1 PENGARUH VARIASI SUHU DAN WAKTU PROSES ANODIZING PADA BAHAN ALUMUNIUM Ahmad Haryono Teknik Mesin Politeknik Pratama Mulia Surakarta ABSTRACT The anodizing process to produce a thin layer of aluminum oxide is porous. These pores can be incorporated to produce aluminum pigment with a variety of colors. Besides the size of the pore is also decisive in the next election on aluminum applications. At this peneleitian uses aluminum by using a variation of the concentration of electrolyte solution. Electrolyte solution used is sulfuric acid with a concentration of 15 % with a current density of 2 A/dm2, room temperature and immersion time for 30, 45 and 60 minutes. On thick specimens measured anodizing anodizing coating with coating thickness. Pore distribution can be observed from the results of a micro photo optical microscope observation. Then observed the influence of the thickness and pore distribution of the abrasion resistance of the oxide layer. The greater the concentration of electrolyte solution tends to decrease the thickness of the oxide layer but increases the size of pores on the surface of the oxide layer thus also improve the abrasion resistance of the oxide layer. With increasing time of anodizing process can increase the thickness of the oxide layer, but it can happen at a certain concentration of electrolyte solution. Optimum results obtained at 30 C temperature variation - 40 C, immersion time 20 minutes and 2 Ampere current dperoleh large flat and bright colors. Keywords : Aluminum, anodizing PENDAHULUAN LATAR BELAKANG MASALAH Perkembangan teknologi global dewasa ini menuntut keahlian dan kita dituntut untuk menjadi enterpreneur dari pada menjadi seorang job siccer dalam penggunaan teknologi. Salah satunya adalah pengembangan tentang wirausaha,oleh karena itu kami membuat alat yang diharapkan nantinya dapat dijadikan peluang usaha melalui proses Anodizing. Proses anodizing pada aluminium ini menghasilkan lapisan tipis oksida yang berpori. Pori ini dapat dimasukkan zat warna sehingga dihasilkan aluminium dengan warna yang Pengaruh variasi suhu dan waktu 12

2 beragam. Selain itu dari besar kecilnya pori ini juga menentukan pada pemilihan aplikasi pada aluminium selanjutnya. PERUMUSAN MASALAH Dari latar belakang masalah diatas, dapat dirumuskan ; Bagaimana pengaruh suhu dan waktu proses Anodizing pada bahan alumunium. TUJUAN DAN MANFAAT 1. Mengetahui pengaruh waktu proses anodizing pada bahan alumunium. 2. Mengetahui pengaruh suhu proses anodizing pada bahan alumunium. 3. Membuka wirausaha baru dibidang anodizing. LANDASAN TESORI Korosi Korosi merupakan proses degradasi sifat material disebabkan reaksi dengan lingkungannya. Korosi sebagai suatu reaksi elektrokimia yang memberikan kontribusi kerusakan fisik suatu material secara signifikan sehingga perlu perhatian untuk mencegah dan meminimalisasi kerugian yang timbul akibat efek korosi Jumlah logam dan paduannya merupakan fungsi dari lingkungan sehingga saling mempengaruhi kedua parameter tersebut antara lain lingkungan air tawar, air laut dan air tanah. Faktor-Faktor Penyebab Korosi Faktor penyebab korosi secara umum melibatkan sifat material antara lain sifat fisik, mekanik dan kimia. Penyebab lainnya juga mempertimbangkan struktur logam, sifat lingkungan sekitar dan reaksi antara antar permukaan logam dan lingkungan Faktor-faktor penyebab korosi yaitu : Struktur Logam. Komposisi, struktur atom, keheterogenan struktur secara microskopik dan makroskopik, tegangan (tarik, tekan dan siklus). Lingkungan. Sifat kimia, konsentrasi bahan reaktif dan pengotor, tekanan, suhu, kecepatan. Antar muka logam Kinetika oksidasi, pelarutan logam, kinetika proses reduksi bahan di dalam larutan, lokasi produk korosi, pertumbuhan film dan pelarutan film. MEKANISME KOROSI Berdasarkan pertimbangan di atas mengindikasikan mekanisme korosi logam sangat komplek dengan melibatkan berbagai cabang bidang antara lain sifat fisik, metalurgi fisik, kimia, bakteri dan lain-lain. Mekanisme korosi tidak terlepas dari reaksi elektrokimia. Reaksi elektrokimia melibatkan perpindahan electron-elektron. Pengaruh variasi suhu dan waktu 13

3 Perpindahan elektron merupakan hasil reaksi redoks (reduksioksidasi). Mekanisme korosi melalui reaksi elektrokimia melibatkan reaksi anodic di daerah anodik. Reaksi anodik (oksidasi) diindikasikan melalui peningktan valensi atau produk electron-elektron. Reaksi anodik yang terjadi pada proses korosi logam yaitu : M -->Mn+ + ne 1. Proses korosi dari logam M adalah proses oksidasi logam menjadi satu ion (n+) dalam pelepasan n electron. Harga dari n bergantung dari sifat logam sebagai contoh besi : Fe-->Fe e 2. Reaksi katodik juga berlangsung di proses korosi. Reaksi katodik diindikasikan melalui penurunan nilai valensi atau konsumsi electron-elektron yang dihasilkan dari reaksi anodic. Reaksi katodik terletak di daerah katoda. Beberapa jenis reaksi katodik yang terjadi selama proses korosi logam yaitu : a) Pelepasan gas hydrogen : 2H- + 2e --> H 2 b) Reduksi oksigen : O H- + 4e --> H 2 O O 2 + H 2 O 4 --> 4 OHc) Reduksi ion logam : Fe e --> Fe 2 + d) Pengendapan logam : 3 Na+ + 3 e --> 3 Na e) Reduksi ion hydrogen : O 2 + 4H+ + 4 e --> 2H 2 O O 2 + 2H 2 O + 4e --> OHf) Reaksi katodik dimana oksigen dari udara akan larut dalam larutan terbuka. Reaksi korosi tersebut sebagai berikut : NaCl.H 2 O 2 Fe + O 2 Fe 2 O 3 ANODISIZNG ALUMUNIUM Anodisasi atau oksida anoda secara luas digunakan untuk tujuan protektif perlindungan dan dekorasi permukaan alumunium. Keseluruhan reaksi oksidasi terjadi seperti dibawah ini : 2Al + 3H2O Al2O3 + 6H+ + 6e- Pada anodisasi alumunium, logam alumunium dipasang pada kaki anoda dan bukan pada katoda. Inilah perbedaan utama dengan proses lapis pada umumnya. Pada lapis diatas alumunium yang dibahas sebelumnya alumunium diproses perlakuan celup, lapis listrik, alumunium diposisikan pada katoda. Pada proses anodisasi selaput oksida pada permukaan alumunium yang terbentuk secara alami ditingkatkan pada ketebalan yang diperlukan. Pada anodisasi benda kerja ditempatkan pada anoda dan dilarutkan dalam larutan asam, benda kerja tidak seperti pada lapis listrik yang ditempatkan pada katoda. Oksigen yang muncul pada proses oksidasi anoda, membentuk lapisan tipis yang sangat rekat dengan substrat. Pengaruh variasi suhu dan waktu 14

4 Proses utama, dalam oksidasi anoda alumunium memerlukan larutan asam sulfat, asam kromat atau campuran asam sulfat dan asam oksalat. Selama proses oksidasi anoda permukaan alumunium dirubah menjadi oksida alumunium. Ketebalan oksida kurang lebih dua kali alumunium yang hilang. Beberapa manfaat dari oksidasi anoda alumunium ( Meningkatkan ketahanan korosi, meningkatkan adhesi cat, sebagai alat untuk pelapisan lebih lanjut, memperbaiki penampilan, meningkatkan isolasi listrik., memungkinkan penggunaan lithografi dan photografi,memperbesar emisivitas, meningkatkan ketahanan abrasi, mendeteksi daerah peka retakan. Lazimnya oksidasi anodik menggunakan asam sulfat, karena selain murah mudah untuk dikontrol, dan hasil pelapisannya mempunyai sifat astetik dan fungsional yang luas. Proses anodisasi dilakukan pada suhu 30 C -60 C, rapat arus A/m 2 dan tegangan antara V. Ketebalan lapisan oksidasi naik sejalan dengan lamanya oksidasi berbalikan, apabila suhu dinaikkan ketebalan menurun. Naiknya suhu mengakibatkan porositas bertambah dan kehilangan ketahanan abrasi. Larutan elektrolit lain yang digunakan dalam oksida anoda: a) Asam kromat Lapisanya buram, terbatas untuk ketebalan maksimum sekitar 10 µm dan jarang digunakan untuk keperluan dekorasi. Fungsinya untuk alas cat khususnya pada peralatan militer. b) Asam fosfat Biasanya digunakan sebelum lapis listrik yaitu pada proses pengerjaan awal. Hasilnya sangat porous dan menyediakan dasar locking mekanis untuk lapis listrik. c) Asam oksalat Hasil lapisan yang berwarna kuning yang kadang lebih keras dari hasil asam sulfat, digunakan untuk anodisasi yang tebal. d) Asam sulfonat Kombinasi dengan asam sulfat digunakan untuk ngembangkan anodik warna terpadu pada logam paduan. Perunggu, emas, kelabu dan hitam adalah warna yang dapat diperoleh. e) Asam borak Digunakan dalam lapis tanggul untuk kepasifan listrik, asam sitrat dan tartrat digunakan juga. PEWARNAAN LAPISAN ANODIZING Hampir semua alumunium dan paduanya dapat dioksidasi anoda dan diwarnai sesuai dengan yang diinginkan. Jenis anodik porous dapat diwarnai dengan obat organik, pigmen anorganik Pengaruh variasi suhu dan waktu 15

