga sesuai dengan jufri (2008), secara umum penampakan struktur makro pada setiap variasi arus pengelasan dan sudut kampuh memiliki bentuk butir yang sama, pengamatan dilakukan pada bagian tengah dan tepi pada patahan -Mg 5083 hasil pengujian tarik dengan pembesaran 50x. 4. KESIMPULAN Berdasarkan dari hasil penelitian dan pembahasan di atas maka dapat diambil kesimpulan sebagai berikut : 1. Variasi arus listrik pada pengelasan tidak begitu berbengaruh terhadap struktur mikro pada tiap spesimen di setiap titik raw material, daerah HAZ dan daerah las. 2. Komposisi logam las terdapat penambahan unsur dari filler las yang digunakan yaitu 5356 dimana unsur dasar dari filler yang digunakan adalah magnesium sehingga membentuk paduan -Mg. 3. Struktur mikro logam las arus 100 A, butirannya lebih halus dibandingkan dengan arus 90 A dan 110 A. Pada arus 80 A bentuk butir cenderung lebih bulat sedangkan pada arus 110 bentuk butir cenderung masih membentuk struktur dendrit. 5. REFERENSI jufri Pengaruh Variasi Sudut Kampuh V Tunggal Dan Kuat Arus Pada Sambungan Logam umunium Mg 5083 Terhadap Kekuatan Tarik Hasil Pengelasan Tig. Universitas Sumatra Utara, Medan. ASTM E 8M Standart Test Methods for Tension Testing of Metallic Material (Metrik). ASTM E 23-02a Standart Test Methods for Notched Bar Impact Testing of Metallic Materials. Awi Andoko., dkk., Analisis Struktur Hasil Repair Welding Tentang fat Fisik Dan Mekanik Pada Cast Wheel uminium Dengan Metode Pengelasan MIG. Universitas Sebelas Maret, Surakarta. I Dewa Made Krishna Muku., Kekuatan Sambungan Las uminium Seri 1100 dengan Variasi Kuat Arus Listrik Pada Proses Las Metal Inert Gas (MIG). Universitas Udayana, Bandung. Kou, S Welding Metallurgy. New York: John Willey, Sons, Inc. Kusmanto., dkk., Studi Tentang Kualitas Hasil Repair Welding Pada Cast Wheels uminium Dengan Metode Pengelasan Oksi Asetilin, TIG Dan MIG Terhadap fat Fisis Dan Mekanis. Universitas Sebelas Maret, Surakarta. Mayus S., dkk., Effect of Welding Current on the Mechanical and Structural Properties of TIG Welded uminium loy AA-5083.
6 International Journal of Mechanical Engineering and Research, India. Radaj, D Heat effects of Welding : Temperature Field, Residual Stress, Distortion. Berlin: Springer-Verlag. Wiryosumarto, H. dan Okumura, T Teknologi Pengelasan Logam. Jakarta: PT. Pradya Paramita.
PENGARUH MASUKAN PANAS (HEAT INPUT) TERHADAP KETANGGUHAN IMPAK SAMBUNGAN LAS TIG Al-13,5Si
PENGARUH MASUKAN PANAS (HEAT INPUT) TERHADAP KETANGGUHAN IMPAK SAMBUNGAN LAS TIG Al-13,5Si Wijoyo Fakultas Teknologi Industri, Program Studi Teknik Mesin Universitas Surakarta Email: joyowi@yahoo.co.id
Lebih terperinciKAJIAN KEKERASAN DAN STRUKTUR MIKRO SAMBUNGAN LAS GMAW BAJA KARBON TINGGI DENGAN VARIASI MASUKAN ARUS LISTRIK
KAJIAN KEKERASAN DAN STRUKTUR MIKRO SAMBUNGAN LAS GMAW BAJA KARBON TINGGI DENGAN VARIASI MASUKAN ARUS LISTRIK Wijoyo Fakultas Teknologi Industri, Program Studi Teknik Mesin Universitas Surakarta Email:
Lebih terperinciPengaruh Kuat Arus Listrik Terhadap Ketangguhan Impak Dan Kekuatan Tarik Sambungan Las MIG Baja Karbon Tinggi
Pengaruh Kuat Arus Listrik Terhadap Ketangguhan Impak Dan Kekuatan Tarik Sambungan Las MIG Baja Karbon Tinggi Bayu Kartiko Aji 1) dan Wijoyo 2) 1 Teknik Mesin Universitas Surakarta Email: kartikaaji.bayu@yahoo.com
Lebih terperinciBAB I PENDAHULUAN. dimana logam menjadi satu akibat panas las, dengan atau tanpa. pengaruh tekanan, dan dengan atau tanpa logam pengisi.
BAB I PENDAHULUAN 1.1. Latar Belakang Pengelasan adalah salah satu proses penggabungan logam dimana logam menjadi satu akibat panas las, dengan atau tanpa pengaruh tekanan, dan dengan atau tanpa logam
Lebih terperinciPENGARUH SUHU PREHEAT DAN VARIASI ARUS PADA HASIL LAS TIG ALUMINIUM PADUAN TERHADAP KEKUATAN TARIK DAN KEKERASAN
Pengaruh Suhu Preheat Dan Variasi Arus Pada Hasil Las Tig Aluminium Paduan PENGARUH SUHU PREHEAT DAN VARIASI ARUS PADA HASIL LAS TIG ALUMINIUM PADUAN TERHADAP KEKUATAN TARIK DAN KEKERASAN Nurfi Ahmadi
Lebih terperinciNASKAH PUBLIKASI PENGARUH VARIASI ARUS TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN SAMBUNGAN PADA PROSES PENGELASAN ALUMUNIUM DENGAN METODE SMAW
NASKAH PUBLIKASI PENGARUH VARIASI ARUS TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN SAMBUNGAN PADA PROSES PENGELASAN ALUMUNIUM DENGAN METODE SMAW Disusun sebagai salah satu syarat menyelesaikan Program
Lebih terperinciPengaruh Variasi Arus terhadap Struktur Mikro, Kekerasan dan Kekuatan Sambungan pada Proses Pengelasan Alumunium dengan Metode MIG
NASKAH PUBLIKASI TUGAS AKHIR Pengaruh Variasi Arus terhadap Struktur Mikro, Kekerasan dan Kekuatan Sambungan pada Proses Pengelasan Alumunium dengan Metode MIG Diajukan untuk Memenuhi Tugas dan Syarat-syarat
Lebih terperinciPengaruh variasi kampuh las dan arus listrik terhadap kekuatan tarik dan struktur mikro sambungan las TIG pada aluminium 5083
Jurnal Kompetensi Teknik Vol. 8, No.2, Mei 2017 27 Pengaruh variasi kampuh las dan arus listrik terhadap kekuatan tarik dan struktur mikro sambungan las TIG pada aluminium 5083 Satrio Hadi 1, Rusiyanto
Lebih terperinciPENGARUH VARIASI ARUS TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN SAMBUNGAN PADA PROSES PENGELASAN ALUMINIUM DENGAN METODE MIG
PENGARUH VARIASI ARUS TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN SAMBUNGAN PADA PROSES PENGELASAN ALUMINIUM DENGAN METODE MIG Tri Widodo Besar Riyadi 1, Lastono Aji 2 1,2 Jurusan Teknik Mesin, Fakultas
Lebih terperinciBAB I PENDAHULUAN. atau non ferrous dengan memanaskan sampai suhu pengalasan, dengan atau tanpa menggunakan logam pengisi ( filler metal ).
BAB I PENDAHULUAN 1.1. Latar Belakang Pengelasan adalah proses penyambungan material ferrous atau non ferrous dengan memanaskan sampai suhu pengalasan, dengan atau tanpa menggunakan logam pengisi ( filler
Lebih terperinciIV. HASIL DAN PEMBAHASAN
IV. HASIL DAN PEMBAHASAN A. DATA ALAT DAN MATERIAL PENELITIAN 1. Material Penelitian Material yang digunakan adalah baja AISI 1045 berupa pelat yang memiliki komposisi kimia sebagai berikut : Tabel 7.
Lebih terperinciBAB I PENDAHULUAN. 1.1 Latar Belakang. Pengembangan teknologi di bidang konstruksi yang semakin maju tidak
BAB I PENDAHULUAN 1.1 Latar Belakang Pengembangan teknologi di bidang konstruksi yang semakin maju tidak dapat dipisahkan dari pengelasan karena mempunyai peranan penting dalam rekayasa dan reparasi logam.
Lebih terperinciJl. Menoreh Tengah X/22, Sampangan, Semarang *
ANALISA PENGARUH KUAT ARUS TERHADAP STRUKTUR MIKRO, KEKERASAN, KEKUATAN TARIK PADA BAJA KARBON RENDAH DENGAN LAS SMAW MENGGUNAKAN JENIS ELEKTRODA E7016 Anjis Ahmad Soleh 1*, Helmy Purwanto 1, Imam Syafa
Lebih terperinciBAB I PENDAHULUAN. Universitas Sumatera Utara
BAB I PENDAHULUAN 1.1. Latar Belakang Pengelasan adalah proses penyambungan material ferrous atau non ferrous dengan memanaskan sampai suhu pengelasan, dengan atau tanpa menggunakan logam pengisi ( filler
Lebih terperinciPENGARUH WAKTU PENGELASAN GMAW TERHADAP SIFAT FISIK MEKANIK SAMBUNGAN LAS LOGAM TAK SEJENIS ANTARA ALUMINIUM DAN BAJA KARBON RENDAH
PENGARUH WAKTU PENGELASAN GMAW TERHADAP SIFAT FISIK MEKANIK SAMBUNGAN LAS LOGAM TAK SEJENIS ANTARA ALUMINIUM DAN BAJA KARBON RENDAH Bi Asngali dan Triyono Jurusan Teknik Mesin Universitas Sebelas Maret
Lebih terperinciKUALITAS REPAIR WELDING MENGGUNAKAN METODE PENGELASAN TIG DENGAN PERLAKUAN PREHEATING DAN POST WELD HEAT TREATMENT PADA CAST WHEEL ALUMINIUM
KUALITAS REPAIR WELDING MENGGUNAKAN METODE PENGELASAN TIG DENGAN PERLAKUAN PREHEATING DAN POST WELD HEAT TREATMENT PADA CAST WHEEL ALUMINIUM Dewi Rima Ratri Siwi 1) Budhi Harjanto 2) Nyenyep Sriwardani
Lebih terperinciSKRIPSI / TUGAS AKHIR
SKRIPSI / TUGAS AKHIR PENGARUH BENTUK KAMPUH LAS TIG TERHADAP SIFAT MEKANIK MATERIAL BAJA ST 37 CAHYANA SUHENDA (20408217) JURUSAN TEKNIK MESIN LATAR BELAKANG Pada era industrialisasi dewasa ini teknik
Lebih terperinciBAB I PENDAHULUAN. dalam penyambungan batang-batang terutama pada bahan besi tuang
BAB I PENDAHULUAN 1.1. Latar Belakang Pada waktu ini teknik las telah banyak dipergunakan secara luas dalam penyambungan batang-batang terutama pada bahan besi tuang (cast iron), besi dan baja. Luasnya
Lebih terperinciPERBANDINGAN KARAKTERISTIK SIFAT MEKANIS PENGELASAN ASTM A790 DAN ASTM A106 Gr. B HASIL PROSES PENGELASAN GTAW YANG DIAPLIKASIKAN PADA PIPA GEOTHERMAL
PERBANDINGAN KARAKTERISTIK SIFAT MEKANIS PENGELASAN ASTM A790 DAN ASTM A106 Gr. B HASIL PROSES PENGELASAN GTAW YANG DIAPLIKASIKAN PADA PIPA GEOTHERMAL Pathya Rupajati 1), Hengky Fernando 2), Dwita Suastiyanti
Lebih terperinciIV. HASIL DAN PEMBAHASAN
IV. HASIL DAN PEMBAHASAN A. DATA ALAT DAN MATERIAL PENELITIAN 1. Material Penelitian Tipe Baja : AISI 1045 Bentuk : Pelat Tabel 7. Komposisi Kimia Baja AISI 1045 Pelat AISI 1045 Unsur Nilai Kandungan Unsur
Lebih terperinciBAB I PENDAHULUAN. logam menjadi satu akibat adanya energi panas. Teknologi pengelasan. selain digunakan untuk memproduksi suatu alat, pengelasan
BAB I PENDAHULUAN A. Latar Belakang Pengelasan adalah suatu proses penggabungan logam dimana logam menjadi satu akibat adanya energi panas. Teknologi pengelasan selain digunakan untuk memproduksi suatu
Lebih terperinciPENGARUH MEDIA PENDINGIN TERHADAP HASIL PENGELASAN TIG PADA BAJA KARBON RENDAH
Pengaruh Media.. Baja Karbon Rendah PENGARUH MEDIA PENDINGIN TERHADAP HASIL PENGELASAN TIG PADA BAJA KARBON RENDAH Dosen Jurusan Teknik Mesin Fakultas Teknik Universitas Janabadra INTISARI Las TIG adalah
Lebih terperinci16 Media SainS, Volume 4 Nomor 1, April 2012 ISSN 2085-3548
16 PENGARUH BESAR ARUS TEMPER BEAD WELDING TERHADAP KETANGGUHAN HASIL LAS SMAW PADA BAJA ST37 (Effect Large Current of Temper Bead Welding Against Toughness of SMAW Welding Results ST37 Steel) Ahmadil
Lebih terperinciPENGARUH FILLER DAN ARUS LISTRIK TERHADAP SIFAT FISIK- MEKANIK SAMBUNGAN LAS GMAW LOGAM TAK SEJENIS ANTARA BAJA KARBON DAN J4