5 tertentu dan secara lapis listrik pula. Teknik pewarnaan aluminium antara lain : a) Pewarna organik. Setelah anodisasi dan pembilasan dengan air dingin, benda kerja dimasukkan dalam larutan pelarut organik yang mengandung beberapa gram/liter pewarna pada suhu 65 O C, Konsentrasi pewarna dan kontrol ph bervariasi terhadap pewarna. Waktu celup 5-15 menit. Setelah pewarnaan, benda kerja dibilas dalam air dingin. b) Pigmentasi dengan mineral. Mengsi lapisan anodik dengan pigmen mineral termasuk bahan-bahan tak larut seperti oksida logam, sulfida dan besi sianid dalam lubang oksida bisa sampai dua proses. Hasil dapat lebih baik daripada pewarna organik. c) Lapis listrik. Metode dan bahan yang digunakan masih menjadi rahasia perusahaan, tetapi prinsipnya seperti pada lapis listrik. Hasilnya paling baik dari metode yang lain. Tabel 2.1. Komposisi Larutan Solut ion No. Type of Solution Composition Operating temperature Cycle time, min C F 1 Alkaline clening Alkali, inhibited Chemical brightening H 3 PO 4 and HNO ½-5 3 Desmutting HNO 3, vol % Room Room 2 4 Anodzing H 2 SO 4, 15 Wt % ALAT DAN BAHAN a. Mesin Poles b. Power Suplly c. Kabel Penghubung d. Heatter ( Pemanas ) e. Termometer f. Bak g. Gelas Ukur h. Timbangan Bahan yang digunakan untuk Anodizing adalah: a) Alumunium b) Sulfuric Acid c) Niitric Acid d) Sodium Hydroxide (NaOH) e) Asam Florat f) Aquadest Pengaruh variasi suhu dan waktu 16

6 DIAGRAM PENELITIAN Pengumpulan Data Pembuatan Alat Uji Coba Pengaruh suhu terhadap hasil Anodizing Pengaruh lama pencelupan terhadap hasil Anodizing Hasil dan Pembahasan Selesai Gambar 3.1. Diagram Alir Penelitian HASIL DAN PEMBAHASAN Proses pengujian suhu terhadap hasil Anodizing Pada penelitian ini bahan menggunakan plat alumunium panjang 20 cm lebar 3 cm tebal 1,5 mm. Suhu yang digunakan ( tahap 1 ), ( tahap 2 ), dan suhu ( tahap 3 ). Untuk menjaga suhu berada pada ukuran tersebut agar suhu kamar tidak menurun atau melebihi batas ukur tersebut dengan cara Setiap 5 menit kita mengecek suhu dengan thermometer, ketika suhu mengalami kenaikan atau melebihi batas ukur hal yang kita lakukan adalah mematikan alat pemanas, ketika suhu mengalami penurunan hal yang kita lakukan adalah menghidupkan alat pemanas. Hal itu kita jaga agar suhu kamar tetap pada suhu yang kita tentukan pada uji coba. Tabel 4.1. pengaruh suhu terhadap proses anodizing. Pengaruh variasi suhu dan waktu 17

7 Tabel 4.1. Hasil Pengujian No Suhu Variable Waktu Konstan Ampere Konstan Hasil menit 2 Ampere Warna tidak rata menit 2 Ampere Warna rata dan cerah menit 2 Ampere Warna rata dan gelap A B C Gambar 4.1. Struktur mikro hasil pengujian. Proses pengujian lama pencelupan terhadap hasil Anodizing. Pada penelitian inivariasi yang digunakan 20 menit, 30 menit, dan 40 menit. Tabel 4.2. Variasi waktu pencelupan terhadap hasil anodizing. NO Suhu Konstan Waktu Variable Ampere Konstan Hasil menit 2 Ampere Warna tidak rata menit 2 Ampere Warna gelap dan rata menit 2 Ampere Warna cerah dan tidak rata A B C t = 20 menit. t = 30 menit t = 40 menit Gambar 4.2. Struktur mikro hasil pengujian. Pengaruh variasi suhu dan waktu 18

8 PENUTUP Kesimpulan 1. Kegagalan terjadi karena terlalu lamanya pengentasan setelah proses anodis sebelum proses pewarnaan atau dyeing. Hal itu akan mengakibatkan suhu pada benda kerja menurun menjadi dingin dan pori pada benda kerja nenyempit, sehingga pada waktu dyeing, bahan pawarna tidak masuk kedalam pori - pori benda kerja. Akibatnya pewarna tidak bisa menempel pada permukaan benda kerja. 2. Waktu yang ditentukan arus dari power suplay harus mengalir dari anoda benda kerja menyebabkan pori luar alumunium meloncat ke katoda alumunium melingkar, dan proses ini tidak boleh berhenti sedetikpun apabila terjadi maka benda kerja tidak berhasil karena waktu yang kita tentukan belum tercapai sehingga anodis belum sempurna. 3. Hasil yang optimum diperoleh pada variasi suhu 30 o C 40 o C, waktu pencelupan 20 menit dan besar arus 2 Ampere dperoleh warna rata dan cerah. (Elektro Plating). Andi Offset. Yogyakarta KR. Trethewey dan J. Chamberlain. Korosi Untuk Mahasiswa dan Rekayasawan. PT. Gramedia Pustaka Utama. Jakarta Soleh Wahyudi, MT. Buku Saku Elekroplating. Technic. Cimahi Bandung (2006) odizing101/ cjnical/anodizing.html 33.pdf wts_content_file/255/ pdf alumunium.com anodizing explained.htm DAFTAR PUSTAKA Anton J Hartono dan Tomijiro Kanoko. Mengenal Pelapisan Logam Pengaruh variasi suhu dan waktu 19

PENGARUH KUAT ARUS DAN WAKTU TERHADAP HASIL PEWARNAAN DAN MASSA ALUMINIUM PADA PROSES ANODIZING DENGAN ELEKTROLIT H 2 SO 4 15%

PENGARUH KUAT ARUS DAN WAKTU TERHADAP HASIL PEWARNAAN DAN MASSA ALUMINIUM PADA PROSES ANODIZING DENGAN ELEKTROLIT H 2 SO 4 15% PENGARUH KUAT ARUS DAN WAKTU TERHADAP HASIL PEWARNAAN DAN MASSA ALUMINIUM PADA PROSES ANODIZING DENGAN ELEKTROLIT H 2 SO 4 15% Arif Andrianto*, Suwardiyono, Laeli Kurniasari Jurusan Teknik Kimia Fakultas

Lebih terperinci

BAB I PENDAHULUAN 1.1. Latar belakang

BAB I PENDAHULUAN 1.1. Latar belakang BAB I PENDAHULUAN 1.1. Latar belakang Aluminium merupakan jenis logam yang banyak digunakan dalam industri maupun rumah tangga. Aluminium banyak dimanfaatkan dikarenakan memiliki kelebihan diantaranya

Lebih terperinci

PENGARUH VARIASI RAPAT ARUS TERHADAP KETEBALAN LAPISAN ELEKTROPLATING SENG PADA BAJA KARBON RENDAH. Nizam Effendi *)

PENGARUH VARIASI RAPAT ARUS TERHADAP KETEBALAN LAPISAN ELEKTROPLATING SENG PADA BAJA KARBON RENDAH. Nizam Effendi *) PENGARUH VARIASI RAPAT ARUS TERHADAP KETEBALAN LAPISAN ELEKTROPLATING SENG PADA BAJA KARBON RENDAH Nizam Effendi *) Abstrak Tujuan penelitian ini adalah untuk mengetahui pengaruh variasi rapat arus terhadap