PENGARUH FILLER DAN ARUS LISTRIK TERHADAP SIFAT FISIK- MEKANIK SAMBUNGAN LAS GMAW LOGAM TAK SEJENIS ANTARA BAJA KARBON DAN J4 Petrus Heru Sudargo 1), Triyono 2), Kuncoro Diharjo 2) 1) Pasca Sarjana Jurusan
Lebih terperinciBAB I PENDAHULUAN. bermanfaat bagi kebutuhan teknologi maupun kebutuhan rumah. berpengaruh pada penurunan kualitas barang produksi seperti
BAB I PENDAHULUAN 1.1. Latar Belakang Kuningan merupakan salah satu logam yang sangat bermanfaat bagi kebutuhan teknologi maupun kebutuhan rumah tangga. Cara atau pemilihan pengelasan yang salah akan berpengaruh
Lebih terperinciEFFECT OF POST HEAT TEMPERATURE TO HARDNESS AND MACROSTRUCTURE IN WELDED STELL ST 37
EFFECT OF POST HEAT TEMPERATURE TO HARDNESS AND MACROSTRUCTURE IN WELDED STELL ST 37 Subardi 1), Djoko Suprijanto 2), Roza Lyndu R. Mahendra 3) Abstract The present study aims to investigate the effect
Lebih terperinciIV. HASIL DAN PEMBAHASAN
52 IV. HASIL DAN PEMBAHASAN A. DATA PENELITIAN 1. Material Penelitian a. Tipe Baja : A 516 Grade 70 Bentuk : Plat Tabel 7. Komposisi Kimia Baja A 516 Grade 70 Komposisi Kimia Persentase (%) C 0,1895 Si
Lebih terperinciSTUDI BAHAN ALUMUNIUM VELG MERK SPRINT DENGAN METODE TERHADAP SIFAT FISIS DAN MEKANIS
NASKAH PUBLIKASI STUDI BAHAN ALUMUNIUM VELG MERK SPRINT DENGAN METODE STANDARD ASTM TERHADAP SIFAT FISIS DAN MEKANIS Tugas Akhir ini Disusun Guna Memperoleh Gelar Sarjana Strata Satu Jurusan Teknik Mesin
Lebih terperinciPengaruh Jenis Elektroda Pada Pengelasan Dengan SMAW Terhadap Sifat Fisis dan Mekanis Pada Baja Profil IWF
TUGAS AKHIR Pengaruh Jenis Elektroda Pada Pengelasan Dengan SMAW Terhadap Sifat Fisis dan Mekanis Pada Baja Profil IWF Disusun : DIDIT KURNIAWAN NIM : D.200.03.0169 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK
Lebih terperinciPengaruh Variasi Arus dan Jenis Elektrode pada Pengelasan Smaw Terhadap Sifat Mekanik Baja Karbon
Jurnal Ilmiah Teknik Mesin CakraM Vol. 3 No.2. Oktober 2009 (144-149) Pengaruh Variasi Arus dan Jenis Elektrode pada Pengelasan Smaw Terhadap Sifat Mekanik Baja Karbon I Made Gatot Karohika Jurusan Teknik
Lebih terperinciJl. Prof. Sudarto, SH, Tembalang, Semarang Jurusan Teknik Mesin, Fakultas Teknik, Universitas Diponegoro
D.13 PENGARUH POST-WELD HEAT TREATMENT DAN ARAH PENGELASAN TIG (TUNGSTEN INERT GAS) TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PADA PENYAMBUNGAN ALUMINIUM PADUAN 6061 Sofyan Abdillah 1*, Gunawan Dwi Hariyadi,
Lebih terperinciSTUDI PENGARUH VARIASI KUAT ARUS PENGELASAN PELAT AISI 444 MENGGUNAKAN ELEKTRODA AWS E316L
EKSERGI Jurnal Teknik Energi Vol 13 No. 1 Januari 2017; 10-14 STUDI PENGARUH VARIASI KUAT ARUS PENGELASAN PELAT AISI 444 MENGGUNAKAN ELEKTRODA AWS E316L Ojo Kurdi Departement Teknik Mesin, Fakultas Teknik,
Lebih terperinciANALISIS KUALITAS HASIL REPAIR WELDING TERHADAP SIFAT FISIS DAN MEKANIS PADA CAST WHEEL ALUMINIUM DENGAN METODE PENGELASAN OKSI-ASETILIN
ANALISIS KUALITAS HASIL REPAIR WELDING TERHADAP SIFAT FISIS DAN MEKANIS PADA CAST WHEEL ALUMINIUM DENGAN METODE PENGELASAN OKSI-ASETILIN Nur Chafiedz, Budi Harjanto, & Suharno Prodi. Pendidikan Teknik
Lebih terperinciPENGARUH ARUS PENGELASAN LAS TIG TERHADAP KARAKTERISTIK SIFAT MEKANIS STAINLESS STEEL TYPE 304 ABSTRAK
PENGARUH ARUS PENGELASAN LAS TIG TERHADAP KARAKTERISTIK SIFAT MEKANIS STAINLESS STEEL TYPE 304 Antonius Widyatmoko 1, Muh Amin 2 dan Solechan 3 ABSTRAK Stainless steel merupakan baja paduan tinggi karena
Lebih terperinciANALISA KETANGGUHAN DAN STRUKTUR MIKRO PADA DAERAH LAS DAN HAZ HASIL PENGELASAN TUNGSTEN INERT GAS ( TIG ) PADA ALUMINIUM ALLOY 6061 SKRIPSI
ANALISA KETANGGUHAN DAN STRUKTUR MIKRO PADA DAERAH LAS DAN HAZ HASIL PENGELASAN TUNGSTEN INERT GAS ( TIG ) PADA ALUMINIUM ALLOY 6061 SKRIPSI Skripsi Yang Diajukan Untuk Melengkapi Syarat Memperoleh Gelar
Lebih terperinciPENGARUH FILLER DAN ARUS LISTRIK TERHADAP SIFAT FISIK-MEKANIK SAMBUNGAN LAS GMAW LOGAM TAK SEJENIS ANTARA BAJA KARBON DAN J4
PENGARUH FILLER DAN ARUS LISTRIK TERHADAP SIFAT FISIK-MEKANIK SAMBUNGAN LAS GMAW LOGAM TAK SEJENIS ANTARA BAJA KARBON DAN J4 Petrus Heru Sudargo 1*, Sarwoko 1 1 Jurusan Teknik Mesin, Akademi Teknologi
Lebih terperinciPENGARUH SUHU NORMALIZING TERHADAP SIFAT FISIS DAN MEKANIS PENGELASAN BAJA PLAT KAPAL. Sutrisna*)
PENGARUH SUHU NORMALIZING TERHADAP SIFAT FISIS DAN MEKANIS PENGELASAN BAJA PLAT KAPAL Sutrisna*) Abstrak Pengelasana adalah proses penyambungan dua buah logam atau lebih melalui proses pencairan setempat.