Lebih terperinci

PENGARUH VARIASI WAKTU ANODIZING TERHADAP STRUKTUR PERMUKAAN, KETEBALAN LAPISAN OKSIDA DAN KEKERASAN ALUMINIUM 1XXX. Sulaksono Cahyo Prabowo

PENGARUH VARIASI WAKTU ANODIZING TERHADAP STRUKTUR PERMUKAAN, KETEBALAN LAPISAN OKSIDA DAN KEKERASAN ALUMINIUM 1XXX. Sulaksono Cahyo Prabowo 1 PENGARUH VARIASI WAKTU ANODIZING TERHADAP STRUKTUR PERMUKAAN, KETEBALAN LAPISAN OKSIDA DAN KEKERASAN ALUMINIUM 1XXX Sulaksono Cahyo Prabowo Jurusan Teknik Mesin Fakultas Teknik Universitas Muhammadiyah

Lebih terperinci

OPTIMASI PROSES PELAPISAN ANODISASI KERAS PADA PADUAN ALUMINIUM

OPTIMASI PROSES PELAPISAN ANODISASI KERAS PADA PADUAN ALUMINIUM OPTIMASI PROSES PELAPISAN ANODISASI KERAS PADA PADUAN ALUMINIUM Eka Febriyanti Balai Besar Teknologi Kekuatan Struktur (B2TKS) BPPT Kawasan Puspitek Serpong Tangerang 15314 E-mail : eka.ndut@yahoo.com

Lebih terperinci

BAB I PENDAHULUAN 1.1. Latar Belakang

BAB I PENDAHULUAN 1.1. Latar Belakang BAB I PENDAHULUAN 1.1. Latar Belakang Anodizing atau yang dikenal dengan nama pelapisan logam (plating) atau (surface treatment), adalah suatu perlakuan permukaan untuk melapisi permukaan logam agar terlindung

Lebih terperinci

BAB III METODE PENELITIAN. 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik

BAB III METODE PENELITIAN. 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik BAB III METODE PENELITIAN 3.1 Tempat dan Waktu Pelaksanaan Waktu dan tempat analisis sebagai berikut : 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik Departemen Teknik Mesin Sekolah

Lebih terperinci

BAB III METODOLOGI PENELITIAN. penelitian eksperimental nyata (true experimental research). Dalam hal ini

BAB III METODOLOGI PENELITIAN. penelitian eksperimental nyata (true experimental research). Dalam hal ini BAB III METODOLOGI PENELITIAN A. Metoda Penelitian Metoda penelitian yang digunakan dalam penelitian ini adalah metoda penelitian eksperimental nyata (true experimental research). Dalam hal ini penelitian

Lebih terperinci

I. PENDAHULUAN. Aluminium digunakan secara luas, karena mempunyai sifat sifat seperti

I. PENDAHULUAN. Aluminium digunakan secara luas, karena mempunyai sifat sifat seperti I. PENDAHULUAN A. Latar Belakang Aluminium digunakan secara luas, karena mempunyai sifat sifat seperti ringan, bercahaya, daya hantar listrik tinggi, dan mudah dipadukan dengan unsur unsur lain. Sifat

Lebih terperinci

PENGARUH KUAT ARUS PADA PROSES ANODIZING TERHADAP KARAKTERISTIK VELG MOBIL MERK BSA

PENGARUH KUAT ARUS PADA PROSES ANODIZING TERHADAP KARAKTERISTIK VELG MOBIL MERK BSA 34 PENGARUH KUAT ARUS PADA PROSES ANODIZING TERHADAP KARAKTERISTIK VELG MOBIL MERK BSA Hanung Hermawan 1), Nani Mulyaningsih 2), Catur Pramono 3) 1 Jurusan Teknik Mesin, Fakultas Teknik, Universitas Tidar

Lebih terperinci

BAB II TINJAUAN PUSTAKA. (C), serta unsur-unsur lain, seperti : Mn, Si, Ni, Cr, V dan lain sebagainya yang

BAB II TINJAUAN PUSTAKA. (C), serta unsur-unsur lain, seperti : Mn, Si, Ni, Cr, V dan lain sebagainya yang BAB II TINJAUAN PUSTAKA 2.1 Baja Baja merupakan paduan yang terdiri dari unsur utama besi (Fe) dan karbon (C), serta unsur-unsur lain, seperti : Mn, Si, Ni, Cr, V dan lain sebagainya yang tersusun dalam

Lebih terperinci

BAB III METODOLOGI PENELITIAN. 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik

BAB III METODOLOGI PENELITIAN. 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik BAB III METODOLOGI PENELITIAN 3.1.Tempat dan Waktu Pelaksanaan Waktu dan tempat analisis sebagai berikut : 1. Tempat pengambilan data bertempat di Laboratorium Bahan Teknik Departemen Teknik Mesin Sekolah

Lebih terperinci

PENGARUH ARUS PADA PROSES ANODISASI ALUMINUM TERHADAP KETEBALAN LAPISAN OKSIDA DAN LAJU KOROSI

PENGARUH ARUS PADA PROSES ANODISASI ALUMINUM TERHADAP KETEBALAN LAPISAN OKSIDA DAN LAJU KOROSI PENGARUH ARUS PADA PROSES ANODISASI ALUMINUM TERHADAP KETEBALAN LAPISAN OKSIDA DAN LAJU KOROSI Agung Setyo Darmawan 1, Tri Widodo Besar Riyadi 2 1 Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah

Lebih terperinci

BAB IV ANALISA DAN PEMBAHASAN

BAB IV ANALISA DAN PEMBAHASAN BAB IV ANALISA DAN PEMBAHASAN 4.1. Hasil Anodizing Hasil anodizing aluminium 1XXX dengan variasi intensitas arus 0,016A/mm 2, 0,022A/mm 2, 0,028A/mm² dan waktu pencelupan 10 menit, terdapat kegagalan atau

Lebih terperinci

BAB IV ANALISIS DAN PEMBAHASAN

BAB IV ANALISIS DAN PEMBAHASAN BAB IV ANALISIS DAN PEMBAHASAN Setelah dilakukan pengujian anodizing pada aluminium seri 1xxx, maka diperoleh data-data pengujian yang kemudian dijabarkan melalui beberapa sub-sub pembahasan dari masing-masing

Lebih terperinci

PELAPISAN ALUMINIUM DENGAN PROSES ANODISASI MULTIWARNA UNTUK APLIKASI KOMPONEN DEKORATIF SECARA PRAKTIS

PELAPISAN ALUMINIUM DENGAN PROSES ANODISASI MULTIWARNA UNTUK APLIKASI KOMPONEN DEKORATIF SECARA PRAKTIS POLITEKNOLOGI VOL. 11 NO. 3, SEPTEMBER 2012 PELAPISAN ALUMINIUM DENGAN PROSES ANODISASI MULTIWARNA UNTUK APLIKASI KOMPONEN DEKORATIF SECARA PRAKTIS Dewin Purnama 1, Vika Rizkia 2 1 Jurusan Teknik Mesin

Lebih terperinci

BAB I PENDAHULUAN 1.1. Latar Belakang

BAB I PENDAHULUAN 1.1. Latar Belakang BAB I PENDAHULUAN 1.1. Latar Belakang Aluminium sering digunakan untuk pabrikasi. Karena aluminium memiliki sifat yang lunak dan mudah di bentuk di bandingkan dengan material logam lainnya. Untuk segi

Lebih terperinci

BAB II DASAR TEORI. Pengaruh penambahan konsentrasi..., Martino R. Hutasoit, FT UI, 2008

BAB II DASAR TEORI. Pengaruh penambahan konsentrasi..., Martino R. Hutasoit, FT UI, 2008 BAB II DASAR TEORI 2.1 ALUMINIUM Dalam penggunaan logam di bidang industri, aluminium merupakan logam yang paling banyak kedua digunakan setelah baja. Hal ini berarti dalam klasifikasi logam non ferrous,

Lebih terperinci

BAB I PENDAHULUAN 1.1. Latar Belakang

BAB I PENDAHULUAN 1.1. Latar Belakang BAB I PENDAHULUAN 1.1. Latar Belakang Aluminium merupakan jenis logam yang banyak digunakan dalam kehidupan sehari-hari. Material ini dipergunakan dalam bidang yang luas bukan saja dalam alat-alat rumah

Lebih terperinci

BAB I PENDAHULUAN. 1.1 Latar Belakang. Proses akhir logam (metal finishing) merupakan bidang yang sangat luas,

BAB I PENDAHULUAN. 1.1 Latar Belakang. Proses akhir logam (metal finishing) merupakan bidang yang sangat luas, BAB I PENDAHULUAN 1.1 Latar Belakang Proses akhir logam (metal finishing) merupakan bidang yang sangat luas, yang dimana tujuan utamanya adalah untuk mencegah logam dengan korosifnya, namun juga mendapatkan