Lebih terperinciJurnal Dinamis Vol.II,No.14, Januari 2014 ISSN
PENGARUH MASUKAN PANAS TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KETANGGUHAN PADA PENGELASAN SHIELD METAL ARC WELDING (SMAW) DARI PIPA BAJA DIAMETER 2,5 INCHI Susri Mizhar, Ivan Hamonangan Pandiangan Jurusan
Lebih terperinciSTUDI METALOGRAFI HASIL PENGELASAN SPOT WELDING TIPE KONVENSIONAL DAN PENAMBAHAN GAS ARGON
D.14 STUDI METALOGRAFI HASIL PENGELASAN SPOT WELDING TIPE KONVENSIONAL DAN PENAMBAHAN GAS ARGON Muh Alfatih Hendrawan *, Tutur Angga Kusuma Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah
Lebih terperinciPENGARUH FEED RATE TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN BENDING PADA PENGELASAN FRICTION STIR WELDING ALUMINIUM 5052
PENGARUH FEED RATE TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KEKUATAN BENDING PADA PENGELASAN FRICTION STIR WELDING ALUMINIUM 505 Lukito Adi Wicaksono Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah
Lebih terperinciPENGARUH HEAT TREATMENT
TUGAS AKHIR PENGARUH HEAT TREATMENT SESUDAH PENGELASAN (POST WELD) PADA BAJA TAHAN KARAT AUSTENITIK TERHADAP KEKUATAN TARIK, KEKERASAN, STRUKTUR MIKRO, DAN KOMPOSISI KIMIA Disusun : CATUR WIDODO YUNIANTO
Lebih terperinciBAB I PENDAHULUAN. peningkatan efisiensi penggunaan BBM. Penggantian bahan pada. sehingga dapat menurunkan konsumsi penggunaan BBM.
BAB I PENDAHULUAN 1.1 Latar Belakang Masalah Keterbatasan sumber energi bahan bakar minyak (BBM) dewasa ini telah memacu perkembangan teknologi otomotif yang mengarah pada peningkatan efisiensi penggunaan
Lebih terperinciPERLAKUAN PEMANASAN AWAL ELEKTRODA TERHADAP SIFAT MEKANIK DAN FISIK PADA DAERAH HAZ HASIL PENGELASAN BAJA KARBON ST 41
C.8 PERLAKUAN PEMANASAN AWAL ELEKTRODA TERHADAP SIFAT MEKANIK DAN FISIK PADA DAERAH HAZ HASIL PENGELASAN BAJA KARBON ST 41 Fauzan Habibi, Sri Mulyo Bondan Respati *, Imam Syafa at Jurusan Teknik Mesin
Lebih terperinciBAB I PENDAHULUAN. mempunyai peranan yang sangat penting dalam rekayasa serta reparasi
1 BAB I PENDAHULUAN 1.1 Latar Belakang Pengembangan teknologi dalam bidang konstruksi yang semakin maju dewasa ini, tidak akan terlepas dari teknologi atau teknik pengelasan karena mempunyai peranan yang
Lebih terperinciKata Kunci: Pengelasan Berbeda, GMAW, Variasi Arus, Struktur Mikro
B.8 PENGARUH FILLER DAN ARUS LISTRIK PENGELASAN LOGAM TAK SEJENIS BAJA (AISI 1045) DENGAN BAJA TAHAN KARAT (AISI 316L) TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO Petrus Heru Sudargo *, Bambang Teguh Baroto
Lebih terperinciLEMBAR PENGESAHAN SKRIPSI PENGARUH TERHADAP KEKUATAN TARIK PADA LAS SMAW (SHIELDED METAL ARC WELDING) DENGAN METODE EKSPERIMEN
LEMBAR PENGESAHAN SKRIPSI PENGARUH TERHADAP KEKUATAN TARIK PADA LAS SMAW (SHIELDED METAL ARC WELDING) DENGAN METODE EKSPERIMEN (Studi Kasus: PT.FREEPORT INDONESIA, Papua) Oleh : NAMA : PETRUS KADEPA NIM
Lebih terperinciBAB IV DATA DAN ANALISA
BAB IV DATA DAN ANALISA Pengelasan plug welding pada material tak sejenis antara logam tak sejenis antara baja tahan karat 304L dan baja karbon SS400 dilakukan untuk mengetahui pengaruh arus pengelasan
Lebih terperinciSIFAT MEKANIK DAN STRUKTUR MIKRO SAMBUNGAN LAS ALUMINIUM 6061 HASIL FRICTION WELDING ABSTRACT
SIFAT MEKANIK DAN STRUKTUR MIKRO SAMBUNGAN LAS ALUMINIUM 6061 HASIL FRICTION WELDING Hendry Wicaksana S 1, Santoso Mulyadi 2, Ahmad Syuhri 2 1 Alumni Teknik Mesin Fakultas Teknik Universitas Jember, Jl.
Lebih terperinciProsiding SNATIF Ke -4 Tahun 2017 ISBN:
PENGARUH ARUS LISTRIK DAN FILLER PENGELASAN LOGAM BERBEDA BAJA KARBON RENDAH (ST 37) DENGAN BAJA TAHAN KARAT (AISI 316L) TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO Bambang Teguh Baroto 1*, Petrus Heru Sudargo
Lebih terperinciKATA PENGANTAR. Sidoarjo, Desember Fakultas. Universitas Muhammadiyah Sidoarjo 1
KATA PENGANTAR Puji beserta syukur panjatkan kehadirat Tuhan yang Maha Esa. Karena berkat rahmat, hidayahnya, telah mampu menyelesaiakan sebuah makalah tentang pengaruh pengelsan FCAW tanpa dan dengan
Lebih terperinciPenelitian Kekuatan Sambungan Las pada Plat untuk Dek Kapal Berbahan Plat Baja terhadap Sifat Fisis dan Mekanis dengan Metode Pengelasan MIG
TUGAS AKHIR Penelitian Kekuatan Sambungan Las pada Plat untuk Dek Kapal Berbahan Plat Baja terhadap Sifat Fisis dan Mekanis dengan Metode Pengelasan MIG Disusun : MUHAMMAD SULTON NIM : D.200.01.0120 NIRM
Lebih terperinciIr. Hari Subiyanto, MSc
Tugas Akhir TM091486 METALURGI Budi Prasetya Awab Putra NRP 2104 100 018 Dosen Pembimbing: Ir. Hari Subiyanto, MSc ABSTRAK Austenitic stainless steel adalah suatu logam paduan yang mempunyai sifat tahan
Lebih terperinciPenelitian Kekuatan Sambungan Las pada Velg Mobil Berbahan Aluminium terhadap Sifat Fisis dan Mekanis dengan Metode Pengelasan TIG
TUGAS AKHIR Penelitian Kekuatan Sambungan Las pada Velg Mobil Berbahan Aluminium terhadap Sifat Fisis dan Mekanis dengan Metode Pengelasan TIG Disusun : DIDIK HARYANTO NIM : D.200.01.0129 JURUSAN TEKNIK
Lebih terperinciPENGARUH VARIASI KUAT ARUS PENGELASAN TUNGSTEN INERT GAS
PENGARUH VARIASI KUAT ARUS PENGELASAN TUNGSTEN INERT GAS (TIG) TERHADAP KEKUATAN TARIK HASIL SAMBUNGAN LAS PADA BAJA KARBON RENDAH SNI_07_3567_BJDC_SR DENGAN KETEBALAN PLAT 0,68 MM DAN 1,2 MM EFRIZAL ARIFIN
Lebih terperinciBAB I PENDAHULUAN. memiliki andil dalam pengembangan berbagai sarana dan prasarana kebutuhan
BAB I PENDAHULUAN A. Latar Belakang Dalam industri, teknologi konstruksi merupakan salah satu teknologi yang memiliki andil dalam pengembangan berbagai sarana dan prasarana kebutuhan manusia. Perkembangannya
Lebih terperinciINFO TEKNIK Volume 14 No. 2 Desember 2013 ( ) PENGARUH ARUS TERHADAP KEKERASAN HASIL PENGELASAN BAJA ST 60 MENGGUNAKAN PENGELASAN SMAW
INFO TEKNIK Volume 14 No. 2 Desember 2013 (211-218) PENGARUH ARUS TERHADAP KEKERASAN HASIL PENGELASAN BAJA ST 60 MENGGUNAKAN PENGELASAN SMAW Ma ruf Program Studi Teknik Mesin Universitas Lambung Mangkurat.
Lebih terperinciANALISIS STRUKTUR HASIL REPAIR WELDING TENTANG SIFAT FISIK DAN MEKANIK PADA CAST WHEEL ALUMINIUM DENGAN METODE PENGELASAN MIG
ANALISIS STRUKTUR HASIL REPAIR WELDING TENTANG SIFAT FISIK DAN MEKANIK PADA CAST WHEEL ALUMINIUM DENGAN METODE PENGELASAN MIG Awi Andoko 1) Budi Harjanto 2) Yuyun Estriyanto 3) Pendidikan Teknik Mesin,
Lebih terperinciPENGARUH KECEPATAN PUTAR TOOL TERHADAP SIFAT MEKANIK SAMBUNGAN ALUMINIUM 1XXX DENGAN METODE FRICTION STIR WELDING. Tri Angga Prasetyo ( )
PENGARUH KECEPATAN PUTAR TOOL TERHADAP SIFAT MEKANIK SAMBUNGAN ALUMINIUM 1XXX DENGAN METODE FRICTION STIR WELDING Tri Angga Prasetyo (20120130136) Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhammdiyan
Lebih terperinciI. PENDAHULUAN. sampah. Karena suhu yang diperoleh dengan pembakaran tadi sangat rendah maka
I. PENDAHULUAN A. Latar Belakang Teknik penyambungan logam telah diketahui sejak dahulu kala. Sumber energi yang digunakan pada zaman dahulu diduga dihasilkan dari pembakaran kayu atau sampah. Karena suhu
Lebih terperinciBAB I PENDAHULUAN. A. Latar Belakang Masalah
BAB I PENDAHULUAN A. Latar Belakang Masalah Banyaknya kendaraan bermotor dan alat transportasi yang diproduksi di Indonesia, semakin banyak pula jumlah spare part yang diproduksi sebagai pengganti komponen
Lebih terperinciIV. HASIL DAN PEMBAHASAN
IV. HASIL DAN PEMBAHASAN A. Data Alat Dan Material Penelitian 1. Material penelitian Tipe Baja : AISI 1045 Bentuk : Pelat Tabel 3. Komposisi kimia baja AISI 1045 Pelat AISI 1045 Unsur Nilai Kandungan Unsur
Lebih terperinciDASAR TEKNOLOGI PENGELASAN