Lebih terperinci

BAB I PEDAHULUAN. 1.1 Latar Belakang. Pipa merupakan salah satu kebutuhan yang di gunakan untuk

BAB I PEDAHULUAN. 1.1 Latar Belakang. Pipa merupakan salah satu kebutuhan yang di gunakan untuk BAB I PEDAHULUAN 1.1 Latar Belakang Pipa merupakan salah satu kebutuhan yang di gunakan untuk mendistribusikan aliran fluida dari suatu tempat ketempat yang lain. Berbagi jenis pipa saat ini sudah beredar

Lebih terperinci

BAB III METODE PENELITIAN

BAB III METODE PENELITIAN BAB III METODE PENELITIAN 3.1. Diagram Alir Penelitian Untuk mempermudah penelitian proses anodizing maka dibuat diagram alir penelitian proses anodizing, dapat ditunjukkan pada Gambar 3.1. Mulai Observasi

Lebih terperinci

PENGARUH SUHU LARUTAN ELEKTROLIT DAN WAKTU PELAPISAN TEMBAGA PADA PLAT BAJA LUNAK TERHADAP NILAI KETEBALAN ABSTRACT

PENGARUH SUHU LARUTAN ELEKTROLIT DAN WAKTU PELAPISAN TEMBAGA PADA PLAT BAJA LUNAK TERHADAP NILAI KETEBALAN ABSTRACT PENGARUH SUHU LARUTAN ELEKTROLIT DAN WAKTU PELAPISAN TEMBAGA PADA PLAT BAJA LUNAK TERHADAP NILAI KETEBALAN B a s m a l Teknik Otomotif, Politeknik Pratama Mulia, Surakarta 57149, Indonesia ABSTRACT Effect

Lebih terperinci

BAB II LANDASAN TEORI

BAB II LANDASAN TEORI BAB II LANDASAN TEORI 2.1. ALUMINIUM Aluminium merupakan logam dengan karakteristik massa jenis yang relative rendah (2,7 g/cm 3 ), terletak pada golongan IIIA, dan memiliki nomor atom 13, memiliki konduktivitas

Lebih terperinci

VARIASI RAPAT ARUS DALAM PROSES PELAPISAN KHROMIUM KERAS PADA CINCIN TORAK. Yusep Sukrawan 1

VARIASI RAPAT ARUS DALAM PROSES PELAPISAN KHROMIUM KERAS PADA CINCIN TORAK. Yusep Sukrawan 1 VARIASI RAPAT ARUS DALAM PROSES PELAPISAN KHROMIUM KERAS PADA CINCIN TORAK Yusep Sukrawan 1 ABSTRAK VARIASI RAPAT ARUS DALAM PROSES PELAPISAN KHROMIUM KERAS PADA CINCIN TORAK. Pelapisan khromium keras

Lebih terperinci

I. Tujuan. Dasar Teori

I. Tujuan. Dasar Teori I. Tujuan 1. Merangkai rangkaian listrik yang digunakan dalam proses pewarnaan alumunium dalam proses anodizing dengan benar. 2. Dapat menghitung konsentrasi asam sulfat yang digunakan dalam proses pewarnaan

Lebih terperinci

Pertemuan <<22>> <<PENCEGAHAN KOROSI>>

Pertemuan <<22>> <<PENCEGAHAN KOROSI>> Matakuliah Tahun : Versi : / : Pertemuan 1 Learning Outcomes Pada akhir pertemuan ini, diharapkan mahasiswa akan mampu

Lebih terperinci

Pengaruh Jarak Anoda-Katoda dan Durasi Pelapisan Terhadap Laju Korosi pada Hasil Electroplating Hard Chrome

Pengaruh Jarak Anoda-Katoda dan Durasi Pelapisan Terhadap Laju Korosi pada Hasil Electroplating Hard Chrome JTERA - Jurnal Teknologi Rekayasa, Vol. 1, No. 1, Desember 2016, Hal. 1-6 ISSN 2548-737X Pengaruh Jarak Anoda-Katoda dan Durasi Pelapisan Terhadap Laju Korosi pada Hasil Electroplating Hard Chrome Abid

Lebih terperinci

LAPORAN TUGAS AKHIR PENGARUH VARIASI ARUS TERHADAP KETEBALAN LAPISAN, NILAI KEKERASAN, DAN LAJU KOROSI PADA PROSES ANODIZING

LAPORAN TUGAS AKHIR PENGARUH VARIASI ARUS TERHADAP KETEBALAN LAPISAN, NILAI KEKERASAN, DAN LAJU KOROSI PADA PROSES ANODIZING LAPORAN TUGAS AKHIR PENGARUH VARIASI ARUS TERHADAP KETEBALAN LAPISAN, NILAI KEKERASAN, DAN LAJU KOROSI PADA PROSES ANODIZING Disusun Untuk Memenuhi Tugas dan Syarat syarat Guna Memperoleh Gelar Sarjana

Lebih terperinci

STUDI PELAPISAN KROM DENGAN PROSES ELEKTROPLATING PADA HANDEL REM SEPEDA MOTOR DENGAN VARIASI RAPAT ARUS

STUDI PELAPISAN KROM DENGAN PROSES ELEKTROPLATING PADA HANDEL REM SEPEDA MOTOR DENGAN VARIASI RAPAT ARUS STUDI PELAPISAN KROM DENGAN PROSES ELEKTROPLATING PADA HANDEL REM SEPEDA MOTOR DENGAN VARIASI RAPAT ARUS NASKAH PUBLIKASI Untuk Memenuhi Sebagian Persyaratan Guna Mencapai Derajat Sarjana S-1 Teknik Mesin

Lebih terperinci

BAB I PENDAHULUAN. terjadinya perubahan metalurgi yaitu pada struktur mikro, sehingga. ketahanan terhadap laju korosi dari hasil pengelasan tersebut.

BAB I PENDAHULUAN. terjadinya perubahan metalurgi yaitu pada struktur mikro, sehingga. ketahanan terhadap laju korosi dari hasil pengelasan tersebut. BAB I PENDAHULUAN 1.1 Latar Belakang Pengelasan merupakan proses penyambungan setempat dari logam dengan menggunakan energi panas. Akibat panas maka logam di sekitar lasan akan mengalami siklus termal

Lebih terperinci

PENINGKATAN KETAHANAN KOROSI BAJA JIS S45C HASIL ELECTROPLATING NIKEL PADA APLIKASI MATERIAL CRYOGENIC

PENINGKATAN KETAHANAN KOROSI BAJA JIS S45C HASIL ELECTROPLATING NIKEL PADA APLIKASI MATERIAL CRYOGENIC PENINGKATAN KETAHANAN KOROSI BAJA JIS S45C HASIL ELECTROPLATING NIKEL PADA APLIKASI MATERIAL CRYOGENIC Mirza Pramudia 1 1 Fakultas Teknik, Universitas Trunojoyo, Madura Jl. Raya Telang, Po. Box 2 Kamal,

Lebih terperinci

Makalah seminar PENGARUH TEMPERATUR DYEING PADA PROSES ANODIZING TERHADAP KETEBALAN DAN LAJU KOROSI UNTUK BAHAN COR KUNINGAN

Makalah seminar PENGARUH TEMPERATUR DYEING PADA PROSES ANODIZING TERHADAP KETEBALAN DAN LAJU KOROSI UNTUK BAHAN COR KUNINGAN REVISI Makalah seminar PENGARUH TEMPERATUR DYEING PADA PROSES ANODIZING TERHADAP KETEBALAN DAN LAJU KOROSI UNTUK BAHAN COR KUNINGAN Oleh : 1. Bibit Sugito 2. Pramuko IP 3. Agung Supriyadi TEKNIK MESIN

Lebih terperinci

PENGARUH KUAT ARUS LISTRIK TERHADAP KEKERASAN, KECERAHAN DAN KETEBALAN LAPISAN OKSIDA HASIL PROSES ANODIZING PADA ALUMINIUM

PENGARUH KUAT ARUS LISTRIK TERHADAP KEKERASAN, KECERAHAN DAN KETEBALAN LAPISAN OKSIDA HASIL PROSES ANODIZING PADA ALUMINIUM PENGARUH KUAT ARUS LISTRIK TERHADAP KEKERASAN, KECERAHAN DAN KETEBALAN LAPISAN OKSIDA HASIL PROSES ANODIZING PADA ALUMINIUM Wawan Hartanto Program Studi S-1 Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah

Lebih terperinci

Handout. Bahan Ajar Korosi

Handout. Bahan Ajar Korosi Handout Bahan Ajar Korosi PENDAHULUAN Aplikasi lain dari prinsip elektrokimia adalah pemahaman terhadap gejala korosi pada logam dan pengendaliannya. Berdasarkan data potensial reduksi standar, diketahui

Lebih terperinci

PERCOBAAN IV ANODASI ALUMINIUM

PERCOBAAN IV ANODASI ALUMINIUM LAPORAN PRAKTIKUM KIMIA ANORGANIK PERCOBAAN IV ANODASI ALUMINIUM NAMA : RACHMA SURYA M NIM : H311 12 267 KELOMPOK/REGU : III (TIGA)/VII (TUJUH) HARI/TANGGAL PERCOBAAN : RABU/23 OKTOBER 2013 ASISTEN : HASMINISARI

Lebih terperinci

BAB I PANDAHULUAN. Berbagai industri barang perhiasan, kerajinan, komponen sepeda. merupakan pelapisan logam pada benda padat yang mempunyai

BAB I PANDAHULUAN. Berbagai industri barang perhiasan, kerajinan, komponen sepeda. merupakan pelapisan logam pada benda padat yang mempunyai BAB I PANDAHULUAN 1.1 Latar Belakang Kehidupan modern tak lepas dari peranan industri elektroplating. Berbagai industri barang perhiasan, kerajinan, komponen sepeda motor, mobil, mesin, barang elektronik,

Lebih terperinci

BAB I PENDAHULUAN. permukaan bumi dan paling berlimpah ketiga. Melimpahnya aluminium

BAB I PENDAHULUAN. permukaan bumi dan paling berlimpah ketiga. Melimpahnya aluminium BAB I PENDAHULUAN 1.1. Latar Belakang Aluminium merupakan elemen yang berjumlah sekitar 8% dari permukaan bumi dan paling berlimpah ketiga. Melimpahnya aluminium menjadikanya salah satu logam yang sering

Lebih terperinci

BAB III METODOLOGI PENELITIAN

BAB III METODOLOGI PENELITIAN BAB III METODOLOGI PENELITIAN 3.1 Tempat Penelitian Proses pelapisan plastik ABS dengan menggunakan metode elektroplating dilaksanakan di PT. Rekayasa Plating Cimahi, sedangkan pengukuran kekasaran, ketebalan

Lebih terperinci

BAB III METODOLOGI PENELITIAN

BAB III METODOLOGI PENELITIAN BAB III METODOLOGI PENELITIAN 3.1 DIAGRAM ALIR PENELITIAN Aluminum Foil 99,9% Pemotongan Sampel Degreasing dengan NaOH Pembuatan sampel anodisasi Anodisasi 150 ml H 2 SO 4 3M + 150 ml H 2 C 2 O 4 0,5M

Lebih terperinci

PENGARUH VARIASI WAKTU PROSES ANODIZING TERHADAP KARAKTERISTIK VELG RACING MERK SPRINT

PENGARUH VARIASI WAKTU PROSES ANODIZING TERHADAP KARAKTERISTIK VELG RACING MERK SPRINT 41 PENGARUH VARIASI WAKTU PROSES ANODIZING TERHADAP KARAKTERISTIK VELG RACING MERK SPRINT Rachman Satya Pamungkas 1), Xander Salahudin 2), Nani Mulyaningsih 3) 1 Jurusan Teknik Mesin, Fakultas Teknik,

Lebih terperinci

PENGARUH VARIASI KUAT ARUS LISTRIK PADA PROSES ANODIZING TERHADAP KEKERASAN PERMUKAAN LOGAM ALUMINIUM SERI 2XXX

PENGARUH VARIASI KUAT ARUS LISTRIK PADA PROSES ANODIZING TERHADAP KEKERASAN PERMUKAAN LOGAM ALUMINIUM SERI 2XXX PENGARUH VARIASI KUAT ARUS LISTRIK PADA PROSES ANODIZING TERHADAP KEKERASAN PERMUKAAN LOGAM ALUMINIUM SERI 2XXX Ahmad Yulizal Untung Program Studi S-1 Teknik Mesin, Fakultas Teknik, Universitas Muhammadiyah

Lebih terperinci

PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL

PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL Firlya Rosa. S.S.T., M.T. 1 Jurusan Teknik Mesin, Fakultas Teknik Universitas Bangka Belitung firlya@ubb.ac.id 1 Rodiawan, S.T.,

Lebih terperinci

BAB II TINJAUAN PUSTAKA

BAB II TINJAUAN PUSTAKA 5 BAB II TINJAUAN PUSTAKA 2.1. ALUMINIUM Aluminium merupakan logam dengan karakteristik massa jenis yang relative rendah (2,7 g/cm 3 ), terletak pada golongan IIIA, dan memiliki nomor atom 13, memiliki

Lebih terperinci

BAB I PENDAHULUAN. manufacturing dan automotive, maka banyak sekali inovasi-inovasi maupun

BAB I PENDAHULUAN. manufacturing dan automotive, maka banyak sekali inovasi-inovasi maupun BAB I PENDAHULUAN 1.1. Latar Belakang Dengan semakin berkembangnya dunia industri, khususnya dunia manufacturing dan automotive, maka banyak sekali inovasi-inovasi maupun penemuan baru yang terdapat dalam

Lebih terperinci

Laju Korosi Baja Dalam Larutan Asam Sulfat dan Dalam Larutan Natrium Klorida

Laju Korosi Baja Dalam Larutan Asam Sulfat dan Dalam Larutan Natrium Klorida Laju Korosi Baja Dalam Larutan Asam Sulfat dan Dalam Larutan Natrium Klorida Diah Riski Gusti, S.Si, M.Si, jurusan PMIPA FKIP Universitas Jambi Abstrak Telah dilakukan penelitian laju korosi baja dalam

Lebih terperinci

BAB IV DATA HASIL PENELITIAN

BAB IV DATA HASIL PENELITIAN BAB IV DATA HASIL PENELITIAN 4.1. PENGAMATAN VISUAL bab ini. Data hasil proses anodisasi dengan variabel pada penelitian ini terurai pada Gambar 4.1. Foto permukaan sampel sebelum dianodisasi (a) (b) (c)

Lebih terperinci

BAB II KOROSI dan MICHAELIS MENTEN

BAB II KOROSI dan MICHAELIS MENTEN BAB II : MEKANISME KOROSI dan MICHAELIS MENTEN 4 BAB II KOROSI dan MICHAELIS MENTEN Di alam bebas, kebanyakan logam ditemukan dalam keadaan tergabung secara kimia dan disebut bijih. Oleh karena keberadaan

Lebih terperinci

STUDI PELAPISAN KROM PADA BAJA KARBON DENGAN VARIASI WAKTU PENCELUPAN 10, 20, 30, 40, 50 MENIT DAN TEGANGAN 9 VOLT DENGAN ARUS 5 AMPERE

STUDI PELAPISAN KROM PADA BAJA KARBON DENGAN VARIASI WAKTU PENCELUPAN 10, 20, 30, 40, 50 MENIT DAN TEGANGAN 9 VOLT DENGAN ARUS 5 AMPERE STUDI PELAPISAN KROM PADA BAJA KARBON DENGAN VARIASI WAKTU PENCELUPAN 10, 20, 30, 40, 50 MENIT DAN TEGANGAN 9 VOLT DENGAN ARUS 5 AMPERE Disusun Sebagai Syarat Untuk Mencapai Gelar Sarjana Teknik Jurusan

Lebih terperinci

BAB II TINJAUAN PUSTAKA

BAB II TINJAUAN PUSTAKA BAB II TINJAUAN PUSTAKA 2.1. Kajian Pustaka. Aluminium adalah material logam yang banyak digunakan pada berbagai macam aplikasi seperti di bidang industri hingga keperluan rumah tangga. Alumunium memiliki

Lebih terperinci

TUGAS AKHIR PENGARUH VARIASI WAKTU PENCELUPAN PADA PROSES ANODIZING ALUMINIUM SERI 1XXX

TUGAS AKHIR PENGARUH VARIASI WAKTU PENCELUPAN PADA PROSES ANODIZING ALUMINIUM SERI 1XXX TUGAS AKHIR PENGARUH VARIASI WAKTU PENCELUPAN PADA PROSES ANODIZING ALUMINIUM SERI 1XXX Aji istomo Universitas Muhammadiyah Yogyakarta, Teknik Mesin, Fakultas Teknik, Yogyakarta 55183, Indonesia Aji.istomo.2011@ft.umy.ac.id

Lebih terperinci

PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL

PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL 1 PELAPISAN EMAS PADA KERAJINAN TANGAN PEWTER UNTUK MENINGKATKAN NILAI JUAL Firlya Rosa. S. 1 Jurusan Teknik Mesin, Fakultas Teknik Universitas Bangka Belitung firlya@ubb.ac.id 1 Rodiawan, 2 Jurusan Teknik

Lebih terperinci

BAB IV HASIL PENELITIAN

BAB IV HASIL PENELITIAN BAB IV HASIL PENELITIAN 4.1 PENGAMATAN VISUAL Pengamatan visual dilakukan terhadap sampel sebelum dilakukan proses anodisasi dan setelah proses anodisasi. Untuk sampel yang telah mengalami proses anodisasi,

Lebih terperinci

Pengaruh Rapat Arus Terhadap Ketebalan Dan Struktur Kristal Lapisan Nikel pada Tembaga

Pengaruh Rapat Arus Terhadap Ketebalan Dan Struktur Kristal Lapisan Nikel pada Tembaga ISSN:2089 0133 Indonesian Journal of Applied Physics (2012) Vol.2 No.1 halaman 1 April 2012 Pengaruh Rapat Arus Terhadap Ketebalan Dan Struktur Kristal Lapisan Nikel pada Tembaga ABSTRACT Setyowati, Y.