DASAR TEKNOLOGI PENGELASAN Pengelasan adalah suatu proses dimana bahan dengan jenis sama digabungkan menjadi satu sehingga terbentuk suatu sambungan melalui ikatan kimia yang dihasilkan dari pemakaian
Lebih terperinciGambar 2.1. Proses pengelasan Plug weld (Martin, 2007)
BAB II DASAR TEORI 2.1 TINJAUAN PUSTAKA Proses pengelasan semakin berkembang seiring pertumbuhan industri, khususnya di bidang konstruksi. Banyak metode pengelasan yang dikembangkan untuk mengatasi permasalahan
Lebih terperinciTUGAS AKHIR PENGARUH KEKUATAN LAS BERBAHAN KUNINGAN TERHADAP PROSES PENGELASAN TIG DAN OXY-ACETYLENE
TUGAS AKHIR PENGARUH KEKUATAN LAS BERBAHAN KUNINGAN TERHADAP PROSES PENGELASAN TIG DAN OXY-ACETYLENE Disusun : AGUS SUPRAPTO NIM : D 200 05 0045 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS MUHAMMADIYAH
Lebih terperinciJournal of Mechanical Engineering Learning
JMEL 1 (1) (2012) Journal of Mechanical Engineering Learning http://journal.unnes.ac.id/sju/index.php/jmel PENGARUH TEMPERATUR ANNEALING SAMBUNGAN LAS SMAW (SHIELDED METAL ARC WELDING)TERHADAP SIFAT MEKANIS
Lebih terperinciPENGARUH WAKTU DAN JARAK TITIK PADA PENGELASAN TITIK TERHADAP KEKUATAN GESER HASIL SAMBUNGAN LAS
UNIVERSITAS DIPONEGORO PENGARUH WAKTU DAN JARAK TITIK PADA PENGELASAN TITIK TERHADAP KEKUATAN GESER HASIL SAMBUNGAN LAS TUGAS SARJANA Disusun oleh: ERI NUGROHO L2E 604 208 FAKULTAS TEKNIK JURUSAN TEKNIK
Lebih terperinciAnalisa Sifat Mekanik Hasil Pengelasan GMAW Baja SS400 Studi Kasus di PT INKA Madiun
Analisa Sifat Mekanik Hasil Pengelasan GMAW Baja SS400 Studi Kasus di PT INKA Madiun LATAR BELAKANG LATAR BELAKANG Baja SS 400 sebagai baja karbon rendah Dapat dilakukan proses pengelasan dengan metode
Lebih terperinciANALISIS KUALITAS REPAIR WELDING CAST WHEEL
ANALISIS KUALITAS REPAIR WELDING CAST WHEEL ALUMINIUM MENGGUNAKAN METODE PENGELASAN OKSI-ASETILIN DENGAN PERLAKUAN PREHEATING DAN POST WELD HEAT TREATMENT Aftoni Heri Septian Pamungkas 1) Budhi Harjanto
Lebih terperinciIII. METODOLOGI PENELITIAN. 2. Badan Latihan Kerja (BLK) Bandar Lampung sebagai tempat pengelasan
III. METODOLOGI PENELITIAN A. Tempat Penelitian Penelitian ini dilakukan di : 1. STM 2 Mei Bandar Lampung sebagai tempat pembuatan kampuh las dan pembentukan spesimen. 2. Badan Latihan Kerja (BLK) Bandar
Lebih terperinciANALISA PERBEDAAN SIFAT MEKANIK DAN STRUKTUR MIKRO PADA PISTON HASIL PROSES PENGECORAN DAN TEMPA
ANALISA PERBEDAAN SIFAT MEKANIK DAN STRUKTUR MIKRO PADA PISTON HASIL PROSES PENGECORAN DAN TEMPA Ahmad Haryono 1*, Kurniawan Joko Nugroho 2* 1 dan 2 Jurusan Teknik Mesin, Politeknik Pratama Mulia Surakarta
Lebih terperinciVARIASI ARUS LISTRIK TERHADAP SIFAT MEKANIK MIKRO SAMBUNGAN LAS BAJA TAHAN KARAT AISI 304
ISSN 2338-8102 VARIASI ARUS LISTRIK TERHADAP SIFAT MEKANIK MIKRO SAMBUNGAN LAS BAJA TAHAN KARAT AISI 304 Yunus Yakub dan Media Nofri Program Studi Teknik Mesin FTI ISTN Email: yunus_yakub@yahoo.com Abstrak:
Lebih terperinciANALISIS SIFAT MEKANIK LAS TIG PADA PLAT ALUMINIUM SERI 5 DENGAN VARIABEL KUAT ARUS 65; 70; 75 A UNTUK MANUFAKTUR KENDARAAN AIR SAMPAN (CANOE)
ANALISIS SIFAT MEKANIK LAS TIG PADA PLAT ALUMINIUM SERI 5 DENGAN VARIABEL KUAT ARUS 65; 70; 75 A UNTUK MANUFAKTUR KENDARAAN AIR SAMPAN (CANOE) Andika Wisnujati Program Studi D3 Teknik Mesin, Program Vokasi
Lebih terperinciAnalisa Kekuatan Tarik Baja Konstruksi Bj 44 Pada Proses Pengelasan SMAW dengan Variasi Arus Pengelasan
Analisa Kekuatan Tarik Baja Konstruksi Bj 44 Pada Proses Pengelasan SMAW dengan Variasi Arus Pengelasan Imam Basori Universitas Negeri Jakarta, Fakultas Teknik, Jurusan Teknik Mesin Jl. Rawamangun Muka,
Lebih terperinciANALISA KEKUATAN BENDING PADA PENGELASAN FRICTION STIR WELDING ALUMINIUM 6110
ANALISA KEKUATAN BENDING PADA PENGELASAN FRICTION STIR WELDING ALUMINIUM 6110 Jarot Wijayanto Staf Pengajar Jurusan Teknik Mesin Institut Sins & Teknologi Akprind Yogyakarta Emai: jarot@akprind.ac.id ABSTRAK
Lebih terperinciTUGAS AKHIR ANALISIS KEKUATAN LAS BERBAHAN ALUMINIUM MAMPU LAS TERHADAP SIFAT FISIS DAN MEKANIS
TUGAS AKHIR ANALISIS KEKUATAN LAS BERBAHAN ALUMINIUM MAMPU LAS TERHADAP SIFAT FISIS DAN MEKANIS Diajukan Untuk Memenuhi Tugas Dan Syarat-Syarat Guna Memperoleh Gelar Sarjana Teknik Jurusan Teknik Mesin
Lebih terperinciBAB I PENDAHULUAN. 1.1 Latar Belakang