Lebih terperinci

Penentuan Laju Korosi pada Suatu Material

Penentuan Laju Korosi pada Suatu Material Penentuan Laju Korosi pada Suatu Material Sarasati Istiqomah (0823320), Vina Puji Lestari (08233006), Imroatul Maghfioh (0823325), Ihfadni Nazwa (0823326), Faridhatul Khasanah (0823334), Darmawan (0823339),

Lebih terperinci

KIMIA ELEKTROLISIS

KIMIA ELEKTROLISIS KIMIA ELEKTROLISIS A. Tujuan Pembelajaran Mempelajari perubahan-perubahan yang terjadi pada reaksi elektrolisis larutan garam tembaga sulfat dan kalium iodida. Menuliskan reaksi reduksi yang terjadi di

Lebih terperinci

Pengaruh Parameter Proses Pelapisan Nikel Terhadap Ketebalan Lapisan

Pengaruh Parameter Proses Pelapisan Nikel Terhadap Ketebalan Lapisan Pengaruh Parameter Proses Pelapisan Nikel Terhadap Ketebalan Lapisan Bambang Santosa dan Martijanti Syamsa Jurusan Teknik Mesin, Universitas Jenderal Achmad Yani, Bandung Email: martijanti@yahoo.co.id

Lebih terperinci

BAB II TINJAUAN PUSTAKA

BAB II TINJAUAN PUSTAKA BAB II TINJAUAN PUSTAKA 2.1. Kajian Pustaka Aluminium merupakan salah satu material logam yang banyak dimanfaatkan dan dikembangkan pada berbagai macam aplikasi khususnya dalam dunia perindustrian. Agar

Lebih terperinci

PENGARUH WAKTU PENCELUPAN DAN TEMPERATUR PROSES ELEKTROPLATING TERHADAP KETEBALAN DAN KEKERASAN PERMUKAAN BAJA ST 42

PENGARUH WAKTU PENCELUPAN DAN TEMPERATUR PROSES ELEKTROPLATING TERHADAP KETEBALAN DAN KEKERASAN PERMUKAAN BAJA ST 42 JTM. Volume 03 Nomor 01 Tahun 2014, 176 183 PENGARUH WAKTU PENCELUPAN DAN TEMPERATUR PROSES ELEKTROPLATING TERHADAP KETEBALAN DAN KEKERASAN PERMUKAAN BAJA ST 42 Ratih Deviana S1 Pendidikan Teknik Mesin,

Lebih terperinci

Anodizing Aluminium Dengan Menggunakan Pewarna Tembaga Nitrat Dan Kalium Permanganat PENELITIAN

Anodizing Aluminium Dengan Menggunakan Pewarna Tembaga Nitrat Dan Kalium Permanganat PENELITIAN Anodizing Aluminium Dengan Menggunakan Pewarna Tembaga Nitrat Dan Kalium Permanganat PENELITIAN Oleh : EDVIN MAHARDIKA ( 0631010059 ) ANIK TRESNAWATI ( 0631010088 ) JURUSAN TEKNIK KIMIA FAKULTAS TEKNOLOGI

Lebih terperinci

BAB III METODE PENELITIAN

BAB III METODE PENELITIAN BAB III METODE PENELITIAN 3.1. Diagram Alir Penelitian Mulai Identifikasi Masalah Kajian Pustaka Persiapan Alat dan Bahan Aluminium Seri 1XXX Cleaning Na 2CO 3 50 gram + 1 liter RO Waktu cleaning 2 menit

Lebih terperinci

Momentum, Vol. 13, No. 2, Oktober 2017, Hal ISSN

Momentum, Vol. 13, No. 2, Oktober 2017, Hal ISSN Momentum, Vol. 13, No. 2, Oktober 217, Hal. 19-24 ISSN 216-7395 PENGARUH TEGANGAN PELAPISAN NIKEL PADA TEMBAGA DALAM PELAPISAN KHROM DEKORATIF TERHADAP KETEBALAN, KEKERASAN DAN KEKASARAN LAPISAN Musa Assegaff

Lebih terperinci

Elektrokimia. Sel Volta

Elektrokimia. Sel Volta TI222 Kimia lanjut 09 / 01 47 Sel Volta Elektrokimia Sel Volta adalah sel elektrokimia yang menghasilkan arus listrik sebagai akibat terjadinya reaksi pada kedua elektroda secara spontan Misalnya : sebatang

Lebih terperinci

BAB I PENDAHULUAN. Dalam teknologi pengerjaan logam, proses electroplating. dikategorikan sebagai proses pengerjaan akhir (metal finishing).

BAB I PENDAHULUAN. Dalam teknologi pengerjaan logam, proses electroplating. dikategorikan sebagai proses pengerjaan akhir (metal finishing). BAB I PENDAHULUAN 1.1. Latar Belakang Masalah Dalam teknologi pengerjaan logam, proses electroplating dikategorikan sebagai proses pengerjaan akhir (metal finishing). Secara sederhana, electroplating dapat

Lebih terperinci

PENGARUH VARIASI WAKTU PENAHANAN PENCELUPAN TERHADAP KETEBALAN LAPISAN DAN LAJU KOROSI PADA KUNINGAN COR YANG DI ANODIZING

PENGARUH VARIASI WAKTU PENAHANAN PENCELUPAN TERHADAP KETEBALAN LAPISAN DAN LAJU KOROSI PADA KUNINGAN COR YANG DI ANODIZING TUGAS AKHIR PENGARUH VARIASI WAKTU PENAHANAN PENCELUPAN TERHADAP KETEBALAN LAPISAN DAN LAJU KOROSI PADA KUNINGAN COR YANG DI ANODIZING Disusun : P R I A D I NIM : D 200 030 074 JURUSAN TEKNIK MESIN FAKULTAS

Lebih terperinci

I. PENDAHULUAN. Indonesia memiliki lahan tambang yang cukup luas di beberapa wilayahnya.

I. PENDAHULUAN. Indonesia memiliki lahan tambang yang cukup luas di beberapa wilayahnya. 1 I. PENDAHULUAN 1.1 Latar Belakang Indonesia memiliki lahan tambang yang cukup luas di beberapa wilayahnya. Salah satu bahan tambang yang banyak fungsinya yaitu batu bara, misalnya untuk produksi besi

Lebih terperinci

BAB I PENDAHULUAN. juga menjadi bisnis yang cukup bersaing dalam perusahaan perbajaan.