BAB I PENDAHULUAN 1.1 Latar Belakang Pengembangan teknologi dalam bidang konstruksi yang semakin maju dewasa ini, tidak akan terlepas dari teknologi atau teknik pengelasan karena mempunyai peranan yang
Lebih terperinciPENGARUH VARIASI SUHU POST WELD HEAT TREATMENT ANNEALING
PENGARUH VARIASI SUHU POST WELD HEAT TREATMENT ANNEALING TERHADAP SIFAT MEKANIS MATERIAL BAJA EMS-45 DENGAN METODE PENGELASAN SHIELDED METAL ARC WELDING (SMAW) Fakultas Teknik Universitas Negeri Semarang
Lebih terperinciJournal of Mechanical Engineering Learning
JMEL 1 (1) (2012) Journal of Mechanical Engineering Learning http://journal.unnes.ac.id/sju/index.php/jmel PENGARUH PROSES ANNEALINGPADA SAMBUNGAN LAS SMAW TERHADAP STRUKTUR MIKRO DAN KEKERASAN BAJA S45C
Lebih terperinciANALISIS PENGARU ARUS PENGELASAN DENGAN METODE SMAW DENGAN ELEKTRODA E7018 TERHADAP KEKUATAN TARIK DAN KETANGGUHAN PADA BAJA KARBON RENDAH ABSTRAK
ANALISIS PENGARU ARUS PENGELASAN DENGAN METODE SMAW DENGAN ELEKTRODA E7018 TERHADAP KEKUATAN TARIK DAN KETANGGUHAN PADA BAJA KARBON RENDAH Yafet Bontong Staf Pengajar Prodi Teknik Mesin Universitas Kristen
Lebih terperinciBAB II DASAR TEORI Tinjauan Pustaka
BAB II DASAR TEORI 2.1. Tinjauan Pustaka Pengelasan logam tak sejenis antara baja tahan karat dan baja karbon banyak diterapkan di bidang teknik, diantaranya kereta api, otomotif, kapal dan industri lain.
Lebih terperinciEVALUASI KEKUATAN DAN STRUKTUR MIKRO SAMBUNGAN LAS TIG PADA PIPA ZIRCONIUM
EVALUASI KEKUATAN DAN STRUKTUR MIKRO SAMBUNGAN LAS TIG PADA PIPA ZIRCONIUM B.Bandriyana 1 ; Maradu Sibarani 2 1 Pusat Teknologi Bahan Industri Nuklir-BATAN 2 Pusat Teknologi Bahan Bakar dan Daur Ulang
Lebih terperinciSTUDI KUALITAS WELDING REPAIR DENGAN METODE PENGELASAN TIG DENGAN PERLAKUAN PWHT PADA CAST WHEEL ALUMINIUM
STUDI KUALITAS WELDING REPAIR DENGAN METODE PENGELASAN TIG DENGAN PERLAKUAN PWHT PADA CAST WHEEL ALUMINIUM Alfin Munfiroh, Budi Harjanto, Yuyun Estriyanto. Prodi. Pendidikan Teknik Mesin, Jurusan Pendidikan
Lebih terperinciPENGARUH HEAT TREATMENT TERHADAP PERUBAHAN SIFAT FISIS DAN MEKANIS PADA VELG MERK STOMP YANG MEMENUHI STANDART ASTM
Naskah Publikasi PENGARUH HEAT TREATMENT TERHADAP PERUBAHAN SIFAT FISIS DAN MEKANIS PADA VELG MERK STOMP YANG MEMENUHI STANDART ASTM Tugas Akhir ini Disusun Guna Memperoleh Gelar Sarjana Strata Satu Jurusan
Lebih terperinciPengaruh Variasi Waktu dan Tebal Plat Pada Las Titik terhadap Sifat Fisis dan Mekanis Sambungan Las Baja Karbon Rendah
TUGAS AKHIR Pengaruh Variasi Waktu dan Tebal Plat Pada Las Titik terhadap Sifat Fisis dan Mekanis Sambungan Las Baja Karbon Rendah Disusun : MT ERRY DANIS NIM : D.200.01.0055 NIRM : 01.6.106.03030.50055
Lebih terperinciPENGARUH VARIASI SUHU PREHEAT TERHADAP SIFAT MEKANIK MATERIAL SA 516 GRADE 70 YANG DISAMBUNG DENGAN METODE PENGELASAN SMAW
Abstrak PENGARUH VARIASI SUHU PREHEAT TERHADAP SIFAT MEKANIK MATERIAL SA 516 GRADE 70 YANG DISAMBUNG DENGAN METODE PENGELASAN SMAW Gathot DW1*, Nur H 2* Budi LS 3*,Abdillah GB 4* Prodi D-3 Teknik Mesin
Lebih terperinciI. PENDAHULUAN. keling. Ruang lingkup penggunaan teknik pengelasan dalam konstruksi. transportasi, rel, pipa saluran dan lain sebagainya.
I. PENDAHULUAN A. Latar Belakang Pengembangan teknologi di bidang konstruksi yang semakin maju tidak dapat dipisahkan dari pengelasan, karena mempunyai peranan penting dalam rekayasa dan reparasi logam.
Lebih terperinciPENGARUH VARIASI ARUS LAS TERHADAP SIFAT MEKANIK DAN KETANGGUHAN LAS SMAW DENGAN ELEKTRODA NSN308
PENGARUH VARIASI ARUS LAS TERHADAP SIFAT MEKANIK DAN KETANGGUHAN LAS SMAW DENGAN ELEKTRODA NSN308 SKRIPSI Skripsi Yang Diajukan Untuk Melengkapi Syarat Memperoleh Gelar Sarjana Teknik ALBERT TANDIKA NIM.
Lebih terperinciSTUDI KOMPARASI KUALITAS HASIL PENGELASAN PADUAN ALUMINIUM DENGAN SPOT WELDING KONVENSIONAL DAN PENAMBAHAN GAS ARGON
STUDI KOMPARASI KUALITAS HASIL PENGELASAN PADUAN ALUMINIUM DENGAN SPOT WELDING KONVENSIONAL DAN PENAMBAHAN GAS ARGON Muh Alfatih Hendrawan 1 1 Jurusan Teknik Mesin Fakultas Teknik Universitas Muhammadiyah
Lebih terperinciPENGARUH FILLER PLAT DAN VARIASI TEBAL PLAT PADA SPOT WELDING ANTARA BAJA-ALLUMUNIUM TERHADAP BEBAN GESER.