BAB I PENDAHULUAN. juga menjadi bisnis yang cukup bersaing dalam perusahaan perbajaan. BAB I PENDAHULUAN 1.1. Latar Belakang. Pipa merupakan salah satu kebutuhan yang di gunakan untuk mendistribusikan aliran fluida dari suatu tempat ketempat yang lain. Berbagi jenis pipa saat ini sudah beredar

Lebih terperinci

BAB III METODOLOGI PENELITIAN. Studi Literatur. Pemotongan Sampel. Degreasing dengan larutan Acetone

BAB III METODOLOGI PENELITIAN. Studi Literatur. Pemotongan Sampel. Degreasing dengan larutan Acetone 24 BAB III METODOLOGI PENELITIAN 3.1 DIAGRAM ALIR PENELITIAN Studi Literatur Pemotongan Sampel Degreasing dengan larutan Acetone Rinsing mengunakan H 2 O Rinsing mengunakan Ethanol * Anodizing Larutan

Lebih terperinci

PENGARUH PENAMBAHAN KONSENTRASI ASAM OKSALAT TERHADAP KETEBALAN LAPISAN OKSIDA PADA ALUMINIUM FOIL HASIL PROSES ANODISASI SKRIPSI

PENGARUH PENAMBAHAN KONSENTRASI ASAM OKSALAT TERHADAP KETEBALAN LAPISAN OKSIDA PADA ALUMINIUM FOIL HASIL PROSES ANODISASI SKRIPSI PENGARUH PENAMBAHAN KONSENTRASI ASAM OKSALAT TERHADAP KETEBALAN LAPISAN OKSIDA PADA ALUMINIUM FOIL HASIL PROSES ANODISASI SKRIPSI Oleh MARTINO R. HUTASOIT 04 04 04 050 X DEPARTEMEN TEKNIK METALURGI & MATERIAL

Lebih terperinci

Ekstraksi Zat Warna dari Kulit Manggis dan Pemanfaatannya untuk Pewarna Logam Aluminium Hasil Anosidasi. Agustinus Ngatin dan Edy Wahyu Sri Mulyono

Ekstraksi Zat Warna dari Kulit Manggis dan Pemanfaatannya untuk Pewarna Logam Aluminium Hasil Anosidasi. Agustinus Ngatin dan Edy Wahyu Sri Mulyono Ekstraksi Zat Warna dari Kulit Manggis dan Pemanfaatannya untuk Pewarna Logam Aluminium Hasil Anosidasi Agustinus Ngatin dan Edy Wahyu Sri Mulyono Jurusan Teknik Kimia Politeknik Negeri Bandung Jl.Gegerkalong

Lebih terperinci

PENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH

PENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH TUGAS AKHIR PENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH Diajukan guna memenuhi sebagian syarat memperoleh derajat sarjana S1 pada

Lebih terperinci

BAB II TINJAUAN PUSTAKA DAN DASAR TEORI

BAB II TINJAUAN PUSTAKA DAN DASAR TEORI BAB II TINJAUAN PUSTAKA DAN DASAR TEORI 2.1 Tinjauan Pustaka Dalam metode pelapisan plastik ABS dengan elektroplating ada beberapa aspek yang harus diperhatikan, diantaranya adalah tingkat kecerahan suatu

Lebih terperinci

BAB 4 HASIL DAN ANALISA

BAB 4 HASIL DAN ANALISA 30 BAB 4 HASIL DAN ANALISA 4.1 Hasil Pengujian Polarisasi Potensiodinamik 4.1.1 Data Laju Korosi (Corrosion Rate) Pengujian polarisasi potensiodinamik dilakukan berdasarkan analisa tafel dan memperlihatkan

Lebih terperinci

BAB IV ANALISIS DAN PEMBAHASAN

BAB IV ANALISIS DAN PEMBAHASAN BAB IV ANALISIS DAN PEMBAHASAN 4.1 Hasil pengamatan kecerahan spesimen anodizing Setelah dilakukan pengujian maka diperoleh data-data pengujian material. Kemudian data dijelaskan pada sub-sub pembahasan

Lebih terperinci

ELEKTROKIMIA DAN KOROSI (Continued) Ramadoni Syahputra

ELEKTROKIMIA DAN KOROSI (Continued) Ramadoni Syahputra ELEKTROKIMIA DAN KOROSI (Continued) Ramadoni Syahputra 3.3 KOROSI Korosi dapat didefinisikan sebagai perusakan secara bertahap atau kehancuran atau memburuknya suatu logam yang disebabkan oleh reaksi kimia

Lebih terperinci

BAB IV HASIL DAN PEMBAHASAN. 4.1 Korosi Baja Karbon dalam Lingkungan Elektrolit Jenuh Udara

BAB IV HASIL DAN PEMBAHASAN. 4.1 Korosi Baja Karbon dalam Lingkungan Elektrolit Jenuh Udara BAB IV HASIL DAN PEMBAHASAN 4.1 Korosi Baja Karbon dalam Lingkungan Elektrolit Jenuh Udara Untuk mengetahui laju korosi baja karbon dalam lingkungan elektrolit jenuh udara, maka dilakukan uji korosi dengan

Lebih terperinci

Mekanika Jurnal Teknik Mesin, Volume 1 No. 2, Abstract

Mekanika Jurnal Teknik Mesin, Volume 1 No. 2, Abstract ANALISA PENGARUH VARIASI TEGANGAN LISTRIK DAN JARAK ANODA DENGAN KATODA PADA PROSES ANODISASI TERHADAP TINGKAT KILAP MATERIAL KOMPOSIT AL ABU DASAR BATUBARA Edi Santoso 1, Fatehur Rohman 2 Program Studi

Lebih terperinci

PELAPISAN STAINLESS STEEL AISI 304 MENGGUNAKAN NIKEL (Ni) MELALUI PROSES ELEKTROPLATING

PELAPISAN STAINLESS STEEL AISI 304 MENGGUNAKAN NIKEL (Ni) MELALUI PROSES ELEKTROPLATING PELAPISAN STAINLESS STEEL AISI 4 MENGGUNAKAN NIKEL (Ni) MELALUI PROSES ELEKTROPLATING Yoga Setiawan Ady N, Sulistyo Mahasiswa Jurusan Teknik Mesin, Fakultas Teknik, Universitas Diponegoro Dosen Jurusan

Lebih terperinci

EKSTRAK DAUN GAMBIR SEBAGAI INHIBITOR KOROSI Oleh: Dr. Ahmad Fadli, Ir.Rozanna Sri Irianty, M.Si, Komalasari, ST., MT. Abstralc

EKSTRAK DAUN GAMBIR SEBAGAI INHIBITOR KOROSI Oleh: Dr. Ahmad Fadli, Ir.Rozanna Sri Irianty, M.Si, Komalasari, ST., MT. Abstralc EKSTRAK DAUN GAMBIR SEBAGAI INHIBITOR KOROSI Oleh: Dr. Ahmad Fadli, Ir.Rozanna Sri Irianty, M.Si, Komalasari, ST., MT Abstralc Secara awam icorosi ditcenai sebagai penglcaratan, merupakan suatu peristiwa

Lebih terperinci

MODUL I SIFAT KOLIGATIF LARUTAN Penurunan Titik Beku Larutan

MODUL I SIFAT KOLIGATIF LARUTAN Penurunan Titik Beku Larutan MODUL I SIFAT KOLIGATIF LARUTAN Penurunan Titik Beku Larutan - Siswa mampu membuktikan penurunan titik beku larutan akibat penambahan zat terlarut. - Siswa mampu membedakan titik beku larutan elektrolit

Lebih terperinci

BAB II TINJAUAN PUSTAKA

BAB II TINJAUAN PUSTAKA BAB II TINJAUAN PUSTAKA 2.1. Kajian Pustaka Aluminium merupakan material logam yang banyak dikembangkan dan di manfaatkan di dalam beberapa bindang terutama di bidang peindustrian. Agar kualitas fisik

Lebih terperinci

PENGARUH LAJU KOROSI PELAT BAJA LUNAK PADA LINGKUNGAN AIR LAUT TERHADAP PERUBAHAN BERAT.

PENGARUH LAJU KOROSI PELAT BAJA LUNAK PADA LINGKUNGAN AIR LAUT TERHADAP PERUBAHAN BERAT. PENGARUH LAJU KOROSI PELAT BAJA LUNAK PADA LINGKUNGAN AIR LAUT TERHADAP PERUBAHAN BERAT. Hartono Program Diploma III Teknik Perkapala, Fakultas Teknik, Universitas Diponegoro ABSTRACT One of the usage

Lebih terperinci

PENGARUH KONSENTRASI NIKEL DAN KLORIDA TERHADAP PROSES ELEKTROPLATING NIKEL

PENGARUH KONSENTRASI NIKEL DAN KLORIDA TERHADAP PROSES ELEKTROPLATING NIKEL PENGARUH KONSENTRASI NIKEL DAN KLORIDA TERHADAP PROSES ELEKTROPLATING NIKEL Mentik Hulupi Agustinus Ngatin Teknik Kimia, Politeknik Negeri Bandung Jl. Gegerkalong Hilir, Ds. Ciwaruga, Bandung E-mail: hulupimentik@yahoo.com

Lebih terperinci

BAB 1 PENDAHULUAN Latar Belakang

BAB 1 PENDAHULUAN Latar Belakang BAB 1 PENDAHULUAN 1.1. Latar Belakang Korosi dapat didefinisikan sebagai penurunan mutu suatu logam akibat reaksi elektrokimia dengan lingkungannya, yang melibatkan pergerakan ion logam ke dalam larutan

Lebih terperinci

SKRIPSI. PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM :

SKRIPSI. PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM : SKRIPSI PENGARUH PENAMBAHAN SILIKON TERHADAP LAJU KOROSI PADA PADUAN PERUNGGU TIMAH PUTIH ( 85 Cu 15 Sn ) Oleh : Yoppi Eka Saputra NIM : 1104305004 JURUSAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS UDAYANA

Lebih terperinci

PENGARUH PROSENTASE KARBON PADA BAJA KARBON PROSES ELECTROPLATING TEMBAGA

PENGARUH PROSENTASE KARBON PADA BAJA KARBON PROSES ELECTROPLATING TEMBAGA NASKAH PUBLIKASI ILMIAH PENGARUH PROSENTASE KARBON PADA BAJA KARBON PROSES ELECTROPLATING TEMBAGA Disusun Untuk Memenuhi Tugas dan Syarat - Syarat Guna Memperoleh Gelar Sarjan Teknik (S1) Jurusan Teknik

Lebih terperinci

BAB I PENDAHULUAN 1.1. Latar Belakang

BAB I PENDAHULUAN 1.1. Latar Belakang 1 BAB I PENDAHULUAN 1.1. Latar Belakang Korosi merupakan salah satu permasalahan penting yang harus dihadapi oleh berbagai macam sektor industri di Indonesia terutama industri perkapalan. Tidak sedikit

Lebih terperinci

PUBLIKASI ILMIAH. Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan Teknik Mesin Fakultas Teknik.