PENGARUH FILLER PLAT DAN VARIASI TEBAL PLAT PADA SPOT WELDING ANTARA BAJA-ALLUMUNIUM TERHADAP BEBAN GESER. Siswanto 1, Ardi Widaytmoko 2, Teguh Wiyono 3 1. Teknik Mesin, Politeknik Pratama Mulia, Surakarta
Lebih terperinciBAB I PENDAHULUAN. Banyak cara yang dapat dilakukan dalam teknik penyambungan logam misalnya
BAB I PENDAHULUAN A. Latar Belakang Teknik penyambungan logam telah diketahui sejak dahulu kala. Sumber energi yang digunakan pada zaman dahulu diduga dihasilkan dari pembakaran kayu atau sampah. Karena
Lebih terperinciGambar 4.1. Hasil pengamatan struktur mikro.
38 BAB IV HASIL DAN PEMBAHASAN 4.1 Struktur Mikro Struktur mikro yang dihasilkan pada Gambar 4.1 memiliki tiga bagian, titik 0 mm dan 5 mm dari sumbu las masuk pada daerah las, titik 10 mm dan 15 mm sudah
Lebih terperinciPENGARUH TEBAL PELAT BAJA KARBON RENDAH LAMA PENEKANAN DAN TEGANGAN LISTRIK PADA PENGELASAN TITIK TERHADAP SIFAT FISIS DAN MEKANIS
PENGARUH TEBAL PELAT BAJA KARBON RENDAH LAMA PENEKANAN DAN TEGANGAN LISTRIK PADA PENGELASAN TITIK TERHADAP SIFAT FISIS DAN MEKANIS Joko Waluyo 1 1 Jurusan Teknik Mesin Institut Sains & Teknologi AKPRIND
Lebih terperinciTUGAS AKHIR. PENGARUH JENIS ELEKTRODA PADA HASIL PENGELASAN PELAT BAJA St 32 DENGAN KAMPUH V TUNGGAL TERHADAP STRUKTUR MIKRO DAN KEKUATAN TARIKNYA
TUGAS AKHIR PENGARUH JENIS ELEKTRODA PADA HASIL PENGELASAN PELAT BAJA St 32 DENGAN KAMPUH V TUNGGAL TERHADAP STRUKTUR MIKRO DAN KEKUATAN TARIKNYA Diajukan Sebagai Salah Satu Syarat Menyelesaikan Program
Lebih terperinciAnalisis Perbandingan Laju Korosi Pelat ASTM A36 antara Pengelasan di Udara Terbuka dan Pengelasan Basah Bawah Air dengan Variasi Tebal Pelat
JURNAL TEKNIK POMITS Vol. 2, 1, (2013) ISSN: 2337-3539 (2301-9271 Print) G-73 Analisis Perbandingan Pelat ASTM A36 antara di Udara Terbuka dan Basah Bawah Air dengan Variasi Tebal Pelat Yanek Fathur Rahman,
Lebih terperinciTUGAS AKHIR STUDI METALOGRAFI HASIL PENGELASAN TITIK (SPOT WELDING) PADA PENGELASAN DI LINGKUNGAN UDARA DAN DI LINGKUNGAN GAS ARGON
TUGAS AKHIR STUDI METALOGRAFI HASIL PENGELASAN TITIK (SPOT WELDING) PADA PENGELASAN DI LINGKUNGAN UDARA DAN DI LINGKUNGAN GAS ARGON Disusun dan Diajukan Untuk Melengkapi Syarat-Syarat Guna Memperoleh Gelar
Lebih terperinciPENGARUH PREHEAT TERHADAP STRUKTUR MIKRO DAN KEKUATAN TARIK LAS LOGAM TAK SEJENIS BAJA TAHAN KARAT AUSTENITIK AISI 304 DAN BAJA KARBON A36
PENGARUH PREHEAT TERHADAP STRUKTUR MIKRO DAN KEKUATAN TARIK LAS LOGAM TAK SEJENIS BAJA TAHAN KARAT AUSTENITIK AISI 304 DAN BAJA KARBON A36 Saifudin 1, Mochammad Noer Ilman 2 Jurusan Teknik Mesin dan Industri,
Lebih terperinciSTUDI KEKUATAN BENDING DAN KEKERASAN PADA PENGELASAN ALUMINIUM DENGAN MENGGUNAKAN LAS SMAW (SHIELDED METAL ARC WELING)
STUDI KEKUATAN BENDING DAN KEKERASAN PADA PENGELASAN ALUMINIUM DENGAN MENGGUNAKAN LAS SMAW (SHIELDED METAL ARC WELING) Urip Prasmayobi Teknik Mesin, Fakultas Teknik, Universitas Halu Oleo Kendari Kampus
Lebih terperinciPENGARUH ARUS TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK PRODUK LAS TEMBAGA DAN BAJA KARBON DENGAN METODE TUNGSTEN INERT GAS (TIG)
TUGAS AKHIR PENGARUH ARUS TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK PRODUK LAS TEMBAGA DAN BAJA KARBON DENGAN METODE TUNGSTEN INERT GAS (TIG) Diajukan Untuk Memenuhi Tugas dan Syarat-Syarat Guna Memperoleh
Lebih terperinciAnalisa Perbandingan Kualitas Hasil Pengelasan Dan Struktur Mikro Material Aluminium 5083 Dan 6082 Menggunakan Metode Pengelasan GMAW Dan GTAW
TUG AS AK HIR Analisa Perbandingan Kualitas Hasil Pengelasan Dan Struktur Mikro Material Aluminium 5083 Dan 6082 Menggunakan Metode Pengelasan GMAW Dan GTAW DIS US UN OLEH : AC HMAD VENDY NAFIYANTO 4104.100.013
Lebih terperinciANALISA PENGARUH PENGELASAN FCAW PADA SAMBUNGAN MATERIAL GRADE A DENGAN MATERIAL GRADE DH 36. Oleh :
SEMINAR TUGAS AKHIR ANALISA PENGARUH PENGELASAN FCAW PADA SAMBUNGAN MATERIAL GRADE A DENGAN MATERIAL GRADE DH 36 Oleh : FARIDA TRI HASTUTI 4306 100 112 DOSEN PEMBIMBING 1. YEYES MULYADI, ST, M.Sc. 2. Ir.
Lebih terperinci