PUBLIKASI ILMIAH. Disusun sebagai salah satu syarat menyelesaikan Program Studi Strata I pada Jurusan Teknik Mesin Fakultas Teknik. STUDI PELAPISAN KROM PADA BAJA KARBON DENGAN RAPAT ARUS 5 AMPERE TEGANGAN 12 VOLT DAN VARIASI WAKTU PENCELUPAN 10, 20, 30, 40 DAN 50 MENIT UNIVERSITAS MUHAMMADIYAH SURAKARTA PUBLIKASI ILMIAH Disusun sebagai

Lebih terperinci

Gambar 4.1 Hasil anodizing aluminium 1XXX dengan suhu elektrolit o C dan variasi waktu pencelupan (a) 5 menit. (b) 10 menit. (c) 15 menit.

Gambar 4.1 Hasil anodizing aluminium 1XXX dengan suhu elektrolit o C dan variasi waktu pencelupan (a) 5 menit. (b) 10 menit. (c) 15 menit. BAB IV ANALISA DAN PEMBAHASAN 1.1. Hasil Anodizing Hasil anodizing spesimen aluminium 1XXX dengan suhu elektrolit yang dijaga antara 40-45 o C dan waktu pencelupan anodizing selama 5, 10 dan 15 menit dapat

Lebih terperinci

PENGARUH WAKTU DAN LUAS PERMUKAAN TERHADAP KETEBALAN PRODUK PADA ELEKTROPLATING ACID ZINC

PENGARUH WAKTU DAN LUAS PERMUKAAN TERHADAP KETEBALAN PRODUK PADA ELEKTROPLATING ACID ZINC Jurnal Ilmiah Teknik Kimia UNPAM, Vol. 1 No. 1 (Januari, 2017) ISSN 2549-0699 PENGARUH WAKTU DAN LUAS PERMUKAAN TERHADAP KETEBALAN PRODUK PADA ELEKTROPLATING ACID ZINC Study of Impact Time and Surface

Lebih terperinci

TUGAS AKHIR KARAKTERISASI PERMUKAAN MULTILAPIS KROM DAN TEMBAGA PADA BAJA KARBON HASIL PROSES ELECTROPLATING

TUGAS AKHIR KARAKTERISASI PERMUKAAN MULTILAPIS KROM DAN TEMBAGA PADA BAJA KARBON HASIL PROSES ELECTROPLATING TUGAS AKHIR KARAKTERISASI PERMUKAAN MULTILAPIS KROM DAN TEMBAGA PADA BAJA KARBON HASIL PROSES ELECTROPLATING Disusun Sebagai Syarat Untuk Mencapai Gelar Sarjana Teknik Jurusan Teknik Mesin Fakultas Teknik

Lebih terperinci

BAB IV ANALISIS DAN PEMBAHASAN 4.2 DATA HASIL ARANG TEMPURUNG KELAPA SETELAH DILAKUKAN AKTIVASI

BAB IV ANALISIS DAN PEMBAHASAN 4.2 DATA HASIL ARANG TEMPURUNG KELAPA SETELAH DILAKUKAN AKTIVASI 39 BAB IV ANALISIS DAN PEMBAHASAN 4.1 PENDAHULUAN Hasil eksperimen akan ditampilkan pada bab ini. Hasil eksperimen akan didiskusikan untuk mengetahui keoptimalan arang aktif tempurung kelapa lokal pada

Lebih terperinci

BAB IV ANALISIS DAN PEMBAHASAN

BAB IV ANALISIS DAN PEMBAHASAN BAB IV ANALISIS DAN PEMBAHASAN Setelah dilakukan pengujian, maka diperoleh data-data pengujian. Kemudian data-data tersebut dijabarkan dalam beberapa sub-sub pembahasan dari masing-masing setiap jenis

Lebih terperinci

PENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH

PENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH PENGARUH VARIASI ARUS LISTRIK TERHADAP KETEBALAN LAPISAN TEMBAGA PADA PROSES ELEKTROPLATING PLAT BAJA KARBON RENDAH NASKAH PUBLIKASI Diajukan guna memenuhi sebagian syarat memperoleh derajat sarjana S1

Lebih terperinci

BAB I PENDAHULUAN. 1.1 Latar Belakang

BAB I PENDAHULUAN. 1.1 Latar Belakang 1.1 Latar Belakang BAB I PENDAHULUAN Di negara berkembang seperti Indonesia, pelapisan logam krom memegang peranan yang cukup penting terutama di sektor industri. Beberapa sektor industri yang menggunakan

Lebih terperinci

BAB II TINJAUAN PUSTAKA DAN LANDASAN TEORI. industry manufaktur khususnya di bidang otomotif. Agar kualitas fisik maupun

BAB II TINJAUAN PUSTAKA DAN LANDASAN TEORI. industry manufaktur khususnya di bidang otomotif. Agar kualitas fisik maupun BAB II TINJAUAN PUSTAKA DAN LANDASAN TEORI 2.1.Kajian Pustaka Aluminium merupakan salah satu material logam yang banyak dimanfaatkan dan dikembangkan. Dalam berbagai macam aplikasi khususnya dalam dunia

Lebih terperinci

Sudaryatno Sudirham ing Utari. Mengenal. Sudaryatno S & Ning Utari, Mengenal Sifat-Sifat Material (1)

Sudaryatno Sudirham ing Utari. Mengenal. Sudaryatno S & Ning Utari, Mengenal Sifat-Sifat Material (1) Sudaryatno Sudirham ing Utari Mengenal Sifat-Sifat Material (1) 16-2 Sudaryatno S & Ning Utari, Mengenal Sifat-Sifat Material (1) BAB 16 Oksidasi dan Korosi Dalam reaksi kimia di mana oksigen tertambahkan

Lebih terperinci

DAFTAR ISI LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL...

DAFTAR ISI LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL... DAFTAR ISI Halaman LEMBAR PENGESAHAN... LEMBAR PERSETUJUAN... ABSTRAK... ABSTRACT... KATA PENGANTAR... DAFTAR ISI... DAFTAR GAMBAR... DAFTAR TABEL... DAFTAR LAMPIRAN... i ii iii iv v vi ix xi xii BAB 1

Lebih terperinci

SKRIPSI KUALITAS ELEKTRO PLATING ALUMINIUM DENGAN NIKEL AKIBAT VARIASI ALUMINIUM NIKEL ALUMINIUM SENG NIKEL ALUMINIUM SENG TEMBAGA NIKEL

SKRIPSI KUALITAS ELEKTRO PLATING ALUMINIUM DENGAN NIKEL AKIBAT VARIASI ALUMINIUM NIKEL ALUMINIUM SENG NIKEL ALUMINIUM SENG TEMBAGA NIKEL SKRIPSI KUALITAS ELEKTRO PLATING ALUMINIUM DENGAN NIKEL AKIBAT VARIASI ALUMINIUM NIKEL ALUMINIUM SENG NIKEL ALUMINIUM SENG TEMBAGA NIKEL Oleh : I WAYAN AGUS SAPUTRA 0919351029 JURUSAN TEKNIK MESIN FAKULTAS

Lebih terperinci

BAB I PENDAHULUAN 1.1 Latar belakang

BAB I PENDAHULUAN 1.1 Latar belakang BAB I PENDAHULUAN 1.1 Latar belakang Dalam proses pembuatan komponen-komponen atau peralatan-peralatan permesinan dan industri, dibutuhkan material dengan sifat yang tinggi maupun ketahanan korosi yang

Lebih terperinci